CN101607413B - Method for manufacturing concave-convex wood grain on magnesite profiles and magnesite profiles with concave-convex wood grain veneers thereof - Google Patents
Method for manufacturing concave-convex wood grain on magnesite profiles and magnesite profiles with concave-convex wood grain veneers thereof Download PDFInfo
- Publication number
- CN101607413B CN101607413B CN2009101625131A CN200910162513A CN101607413B CN 101607413 B CN101607413 B CN 101607413B CN 2009101625131 A CN2009101625131 A CN 2009101625131A CN 200910162513 A CN200910162513 A CN 200910162513A CN 101607413 B CN101607413 B CN 101607413B
- Authority
- CN
- China
- Prior art keywords
- magnesite
- profiles
- maintenance
- brush
- wood grain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a method for manufacturing concave-convex wood grain on magnesite profiles, and magnesite profiles with concave-convex wood grain veneers thereof, aiming at solving the problems of poor wood grain quality and high cost of the existing magnesite profiles. The manufacturing method sequentially comprises the following steps of: spraying barrier paint on the surface of carbonized wood; brushing a layer of magnesite pulp, laying a layer of glass fiber fabric, brushing and laying again till reaching mould design thickness, initial curing, demoulding, curing again, trimming by cutting convex parts and filling concave parts, and spraying automobile paint or epoxy resin gel-coated paint for 3-4 times to manufacture a magnesite mould; brushing a layer of magnesite pulp on the magnesite mould, laying a layer of glass fiber fabric on the magnesite mould, brushing and laying again till reaching profiles design thickness, initial curing, demoulding, curing again, trimming by cutting convex parts and filling concave parts, coloring, and spraying finish for 3-4 times; and filling the concave parts by using putty. The manufacturing method has strong operability, and can manufacture high-imitation wood grain on magnesite profiles with simplicity, reliability, low cost of the mould, and high efficiency. The wood grain on magnesite profiles has strong stereoscopic impression and high imitation, and also has the texture and appearance of real wood grain even being observed at close range.
Description
Technical field
The present invention relates to a kind of magnesite profiles, particularly relate to concavo-convex wood grain preparation method of a kind of magnesite profiles and concavo-convex graining magnesite profiles thereof.
Background technology
At present, magnesite profiles is better than timber, and both, had and improved the antidetonation coefficient for brick, generation watt, ecological, environmental protective, fire protection flame retarding, waterproof is indeformable, heat preservation energy-saving sound insulation, protection against rodents advantage such as damage by worms.Can be used for fields such as building, ornament materials, door and window, furniture, handicraft, have energy-conserving and environment-protective, long service life, it is day by day deficient to alleviate present global warming, the forest reserves, wooden cost is more and more higher and more and more rare, and a large amount of harvest of forest trees make natural environment, resource and the ecological balance be subjected to the puzzlement of heavy damage.So, magnesite profiles with above-mentioned many advantages is welcome by society and market more and more, but its facing wood grain emulation degree can not satisfy society need far away, be that its facing wood grain is when distant surveillance, texture and outward appearance with truewood line, but during close-ups, its wood grain face is obviously distortion just.
Summary of the invention
The object of the invention is to overcome the above-mentioned defective of prior art, provides a kind of can obtain close-ups the time, also has the concavo-convex wood grain preparation method of magnesite profiles of higher emulation graining.The concavo-convex graining magnesite profiles that provides this method to obtain also is provided the inventive method.
