CN101584507A - Production process of cold silicone liner - Google Patents

Production process of cold silicone liner Download PDF

Info

Publication number
CN101584507A
CN101584507A CNA2009100996577A CN200910099657A CN101584507A CN 101584507 A CN101584507 A CN 101584507A CN A2009100996577 A CNA2009100996577 A CN A2009100996577A CN 200910099657 A CN200910099657 A CN 200910099657A CN 101584507 A CN101584507 A CN 101584507A
Authority
CN
China
Prior art keywords
base cloth
cold
production
cylinder
silicone liner
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009100996577A
Other languages
Chinese (zh)
Other versions
CN101584507B (en
Inventor
严惠莲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changxing Shiante Clothing Material Co., Ltd.
Original Assignee
周德财
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 周德财 filed Critical 周德财
Priority to CN2009100996577A priority Critical patent/CN101584507B/en
Publication of CN101584507A publication Critical patent/CN101584507A/en
Application granted granted Critical
Publication of CN101584507B publication Critical patent/CN101584507B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a production process of cold silicone liner, comprising the steps as follows: dipping the produced base cloth, adding with non-ionic microemulsion of amino-modified organic siloxane with 20% fabric weight, the treating temperature being 40 to 50 degrees centigrade, the treatment time being 15 to 20 minutes, then padding, the mangle expression being about 50%, then drying under 120 to 150 degrees centigrade, feeding and dispensing the cold coating; directly painting the polyamide hot-melt adhesive on the base cloth through the cylinder blade; the screen meshes of the cylinder being 140 to 180 screen meshes, the aperture being 0.12 mm, the thickness being 0.02 mm, and the vehicle speed being 30m/min, the environmental temperature in shop being 20 to 30 degrees centigrade, the humidity being 60% to 70%. The invention has the advantages of ensuring the original material and style of the base cloth at maximum without heating; and the products have clear cement and the gum does not fall off, and the bonded fastness and the quality stability are high.

