CN101647766A - Hairspray with function of repairing damaged hair - Google Patents

Abstract

The invention discloses a hairspray with the function of repairing damaged hair, comprising the following components by weight percent: 0.005% to 0.5% of plant extract, 0.01% to 0.2% of diglucoside gallic acid and the balance of auxiliary agent. A lotus extract is mixed with the diglucoside gallic acid for the first time through years of research, and a proper quantity of the auxiliary agent is added. The obtained hairspray can nourish the hair for long, repair the damaged hair, enhance the elasticity of the hair and especially keep the elasticity, nature, luster and softness of hair curves ofcurved hair which is curved chemically.

Description

Has the hairspray of repairing the damaged hair function

Technical field

The present invention relates to a kind of hairspray.

Background technology

Along with people's hair dyes the constantly frequent of soup, the hair quality of people's hair also obtains injury in various degree, hair becomes withered short-tempered lackluster because of impaired, fragile easily broken, and traditional moulding product such as: aqua products such as gel water, gel cream, mousse because add raw material limit, even having preferably, modeling effect can not solve the withered short-tempered worry of hair, what bring to consumer is stiff moulding sensation, and traditional moulding product has been difficult to satisfy the forming hair demand that consumer changes day by day.People press for a kind of moulding that can bring the flexible innervation of people simultaneously can allow withered short-tempered hair give hair good gloss enhancing hair flexible moulding product again.

Summary of the invention

The objective of the invention is to overcome the deficiency that existing hairspray exists, provide a kind of and can moisten hair lastingly, repair damaged hair, strengthen the elastic hairspray of hair.

To achieve these goals, the present invention adopts following technical scheme:

A kind of hairspray with reparation damaged hair function, form by following component and percetage by weight:

Plant extract 0.005%～0.5%, didextrose base gallic acid 0.01%～0.2%, surplus is an auxiliary agent.

In above-mentioned hairspray, described plant extract is to be prepared from by following method: plant is adopted microwave extracting, and extractant is a glycerine water solution.Plant optimization is a lotus, and described lotus comprises one or more mixture in Folium Nelumbinis, Flos Nelumbinis, Rhizoma Nelumbinis, the seedpod of the lotus, Plumula Nelumbinis, Semen Nelumbinis, the lotus belt.The frequency of described microwave extracting is preferably 300～300000MHz, preferred 100～150 ℃ of extraction temperature

In above-mentioned hairspray, preferred version is made up of following component and percetage by weight:

Plant extract 0.005%～5.0%, didextrose base gallic acid 0.01%～2.0%, cationic surfactant 0.1%～1.0%, hard fat chemical compound 0.1%～2.0%, cationic rheology modifier 0.3%～1.5%, silicone oil 1.5%～10%, cationic polymer 0.1～1.5%, be shaped into membrane polymer 0.5～5.0%, surplus is a deionized water.

Above-mentioned cationic surfactant is a quaternary ammonium salt, is selected from hexadecyltrimethylammonium chloride, octadecyl trimethyl ammonium chloride, INCROQUAT TMC-80 ECONOL TM22 and composition thereof.

Above-mentioned hard fat chemical compound is selected from spermol, stearyl alcohol, docosanol or its mixture.

Above-mentioned cationic rheology modifier is selected from chlorination Trimethylamine ethyl-methyl Voncoat R 3310.

Above-mentioned cationic polymer is selected from quaternized copolymer, acrylic acid/dimethyl-dipropenyl ammonium chloride copolymer, quaternised hydroxyethyl-cellulose, guar gum hydroxypropyl-trimethyl ammonium chloride, hydroxyethyl-cellulose/dialkyl dimethyl ammonium chloride copolymer or its mixture of acrylamide/dimethyl-dipropenyl ammonium chloride copolymer, vinylpyrrolidone/Methacrylamide oxypropyl trimethyl ammonium chloride copolymer, vinylpyrrolidone/decil methacrylate.

The above-mentioned membrane polymer that is shaped into is selected from polyvinylpyrrolidone, vinylpyrrolidone/vinyl acetate bipolymer, caprolactam/vinylpyrrolidone/dimethylamino ethyl methacrylate terpolymer, octyl group propionic acid amide ./acrylate/tert-butyl group amino-ethyl methacrylate copolymer, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer, polyquaternary amine-55, Onamer M 6 or its mixture.

