CN101654593A - Method for preparing high-temperature resistant antibacterial non-stick paint - Google Patents
Method for preparing high-temperature resistant antibacterial non-stick paint Download PDFInfo
- Publication number
- CN101654593A CN101654593A CN200810030205A CN200810030205A CN101654593A CN 101654593 A CN101654593 A CN 101654593A CN 200810030205 A CN200810030205 A CN 200810030205A CN 200810030205 A CN200810030205 A CN 200810030205A CN 101654593 A CN101654593 A CN 101654593A
- Authority
- CN
- China
- Prior art keywords
- paint
- temperature resistant
- coating
- percent
- accounting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses high-temperature resistant antibacterial non-stick paint. The paint has remarkable antibacterial effect and obvious non-stick effect. A formulation of the paint basically comprises the following components: a, at least one resin accounting for 65 percent of the paint; b, wax powder accounting for 5 percent of the paint; and c, nano silver powder accounting for 0.2 to 0.6 percent of the paint. The formulation further comprises talc powder accounting for 5 percent of the paint, flatting powder accounting for 3.5 percent of the paint, butanone accounting for 6.6 to 7 percent of the paint, and carbon black accounting for 1.5 percent of the paint. The formulation further comprises dispersing aid accounting for 2 percent of the paint, and non-stick aid accounting for 0.8percent of the paint. The paint has the following advantages of good thermal stability, remarkable environmentally-friendly and antibacterial effects, obvious non-stick effect and preferable performance in the aspects of corrosion resistance, adhesive force, innocuousness, hardness and the like. Meanwhile, the paint has simple manufacturing process, low cost and better application prospect, and can well meet the demands of domestic markets.
Description
[technical field]
The present invention relates to a kind of preparation method who is applied to the high-temperature resistant antibacterial non-stick paint of cooker medicine food and special purpose, belong to the chemistry painting industry technical field.
[background technology]
Non-viscous paint be a kind of coatingsurface be difficult for being adhered to by other viscous substances or adhere after the speciality coating that easily is removed.This kind coating is extremely low because of the surface energy of its coating that forms, non-stick property characteristics such as frictional coefficient is little, easy slip, is widely used in industries such as household electrical appliance, culinary art kitchen tools, automobile, machinery, chemical industry.Non-viscous paint more and more causes coating R﹠D work person's extensive concern as a kind of environment-friendly type speciality coating practical, with high content of technology.How the non-viscous paint technical sophistication at how disperseing the fluoro-resin micro mist, chooses binding resin, how to make mutual compatibility of each resin etc. be still the important topic of present development release coating.Non-viscous paint world demand amount in recent years increases with annual 20%～25% speed.The research and development of China's non-viscous paint also are in the starting stage, and product is also less, can't satisfy domestic demand far away.
Compare with the common non-viscous paint on the market, it is good etc. that this non-viscous paint system has a Heat stability is good, anti-adhesion effects, can be in-20 ℃ of-280 ℃ of scopes life-time service, the short period of time can anti-350 ℃ high temperature.The cooker undercoat that coating forms is at pancake, scrambled egg, fried fish, sticking and be easy to clean when boiling milk; Iron plate is sprayed with this coating, and is when ironing clothes, smooth and pollution resistance good; More superior in aspect performances such as corrosion-resistant, sticking power, nontoxic, hardness.Except that indivedual media, can anti-various acid, alkali, salt and organic medium (solvent); Hardness can not occur scratching delamination with 3H pencil power paddling with the 1-2 kilogram on coating; Good with the metal bonding performance, coating adhesion is strong, and it is once sintered to carry out primary coating, to improve the work efficiency save energy; Because the solid constituent of coating is nontoxic, contains ammonium perfluorocaprylate anything but, it is reasonable to form technology, so coating is nontoxic, can be widely used in cooker, medicine, food product containers etc.
But, be easy to breed bacteria because most of coating are basic ingredient with the organic compound all.And some malignant bacterias just might influence the healthy of people.Medical research shows that the generation of human diseases is exactly by due to various harmful germs and the virus.Non-viscous paint contacts with the mankind frequently especially, interwoveness.
[summary of the invention]
The purpose of present technique invention is to overcome the weak point that prior art exists, and a kind of practicality, high temperature resistant, antibacterial non-stick paint technology of preparing are provided in the non-viscous paint field.
At present, coating mainly contains natural antibacterial agent, organic antibacterial agent, inorganic antiseptic three major types with antiseptic-germicide, inorganic antiseptic is nanometer silver particularly, because surface effects, its antibacterial ability is that the micro nanometer silver ionic is more than 200 times, anti-microbial property also is far longer than traditional silver ion disinfectant, along with coating industry is strict further to the control of the harmful organic compound content of volatility, if there is harmful microorganism in film coated surface, after human body contacts, also can infect various diseases, threaten HUMAN HEALTH.Therefore, in coating, add a small amount of nano-silver powder, make it have anti-microbial property and have practical significance.
