CN101665987A - Alloy germanium chinlon filament and production method thereof - Google Patents
Alloy germanium chinlon filament and production method thereof Download PDFInfo
- Publication number
- CN101665987A CN101665987A CN200910035442A CN200910035442A CN101665987A CN 101665987 A CN101665987 A CN 101665987A CN 200910035442 A CN200910035442 A CN 200910035442A CN 200910035442 A CN200910035442 A CN 200910035442A CN 101665987 A CN101665987 A CN 101665987A
- Authority
- CN
- China
- Prior art keywords
- germanium
- chinlon
- alloy germanium
- crystal
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an alloy germanium chinlon filament and a production method thereof. The alloy germanium chinlon filament comprises the following components in percentage by weight: 2-6 percentof nano alloy germanium and 94-98 percent of chinlon 6 slice. The nano alloy germanium comprises a germanium crystal and a titanium crystal, wherein the weight ratio of the germanium crystal and thetitanium crystal is 3:1. Compared with the common chinlon filament fabric, the fabric made of the alloy germanium chinlon filament has the following technical advantages: far infrared ray function: the fabric can keep warm and promote blood circulation; (2) antistatic ability; (3) deodorization: nano alloy germanium is provided with large holes, has higher deodorizing ability and can repeatedly adsorb and decompose odor; (4) good air permeability, refreshing and comfort.
Description
Technical field
The present invention relates to a kind of functional nylon fibre, specifically, relate to a kind of chinlon filament that adds alloy germanium, belong to the chemical fibre field.
Background technology
Nylon fibre is the Chinese title of synthetic fiber nylon, and the translation title is " nylon ", " nylon " again, and formal name used at school is polyamide fibre, i.e. polyamide fiber.Because chemical fibre factory, Jinzhou is the factory of first synthetic polyamide fibre of China, therefore it named and be " polyamide fibre ".It is the earliest a synthetic fiber kind in the world, because function admirable, raw material resources are abundant, are widely used always.Powerful, ABRASION RESISTANCE is good, shelter has first of the fiber.Its ABRASION RESISTANCE is 10 times of cotton fiber, is 10 times of dry state viscose, is 140 times of hygrometric state fiber.Therefore, its durability is splendid.The elasticity and the elastic return of nylon fabric are fabulous, but yielding under the little external force, so its fabric variable fold in the process of wearing.Ventilating air permeability is poor, easily produces static.The hygroscopicity of nylon fabric belongs to better kind in synthetic fabrics, therefore more comfortable and easy to wear than terylene clothes with the clothes of polyamide fibre making.Good moth-resistant, decay resistance are arranged.Heat-resisting light resistance is all good inadequately, and ironing temperature should be controlled at below 140 ℃.In wearing use, must note the condition of washing, maintenance, in order to avoid the damage fabric.Nylon fabric belongs to light-duty fabric, only lists in synthetic fabrics after polypropylene fibre, the acrylic fabric, therefore, is fit to make anorak, water clothes etc.
Alloy germanium is the health product that Japan is in fashion always, and effect such as have anion, far infrared, stimulate circulation with on the market is made hold concurrently poly-health care and commodity attractive in appearance such as bracelet, necklace by a large amount of utilizations.Through the alloy germanium of high temperature surfaction, has powerful adsorption effect, adsorbable stink, steam etc.The made yarn of alloy germanium junction spar can discharge far infrared efficiently, have warming, function such as keep healthy, stimulate circulation, enhance metabolism.Alloy germanium junction crystal is a piezoelectric, and after piezo-electric crystal was subjected to external force, it just discharged anion automatically.Alloy germanium also has deodorization functions and passes to the function of heat energy fast in addition, and clothes is no longer sticked by sweat, makes the people more comfortable nice and cool in scorching environment.
Relevant product and production method thereof of alloy germanium being added in the chinlon filament do not arranged at present as yet.
Summary of the invention
The functional chinlon filament that the purpose of this invention is to provide a kind of new interpolation alloy germanium material makes the advantage of alloy germanium and polyamide fibre be able to fully concentrate.
Alloy germanium chinlon filament of the present invention comprises following two kinds of compositions according to percentage by weight:
Nano alloy germanium 2-6%
Chinlon 6 section 94-98%,
Said nano alloy germanium comprises germanium crystal and titanium crystallization, and wherein, the weight ratio of germanium crystal and titanium crystallization is 3: 1.
Preferably, alloy germanium chinlon filament of the present invention comprises following two kinds of compositions according to percentage by weight:
Nano alloy germanium 4%
Chinlon 6 section 96%,
Said nano alloy germanium comprises germanium crystal and titanium crystallization, and wherein, the weight ratio of germanium crystal and titanium crystallization is 3: 1.