The present invention adopts microwave-assisted extraction technique to extract effective ingredient in the plant, and the electromagnetic energy that microwave produces quickens to be extracted the effective ingredient of part to the extractant interfacial diffusion.In the microwave radiation process, high-frequency electromagnetic wave penetrates inner vascular bundle of medium and the glandular cell system of being extracted on the one hand.Because absorb microwave energy, the cell interior temperature rises rapidly, make its cell interior pressure surpass cell wall expansion ability to bear, cell rupture.Effective ingredient freely flows out in the cell, can be extracted capture medium and also dissolve under lower temperature conditions, further filters and separates, and just can obtain extract.On the other hand, the electromagnetic energy that microwave produces quickens to be extracted the effective ingredient of part to the extractant interfacial diffusion, during with the water body solvent, hydrone is subjected to the microwave action high speed rotating to become excited state, this high-energy labile state, strengthen the energy delivery that driving force discharged of extraction battery composition and give other material molecules, quicken its warm-up movement, shorten the extraction battery molecule by thing sample diffusion inside to the extractant circle time, make extraction rate improve several times, also reduce extraction temperature simultaneously, improved the extraction quality.

Compared with prior art, the present invention has following beneficial effect:

The present invention is mixed lotus extract and didextrose base gallic acid, and has added proper assistant through years of researches for the first time.Resulting hairspray can moisten hair lastingly, repairs damaged hair, strengthens hair elasticity; Particularly, can keep hai roll elasticity, natural, glossy, not stiff at hair crimping through the chemistry hair-waving.

The specific embodiment

Embodiment 1

Choose fresh lotus, get Folium Nelumbinis, Flos Nelumbinis, Rhizoma Nelumbinis, the seedpod of the lotus, Plumula Nelumbinis, Semen Nelumbinis and seven positions of lotus belt, under the condition of 120 ℃ of microwave frequency 3000MHz and temperature, adopt the glycerine water solution of mass fraction 50% to extract, obtain the lotus extract.Resulting lotus extract and didextrose base gallic acid and auxiliary agent are mixed, as shown in Table 1 and Table 2.

Table 1

	Comparative example	Embodiment 1	Embodiment 2	Embodiment 3	Embodiment 4
						16 octadecanol	??1.0	??1.0	??1.0	??1.0	??1.0
Hexadecyltrimethylammonium chloride	??1.0	??1.0	??1.0	??1.0	??1.0
						Nonionic emulsifier	??0.5	??0.5	??0.5	??0.5	??0.5
Glycerol	??5.0	??5.0	??5.0	??5.0	??5.0
						Acrylamide and dimethyl-dipropenyl ammonium chloride copolymer	??0.5	??0.5	??0.5	??0.5	??0.5
Chlorination Trimethylamine ethyl-methyl Voncoat R 3310	??1.0	??1.0	??1.0	??1.0	??1.0
						Oils and fats	??2.0	??2.0	??2.0	??2.0	??2.0
Silicone oil	??3.0	??3.0	??3.0	??3.0	??3.0
						Polyvinylpyrrolidone	??5.0	??5.0	??5.0	??5.0	??5.0
The lotus extract	??0	??0.5	??2.0	??5.0	??5.0
						Didextrose base gallic acid	??0	??0.5	??1.0	??2.0	??0.5
Antiseptic	??0.15	??0.15	??0.15	??0.15	??0.15
						Deionized water	??TO100	??TO100	??TO100	??TO100	??TO100

Table 2

	Embodiment 5	Embodiment 6	Embodiment 7	Embodiment 8
					16 octadecanol	??1.0	??1.0	??1.0	??1.0

Hexadecyltrimethylammonium chloride	??1.0	??1.0	??1.0	??1.0
					Nonionic emulsifier	??0.5	??0.5	??0.5	??0.5
Glycerol	??5.0	??5.0	??5.0	??5.0
					Acrylamide and dimethyl-dipropenyl ammonium chloride copolymer	??0.5	??0.5	??0.5	??0.5
Chlorination Trimethylamine ethyl-methyl Voncoat R 3310	??1.0	??1.0	??1.0	??1.0
					Oils and fats	??2.0	??2.0	??2.0	??2.0
Silicone oil	??3.0	??3.0	??3.0	??3.0
					Polyvinylpyrrolidone	??5.0	??5.0	??5.0	??5.0
The lotus extract	??2.0	??0.5	??5.0	??0
					Didextrose base gallic acid	??1.0	??2.0	??0	??2.0
Antiseptic	??0.15	??0.15	??0.15	??0.15
					Deionized water	??TO100	??TO100	??TO100	??TO100

The result compares:

After above product used, the comparative result of hair was as shown in table 3.

