CN109403061A - A kind of preparation process of PU spandex fabric low temperature lining - Google Patents

A kind of preparation process of PU spandex fabric low temperature lining Download PDF

Info

Publication number
CN109403061A
CN109403061A CN201811293943.2A CN201811293943A CN109403061A CN 109403061 A CN109403061 A CN 109403061A CN 201811293943 A CN201811293943 A CN 201811293943A CN 109403061 A CN109403061 A CN 109403061A
Authority
CN
China
Prior art keywords
fabric
base fabric
drying
temperature
low temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811293943.2A
Other languages
Chinese (zh)
Inventor
严华荣
许超超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG KINGSAFE INTERLINING CO Ltd
Original Assignee
ZHEJIANG KINGSAFE INTERLINING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG KINGSAFE INTERLINING CO Ltd filed Critical ZHEJIANG KINGSAFE INTERLINING CO Ltd
Priority to CN201811293943.2A priority Critical patent/CN109403061A/en
Publication of CN109403061A publication Critical patent/CN109403061A/en
Pending legal-status Critical Current

Abstract

The invention proposes a kind of preparation processes of PU spandex fabric low temperature lining, successively the following steps are included: base fabric pads processing, cloth feeding, hot melt adhesive layer processing, bake and bank up with earth processing, wind inspection processing, it is PU spandex fabric as base fabric using material, it is formed using low temperature PA glue double-dot coating, since PU can not high temperature resistant, improve conventional coatings technique, coating temperature is reduced to 140 DEG C by original 170 DEG C, it is effectively guaranteed the excellent performance of PU material, product pressing temperature is low, peel strength is good soft, elasticity is good, achievable and elastic fabric, PU fabric merges completely, fabric is set to have better morphological stability, washing size stability and more well-pressed visual effect.

Description

A kind of preparation process of PU spandex fabric low temperature lining
[technical field]
The present invention relates to the field of fabric, especially a kind of preparation process of PU spandex fabric low temperature lining.
[background technique]
With the continuous development of science and technology and improvement of living standard, people are higher and higher to finding out for comfortable features of clothing. It when outdoor sports, can usually go out many sweat, can also encounter the bad weathers such as fog, rainy, this requires clothes to be provided simultaneously with Waterproof, the function of moisture-inhibiting meet the high-comfort requirements of outdoor sports.
Spandex fabric PU coating fabric is exactly the functional textile for integrating waterproof, moisture-inhibiting, radix saposhnikoviae and thermal property, tool Standby wind-proof warming, abrasion-resistant, high waterproof, antiacid alkali and other effects.Especially has waterproof and with more soft, removing jail Spend many advantages, such as strong, tear-resistant.It is world textile industry constantly to a kind of novel fabric of top grade development to show unique characteristics.It should Fabric mainly applies to functional clothing, can not only exclude the sweat and sweat gas of human body in time, meet severe cold wind and snow, strong wind day Dress in the adverse circumstances such as gas when people's activity needs, and is also applied for requirement of the people's daily life to raincoat, can answer extensively For in the outdoor wears such as water-proof jacket, anorak, being a kind of high-grade functional fabric.
But spandex fabric PU coating fabric is not on the make high with common adhesive lining bond difficult, bonding intensity, leverages Using effect reduces product specification.These fabrics itself have excellent elasticity, waterproofing and moisture-penetration performances simultaneously, however not just True can destroy the original excellent performance of fabric with lining, reduce the interior quality and service life of clothes, it is difficult to meet Xiang Zhonggao The demand of shelves development, therefore propose a kind of preparation process of PU spandex fabric low temperature lining.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of preparation work of PU spandex fabric low temperature lining is proposed Skill, product pressing temperature is low, peel strength it is good it is soft, elasticity is good, it can be achieved that merge completely with elastic fabric, PU fabric, Fabric is set to have better morphological stability, washing size stability and more well-pressed visual effect.
To achieve the above object, the invention proposes a kind of preparation processes of PU spandex fabric low temperature lining, comprising the following steps:
A: base fabric pads processing: using PU spandex fabric as base fabric, base fabric being carried out to an immersing and rolling process, base in staining bath Clot is stacked in uniform rotation on A cabinet frame after cloth dyeing, encapsulates yardage roll with plastic cloth, banks up 12~15 hours, after washing Dried, then will base fabric feed three segmented drying chambers in complete drying, the temperature of the drying chamber be followed successively by 60~70 DEG C, 80~90 DEG C, 100~120 DEG C;
B: base fabric cloth feeding: is entered into hot melt adhesive coating step with the speed of 30~35m/min after cooling;
C: hot melt adhesive layer processing: carrying out double-dot coating for silicone oil neutral emulsion and PA glue using cylinder and form hot melt adhesive layer, Base fabric is sent into drying chamber after cooling;
D: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 100~130 DEG C, and drying time is 4~5 minutes, third drying chamber Temperature be 130~140 DEG C, drying time be 2~3 minutes;
E: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, And it carries out the qualified product of quality, appearance to be packaged as finished product.
Preferably, antistatic agent is added in the PA glue in the step c in process of production.
Preferably, the mesh number of cylinder is CP90 in the step c, the aperture of cylinder is 0.26-0.29mm, the thickness of cylinder Degree is 0.16-0.18mm.
Beneficial effects of the present invention: the present invention proposes a kind of preparation process of PU spandex fabric low temperature lining, with material for PU tetra- Face bullet be base fabric, formed using low temperature PA glue double-dot coating, due to PU can not high temperature resistant, improve conventional coatings technique, coating temperature Degree is reduced to 140 DEG C by original 170 DEG C, is effectively guaranteed the excellent performance of PU material, and product pressing temperature is low, and removing is strong Degree it is good it is soft, elasticity is good, it can be achieved that merge completely with elastic fabric, PU fabric, make fabric have better morphological stability, Washing size stability and more well-pressed visual effect.
Feature and advantage of the invention will be described in detail by embodiment.
[specific embodiment]
A kind of preparation process of PU spandex fabric low temperature lining of the present invention, comprising the following steps:
A: base fabric pads processing: using PU spandex fabric as base fabric, base fabric being carried out to an immersing and rolling process, base in staining bath Clot is stacked in uniform rotation on A cabinet frame after cloth dyeing, encapsulates yardage roll with plastic cloth, banks up 12~15 hours, after washing Dried, then will base fabric feed three segmented drying chambers in complete drying, the temperature of the drying chamber be followed successively by 60~70 DEG C, 80~90 DEG C, 100~120 DEG C;
B: base fabric cloth feeding: is entered into hot melt adhesive coating step with the speed of 30~35m/min after cooling;
C: hot melt adhesive layer processing: carrying out double-dot coating for silicone oil neutral emulsion and PA glue using cylinder and form hot melt adhesive layer, Base fabric is sent into drying chamber after cooling;
D: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 100~130 DEG C, and drying time is 4~5 minutes, third drying chamber Temperature be 130~140 DEG C, drying time be 2~3 minutes;
E: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, And it carries out the qualified product of quality, appearance to be packaged as finished product.
Antistatic agent is added in PA glue in the step c in process of production, and the mesh number of cylinder is in the step c CP90, the aperture of cylinder are 0.26-0.29mm, cylinder with a thickness of 0.16-0.18mm.
Technical performance index:
1, peel strength: before washing >=15N/5 × 10cm, after washing >=12N/5 × 10cm;
2, xeothermic change in size: through to -1.5~+0.3, broadwise -1.0~+0.4;
3, change in size is washed: through to -1.5~+0.4, broadwise -1.0~+0.4;
4, solid carbon dioxide washes cosmetic variation >=4 grade;
5, free formaldehyde :≤75ppm is discharged;
6, pressing temperature: 125 DEG C -135 DEG C;
7, elastic extension: > 133%;
8, elastic recovery rate: > 98%.
A kind of preparation process of PU spandex fabric low temperature lining of the present invention, uses PU coating spandex fabric material for base fabric, with clothes Fabric material is consistent, can guarantee that hot-melt adhesive powder can be equably to fabric and lining by seeping when lining cloth is bonded with coating fabric in this way It thoroughly and shifts, lining cloth and coating fabric is made to have preferable bonding effect, solve common thermal smelting adesive lining and be difficult to bond PU painting The problem of layer spandex fabric;
PU coating spandex fabric material is a kind of fabric handled through special process.Fabric feeling is plentiful after painting, flexible, table There is film sense in face, and it can make to form one layer of uniform covering sizing material in web surface, thus reach waterproof, radix saposhnikoviae, the functions such as ventilative. But this fabric is often poor by hot property, if being heated above its ability to bear, it may appear that make fabric Folding Deformation, strength reduction The problems such as;Polyamide hot adhesive strength is high, dry cleaning resistance, washing, but its melting temperature, at 170-180 DEG C, pressing temperature is too Height will appear the problems such as making fabric Folding Deformation, strength reduction.This product is formed using low temperature PA glue double-dot coating, product pressing Temperature is low, and peel strength is good, and be able to satisfy PU coating fabric uses lining needs, and fabric is made to have better morphological stability, washing ruler Very little stability and more well-pressed visual effect.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention Scheme all belong to the scope of protection of the present invention.