For achieving the above object, the concavo-convex wood grain preparation method of magnesite profiles of the present invention in turn includes the following steps: the carbonized wood removing surface is clean, the spray isolation lacquer; Brush one deck magnesite slurry, the shop layer of glass fiber fabric, brush repaves until reaching mould design thickness again, first maintenance, the demoulding, the deburring of recessed benefit formula is cut in maintenance more more, and spray automobile coating or epoxy resin gel coat lacquer 3-4 are all over making the magnesite mould; Brush one deck magnesite slurry on the magnesite mould, the shop layer of glass fiber fabric, brush repaves until reaching profile design thickness again, first maintenance, the demoulding, the deburring of recessed benefit formula is cut in maintenance more more, colouring, spray finish 3-4 time; Recessed benefit is used the atom ash.This preparation method is workable, wood grain fidelity height, wood grain quality stability is strong, be no matter who according to said method operates the magnesite wood-imitating type material that can both make high emulation, and with charing carpentery workshop master mold, do to produce mould, can reduce die cost greatly with the molded magnesite mould of carbonized wood, more convenient extensive copy mold also is convenient to enhance productivity; Promptly this method can be with simple, efficient, workable, the production efficiency height, and the method that die cost is low is made high imitative magnesite profiles wood grain, even this wood grain, all has the texture and the outward appearance of truewood line in close-ups.
Described carbonized wood can be a superficial charring wood, also can be degree of depth carbonized wood, wherein:
Superficial charring wood: be not contain under any chemical agent condition, by localized hyperthermia timber carried out charing and handle that make wood surface form the very thin charring layer of one deck, this charring layer can strengthen the effect of the preservation of timber against decay and antibiont invasion and attack; Its moisture content is low, be difficult for suction, stable material quality, indeformable, complete degreasing do not overflow fat, advantages such as heat-proof quality is good, construction is simple, brushing is convenient, no special odor, the surface has dark-brown aesthetic, be desirable indoor and sauna material, become bathroom and decorate new fashion trend; Its anti-rotting, anti-insect, resistance to deformation cracking, resistance to elevated temperatures also becomes the ideal material of outdoor swimming pool view.
Degree of depth carbonized wood: be timber through the high temperature carbonization technical finesse about 200 degree, because its nutritional labeling is damaged, so have antiseptic insect-repelling function preferably, recombinated owing to its absorbent function tissue fibers again, so its physical property is more stable, not only prolonged service life, and not flexible type, difficult suction, so be again outstanding moistureproof timber.The color and luster of degree of depth carbonized wood is soft, thinks and acts in one and the same way.Carbonization of wood process only relates to steam and temperature, does not add any chemical agent and other foreign substances, and is without any side effects to human body, animal living enviroment, so be again real Green Product.
As optimization, when graining is fitted with ornament, then at section bar again after the maintenance and before spraying paint, with adhesives or inlay bonding and go up ornament; Perhaps, be equipped with again after graining is made and go up ornament at the support or the base of section bar brush pre-buried equipped ornament of shop stage.It can make according to the most simple and reliable mode and comprise that jade jewelry, metal ornament, resin jewelry, woodcarving jewelry, coloured glaze jewelry, porcelain jewelry and magnesite profiles fuse into one, solve that to add the ornament technology difficulty for a long time on timber big, a short-life again historical difficult problem.
As optimization, described ornament comprises jade jewelry, metal ornament, resin jewelry, woodcarving jewelry, coloured glaze jewelry, porcelain jewelry; Described adhesive is an epoxy resin, and described finish is polyester lacquer or outer wall paint.
As optimization, described section bar finish is added with fluorescent material or is fluorescent paint, also is added with fluorescent material in the look essence of described colouring.So design can be brought up magnificent night scene effect with lower energy cost, and fluorescence also has the effect of showing night certainly.
As optimization, every layer of brush of described magnesite slurry 3 millimeter are thick, until required thickness.Described maintenance just is to keep under the condition on 20 ℃ of mean temperatures 24 hours or 120-180 ℃ of baking box oven dry 1-4 hour, described maintenance again is lucifuge maintenance 7 days under environmental condition more than 0 ℃, (depositing did not here need lucifuge in 20-30 days to deposit 20-30 days, the 7 days needs lucifuges in front, temperature all is more than 0 ℃), described isolation lacquer is an automobile coating, what described colouring was used is paint look essence, and described carbonized wood removing surface is to remove with hairbrush to adhere to unreal carbide and other impurity; Make carbonized wood before described carbonized wood removing surface is clean earlier, then clean out again, then spray isolation lacquer; Brush repaves that to repeat the last one deck of how many times all be magnesite material layer or glass cloth again.