For achieving the above object, the present invention takes following technical scheme: the nanometer silver powder of a kind of high-temperature resistant organic silicon resin, the tetrafluoroethylene wax powder that cannot not play stickingly effect, a germicidal action is mixed.
Coating of the present invention also further comprises talcum powder, flatting silica, butanone, carbon black.
For making coating of the present invention reach better effect, increased esters solvent, this esters solvent is a 1-Methoxy-2-propyl acetate
For obtaining more superior performance, coating of the present invention also adds dispersing auxiliary.
Coating raw material of the present invention adopts high speed dispersion and grinds, and adds not sticking auxiliary agent then, obtains high-temperature resistant antibacterial non-stick paint.
Compare with existing coating technology, coating of the present invention has the following advantages: antibacterial effect significantly, sticking effect is obvious.Manufacturing process is simple, with low cost simultaneously, has application promise in clinical practice.
[embodiment]
At first modified, high temperature resistant silicone resin, tetrafluoroethylene wax powder, filler, nanometer silver, toner, solvent, dispersing auxiliary are mixed the basket sand milling in back to fineness less than 10um, add sticking auxiliary agent then and be modulated into finished product.Below in conjunction with specific embodiment the present invention is specifically described.
Specific embodiment 1
Modified, high temperature resistant silicone resin 65%
Tetrafluoroethylene wax powder 5%
Talcum powder 5%
Flatting silica 3.5%
Carbon black 1.5%
1-Methoxy-2-propyl acetate 10%
Butanone 7%
Nanometer silver 0.2%
Dispersing auxiliary 2%
Not sticking auxiliary agent 0.8%
The manufacture method of present embodiment is:
1) at first with the modified, high temperature resistant silicone resin, tetrafluoroethylene wax powder, talcum powder, carbon black, nanometer silver, 1-Methoxy-2-propyl acetate, butanone, dispersing auxiliary drop into conventional dispersion machine respectively and carry out middling speed dispersion 20-30 minute;
2) blending dispersion, with talcum powder, carbon black, nanometer silver and flatting silica are thrown into respectively in the shredder of original dispersion resin and auxiliary agent, make them carry out high speed jointly and grind to disperse, ground 2-3 hour at a high speed, up to fineness less than 10 microns;
3) add not sticking auxiliary agent, stir, make high-temperature resistant antibacterial non-stick paint.
The anti-microbial property experiment of high-temperature resistant antibacterial non-stick paint reaches GB15972-2002 with reference to quality, GB15981-1955, and detection method and the standard of the standard A STMG22-96 of American Society for Testing and Materials.After the testing sample drying, 0.2 milliliter of bacterium liquid to be measured is evenly dripped on sample respectively, cover with film, put in the sterilising vessel, 36 ℃ of temperature, humidity 90%RH places after 24 hours down, add 20 milliliters of elutriants respectively, abundant vibration wash-out, switching NA substratum carries out the viable bacteria numeration, carrying nano silver antibiotic paint sample with do not add anti-biotic material synthetic coating in the same old way recovery bacterium number calculated its antibiotic rate.
The high-temperature resistant antibacterial non-stick paint that present embodiment obtains contains tetrafluoroethylene wax 5%, nanometer silver 0.2%, 300 ℃ were toasted 15 minutes: film coated surface is smooth, 5 of 200 ℃ of continuous fried egg, non-stick pan, use streptococcus aureus and intestinal bacteria to carry out the Performance Detection of antibiotic paint according to aforementioned antibiotic method, it is respectively 98.2% and 98.5% to streptococcus aureus and colibacillary bacteriostasis rate.
Specific embodiment 2
Modified, high temperature resistant silicone resin 65%
Tetrafluoroethylene wax powder 5%
Talcum powder 5%
Flatting silica 3.5%
Carbon black 1.5%
1-Methoxy-2-propyl acetate 10%
Butanone 6.8%
Nanometer silver 0.4%
Dispersing auxiliary 2%
Not sticking auxiliary agent 0.8%
The manufacture method of present embodiment is:
1) at first with the modified, high temperature resistant silicone resin, tetrafluoroethylene wax powder, talcum powder, carbon black, nanometer silver, 1-Methoxy-2-propyl acetate, butanone, dispersing auxiliary drop into conventional dispersion machine respectively and carry out middling speed dispersion 20-30 minute;
2 blending dispersion, with talcum powder, carbon black, nanometer silver and flatting silica are thrown into respectively in the shredder of original dispersion resin and auxiliary agent, make them carry out high speed jointly and grind to disperse, ground 2-3 hour at a high speed, up to fineness less than 10 microns;
3) add not sticking auxiliary agent, stir, make high-temperature resistant antibacterial non-stick paint.
