CN101654835A - 一种高硅氧玻璃纤维厚布及其制造工艺 - Google Patents

一种高硅氧玻璃纤维厚布及其制造工艺 Download PDF

Info

Publication number
CN101654835A
CN101654835A CN200910032193A CN200910032193A CN101654835A CN 101654835 A CN101654835 A CN 101654835A CN 200910032193 A CN200910032193 A CN 200910032193A CN 200910032193 A CN200910032193 A CN 200910032193A CN 101654835 A CN101654835 A CN 101654835A
Authority
CN
China
Prior art keywords
glass fiber
silica glass
high silica
fiber cloth
thick high
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910032193A
Other languages
English (en)
Other versions
CN101654835B (zh
Inventor
尤勇
贺新民
贺广东
刘玉军
贾永梅
杨继喜
贺恒山
周建东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU HENGZHOU SPECIAL GLASS FIBRE MATERIAL CO Ltd
Original Assignee
JIANGSU HENGZHOU SPECIAL GLASS FIBRE MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU HENGZHOU SPECIAL GLASS FIBRE MATERIAL CO Ltd filed Critical JIANGSU HENGZHOU SPECIAL GLASS FIBRE MATERIAL CO Ltd
Priority to CN2009100321938A priority Critical patent/CN101654835B/zh
Publication of CN101654835A publication Critical patent/CN101654835A/zh
Application granted granted Critical
Publication of CN101654835B publication Critical patent/CN101654835B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高硅氧玻璃纤维厚布及其制造工艺，以原始钠硼硅酸盐玻璃纤维原纱为原料，制造工艺工艺包括坯布织造、酸沥滤、水清洗、热处理、后表面处理等。经过上述工艺制备的高硅氧玻璃纤维厚布，二氧化硅含量大于96％。外观平整，颜色均匀一致，能很好的适用于各种后加工制造工艺。耐高温性能优异，可以长期适用于1100℃以下，具有良好的烧蚀性能。广泛应用于制造精密仪表热防护件、烧蚀材料、绝热保温材料等。