The production method of alloy germanium chinlon filament of the present invention is characterized in that, carries out spinning by melt spinning process, mainly may further comprise the steps:
(1) drying: chinlon 6 section and nano alloy germanium are carried out drying;
(2) preparation spin fluid:, utilize master batch output note pump accurately to add nano alloy germanium, with the chinlon 6 section mixed melting according to certain ratio;
(3) spinning: the fine high poly-melt of the one-tenth of fusion is extruded from the spinneret orifice of spinning head, and cooled and solidified becomes silk in the air (or water) around, in process of production, keeps stable temperature, humidity and pressure, and the temperature in the spinning process is 255~258 ℃;
(4) back processing: with the fiber of making carry out successively draw-teisting, after twist, compress and wash, drying, HEAT SETTING, balance, rewinding, packing and inspection process, finally obtain the finished product alloy germanium chinlon filament.
The fabric that alloy germanium chinlon filament of the present invention is made has following technique effect with respect to the nylon fibre fabric of routine: (1) far infrared function, can hold warming the stimulating circulation of temperature; (2) antistatic effect; (3) deodorizing: nano alloy germanium has big hole, has stronger deodorizing capability, can repeat absorption and decompose odor; (4) good permeability is clearly comfortable.
The specific embodiment
The present invention is further illustrated below in conjunction with embodiment, but the scope of protection of present invention is not limited to the scope that embodiment represents.
Embodiment 1
In the present embodiment, the raw material of alloy germanium chinlon filament composition and production method step are as follows:
1, raw material and percentage by weight:
Nano alloy germanium 60g,
Chinlon 6 section 2940g
Wherein, comprise 45g germanium and the crystallization of 15g titanium in the 60g nano alloy germanium.
2, method: carry out spinning by melt spinning process, mainly may further comprise the steps:
(1) drying: chinlon 6 section and nano alloy germanium are carried out drying;
(2) preparation spin fluid:, utilize master batch output note pump accurately to add nano alloy germanium, with the chinlon 6 section mixed melting according to certain ratio;
(3) spinning: the fine high poly-melt of the one-tenth of fusion is extruded from the spinneret orifice of spinning head, and cooled and solidified becomes silk in the air (or water) around, in process of production, keeps stable temperature, humidity and pressure, and the temperature in the spinning process is 255~258 ℃;
(4) back processing: with the fiber of making carry out successively draw-teisting, after twist, compress and wash, drying, HEAT SETTING, balance, rewinding, packing and inspection process, finally obtain the finished product alloy germanium chinlon filament.
Embodiment 2
In the present embodiment, the raw material of alloy germanium chinlon filament composition and production method step are as follows:
1, raw material and percentage by weight:
Nano alloy germanium 180g
Chinlon 6 section 2820g
Wherein, comprise 135g germanium and the crystallization of 45g titanium in the 180g nano alloy germanium.
2, method: identical with embodiment 1.
Embodiment 3
In the present embodiment, the raw material of alloy germanium chinlon filament composition and production method step are as follows:
1, raw material and weight:
Nano alloy germanium 120g
Chinlon 6 section 2880g
Wherein, comprise 90g germanium and the crystallization of 30g titanium in the 120g nano alloy germanium.
2, method: identical with embodiment 1.
Claims (3)
1, alloy germanium chinlon filament is characterized in that, comprises following two kinds of compositions according to percentage by weight:
Nano alloy germanium 2-6%
Chinlon 6 section 94-98%.
Said nano alloy germanium comprises germanium crystal and titanium crystallization, and wherein, the weight ratio of germanium crystal and titanium crystallization is 3: 1.
2, alloy germanium chinlon filament according to claim 1 is characterized in that, comprises following two kinds of compositions according to percentage by weight:
Nano alloy germanium 4%
Chinlon 6 section 96%,
Said nano alloy germanium comprises germanium crystal and titanium crystallization, and wherein, the weight ratio of germanium crystal and titanium crystallization is 3: 1.
3, the production method of a kind of claim 1 or 2 described alloy germanium chinlon filaments is characterized in that, carries out spinning by melt spinning process, mainly may further comprise the steps:
(1) drying: chinlon 6 section and nano alloy germanium are carried out drying;
(2) preparation spin fluid:, utilize master batch output note pump accurately to add nano alloy germanium, with the chinlon 6 section mixed melting according to certain ratio;
(3) spinning: the fine high poly-melt of the one-tenth of fusion is extruded from the spinneret orifice of spinning head, and cooled and solidified becomes silk in the air (or water) around, in process of production, keeps stable temperature, humidity and pressure, and the temperature in the spinning process is 255~258 ℃;
(4) back processing: with the fiber of making carry out successively draw-teisting, after twist, compress and wash, drying, HEAT SETTING, balance, rewinding, packing and inspection process, finally obtain the finished product alloy germanium chinlon filament.