The high-temperature resistant antibacterial non-stick paint that present embodiment obtains contains tetrafluoroethylene wax 5%, and 0.2%, 300 ℃ of nanometer silver baking 15 minutes: film coated surface is smooth, 5 of 200 ℃ of continuous fried egg, non-stick pan; Use streptococcus aureus and intestinal bacteria to carry out the Performance Detection of antibiotic paint according to aforementioned antibiotic method, it is respectively 98.6% and 98.8% to streptococcus aureus and colibacillary bacteriostasis rate.
Specific embodiment 3
Modified, high temperature resistant silicone resin 65%
Tetrafluoroethylene wax powder 5%
Talcum powder 5%
Flatting silica 3.5%
Carbon black 1.5%
1-Methoxy-2-propyl acetate 10%
Butanone 6.6%
Nanometer silver 0.6%
Dispersing auxiliary 2%
Not sticking auxiliary agent 0.8%
The manufacture method of present embodiment is:
1) at first with the modified, high temperature resistant silicone resin, tetrafluoroethylene wax powder, talcum powder, carbon black, nanometer silver, 1-Methoxy-2-propyl acetate, butanone, dispersing auxiliary drop into conventional dispersion machine respectively and carry out middling speed dispersion 20-30 minute;
2 blending dispersion, with talcum powder, carbon black, nanometer silver and flatting silica are thrown into respectively in the shredder of original dispersion resin and auxiliary agent, make them carry out high speed jointly and grind to disperse, ground 2-3 hour at a high speed, up to fineness less than 10 microns;
3) add not sticking auxiliary agent, stir, make high-temperature resistant antibacterial non-stick paint.
The high-temperature resistant antibacterial non-stick paint that present embodiment obtains contains tetrafluoroethylene wax 5%, nanometer silver 0.2%, 300 ℃ were toasted 15 minutes: film coated surface is smooth, 5 of 200 ℃ of continuous fried egg, non-stick pan, use streptococcus aureus and intestinal bacteria to carry out the Performance Detection of antibiotic paint according to aforementioned antibiotic method, it is respectively 98.8% and 98.8% to streptococcus aureus and colibacillary bacteriostasis rate.
Show through testing repeatedly, the not viscosity of this high temperature antibacterial non-stick paint all keeps good, the germ resistance aspect, use streptococcus aureus and intestinal bacteria to carry out the Performance Detection of antibiotic paint according to aforementioned antibiotic method, its to streptococcus aureus and colibacillary bacteriostasis rate all more than 98%.
The physicochemical property of nano-antibacterial non-viscous paint
| Test item | Technical indicator |
| Paint film appearance | Smooth smooth |
| Time of drying | 320-340 ℃ 15 minutes |
| Viscosity (rock field 2#) | 35 seconds/26 ℃ |
| Proportion | ??1.05-1.10 |
| Solid content (300 ℃ 15 minutes) | ??44％ |
| Thickness | ??15-20um |
| Gloss (60 ° of glossometers) | ??45-60° |
| Hardness (Mitsubishi's pencil) | ??3H |
| Viscosity (egg) not | 5 |
| Sticking power (hundred lattice, 3M adhesive tape) | 0 grade |
| Temperature tolerance (200 ℃ dry combustion method 2 hours) | The film coated surface no change, nondiscoloration |
| Antibiotic rate (streptococcus aureus and intestinal bacteria) | More than 98% |
Claims (9)
1, a kind of high-temperature resistant antibacterial non-stick paint is characterized in that: this formulation for coating material comprises following component: a, at least a resin substantially, accounts for the ratio 65% of coating; B, wax powder account for the ratio 5% of coating; C, nano-silver powder account for the ratio 0.2%-0.6% of coating.
2, a kind of high-temperature resistant antibacterial non-stick paint according to claim 1 is characterized in that: also further comprise talcum powder, account for the ratio 5% of coating.
3, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1, it is characterized in that: also further comprise flatting silica, account for the ratio 3.5% of coating.
4, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1, it is characterized in that: also further comprise butanone, account for the ratio 6.6%-7% of coating.
5, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1, it is characterized in that: also further comprise carbon black, account for the ratio 1.5% of coating.
6, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1 to 5, it is characterized in that: described resin is a high-temperature resistant organic silicon resin.
7, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1 to 5, it is characterized in that: described esters solvent is a 1-Methoxy-2-propyl acetate, accounts for the ratio 10% of coating.
8, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1 to 5, it is characterized in that: also further comprise dispersing auxiliary, account for the ratio 2% of coating.
9, according to the described a kind of high-temperature resistant antibacterial non-stick paint of claim 1 to 5, it is characterized in that: also further cannot not comprise stickingly auxiliary agent, account for the ratio 0.8% of coating.