Aqueous fluorescent invisible stitching plaster and preparation method thereof
Technical field
The present invention relates to the printing material field, relate in particular to a kind of aqueous fluorescent invisible stitching plaster and preparation method thereof.
Background technology
Aqueous fluorescent invisible stitching plaster uses on the vamp in printing, because surface will have traditional white mark line to print out before the vamp sewing machine, the sewing machine workman could remove sewing machine by lines, the crying of former traditional mark printing usefulness " white water-based fare paste ".It is to block Printing screen that traditional white water-based fare is stuck with paste shortcoming; The printing back can be fallen in removing by process; Influence the sewing machine lines, and behind the vamp sewing machine because at fare bleeder white point, need send the workman to go to clean the vamp degree of cleaning; Lost labor very, a normal production line is wasted 3-6 people from sewing machine to the moulding meeting.The cortex that more fearful is has as: imitated furs, frosted skin are stuck with paste with traditional printing fare, because can be drawn onto in the cladding body top layer, can occur white trace once more after the cleaning, and because cladding surface, washing back can hardening, variable color, even mouldy, have a strong impact on quality.
Summary of the invention
Technical problem to be solved by this invention is exactly for the defective that overcomes above-mentioned prior art existence a kind of aqueous fluorescent invisible stitching plaster and preparation method thereof to be provided.
The object of the invention can be realized through following technical scheme: a kind of aqueous fluorescent invisible stitching plaster comprises the raw material of following parts by weight: thickening material 10-20, decomposition agent 0.1-0.9, distiller liquor 0.5-1.5 and pure water 65-80;
Said thickening material is the anionic XPA, and decomposition agent is the nonionic polyurethane polymkeric substance, and said distiller liquor is a dimethylethanolamine.
The preparation method of aqueous fluorescent invisible stitching plaster of the present invention may further comprise the steps:
Immerse thickening material, decomposition agent and distiller liquor in the cooling pure water by said ratio, all pour into again after 2-3 hour in the stirrer and stirred 1.5-2 hour, add an amount of fluorescent material after cooling, loading barrel packaging.
Beneficial effect of the present invention: 1, white with tradition, grey fare is stuck with paste and is compared; Aqueous fluorescent invisible stitching plaster of the present invention can be cannot see the white trace of printing under natural light; Remove the trouble of washing the vamp degree of cleaning from, can save the cleaning cost of labor simultaneously, on average can practice thrift 3-6 altogether and clean the employee from the sewing machine line to form wire; Guarantee that simultaneously vamp does not have through washing and original-pack skin appearance color and luster, guaranteed quality are more arranged; 2, can improve printing output about 1/3rd to 1/2nd, use the present invention can prevent web plate not stop up, web plate is not easy to scrap, and employee's printing is lighter, the gas of not too requiring great effort, and output, quality are more stable.And stick with paste with the white fare of tradition and to compare, can not make the askew pin that causes of sewing machine workman pin not in place because of carrying midway and issuance of materials process interrupt line, dry linting yet; 3, can practice thrift a large amount of illumination electricity charge, because printing place can be fluorescent lamp pass 80% with the sewing machine place, can guarantee to operate does not successfully influence ordinary production.
Embodiment
Below in conjunction with specific embodiment the present invention is described further.
Embodiment 1
The described a kind of aqueous fluorescent invisible stitching plaster of present embodiment comprises the raw material of following parts by weight: anionic XPA 10kg, nonionic polyurethane polymkeric substance 0.1kg, dimethylethanolamine 0.5kg and pure water 65kg;
The preparation method of described aqueous fluorescent invisible stitching plaster may further comprise the steps:
Immerse anionic XPA, nonionic polyurethane polymkeric substance and dimethylethanolamine in the cooling pure water by above-mentioned part by weight; All pour into again after 2-3 hour in the stirrer and stirred 1.5-2 hour; Add an amount of fluorescent material after cooling, loading barrel packaging.
Embodiment 2
The described a kind of aqueous fluorescent invisible stitching plaster of present embodiment comprises the raw material of following parts by weight: anionic XPA 15kg, nonionic polyurethane polymkeric substance 0.5kg, dimethylethanolamine 1kg and pure water 65kg;
The preparation method of the described aqueous fluorescent invisible stitching plaster of present embodiment is with embodiment 1.
Embodiment 3
The described a kind of aqueous fluorescent invisible stitching plaster of present embodiment comprises the raw material of following parts by weight: anionic XPA 18kg, nonionic polyurethane polymkeric substance 0.7kg, dimethylethanolamine 1.3kg and pure water 75kg;
The preparation method of the described aqueous fluorescent invisible stitching plaster of present embodiment is with embodiment 1.
Embodiment 4
The described a kind of aqueous fluorescent invisible stitching plaster of present embodiment comprises the raw material of following parts by weight: anionic XPA 20kg, nonionic polyurethane polymkeric substance 0.9kg, dimethylethanolamine 1.5kg and pure water 80kg;
The preparation method of the described aqueous fluorescent invisible stitching plaster of present embodiment is with embodiment 1.
The present invention can bring into play significant role during sewing machine in shoe-making industry, printing industry, service industry, the vamp that uses the present invention to print just can demonstrate lines clearly under fluorescent lamp; Be convenient to sewing machine worker operation, Adidas, thunder treasured, Decathlon, Jim such as draw all to welcome very much this environment-friendly novel product at the client, during printing; The employee will turn off the fluorescent lamp above the board; Suggestion is with black dark Curtains Fabrics, and whether curtain will put down during sewing machine, is determined by factory oneself; If but fluorescent effect is good, curtain can put down; The suggestion during cladding of unlike materials such as printing frosted skin, imitated furs is as long as seal one time is just passable; So both can after having done, with the naked eye cannot see and stay white trace on the footwear material; Can under the irradiation of luminescent lamp, can see fluorescent effect again; Indivedual exotic materialss may stay white trace after drying, as the white trace that stays can take water to add 20% white cat liquid detergent and 20% light-coloured vinegar, get final product with white cotton cleaning.If in this new technology of national industry, in the sewing machine printing of shoe industry, rag trade, artwork industry, promote this technology, then can practice thrift a large amount of costs of labor, illumination cost, reduce the production cost, to strengthening enterprise competitiveness very big meaning is arranged.