CN101412073A - 一种消失模铸造专用涂料 - Google Patents

一种消失模铸造专用涂料 Download PDF

Info

Publication number
CN101412073A
CN101412073A CNA2008102311599A CN200810231159A CN101412073A CN 101412073 A CN101412073 A CN 101412073A CN A2008102311599 A CNA2008102311599 A CN A2008102311599A CN 200810231159 A CN200810231159 A CN 200810231159A CN 101412073 A CN101412073 A CN 101412073A
Authority
CN
China
Prior art keywords
water
hours
weight
stirred
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008102311599A
Other languages
English (en)
Other versions
CN101412073B (zh
Inventor
李德全
李萌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2008102311599A priority Critical patent/CN101412073B/zh
Publication of CN101412073A publication Critical patent/CN101412073A/zh
Application granted granted Critical
Publication of CN101412073B publication Critical patent/CN101412073B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种消失模铸造专用涂料，它包括有粘接料1份，悬浮料3.34份，骨料50－56.66份，水56.67份，石油黄酸钠0.2份，消泡剂0.13份，该涂料的制备方法是：1.在悬浮料纤维素中加入其6－7倍重量的水，浸泡12小时，每小时搅拌一次，使纤维素在水中完全溶解；2.再取膨润土加入其重量6－7的水浸泡10小时，3.将聚乙烯醇一份加入6－7倍重量的水，加温至100－120℃，保持5－8小时；4.将以上三种用水溶解和浸泡的材料放入搅拌机中再加入剩余的水搅拌5小时，混合均匀后加入上述重量的石英砂和铝矾土搅拌6小时、混合均匀后再加入上述重量的消泡剂和石油黄酸钠搅拌3小时即为成品。用本发明生产的涂料生产的铸件的品质，档次及成品率均能达到进口产品的效果。

Description

一种消失模铸造专用涂料
技术领域：
本发明涉及涂料组合物，特别是一种适用于EPS塑料模样刷涂的消失模铸造专用涂料。
背景技术：
涂料是消失模铸造的关键技术之一，它的性能不仅影响模样的气化和气体的迁移，而且和铸件的表面质量、内部缺陷密切相关。它在铸造过程中的作用在于支撑和保护泡沫模型，防止液态金属渗入砂子和粘砂、吸收分解物并使分解气体通过涂层，保护泡沫模样挥发后形成的型腔完整，并保持液态金属热量不会很快散发。目前，我国不少消失模铸造企业使用的是美国亚什兰公司的涂料，也有使用国产涂料的，但存在的问题是价格昂贵。
发明内容：
本发明的目的是提供一种不但能用于生产高档铸造产品，而且价格低廉的消失模铸造专用涂料。
本发明的技术方案是以如下方式完成的，它包括有以下重量组分，粘接料1份，悬浮料3.34份，骨料50-56.66份，水56.67份，石油黄酸钠0.2份，消泡剂0.13份，上述原料组分的悬浮料中膨润土占80％，纤维素占20％，骨料中石英砂占60-66％，铝矾土占40-46％，该涂料的制备方法是；1、在悬浮料纤维素中加入其6-7倍重量的水，浸泡12小时，每小时搅拌一次每次5分钟，使纤维素在水中完全溶解；2再取膨润土加入其重量6-7的水浸泡10小时，3、将聚乙烯醇一份加入6-7倍重量的水，加温至100-120℃，保持5-8小时，使其完全溶于水；4、将以上三种用水溶解和浸泡的材料放入搅拌机中再加入剩余的水搅拌5小时，混合均匀后加入上述重量的石英砂和铝矾土搅拌6小时、混合均匀后再加入上述重量的消泡剂和石油黄酸钠搅拌3小时即为成品。用本发明生产的涂料，经反复试验证明具有以下效果，铸件的品质，档次及成品率均能达到进口产品的效果，成本是进口产品的1/8。
具体实施方式：
实施例1：①先取悬浮料中的纤维素0.667Kg，加入水4.002Kg，浸泡12小时，每小时搅拌5分钟，使其完全溶解于水，②再取悬浮料中的膨润土2.667Kg，加入水15.96Kg，浸泡10小时；③再在粘接剂聚乙烯醇1Kg中加入水7Kg，加温至100-120℃，保持5-8小时，使其完全溶解于水；④将以上三种用水溶解和浸泡的材料放入搅拌机中，再加入水29.708Kg，搅拌5小时，混合均匀后再加入石英砂33.33Kg和铝矾土20Kg搅拌6小时，最后加入消泡剂130g和石油黄酸钠200g，搅拌3小时即为成品涂料。这种涂料适用于大批量生产变矩器壳体。
实施例2：取纤维素0.733Kg，膨润土4Kg、聚乙烯醇1Kg、水56.67Kg，分别按实施例一的①、②、③步骤进行，将上述步骤处理的材料一并放搅拌机中加入剩余的水搅拌5小时，再加入石英砂30Kg，铝矾土23.333Kg搅拌6小时，最后加入消泡剂200g和石油黄酸钠300g搅拌3小时即为成品。这种涂料主要适用于泵体的批量生产。本发明解决了EPS泡沫塑料模样容易产生铸件缺陷的问题，达到了进口涂料的使用效果，使所生产的铸件品质、档次和成品率都有很大提高，同时还大大降低了铸造成本。

Claims (1)

1、一种消失模铸造专用涂料，其特征在于：它包括有以下重量组分，粘接料1份，悬浮料3.34份，骨料50-56.66份，水56.67份，石油黄酸钠0.2份，消泡剂0.13份，上述原料组分的悬浮料中膨润土占80％，纤维素占20％，骨料中石英砂占60-66％，铝矾土占40-46％，该涂料的制备方法是：1、在悬浮料纤维素中加入其6-7倍重量的水，浸泡12小时，每小时搅拌一次每次5分钟，使纤维素在水中完全溶解；2再取膨润土加入其重量6-7的水浸泡10小时，3、将聚乙烯醇一份加入6-7倍重量的水，加温至100-120℃，保持5-8小时，使其完全溶于水；4、将以上三种用水溶解和浸泡的材料放入搅拌机中再加入剩余的水搅拌5小时，混合均匀后加入上述重量的石英砂和铝矾土搅拌6小时、混合均匀后再加入上述重量的消泡剂和石油黄酸钠搅拌3小时即为成品。
CN2008102311599A 2008-11-25 2008-11-25 一种消失模铸造专用涂料 Expired - Fee Related CN101412073B (zh)