CN101653879A - 一种Zn-Mg-Al镁合金钎焊钎料 - Google Patents

一种Zn-Mg-Al镁合金钎焊钎料 Download PDF

Info

Publication number
CN101653879A
CN101653879A CN200910092580A CN200910092580A CN101653879A CN 101653879 A CN101653879 A CN 101653879A CN 200910092580 A CN200910092580 A CN 200910092580A CN 200910092580 A CN200910092580 A CN 200910092580A CN 101653879 A CN101653879 A CN 101653879A
Authority
CN
China
Prior art keywords
brazing
magnesium alloy
solder
filler metal
joint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910092580A
Other languages
English (en)
Other versions
CN101653879B (zh
Inventor
贺定勇
李晓延
马力
崔丽
蒋建敏
王智慧
周正
班书英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing University of Technology
Original Assignee
Beijing University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing University of Technology filed Critical Beijing University of Technology
Priority to CN2009100925800A priority Critical patent/CN101653879B/zh
Publication of CN101653879A publication Critical patent/CN101653879A/zh
Application granted granted Critical
Publication of CN101653879B publication Critical patent/CN101653879B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种Zn－Mg－Al镁合金钎焊钎料属于镁合金焊接连接技术领域。本发明所提供的Zn－Mg－Al镁合金钎焊钎料的化学成分及其质量百分比为：Al：10～13％，Mg：18～20％，余量为Zn。本发明所提供的Zn－Mg－Al镁合金钎焊钎料的熔化温度范围为379～488℃，钎焊温度范围为500～510℃，可适用于固相线温度在510℃以上的镁合金的钎焊。使用该钎料在高频感应钎焊的方式下钎焊AZ31B镁合金，钎焊搭接接头抗剪强度在43～45MPa之间，钎焊对接接头抗拉强度在59～62MPa之间。