As optimization, brush repaves that to repeat the last one deck of how many times all be glass cloth again.Last one deck all is a glass cloth adhesion strength height.
As optimization, the concavo-convex graining magnesite profiles that the concavo-convex wood grain preparation method of described magnesite profiles is made, its special feature are to make through the following step: the carbonized wood removing surface is clean, the spray isolation lacquer; Brush one deck magnesite slurry, the shop layer of glass fiber fabric, brush repaves until reaching the magnesite mould design thickness again, first maintenance, the demoulding, maintenance again uses the atom ash to carry out cutting the deburring of recessed benefit formula more, and spray automobile coating or epoxy resin gel coat lacquer are made the magnesite mould 3-4 time; Brush one deck magnesite slurry on the magnesite mould, the shop layer of glass fiber fabric, brush repaves until reaching the magnesite profiles design thickness again, first maintenance, the demoulding, maintenance again uses the atom ash to carry out cutting the deburring of recessed benefit formula more, and colouring is sprayed finish 3-4 time; Described carbonized wood is superficial charring wood or degree of depth carbonized wood.It is positioned at that 5-6 undergoes no deterioration under the natural conditions through a large amount of evidences, even fade when rotten, also can spray paint by colouring again and renovate.Experimental results show that: it is not worse than strength of cement, acidproof, alkaline-resisting, sun-proof, antiultraviolet, seawater immersion erosion resisting; Fire line is strong, obviously is better than cement, as: magnesite profiles and angle bar, iron pipe are placed on simultaneously on the coal stove and burn a night, second day magnesite shape invariance, and angle bar and square tube have all crumpled and have burnt; In addition, its insulation, sound insulation, waterproof effect are also very good.Carbonized wood can highlight the wood grain of concave-convex surface, produces stereoeffect.
As optimization, graining also is fitted with ornament, at section bar again after the maintenance and before spraying paint, with adhesives or inlay bonding and go up ornament; Perhaps, be equipped with again after graining is made and go up ornament at the support or the base of section bar brush pre-buried equipped ornament of shop stage.Described ornament comprises jade jewelry, metal ornament, resin jewelry, woodcarving jewelry, coloured glaze jewelry, porcelain jewelry.Behind the equipped jewelry can with simple and cheaply mode give magnesite imitative luxurious, the honorable quality of wood products, be particularly suitable for building top-grade building and ornament, top grade decorate and construction material in its cost performance the highest.
As optimization, every layer of brush of described magnesite slurry 3 millimeter are thick, described maintenance just is to keep under the condition on 20 ℃ of mean temperatures 24 hours or 120-180 ℃ of baking box oven dry 1-4 hour, described maintenance again is lucifuge maintenance 7 days under environmental condition more than 0 ℃, (depositing did not here need shading in 20-30 days to deposit 20-30 days, the 7 days needs lucifuges in front, temperature all is more than 0 ℃), described isolation lacquer is an automobile coating, what described colouring was used is paint look essence, and described carbonized wood removing surface is to remove with hairbrush to adhere to unreal carbide and other impurity; Make carbonized wood before described carbonized wood removing surface is clean earlier, then clean out again, then spray isolation lacquer; Brush repaves that to repeat the last one deck of how many times all be magnesite material layer or glass cloth again; Described finish is polyester lacquer or outer wall paint.When last one deck is glass cloth, because glass cloth surface area is big, globality is strong, intensity is higher when boning; When magnesite material was done superficial layer, the surface was too smooth, bad bonding.
