CN101642795B - 聚苯乙烯泡沫消失模用涂料 - Google Patents

聚苯乙烯泡沫消失模用涂料 Download PDF

Info

Publication number
CN101642795B
CN101642795B CN2009101684248A CN200910168424A CN101642795B CN 101642795 B CN101642795 B CN 101642795B CN 2009101684248 A CN2009101684248 A CN 2009101684248A CN 200910168424 A CN200910168424 A CN 200910168424A CN 101642795 B CN101642795 B CN 101642795B
Authority
CN
China
Prior art keywords
stirring
coating
reactor
add
bentonite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009101684248A
Other languages
English (en)
Other versions
CN101642795A (zh
Inventor
孔德礼
刘汉伯
吴振海
李曙生
王崇高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAIZHOU JINCHANG METALLURGICAL EQUIPMENT CO Ltd
Original Assignee
TAIZHOU JINCHANG METALLURGICAL EQUIPMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAIZHOU JINCHANG METALLURGICAL EQUIPMENT CO Ltd filed Critical TAIZHOU JINCHANG METALLURGICAL EQUIPMENT CO Ltd
Priority to CN2009101684248A priority Critical patent/CN101642795B/zh
Publication of CN101642795A publication Critical patent/CN101642795A/zh
Application granted granted Critical
Publication of CN101642795B publication Critical patent/CN101642795B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属化工技术领域，涉及一种聚苯乙烯泡沫消失模用涂料及其制作方法，该涂料由铝矾土、刚玉粉、聚醋酸乙烯乳液、硫酸铝、磷酸氢二钠、膨润土、改性淀粉、苯甲酸钠、丁醇、无水碳酸钠、羧甲基纤维素、乙酸乙酯、壬基酚聚氧乙烯醚和水所组成。制作方法是，将水加入反应釜中，在搅拌状态下向反应釜中加入羧甲基纤维素，将釜温缓慢升至90℃，恒温搅拌10min，停止加热，在搅拌状态下向反应釜中加入硫酸铝，搅拌5min后依次向反应釜中加入磷酸氢二钠、苯甲酸钠、无水碳酸钠、膨润土、铝矾土、刚玉粉，继续搅拌30min后依次向反应釜中加入壬基酚聚氧乙烯醚、改性淀粉、聚醋酸乙烯乳液、丁醇、乙酸乙酯，再搅拌30min后制得涂料。

