CN101565871A - Electromagnetic shielding cladded yarn containing superfine multicomponent stainless steel wires and electromagnetic shielding textile - Google Patents
Electromagnetic shielding cladded yarn containing superfine multicomponent stainless steel wires and electromagnetic shielding textile Download PDFInfo
- Publication number
- CN101565871A CN101565871A CNA2009100985958A CN200910098595A CN101565871A CN 101565871 A CN101565871 A CN 101565871A CN A2009100985958 A CNA2009100985958 A CN A2009100985958A CN 200910098595 A CN200910098595 A CN 200910098595A CN 101565871 A CN101565871 A CN 101565871A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- yarn
- electromagnetic shielding
- cladded
- cladded yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an electromagnetic shielding cladded yarn containing superfine multicomponent stainless steel wires. The cladded yarn comprises a central stainless steel wire. A fibrous layer is coated around the periphery of the central stainless steel wire the diameter of which is 18-23 microns. The mass percentage of the stainless steel wires in the cladded yarn is 18-20 percent. The warp yarn and weft yarn of electromagnetic shielding textile comprising the electromagnetic shielding cladded yarn consist of superfine multicomponent stainless steel wires and terylene/cotton mixed yarn. In the electromagnetic shielding textile, the arrangement ratio of wrap-direction stainless steel cladded yarn to the terylene/cotton mixed yarn is 3:1, 2:1 or 1:1 and the arrangement ratio of weft-direction stainless steel cladded yarn to the terylene/cotton mixed yarn is 2:1 or 1:1. The cladded yarn has not only high electromagnetic shielding function and wider shielding range, but also good wear behavior, and the stainless steel does not contact the skin and not affect the appearance or dyeing and finishing performance of fabric.
Description
Technical field
The invention belongs to textile technology field, be specifically related to a kind of Electromagnetically shielding fabrics that contains superfine multicomponent stainless steel wires.
Background technology
Progress along with the epoch, popularizing and development of electronic product, electromagnetic radiation is endangering the healthy of people unawares, and electromagnetic radiation pollution has become the fourth-largest pollution after waste water, exhaust emission and noise pollution, is universally acknowledged " stealthy killer ".Electromagnetic radiation all can produce adverse influence to nervous system, vision system, fertility system, the cardiovascular system of human body; so the World Health Organization and many countries; all will reduce electromagnetic radiation intensity, and prevent to pollute, the protection public health has been mentioned on the at present the most urgent agenda.Thereby research and development anti-electromagnetic-radiation protection textiles has important practical sense and profound influence.
At present more existing developmental researches about the stainless steel fabric electromangnetic spectrum, but, can influence the feel of fabric because the stainless steel wire diameter is thicker, wearability of fabric is relatively poor.As illustrated in fig. 1 and 2.At present weaving is used contain the stainless steel yarn for and twist thread or yarn bag stainless steel fibre, the two all can have stainless steel wire to be exposed at fabric face outward, influence arrangements such as the outward appearance of fabric and dyeing, and the direct contact skin of stainless steel, and skin is produced necessarily stimulation.
Summary of the invention
The purpose of this invention is to provide a kind of superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains, have better electromagnet shield effect and wider shield ranges.And stainless steel wire is covered by in the fibrage, does not directly contact skin.
Another object of the present invention provides a kind of utilization and contains the Electromagnetically shielding fabrics that superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn and washing/silk/cotton blended yarn is formed.This fabric has wearability preferably, and the outward appearance of fabric and dyeing and finishing performance are also better.
The technical solution used in the present invention is: a kind of superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains, comprise the center stainless steel wire, and be coated with fibrage in the periphery of center stainless steel wire; Center stainless steel wire diameter is the 18-23 micron.
The superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains of the present invention, stainless steel wire quality percentage composition is 18%-20% in the described cladded yarn.
Utilize the Electromagnetically shielding fabrics that contains superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn of the present invention, the warp thread of described fabric and weft yarn are formed by containing superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn and washing/silk/cotton blended yarn.
Electromagnetically shielding fabrics of the present invention, warp-wise stainless steel cladded yarn with wash/the arrangement ratio of silk/cotton blended yarn is 3: 1 or 2: 1 or 1: 1, the Weft-wise stainless steel cladded yarn with wash/the arrangement ratio of silk/cotton blended yarn is 2: 1 or 1: 1.
Electromagnetically shielding fabrics of the present invention, described organizational structure of fabrics are plain weave or twill.
Beneficial effect of the present invention: the superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains provided by the invention, the existing on the market stainless steel wire fineness that contains in the stainless steel wire yarn is thinner at present for the stainless steel wire fineness at its center, the taking of such yarn is better, and it is also soft more to be made into the feel of fabric behind the fabric.And stainless steel wire is coated on fibrage inside fully, and stainless steel wire can directly not contact skin when making fabric, and is comfortable and easy to wear.Utilize the above-mentioned Electromagnetically shielding fabrics that contains superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn, owing to adopt the stainless steel wire of cladded yarn structure and employing superfine multicomponent, not only have good electro-magnetic screen function and wider shield ranges, soft, comfortable and easy to wear, and stainless steel wire is enclosed in the yarn center, do not influence appearance of fabrics and dyeing and finishing performance.