As optimization, the parts that polylith above-mentioned is worn graining are assembled by wood grain mode outwardly and are linked together, and become the surface all with the full wood grain assembly of wood grain; Be in the milk to mould with the magnesite slurry again when bonding together, occur defective after the demoulding and repair colouring with the atom ash; Described section bar finish can add fluorescent material or for fluorescent paint, also is added with fluorescent material in the look essence of described colouring or only repairs at the bulky joint place to use in atom ash, the look essence and can add fluorescent material in the finish.The outer public facility of magnesite profiles build chamber of the present invention that possesses fluorescence property can be that urban landscape is hyperchromic with minimum cost the longest service life, is that cost performance is best, and the most attractive and durable urban public utilities are built ornament materials.
It is because the fidelity height; comprehensive quality is good; cost performance is good, can be widely used in to build high-quality villa, ecological, environmental protective leisure house, ornament materials, garden landscape and gardening view, the indoor door of high-grade parlor environmental protection and furniture handicraft, packing case, cargo pallet, dustbin etc.
After adopting technique scheme, the concavo-convex wood grain preparation method of magnesite profiles of the present invention has workable, can with simple, reliable, die cost is low, high-efficiency method is made high imitative magnesite profiles wood grain.The wood grain third dimension of the concavo-convex graining magnesite profiles that this method obtained is strong, fidelity is high, even in close-ups, all has the texture and the outward appearance of truewood line.
The specific embodiment
The concavo-convex wood grain preparation method of magnesite profiles:
Embodiment one, and the concavo-convex wood grain preparation method of magnesite profiles of the present invention is in turn include the following steps: the carbonized wood surface is cleaned out with hairbrush and is adhered to unreal carbide and other impurity, the automobile coating that spray is used to isolate; The magnesite slurry of brush one deck 3 millimeters thick, the shop layer of glass fiber fabric, brush repaves repeatedly until reaching mould design thickness again, on 20 ℃ of mean temperatures, kept under the condition 24 hours or maintenance was just carried out in 120-180 ℃ of baking box oven dry in 1-4 hour, the demoulding, lucifuge is deposited maintenance in 7 days under environmental condition more than 0 ℃, again under household condition (do not need lucifuge, temperature also is more than 0 ℃) 20-30 days, use the atom ash to carry out cutting the manual deburring of recessed benefit formula more, be that additional part is downcut with cutter, the part that falls in is filled and led up with correction of the defect with the atom ash, and spray automobile coating or epoxy resin gel coat lacquer 3-4 make the magnesite mould all over carrying out cover; The magnesite slurry of brush one deck 3 millimeters thick on the magnesite mould, the shop layer of glass fiber fabric, brush repaves repeatedly until reaching product design thickness again, on 20 ℃ of mean temperatures, keep carrying out in 24 hours maintenance just under the condition, the demoulding, lucifuge maintenance 7 days under environmental condition more than 0 ℃, lucifuge was not deposited 20-30 days, use the atom ash to carry out cutting the manual deburring of recessed benefit formula more, be that additional part is downcut with cutter, the part that falls in is filled and led up with correction of the defect with the atom ash, make and paint the look manual colouring of row that progresses greatly, spray polyester lacquer or carry out cover outer wall paint 3-4 time.
Embodiment two, and the difference of concavo-convex wood grain preparation method of magnesite profiles of the present invention and embodiment one only is: when graining is fitted with ornament, then at section bar again after the maintenance and before spraying paint, with adhesives or inlay bonding and go up ornament; Perhaps, be equipped with again after graining is made and go up ornament at the support or the base of section bar brush pre-buried equipped ornament of shop stage.Described ornament comprises jade jewelry, metal ornament, resin jewelry, woodcarving jewelry, coloured glaze jewelry, porcelain jewelry; Described adhesive is an epoxy resin, and described finish is.
Embodiment three, and the difference of concavo-convex wood grain preparation method of magnesite profiles of the present invention and embodiment one only is: described section bar finish is added with fluorescent material or is fluorescent paint, also is added with fluorescent material in the look essence of described colouring.
Embodiment four, and the difference of concavo-convex wood grain preparation method of magnesite profiles of the present invention and embodiment one only is: make carbonized wood before described carbonized wood removing surface is clean earlier, and then clean out, and then spray isolation lacquer.Compare with the operation of interval certain hour, the wood grain quality significantly improves.