Description

聚苯乙烯泡沫消失模用涂料
所属技术领域
本发明属化工技术领域，涉及一种聚苯乙烯泡沫消失模用涂料及其制备方法。
背景技术
目前，国内外用于聚苯乙烯泡沫消失模的涂料不但品种少，而且还存在着透气性差、粘砂、铸造产品有皱皮以及冷隔和涂料生产成本较高的缺陷。
发明内容
本发明的目的是提供一种透气性好，不粘砂、铸件表面光滑、无冷隔、生产成本低的聚苯乙烯泡沫消失模专用涂料。
为了达到上述目的，本发明的一种聚苯乙烯泡沫消失模涂料主要由铝矾土、刚玉粉、聚醋酸乙烯乳液、硫酸铝、磷酸氢二钠、膨润土、改性淀粉、苯甲酸钠、丁醇、无水碳酸钠、羧甲基纤维素、乙酸乙酯、壬基酚聚氧乙烯醚和水所组成。其重量百分比为：(1)铝矾土(180～200目)占涂料总量的30～60％；(2)刚玉粉(200～300目)占涂料总量的10～30％；(3)聚醋酸乙烯乳液(固含量50％)占涂料总量的1～2％；(4)硫酸铝占涂料总量的2～4％；(5)磷酸氢二钠占涂料总量的0.1～0.5％；(6)膨润土占涂料总量的1～3％；(7)改性淀粉占涂料总量的1～3％；(8)苯甲酸钠占涂料总量的0.1～0.2％；(9)丁醇占涂料总量的0.01～0.02％；(10)无水碳酸钠占涂料总量的0.01～0.03％；(11)羧甲基纤维素占涂料总量的0.5～1.5％；(12)乙酸乙酯占涂料总量的0.01～0.02％；(13)壬基酚聚氧乙烯醚占涂料总量的0.01～0.02％；(14)水占涂料总量的30～40％。
具体实施方式：
将水加入反应釜中，开启反应釜的搅拌浆，搅拌速度为：80γ/min，在搅拌状态下向反应釜中加入羧甲基纤维素，开启反应釜的加热装置，将反应釜的温度缓慢升至90℃(升温速率为：2～5℃/min)，恒温搅拌10min，停止加热，在搅拌状态下向反应釜中加入硫酸铝，搅拌5min后依次向反应釜中加入磷酸氢二钠、苯甲酸钠、无水碳酸钠、膨润土、铝矾土、刚玉粉，继续搅拌30min，然后依次向反应釜中加入壬基酚聚氧乙烯醚、改性淀粉、聚醋酸乙烯乳液、丁醇、乙酸乙酯，再搅拌30min后出料。
本发明的有益效果是：
该涂料生产成本低，耐温性能好(可以耐温1600℃)，铸件表面光滑、无冷隔、不粘砂。
实施例1，将水(30％，重量百分比，以下相同)加入反应釜中，开启反应釜的搅拌浆，搅拌速度为：80γ/min，在搅拌状态下向反应釜中加入羧甲基纤维素(1％)，开启反应釜的加热装置，将反应釜的温度缓慢升至90℃(升温速率为：2～5℃/min)，恒温搅拌10min，停止加热，在搅拌状态下向反应釜中加入硫酸铝(2％)，搅拌5min后依次向反应釜中加入磷酸氢二钠(0.5％)、苯甲酸钠(0.1％)、无水碳酸钠(0.03％)、膨润土(2.84％)、铝矾土(40％)、刚玉粉(20％)，继续搅拌30min，然后依次向反应釜中加入壬基酚聚氧乙烯醚(0.01％)、改性淀粉(2％)、聚醋酸乙烯乳液(1.5％)、丁醇(0.01％)、乙酸乙酯(0.01％)，再搅拌30min后出料。
实施例2，将水(35％，重量百分比，以下相同)加入反应釜中，开启反应釜的搅拌浆，搅拌速度为：80γ/min，在搅拌状态下向反应釜中加入羧甲基纤维素(1.5％)，开启反应釜的加热装置，将反应釜的温度缓慢升至90℃(升温速率为：2～5℃/min)，恒温搅拌10min，停止加热，在搅拌状态下向反应釜中加入硫酸铝(3％)，搅拌5min后依次向反应釜中加入磷酸氢二钠(0.3％)、苯甲酸钠(0.15％)、无水碳酸钠(0.01％)、膨润土(2％)、铝矾土(30％)、刚玉粉(25％)，继续搅拌30min，然后依次向反应釜中加入壬基酚聚氧乙烯醚(0.01％)、改性淀粉(1％)、聚醋酸乙烯乳液(2％)、丁醇(0.01％)、乙酸乙酯(0.02％)，再搅拌30min后出料。

Claims (2)

1.一种聚苯乙烯泡沫消失模用涂料，其特征在于它是由铝矾土、刚玉粉、聚醋酸乙烯乳液、硫酸铝、磷酸氢二钠、膨润土、改性淀粉、苯甲酸钠、丁醇、无水碳酸钠、羧甲基纤维素、乙酸乙酯、壬基酚聚氧乙烯醚和水所组成，重量百分比为：铝矾土30～60％；刚玉粉10～30％；聚醋酸乙烯乳液1～2％；硫酸铝2～4％；磷酸氢二钠0.1～0.5％；膨润土1～3％；改性淀粉1～3％；苯甲酸钠0.1～0.2％；丁醇0.01～0.02％；无水碳酸钠0.01～0.03％；羧甲基纤维素0.5～1.5％；乙酸乙酯0.01～0.02％；壬基酚聚氧乙烯醚0.01～0.02％；水30～40％，各组分含量之和为100％。
2.根据权利要求1所述的一种聚苯乙烯泡沫消失模用涂料，其特征是制备时先将水加入反应釜中，在搅拌状态下向反应釜中加入羧甲基纤维素，将反应釜的温度缓慢升至90℃，恒温搅拌10min，停止加热，在搅拌状态下向反应釜中加入硫酸铝，搅拌5min后依次向反应釜中加入磷酸氢二钠、苯甲酸钠、无水碳酸钠、膨润土、铝矾土、刚玉粉，继续搅拌30min后依次向反应釜中加入壬基酚聚氧乙烯醚、改性淀粉、聚醋酸乙烯乳液、丁醇、乙酸乙酯，再搅拌30min后制得涂料。
CN2009101684248A 2009-08-18 2009-08-18 聚苯乙烯泡沫消失模用涂料 Expired - Fee Related CN101642795B (zh)