Description of drawings
Fig. 1 is the stainless steel of the prior art and the structural representation of twisting thread;
Fig. 2 is a yarn bag stainless steel fibre structural representation of the prior art;
Fig. 3 is the superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn structural representation that contains of the present invention;
Fig. 4 is the stainless steel wire unwinding mode figure that contains superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn of the present invention;
Fig. 5 is the spandex silk unwinding mode figure of normal packet heart yarn;
Fig. 6 is fabric plain weave construction figure;
Fig. 7 is a fabric twill-weave structure chart.
1, be fibrage 2, for stainless steel wire 3, for cotton yarn
The specific embodiment
As shown in Figure 3, a kind of superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains comprises center stainless steel wire 2, is coated with fibrage 1 in the periphery of center stainless steel wire 2, chemical fibre materials such as described fibrage 1 employing cotton fiber or terylene, polyamide fibre.The diameter of center stainless steel wire 2 is the 18-23 micron.And the quality percentage composition of stainless steel wire is 18%-20% in the cladded yarn.The stainless steel cladded yarn is by adopting unwinding equipment, draft apparatus to be spun into through the fine spining machine of transforming.Its unwinding mode is different from the spandex silk unwinding mode of normal packet heart yarn of the prior art as shown in Figure 5 as shown in Figure 4.
Shown in Fig. 6 and 7, utilize a kind of Electromagnetically shielding fabrics that contains superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn and polyester cotton blended yarn composition of the present invention, its fabric construction can be plain weave or twill.Concrete weaving process is as follows:
Weaving method 1:
Whether 1) warp thread is prepared: at first check raw material qualified, Electromagnetically shielding fabrics of the present invention is used to be that 18tex stainless steel cladded yarn, 18tex wash/silk/cotton blended yarn through the weft yarn raw material, then two stainless steel cladded yarns are washed with two/silk/cotton blended yarn is respectively and twist with the fingers into doublet cord, the 3rd step was a warping, with the above-mentioned and yarn twisted with the fingers as warp thread, the stainless steel cladded yarn with wash/the arrangement ratio of silk/cotton blended yarn is generally 3: 1 or 2: 1 or 1: 1, at last for passing denting.
2) weft yarn is prepared: whether the check raw material is qualified earlier, and the used weft yarn raw material of Electromagnetically shielding fabrics of the present invention comprises that 18tex stainless steel cladded yarn, 18tex wash/silk/cotton blended yarn.
3) weave: 18tex stainless steel cladded yarn is set wash/the weft yarn arrangement ratio of cotton yarn is 1: 1 with 18tex, be made into plain weave or
TWILL CLOTH, the arrangement that also can be designed to other is as required compared and institutional framework.
Weaving method 2:
Whether 1) warp thread is prepared: at first check raw material qualified, the used warp thread raw material of Electromagnetically shielding fabrics of the present invention comprises that 18tex stainless steel cladded yarn, 18tex wash/silk/cotton blended yarn, then two stainless steel cladded yarns are washed with two/silk/cotton blended yarn is respectively and twist with the fingers into doublet cord, the 3rd step was a warping, with the above-mentioned and yarn twisted with the fingers as warp thread, the stainless steel cladded yarn with wash/the arrangement ratio of silk/cotton blended yarn is 2: 1 or 1: 1, at last for passing denting.
2) weft yarn is prepared: whether the check raw material is qualified, and the used weft yarn raw material of the present invention comprises that 18tex stainless steel cladded yarn, 18tex wash/silk/cotton blended yarn.
Claims (5)
1, a kind of superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains is characterized in that: comprise the center stainless steel wire, be coated with fibrage in the periphery of center stainless steel wire; Center stainless steel wire diameter is the 18-23 micron.
2, the superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn that contains as claimed in claim 1, it is characterized in that: stainless steel wire quality percentage composition is 18%-20% in the cladded yarn.
3, utilize the Electromagnetically shielding fabrics of claim 1 or 2 described cladded yarns, it is characterized in that: the warp thread of fabric and weft yarn are formed by containing superfine multicomponent stainless steel wires electromagnetic shielding cladded yarn and washing/silk/cotton blended yarn.
4, Electromagnetically shielding fabrics as claimed in claim 3 is characterized in that: warp-wise stainless steel cladded yarn with wash/the arrangement ratio of silk/cotton blended yarn is 3: 1 or 2: 1 or 1: 1, the Weft-wise stainless steel cladded yarn with wash/the arrangement ratio of silk/cotton blended yarn is 2: 1 or 1: 1.
5, Electromagnetically shielding fabrics as claimed in claim 3 is characterized in that: fabric structure is plain weave or twill.