Concavo-convex graining magnesite profiles:
Embodiment one, and the concavo-convex graining magnesite profiles that the concavo-convex wood grain preparation method of magnesite profiles of the present invention is made is to make through the following step: the carbonized wood surface is cleaned out with hairbrush and is adhered to unreal carbide and other impurity, and the automobile coating of usefulness is isolated in spray; The thick magnesite slurry of brush one deck 3 millimeter, the shop layer of glass fiber fabric, to repave until reaching mould design thickness and making last one deck be glass cloth to brush again, on 20 ℃ of mean temperatures, kept under the condition 24 hours or maintenance was just carried out in 120-180 ℃ of baking box oven dry in 1-4 hour, the demoulding, lucifuge maintenance 7 days under environmental condition more than 0 ℃, (not needing lucifuge) deposited 20-30 days, carried out cutting the deburring of recessed benefit formula with the atom ash more, and spray automobile coating or epoxy resin gel coat lacquer 3-4 make the magnesite mould all over cover; The thick magnesite slurry of brush one deck 3 millimeter on the magnesite mould, the shop layer of glass fiber fabric, to repave until reaching section bar product design thickness and making last one deck be glass cloth to brush again, on 20 ℃ of mean temperatures, kept under the condition 24 hours or maintenance was just carried out in 120-180 ℃ of baking box oven dry in 1-4 hour, the demoulding, lucifuge maintenance 7 days under environmental condition more than 0 ℃, (not needing lucifuge) deposited 20-30 days, carry out cutting the deburring of recessed benefit formula with the atom ash more, the paint look progresses greatly, and row is manual paints, and polyester lacquer or outer wall paint 3-4 are all over cover.
Embodiment two, and the difference of the concavo-convex graining magnesite profiles of the present invention and the foregoing description one only is: the parts that polylith above-mentioned is worn graining bond together by wood grain mode outwardly again, become the surface all with the full wood grain assembly of wood grain; Also be in the milk to the slit of centre with the magnesite slurry when bonding together, repair with the atom ash in the slit of bonding, colouring.Also be added with fluorescent material in the look essence of described colouring or only in the atom ash that the bond line place repair to use, add fluorescent material in the look essence and in the section bar finish; Can make these parts have wide effect and the effect of beautifying the environment shown at night.To the grouting of the slit of centre each assembly is bonded together comprehensively.
Embodiment three, and the difference of the concavo-convex graining magnesite profiles of the present invention and the foregoing description one only is: the section bar graining also is fitted with ornament, after maintenance again and before spraying paint, with adhesives or inlay bonding and go up ornament; Perhaps, be equipped with again after graining is made and go up ornament at the support or the base of section bar brush pre-buried equipped ornament of shop stage.
Embodiment four, and the difference of the concavo-convex graining magnesite profiles of the present invention and the foregoing description one only is: make carbonized wood with the superficial charring legal system earlier before described carbonized wood removing surface is clean, and then clean out, and then spray isolation lacquer.Described section bar finish is added with fluorescent material or is fluorescent paint.Have the outdoor structures that epipolic magnesite profiles makes and possess the effect of showing night at night naturally, display position, size shape are beautified the environment at night on the other hand on the one hand.
Claims (15)
1. concavo-convex wood grain preparation method of magnesite profiles, it is characterized in that in turn including the following steps: the carbonized wood removing surface is clean, the spray isolation lacquer; Brush one deck magnesite slurry, the shop layer of glass fiber fabric, brush repaves until reaching mould design thickness again, first maintenance, the demoulding, the deburring of recessed benefit formula is cut in maintenance more more, and spray epoxy resin gel coat lacquer 3-4 is all over making the magnesite mould; Brush one deck magnesite slurry on the magnesite mould, the shop layer of glass fiber fabric, brush repaves until reaching profile design thickness again, first maintenance, the demoulding, the deburring of recessed benefit formula is cut in maintenance more more, colouring, spray finish 3-4 time; Recessed benefit is used the atom ash.