Description

一种高硅氧玻璃纤维厚布及其制造工艺
技术领域
本发明涉及一种耐高温布及其制造工艺，具体涉及一种耐高温的高硅氧玻璃纤维厚布及其制造工艺，属于特种新材料领域。
背景技术
高硅氧玻璃纤维厚布具有耐高温、耐烧蚀、绝热、防火等优点，在较高温度下具有稳定的热性能和介电性能。应用范围很广，尤其在高性能防热领域内有着重要的应用。
发明内容
本发明通过以下技术方案实现：
一种耐高温的高硅氧玻璃纤维厚布的制造工艺，包括以下工艺步骤：
(1).将原始钠硼硅酸盐玻璃纤维原纱通过整经工艺，制备盘头，使用织机织成一定规格(本产品中为1.20mm)的玻璃纤维坯布。
(2).将坯布均匀排布在一组支撑杆上，整体放入到酸沥滤槽内，选择浓度为1.5～3.0mol/L的盐酸注入酸沥滤槽中，在85℃～95℃下处理2.5～4小时，同时使用耐酸泵进行循环搅拌。
(3).酸处理完成后，先进行布的表面喷淋处理去除表面余酸，然后浸泡在清水中，在40℃～60℃温度下水洗。水洗完成后使用PH试纸测试布的表面含酸状态，当PH值大于5时水洗完成。
(4).接着在连续式热处理炉内进行热定型处理，温度为600℃～750℃，处理时间为1小时～2小时。
(5).最后在热处理炉末端进行表面处理，经过浸胶槽浸胶，而后进入立式烘道烘干，在100℃～220℃温度下烘干40分钟～60分钟，烘干后的布经对辊摩擦卷取后即得到成品高硅氧玻璃纤维厚布。
产品规格及理化性能
Figure G2009100321938D00021
本发明的有益效果是：
经过上述工艺制备的高硅氧玻璃纤维厚布，二氧化硅含量大于96％。外观平整，颜色均匀一致，能很好的适用于各种后加工制造工艺。耐高温性能优异，可以长期适用于1100℃以下，具有良好的烧蚀性能。广泛应用于制造精密仪表热防护件、烧蚀材料、绝热保温材料等。
附图说明
附图为本发明工艺流程图。
具体实施方式
实施例一：
(1).将原始钠硼硅酸盐玻璃纤维原纱通过整经工艺，制备盘头，使用织机织成一定规格(本产品定为1.20mm)的玻璃纤维坯布。
(2).将坯布均匀排布在一组支撑杆上，整体放入到酸沥滤槽内，选择浓度为1.5mol/L的盐酸注入酸沥滤槽中，在85℃下处理3小时，同时使用耐酸泵进行循环搅拌。
(3).酸处理完成后，先进行布的表面喷淋处理去除表面余酸，然后浸泡在清水中，在40℃温度下水洗。水洗完成后使用PH试纸测试布的表面含酸状态，当PH值大于5时水洗完成。
(4).接着在连续式热处理炉内进行热定型处理，温度为600℃，处理时间为1.5小时。
(5).最后在热处理炉末端进行表面处理，经过浸胶槽浸胶，而后进入立式烘道烘干，在100℃～220℃温度下烘干40分钟，烘干后的布经对辊摩擦卷取后即得到成品高硅氧玻璃纤维厚布。
实施例二
(1).将原始钠硼硅酸盐玻璃纤维原纱通过整经工艺，制备盘头，使用织机织成一定规格(本产品定为1.20mm)的玻璃纤维坯布。
(2).将坯布均匀排布在一组支撑杆上，整体放入到酸沥滤槽内，选择浓度为3.0mol/L的盐酸注入酸沥滤槽中，在90℃下处理3.5小时，同时使用耐酸泵进行循环搅拌。
(3).酸处理完成后，先进行布的表面喷淋处理去除表面余酸，然后浸泡在清水中，在50℃温度下水洗。水洗完成后使用PH试纸测试布的表面含酸状态，当PH值大于5时水洗完成。
(4).接着在连续式热处理炉内进行热定型处理，温度为700℃，处理时间为1小时。
(5).最后在热处理炉末端进行表面处理，经过浸胶槽浸胶(，而后进入立式烘道烘干，在100℃～220℃温度下烘干1小时，烘干后的布经对辊摩擦卷取后即得到成品高硅氧玻璃纤维厚布。
经以上过程得到的高硅氧玻璃纤维厚布布面平整，颜色均匀一致，表面光滑柔软，无明显瑕疵，二氧化硅含量大于96％，质量稳定。加工工艺性能优异，可以长期使用于1100℃之下。同时适合裁剪、缝合、打孔等后续加工操作。

Claims (6)

1.一种高硅氧玻璃纤维厚布及其制造工艺，以原始钠硼硅酸盐玻璃纤维原纱为原料，其特征在于工艺包括坯布织造、酸沥滤、水清洗、热处理、后表面处理等。
2.如权利要求1所述的一种高硅氧玻璃纤维厚布及其制造工艺，其特征在于将原始钠硼硅酸盐玻璃纤维原纱通过整经工艺，制备盘头，使用织机织成一定规格的玻璃纤维坯布。
3.如权利要求1所述的一种高硅氧玻璃纤维厚布及其制造工艺，其特征在于将坯布均匀排布在一组支撑杆上，整体放入到酸沥滤槽内，选择浓度为1.5～3.0mol/L的盐酸注入酸沥滤槽中，在85℃～95℃下处理1.5～3小时，同时利用酸液循环泵循环搅拌，加强离子交换反应。
4.如权利要求1所述的一种高硅氧玻璃纤维厚布及其制造工艺，其特征在于在40℃～60℃温度下水洗，使用PH试纸测试布的表面含酸状态，当PH值大于5时水洗完成。
5.如权利要求1所述的一种高硅氧玻璃纤维厚布及其制造工艺，其特征在于在连续式热处理炉内进行热定型处理，温度为600℃～750℃，处理时间为0.5小时～1.5小时。
6.如权利要求1所述的一种高硅氧玻璃纤维厚布及其制造工艺，其特征在于最后在热处理炉末端进行表面涂覆处理，将配置好的有机溶液注入浸胶槽，布经过浸胶槽溶液的浸润，而后经导入辊轴进入立式烘道烘干，温度为100℃～220℃，处理时间10分钟～60分钟。烘干后的布经对辊摩擦卷取后即得到成品高硅氧玻璃纤维厚布。
CN2009100321938A 2009-07-10 2009-07-10 一种高硅氧玻璃纤维厚布及其制造工艺 Active CN101654835B (zh)