Claims (3)

1. a kind of preparation process of PU spandex fabric low temperature lining, it is characterised in that: the following steps are included:
A: base fabric pads processing: using PU spandex fabric as base fabric, base fabric being carried out to an immersing and rolling process, base fabric dye in staining bath Clot is stacked in uniform rotation on A cabinet frame after color, encapsulates yardage roll with plastic cloth, banks up 12~15 hours, carries out after washing Drying, then will base fabric feed three segmented drying chambers in complete drying, the temperature of the drying chamber be followed successively by 60~70 DEG C, 80~ 90 DEG C, 100~120 DEG C;
B: base fabric cloth feeding: is entered into hot melt adhesive coating step with the speed of 30~35m/min after cooling;
C: hot melt adhesive layer processing: carrying out double-dot coating for silicone oil neutral emulsion and PA glue using cylinder and form hot melt adhesive layer, cooling Base fabric is sent into drying chamber afterwards;
D: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, is dried The dry time is 5~7 minutes, and the temperature of the second drying chamber is 100~130 DEG C, and drying time is 4~5 minutes, the temperature of third drying chamber It is 130~140 DEG C, drying time is 2~3 minutes;
E: winding inspection processing: base fabric is wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, and will The qualified product of quality, appearance carries out being packaged as finished product.
2. a kind of preparation process of PU spandex fabric low temperature lining as described in claim 1, it is characterised in that: in the step c Antistatic agent is added in PA glue in process of production.
3. a kind of preparation process of PU spandex fabric low temperature lining as described in claim 1, it is characterised in that: circle in the step c The mesh number of net is CP90, and the aperture of cylinder is 0.26-0.29mm, cylinder with a thickness of 0.16-0.18mm.
CN201811293943.2A 2018-11-01 2018-11-01 A kind of preparation process of PU spandex fabric low temperature lining Pending CN109403061A (en)