2. concavo-convex wood grain preparation method of magnesite profiles, it is characterized in that in turn including the following steps: the carbonized wood removing surface is clean, the spray isolation lacquer; Brush one deck magnesite slurry, the shop layer of glass fiber fabric, brush repaves until reaching mould design thickness again, first maintenance, the demoulding, the deburring of recessed benefit formula is cut in maintenance more more, and spray automobile coating 3-4 is all over making the magnesite mould; Brush one deck magnesite slurry on the magnesite mould, the shop layer of glass fiber fabric, brush repaves until reaching profile design thickness again, first maintenance, the demoulding, the deburring of recessed benefit formula is cut in maintenance more more, colouring, spray finish 3-4 time; Recessed benefit is used the atom ash.
3. according to claim 1 or the concavo-convex wood grain preparation method of 2 described magnesite profiles, it is characterized in that when graining is fitted with ornament, then at section bar again after the maintenance and before spraying paint, with adhesives or inlay bonding and go up ornament; Perhaps, be equipped with again after graining is made and go up ornament at the support or the base of section bar brush pre-buried equipped ornament of shop stage.
4. according to the concavo-convex wood grain preparation method of the described magnesite profiles of claim 3, it is characterized in that described ornament comprises jade jewelry, metal ornament, resin jewelry, woodcarving jewelry, coloured glaze jewelry, porcelain jewelry; Described adhesive is an epoxy resin, and described finish is the polyester lacquer.
5. according to the concavo-convex wood grain preparation method of the described magnesite profiles of claim 3, it is characterized in that described ornament comprises jade jewelry, metal ornament, resin jewelry, woodcarving jewelry, coloured glaze jewelry, porcelain jewelry; Described adhesive is an epoxy resin, and described finish is outer wall paint.
6. according to claim 1 or the concavo-convex wood grain preparation method of 2 described magnesite profiles, it is characterized in that described section bar finish is a fluorescent paint, also is added with fluorescent material in the look essence of described colouring.
7. according to claim 1 or the concavo-convex wood grain preparation method of 2 described magnesite profiles, it is characterized in that every layer of brush of described magnesite slurry 3 millimeter are thick, until required thickness, described maintenance just is to keep under the condition on 20 ℃ of mean temperatures 24 hours or 120-180 ℃ of baking box oven dry 1-4 hour, described maintenance again is lucifuge maintenance 7 days under environmental condition more than 0 ℃, deposited 20-30 days, described isolation lacquer is an automobile coating, what described colouring was used is paint look essence, and described carbonized wood removing surface is to remove with hairbrush to adhere to unreal carbide and other impurity; Make carbonized wood before described carbonized wood removing surface is clean earlier, then clean out again, then spray isolation lacquer; Brush repaves that to repeat the last one deck of how many times all be magnesite material layer or glass cloth again.
8. according to the concavo-convex wood grain preparation method of the described magnesite profiles of claim 7, it is characterized in that brushing again and repave that to repeat the last one deck of how many times all be glass cloth.
9. the concavo-convex graining magnesite profiles made of the concavo-convex wood grain preparation method of the described magnesite profiles of claim 1, it is characterized in that making through the following step: the carbonized wood removing surface is clean, the spray isolation lacquer; Brush one deck magnesite slurry, the shop layer of glass fiber fabric, brush repaves until reaching the magnesite mould design thickness again, first maintenance, the demoulding, maintenance again uses the atom ash to carry out cutting the deburring of recessed benefit formula more, and spray epoxy resin gel coat lacquer is made the magnesite mould 3-4 time; Brush one deck magnesite slurry on the magnesite mould, the shop layer of glass fiber fabric, brush repaves until reaching the magnesite profiles design thickness again, first maintenance, the demoulding, maintenance again uses the atom ash to carry out cutting the deburring of recessed benefit formula more, and colouring is sprayed finish 3-4 time; Described carbonized wood is superficial charring wood or degree of depth carbonized wood.