Description

一种Zn-Mg-Al镁合金钎焊钎料
技术领域
本发明涉及一种Zn-Mg-Al镁合金钎焊钎料，属于镁合金焊接连接技术领域。
背景技术
镁及其镁合金是目前金属结构材料中最轻的一种，具有密度低、比强度高、减振性好、电磁屏蔽性好、导电导热性好、加工性好、热成形性好、易回收等优点而备受青睐。在汽车、电子、电器、交通、航天、航空和国防军事工业领域具有极其重要的应用价值和广阔的应用前景。但是，目前已商业应用的镁合金钎料品种很少，如美国的BMg-1(美国试验材料学会牌号AZ92A)、BMg-2a(美国试验材料学会牌号AZ125A)钎料钎焊温度范围分别是604～616℃和582～610℃，此钎焊温度太高，且配以的钎剂熔点温度也较高(538℃以上)，[Committee on brazing and soldering.BrazingManual[M].Third edition revised，1975，161-168.]。日本的MC 3标准镁合金钎料的成分非常接近于美国的BMg-1，该钎料钎焊温度范围是605～615℃，此钎焊温度也太高。因此，上述的三种镁合金钎料只适用于钎焊AZ10A、K1A、M1A等几种镁合金，并不适用于钎焊广泛应用的如Mg-Al-Zn系、Mg-Zn-Zr系、Mg-Mn系等镁合金。日本新研发的一种镁合金钎料In-Mg-Zn-Al(钎料熔化温度范围在449～490℃)中含有大量的贵重金属In(铟)，其中In的质量百分比占到了65％左右，使得钎料成本明显提高[T.Watanabe，S.Komatsu，K.Oohara.Development of flux and filler metal for brazingmagnesium alloy AZ31B[J].Welding Journal，2005，84(3)：37-40.]。另外日本新研发的镁合金钎料Mg-Sn-In-Al(钎料熔化温度范围在457～500℃)中In质量百分比占到了20％左右，钎料成本也较高。[T.Watanabe，K.Oohara.Brazing of AZ31B magnesium alloy sheet[c].Conference onprocessing and manufacturing of advanced materials，Thermec 2006，2007，1603-1608.]。
因此，研制一种钎焊温度合适、价格低廉、易获得、工艺性能优良、接头综合性能良好的钎料就成为镁合金结构件连接制造中急需解决的技术问题。
另一方面，由于产品轻量化的需求，对应用广泛的一些镁合金进行钎焊的需求越来越迫切。因此研究开发这些镁合金钎焊所需的低熔点钎料，并使其付诸实施成为镁合金结构件制造过程中凾待解决的关键技术之一。
发明内容
本发明的目的是提供一种具有较低钎焊温度的Zn-Mg-Al镁合金钎焊钎料。
本发明所提供的Zn-Mg-Al镁合金钎焊钎料的化学成分及其质量百分比为：Al：10～13％，Mg：18～20％，余量为Zn。
本发明所提供的Zn-Mg-Al镁合金钎焊钎料采用熔剂保护法进行熔炼。钎料可以以块状、棒状、粒状、片状等形式使用。块状、粒状钎料可以熔炼后采用机械方法获得；棒状、片状钎料可以采用精密铸造方法获得。本发明所提供的Zn-Mg-Al镁合金钎焊钎料可以采用保护气氛钎焊、感应钎焊、炉中钎焊、火焰钎焊、浸沾钎焊、超声波钎焊等工艺用于固相线温度在510℃以上的镁合金及其构件的钎焊。
本发明具有以下有益效果：
本发明所提供的Zn-Mg-Al镁合金钎焊钎料的熔化温度范围为379～488℃，钎焊温度范围为500～510℃。在此钎焊温度下，钎料具有良好的铺展性和间隙填充性，可适用于固相线温度在510℃以上的镁合金的钎焊。尤其是采用高频感应钎焊工艺钎焊AZ31B镁合金接头时，只对接头部分加热，母材其余部分被加热较少，可有效地避免AZ31B镁合金基体材料的氧化和过烧，钎焊搭接接头抗剪强度在43～45MPa之间，钎焊对接接头抗拉强度在59～62MPa之间。
以下结合具体实施方式对本发明作进一步说明。
具体实施方式
实施例1：
钎料的化学成分及其质量百分比为：Al：11.6％，Mg：18.0％，余量为Zn。采用熔剂保护法进行钎料合金熔炼，浇注成铸锭，然后采用机械分割将钎料分成长条块状。钎焊前AZ31B镁合金试样经砂纸打磨、丙酮清洗去除表面污物，钎料置于接头处，并在接头及钎料部位均匀撒布钎剂，接头由夹具固定后放入氩气保护装置进行高频感应钎焊。钎焊过程中氩气流量为0.3L/min，升温速度为300℃/min，钎焊温度范围为500～510℃，保温120s后，冷却至室温。钎焊后，接头外观成形良好，测定钎焊接头抗剪强度和抗拉强度，结果如表1中所示。
实施例2
钎料的化学成分及其质量百分比为：Al：10.2％，Mg：19.8％，余量为Zn。采用熔剂保护法进行钎料合金熔炼，浇注成铸锭，然后采用机械分割将钎料分成长条块状。钎焊前AZ31B镁合金试样经砂纸打磨、丙酮清洗去除表面污物，钎料置于接头处，并在接头及钎料部位均匀撒布钎剂，接头由夹具固定后放入氩气保护装置进行高频感应钎焊。钎焊过程中氩气流量为0.3L/min，升温速度为300℃/min，钎焊温度范围为500～510℃，保温120s后，冷却至室温。钎焊后，接头外观成形良好，测定钎焊接头抗剪强度和抗拉强度，结果如表1中所示。
实施例3
钎料的化学成分及其质量百分比为：Al：13.0％，Mg：20.0％，余量为Zn。采用熔剂保护法进行钎料合金熔炼，浇注成铸锭，然后采用机械分割将钎料分成长条块状。钎焊前AZ31B镁合金试样经砂纸打磨、丙酮清洗去除表面污物，钎料置于接头处，并在接头及钎料部位均匀撒布钎剂，接头由夹具固定后放入氩气保护装置进行高频感应钎焊。钎焊过程中氩气流量为0.3L/min，升温速度为300℃/min，钎焊温度范围为500～510℃，保温120s后，冷却至室温。钎焊后，接头外观成形良好，测定钎焊接头抗剪强度和抗拉强度，结果如表1中所示。
Figure G2009100925800D00041
表1、实施例1-3中制备的钎料的化学成分及质量百分比以及钎焊接头力学性能

Claims (1)

1.一种Zn-Mg-Al镁合金钎焊钎料，其特征在于，所述钎料的化学成分及其质量百分比为：Al：10～13％，Mg：18～20％，余量为Zn。
CN2009100925800A 2009-09-11 2009-09-11 一种用于镁合金钎焊的Zn-Mg-Al钎料 Expired - Fee Related CN101653879B (zh)