Description

A kind of production process of cold silicone liner
Technical field
The present invention relates to a kind of production technology of adhesive lining, specifically, relate to a kind of production process of cold silicone liner.
Background technology
The lining cloth of conventional coatings technology (hot melt transfer, dusting, powder point), base cloth needs the high temperature heating in the production process, and rubber powder is transferred on the base cloth under molten condition, cools off rolling then and forms.Because base cloth needs the high temperature heating, the style of lining itself can't embody, thereby has influenced the moulding of clothes and taken performance.
Summary of the invention
The object of the present invention is to provide a kind of production process of cold silicone liner, can effectively solve existing lining cloth coating technology needs the high temperature heating and fabric style can't be embodied, and influences the problem of apparel modeling and performance.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions: a kind of production process of cold silicone liner comprises the steps:
A. the base cloth of producing is carried out impregnation process, add the nonionic mes liquid of the amino-modified silicone oxygen alkane of fabric weight 1%-3%, treatment temperature is 40-50 ℃, processing time is 15-20 minute, adopt then and pad technology, pick-up rate is about 50%, again 120-150 ℃ of oven dry;
B. the check, cropping;
C. the cold spot coating is advanced cloth, some glue: directly be applied on the base cloth equably by the cylinder scraper polyamide hot, the cylinder order is counted 140-180 order, aperture 0.12mm, thickness 0.02mm, the speed of a motor vehicle: 30m/min, 20-30 ℃ of workshop condition temperature, humidity: 60%-70%;
D. again through batching, checking, obtain finished product.
Preferably, the nonionic mes liquid addition of the amino-modified silicone oxygen alkane of described A step is 2% of a fabric weight, and treatment temperature is 50 ℃, and the processing time is 20 minutes, 140 ℃ of bake out temperatures; The cylinder order number of described C step is 180 orders; Can reach the technological parameter of better effects.
Compared with prior art, advantage of the present invention is: adopt the super flexible nonwoven base cloth handled through silicone oil and polyamide hot to form through cold spot is transfer coated, need not heating, original material of base cloth and style have been guaranteed to the full extent, product glue point is clear, do not fall glue, adhesive fastness and quality stability height.It is convenient to change product operation simultaneously, changes kind, draping and only needs a few minutes, will treat that unlike powder point method the engraved roll cooling reheated after two hours.
Description of drawings
Fig. 1 is the process route chart of a kind of production process of cold silicone liner of the present invention.
The specific embodiment
Consult the embodiment of Fig. 1 for a kind of production process of cold silicone liner of the present invention, a kind of production process of cold silicone liner, comprise the steps: that A. carries out impregnation process to the base cloth of producing, the nonionic mes liquid that adds the amino-modified silicone oxygen alkane of fabric weight 2%, treatment temperature is 50 ℃, and the processing time is 20 minutes, adopts then and pads technology, pick-up rate is about 50%, again 140 ℃ of oven dry; B. the check, cropping; C. the cold spot coating is advanced cloth, some glue: polyamide hot directly is applied on the base cloth equably several 180 orders of cylinder order, aperture 0.12mm, thickness 0.02mm, the speed of a motor vehicle: 30m/min, 20-30 ℃ of workshop condition temperature, humidity: 60%-70% by the cylinder scraper; D. again through batching, checking, obtain finished product.
Directly equably spread upon base cloth on by the cylinder scraper polyamide hot, owing to need not to add any additive that influences the rubber powder fastness, so under the situation of equal spread, compare with transmission slurry point, it is many that fastness is better than sizing point padding cloth, saved and sized mixing, need not evaporate in the slurry 70% moisture content, energy-conservation about 50%.It is convenient to change product operation simultaneously, changes kind, draping and only needs 4 minutes, will treat that unlike powder point method the engraved roll cooling reheated after two hours.Because of base cloth does not need high temperature heating, spin, non-woven base cloth all can keep original material of base cloth and style.Compare with slurry point method, do not need auxiliary agent, adhesive fastness and quality stability height.Following table is for adopting the NT5255 basic mechanical design feature index of this explained hereafter:
Project Technical indicator
Peel strength 〉=8N/5 * 10cm or base cloth tear
The washing change in size Warp-wise 〉=-1.5% broadwise 〉=-1.0%
Xeothermic change in size Warp-wise 〉=-2.0% broadwise 〉=1.0%
Dried, water-cleaning appearance changes 5 grades
Discharge free formaldehyde (mg/kg) ??0
The above only is specific embodiments of the invention, but architectural feature of the present invention is not limited thereto, and any those skilled in the art is in the field of the invention, and the variation of being done or modify all is encompassed among the claim of the present invention.

Claims (3)

1. a production process of cold silicone liner is characterized in that: comprise the steps:
A. the base cloth of producing is carried out impregnation process, add the nonionic mes liquid of the amino-modified silicone oxygen alkane of fabric weight 1%-3%, treatment temperature is 40-50 ℃, processing time is 15-20 minute, adopt then and pad technology, pick-up rate is about 50%, again 120-150 ℃ of oven dry;
B. the check, cropping;
C. the cold spot coating is advanced cloth, some glue: directly be applied on the base cloth equably by the cylinder scraper polyamide hot, the cylinder order is counted 140-180 order, aperture 0.12mm, thickness 0.02mm, the speed of a motor vehicle: 30m/min, 20-30 ℃ of workshop condition temperature, humidity: 60%-70%;
D. again through batching, checking, obtain finished product.
2. a kind of production process of cold silicone liner as claimed in claim 1, it is characterized in that: the nonionic mes liquid addition of the amino-modified silicone oxygen alkane of described A step is 2% of a fabric weight, treatment temperature is 50 ℃, and the processing time is 20 minutes, 140 ℃ of bake out temperatures.
3. a kind of production process of cold silicone liner as claimed in claim 1 is characterized in that: the cylinder order number of described C step is 180 orders.
CN2009100996577A 2009-06-15 2009-06-15 Production process of cold silicone liner Expired - Fee Related CN101584507B (en)