10. the concavo-convex graining magnesite profiles made of the concavo-convex wood grain preparation method of the described magnesite profiles of claim 2, it is characterized in that making through the following step: this removing surface of charing is clean, the spray isolation lacquer; Brush one deck magnesite slurry, the shop layer of glass fiber fabric, brush repaves until reaching the magnesite mould design thickness again, first maintenance, the demoulding, maintenance again uses the atom ash to carry out cutting the deburring of recessed benefit formula more, and the spray automobile coating is made the magnesite mould 3-4 time; Brush one deck magnesite slurry on the magnesite mould, the shop layer of glass fiber fabric, brush repaves until reaching the magnesite profiles design thickness again, first maintenance, the demoulding, maintenance again uses the atom ash to carry out cutting the deburring of recessed benefit formula more, and colouring is sprayed finish 3-4 time; Described carbonized wood is superficial charring wood or degree of depth carbonized wood.
11. according to claim 9 or 10 described concavo-convex graining magnesite profiles, it is characterized in that graining also is fitted with ornament, at section bar again after the maintenance and before spraying paint, with adhesives or inlay bonding and go up ornament; Perhaps, be equipped with again after graining is made and go up ornament at the support or the base of section bar brush pre-buried equipped ornament of shop stage.
12. according to claim 9 or 10 described concavo-convex graining magnesite profiles, it is characterized in that every layer of brush of described magnesite slurry 3 millimeter are thick, described maintenance just is to keep under the condition on 20 ℃ of mean temperatures 24 hours or 120-180 ℃ of baking box oven dry 1-4 hour, described maintenance again is lucifuge maintenance 7 days under environmental condition more than 0 ℃, deposited 20-30 days, described isolation lacquer is an automobile coating, what described colouring was used is paint look essence, and described carbonized wood removing surface is to remove with hairbrush to adhere to unreal carbide and other impurity; Make carbonized wood before described carbonized wood removing surface is clean earlier, then clean out again, then spray isolation lacquer; Brush repaves that to repeat the last one deck of how many times all be magnesite material layer or glass cloth again; Described finish is the polyester lacquer.
13. according to claim 9 or 10 described concavo-convex graining magnesite profiles, it is characterized in that every layer of brush of described magnesite slurry 3 millimeter are thick, described maintenance just is to keep under the condition on 20 ℃ of mean temperatures 24 hours or 120-180 ℃ of baking box oven dry 1-4 hour, described maintenance again is lucifuge maintenance 7 days under environmental condition more than 0 ℃, deposited 20-30 days, described isolation lacquer is an automobile coating, what described colouring was used is paint look essence, and described carbonized wood removing surface is to remove with hairbrush to adhere to unreal carbide and other impurity; Make carbonized wood before described carbonized wood removing surface is clean earlier, then clean out again, then spray isolation lacquer; Brush repaves that to repeat the last one deck of how many times all be magnesite material layer or glass cloth again; Described finish is outer wall paint.
14. according to the described concavo-convex graining magnesite profiles of claim 12, it is characterized in that polylith above-mentioned wears the parts of graining and assemble by wood grain mode outwardly and link together, become the surface all with the full wood grain assembly of wood grain; Be in the milk to mould with the magnesite slurry again when bonding together, occur defective after the demoulding and repair colouring with the atom ash; Described section bar finish is a fluorescent paint, also is added with in the look essence of described colouring in fluorescent material or the look essence He in the finish to add fluorescent material.
15. according to the described concavo-convex graining magnesite profiles of claim 13, it is characterized in that polylith above-mentioned wears the parts of graining and assemble by wood grain mode outwardly and link together, become the surface all with the full wood grain assembly of wood grain; Be in the milk to mould with the magnesite slurry again when bonding together, occur defective after the demoulding and repair colouring with the atom ash; Described section bar finish is a fluorescent paint, also is added with in the look essence of described colouring in fluorescent material or the look essence He in the finish to add fluorescent material.