Table 3

	Comparative example	Embodiment 1	Embodiment 2	Embodiment 3	Embodiment 4	Embodiment 5	Embodiment 6	Embodiment 7	Embodiment 8
										Water contact angle (unit: degree)	??85.6	??92.5	??96.5	??102.5	??95.6	??115.2	??94.56	??98.8	??102.9
Short-tempered sensory evaluation scores	??2.6	??3.1	??3.2	??3.4	??3.5	??4.5	??3.6	??3.9	??4.0
										Hair style keeps persistency	??3.5	??3.9	??3.8	??4.0	??3.8	??4.8	??3.6	??3.5	??4.6

Moisture feeling

??3.0

??3.5

??3.5

??4.5

??4.4

??4.7

??3.5

??4.4

??4.0

In the table 3, water contact angle is to use instrument test, and other index is by the average mark after the evaluation group assessment of specialty.

Shown by above result: the water contact angle of embodiment 1-8, short-tempered sense, hair style keep persistency and moisture feeling all to improve significantly than comparative example.Wherein, every performance the best of embodiment 5.

Claims (8)

1, a kind of hairspray with reparation damaged hair function is characterized in that being made up of following component and percetage by weight:

Plant extract 0.005%～5.0%, didextrose base gallic acid 0.01%～2.0%, surplus is an auxiliary agent.

2, hairspray as claimed in claim 1 is characterized in that being made up of following component and percetage by weight:

Plant extract 0.005%～5.0%, didextrose base gallic acid 0.01%～2.0%, cationic surfactant 0.1%～1.0%, hard fat chemical compound 0.1%～2.0%, cationic rheology modifier 0.3%～1.5%, silicone oil 1.5%～10%, cationic polymer 0.1～1.5%, be shaped into membrane polymer 0.5～5.0%, surplus is a deionized water.

3, hairspray as claimed in claim 1, it is characterized in that described plant extract is to be prepared from by following method: plant is adopted microwave extracting, and extractant is a glycerine water solution.

4,, it is characterized in that described plant extract is the lotus extract as claim 1 or 2 or 3 described hairsprays.

5, hairspray as claimed in claim 5 is characterized in that described lotus extract is one or more mixture in Folium Nelumbinis, Flos Nelumbinis, Rhizoma Nelumbinis, the seedpod of the lotus, Plumula Nelumbinis, Semen Nelumbinis, the lotus belt.

6, hairspray as claimed in claim 2 is characterized in that described cationic surfactant is a quaternary ammonium salt;

Described hard fat chemical compound is selected from spermol, stearyl alcohol, docosanol or its mixture;

Described cationic rheology modifier is a chlorination Trimethylamine ethyl-methyl Voncoat R 3310;

Described cationic polymer is selected from quaternized copolymer, acrylic acid/dimethyl-dipropenyl ammonium chloride copolymer, quaternised hydroxyethyl-cellulose, guar gum hydroxypropyl-trimethyl ammonium chloride, hydroxyethyl-cellulose/dialkyl dimethyl ammonium chloride copolymer or its mixture of acrylamide/dimethyl-dipropenyl ammonium chloride copolymer, vinylpyrrolidone/Methacrylamide oxypropyl trimethyl ammonium chloride copolymer, vinylpyrrolidone/decil methacrylate;

The described membrane polymer that is shaped into is selected from polyvinylpyrrolidone, vinylpyrrolidone/vinyl acetate bipolymer, caprolactam/vinylpyrrolidone/dimethylamino ethyl methacrylate terpolymer, octyl group propionic acid amide ./acrylate/tert-butyl group amino-ethyl methacrylate copolymer, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer, polyquaternary amine-55, Onamer M 6 or its mixture.

7, hairspray as claimed in claim 3, the frequency that it is characterized in that described microwave extracting is 300～300000MHz.

8,, it is characterized in that described extraction temperature is selected from 100～150 ℃ as claim 3 or 7 described hairsprays.