CN101638925B - 一种矿渣聚苯乙烯泡沫复合轻质夹芯板 - Google Patents
一种矿渣聚苯乙烯泡沫复合轻质夹芯板 Download PDFInfo
- Publication number
- CN101638925B CN101638925B CN2009100176614A CN200910017661A CN101638925B CN 101638925 B CN101638925 B CN 101638925B CN 2009100176614 A CN2009100176614 A CN 2009100176614A CN 200910017661 A CN200910017661 A CN 200910017661A CN 101638925 B CN101638925 B CN 101638925B
- Authority
- CN
- China
- Prior art keywords
- parts
- polystyrene foam
- slag
- sandwich panel
- slags
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于新型建筑材料的技术领域,涉及一种以矿渣为主要面层材料,在聚苯乙烯泡沫塑料板芯层材料上复合制成的轻质夹芯板材,夹芯板两侧向带有梯形、三角形或半圆形的凹槽。本发明中外敷于聚苯乙烯泡沫塑料板上的面层材料是由以下重量份的原料制成:矿渣粉100份;硫铝酸盐水泥2-7份;脱硫建筑石膏1.5-5.5份;芒硝0.5-5份;生石灰4-11份;水料质量比0.45-0.70。本发明的产品性能达到国家质量标准,具有轻质高强、保温隔热、隔音等功能,是一种能应用于框架结构建筑的墙体材料。
Description
技术领域
本发明属于新型建筑材料的技术领域,涉及一种利用高炉矿渣为主要原料制作的框架结构建筑用轻质夹芯板。
背景技术
传统的墙体材料多为实心粘土砖,它不仅消耗大量的能源,而且严重毁坏耕地。近年来,随着国家限制、禁止使用实心粘土砖等政策的实施,各种新型的墙体材料层出不穷。目前,框架结构建筑在我国已悄然兴起,并且愈来愈热。围护墙体是框架结构建筑的主要组成部分,在框架结构建筑中,要求墙体具有轻质,隔热、隔声、耐冲击、防火等性能。用作框架结构建筑围护墙体的轻质墙材,因适应产业化要求而得到更多的关注。
高炉矿渣是冶炼生铁时从高炉中排出的一种废渣。在冶炼生铁时,加入高炉的原料,除了铁矿石和燃料(焦炭)外,还有助熔剂。当炉温达到1400℃~1600℃时,助熔剂与铁矿石发生高温反应生成生铁和矿渣。随着我国钢铁工业的发展,高炉矿渣排量日益增多,历年来已经堆积矿渣近15×107吨,占地约1000平方公里。为了处理这些废渣,国家每年花费巨额资金修筑排渣场和铁路线,浪费大量人力物力,每逢刮风天气,沙尘四起,遇到暴雨,泥沙倾泻而下,侵占农田,污染水源,给生态环境造成了严重的危害。
高炉矿渣兼具胶凝性与火山灰活性,其玻璃体结构内含有较高的能量,潜在活性大,但是矿渣的活性需要通过一定的物理化学方法进行激发才能很好地发挥出来。利用粉磨和掺加外加剂的方法对高炉矿渣进行改性,使矿渣的活性使矿渣的活性得到激发,提高矿渣的各项性能,改性后的矿渣适宜于制作轻质墙体材料。利用矿渣生产夹芯板墙体材料,有利于节约能源、节约土地,有利于环境保护。
发明内容
本发明利用经粉磨后细度达到240目的矿渣粉,配以硫铝酸盐水泥、脱硫建筑石膏、芒硝、生石灰等为面层材料,以聚苯乙烯泡沫塑料板为芯层材料,复合而成矿渣轻质夹芯板材,产品具有轻质高强、保温隔热、隔声、防火、呼吸功能等性质,是一种节能环保墙体材料。
为实现上述目的,本发明采用如下技术方案:将矿渣粉、硫铝酸盐水泥、脱硫建筑石膏、芒硝、生石灰按一定比例混合后,加水搅拌为均匀的浆体,利用模具将浆体外敷于厚度为20-100mm的聚苯乙烯泡沫塑料板上下表面和两侧面,待浆体完全硬化后脱模,形成矿渣聚苯乙烯泡沫复合轻质夹芯板。本发明制作的矿渣轻质夹芯板长2500-3500mm,宽600mm,高60、90、120mm。
本发明制作的矿渣轻质夹芯板两侧向带有凹槽,凹槽可以是梯形、三角形或半圆形,便于建筑施工安装,避免墙体裂缝等问题。
本发明的矿渣轻质夹芯板,利用利用经粉磨后细度达到240目的矿渣粉和聚苯乙烯泡沫塑料板为主要原料制作,夹芯板两侧向带有梯形凹槽,凹槽可以是梯形、三角形或半圆形,其中外敷于聚苯乙烯泡沫塑料板上的面层材料是由以下重量份的原料制成:
矿渣粉 100份
硫铝酸盐水泥 2-7份
脱硫建筑石膏 1.5-5.5份
芒硝 0.5-5份
生石灰 4-11份
水料质量比 0.45-0.70
附图说明
图1为本发明的矿渣轻质夹芯板的结构示意图。
图2为本发明的矿渣轻质夹芯板的横剖面图。
图中,1为矿渣轻质夹芯板,2为矿渣面层材料,3为聚苯乙烯泡沫塑料板,4为侧向凹槽。
具体实施方式
实施例一
如图1和图2所示,是本发明的矿渣聚苯乙烯泡沫复合轻质夹芯板的结构示意图和横剖面图,矿渣聚苯乙烯泡沫复合轻质夹芯板是在聚苯乙烯泡沫板3上浇铸矿渣浆体面层材料2所制成,夹芯板两侧有两个侧向凹槽4,凹槽可以是梯形、半圆形或者三角形,用于安装使用。以经粉磨处理的矿渣粉、硫铝酸盐水泥、脱硫建筑石膏、芒硝、生石灰为原料按比例混合均匀,加水搅拌为浆体。利用成型模具,将料浆外敷于板长2500mm、板宽500mm、板厚40mm的聚苯乙烯泡沫塑料板的上下表面和两侧面,待料浆完全硬化后脱模而成。本发明的矿渣轻质夹芯板面层材料,是由以下重量份的原料制成:
矿渣粉 100份
硫铝酸盐水泥 4份
脱硫建筑石膏 3份
芒硝 0.5份
生石灰 7份
水料质量比 0.45
制作的矿渣轻质夹芯板尺寸为2500mm×600mm×60mm,技术性能测试结果如表1。
表1
实施例二
如图1和图2所示,是本发明的矿渣聚苯乙烯泡沫复合轻质夹芯板的结构示意图和横剖面图,矿渣聚苯乙烯泡沫复合轻质夹芯板是在聚苯乙烯泡沫板3上浇铸矿渣浆体面层材料2所制成,夹芯板两侧有两个侧向凹槽4,凹槽可以是梯形、半圆形或者三角形,用于安装使用。以经粉磨处理的矿渣粉、硫铝酸盐水泥、脱硫建筑石膏、芒硝、生石灰为原料按比例混合均匀,加水搅拌为浆体。利用成型模具,将料浆外敷于板长3000mm、板宽520mm、板厚60mm的聚苯乙烯泡沫塑料板的上下表面和两侧面和侧面,待料浆完全硬化后脱模而成。本发明的矿渣轻质夹芯板面层材料,是由以下重量份的原料制成:
矿渣粉 100份
硫铝酸盐水泥 7份
脱硫建筑石膏 1.5份
芒硝 3份
生石灰 11份
水料质量比 0.57
制作的矿渣轻质夹芯板尺寸为3000mm×600mm×90mm,技术性能测试结果如表2。
表2
实施例三
如图1和图2所示,是本发明的矿渣聚苯乙烯泡沫复合轻质夹芯板的结构示意图和横剖面图,矿渣聚苯乙烯泡沫复合轻质夹芯板是在聚苯乙烯泡沫板3上浇铸矿渣浆体面层材料2所制成,夹芯板两侧有两个侧向凹槽4,凹槽可以是梯形、半圆形或者三角形,用于安装使用。以经粉磨处理的矿渣粉、硫铝酸盐水泥、脱硫建筑石膏、芒硝、生石灰为原料按比例混合均匀,加水搅拌为浆体。利用成型模具,将料浆外敷于板长3200mm、板宽530mm、板厚80mm的聚苯乙烯泡沫塑料板的上下表面和两侧面,待料浆完全硬化后脱模而成。本发明的矿渣轻质夹芯板面层材料,是由以下重量份的原料制成:
矿渣粉 100份
硫铝酸盐水泥 2份
脱硫建筑石膏 5.5份
芒硝 2.5份
生石灰 6份
水料质量比 0.66
制作的矿渣轻质夹芯板尺寸为3200mm×600mm×120mm,技术性能测试结果如表3。
表3
实施例四
如图1和图2所示,是本发明的矿渣聚苯乙烯泡沫复合轻质夹芯板的结构示意图和横剖面图,矿渣聚苯乙烯泡沫复合轻质夹芯板是在聚苯乙烯泡沫板3上浇铸矿渣浆体面层材料2所制成,夹芯板两侧有两个侧向凹槽4,凹槽可以是梯形、半圆形或者三角形,用于安装使用。以经粉磨处理的矿渣粉、硫铝酸盐水泥、脱硫建筑石膏、芒硝、生石灰为原料按比例混合均匀,加水搅拌为浆体。利用成型模具,将料浆外敷于板长3500mm、板宽540mm、板厚90mm的聚苯乙烯泡沫塑料板的上下表面和两侧面,待料浆完全硬化后脱模而成。本发明的矿渣轻质夹芯板面层材料,是由以下重量份的原料制成:
矿渣粉 100份
硫铝酸盐水泥 5份
脱硫建筑石膏 2.5份
芒硝 5份
生石灰 4份
水料质量比 0.70
制作的矿渣轻质夹芯板尺寸为3500mm×600mm×120mm,技术性能测试结果如表4。
表4
Claims (1)
1.一种矿渣聚苯乙烯泡沫复合轻质夹芯板,其特征在于:利用经粉磨处理的矿渣粉和聚苯乙烯泡沫塑料板为主要原料复合而成的轻质夹芯板材,夹芯板两侧向带有梯形、三角形或半圆形的凹槽,其中外敷于聚苯乙烯泡沫板上的面层材料是由以下重量份的原料制成:
矿渣粉 100份
硫铝酸盐水泥 2-7份
脱硫建筑石膏 1.5-5.5份
芒硝 0.5-5份
生石灰 4-11份
水料质量比 0.45-0.70。