CN101560717A - Manufacturing method of fuzz-pilling resistant cellulose fiber weft-knitted fabric - Google Patents
Manufacturing method of fuzz-pilling resistant cellulose fiber weft-knitted fabric Download PDFInfo
- Publication number
- CN101560717A CN101560717A CNA2008100361983A CN200810036198A CN101560717A CN 101560717 A CN101560717 A CN 101560717A CN A2008100361983 A CNA2008100361983 A CN A2008100361983A CN 200810036198 A CN200810036198 A CN 200810036198A CN 101560717 A CN101560717 A CN 101560717A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- weft
- fabric
- cellulose fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method of a fuzz-pilling resistant cellulose fiber weft-knitted fabric, comprising the following steps: (1) processing spun yarn: synchronously drawing and spinning two ribbons consisting of cellulose fiber and cotton to obtain a blended yarn of the cellulose fiber and cotton fiber; (2) taking the blended yarn of the cellulose fiber and the cotton fiber, which is obtained in the step (1), as a wire gauze, and knitting the blended yarn with a naked spandex yarn by a weft plain knitting method, wherein each knitting system knits one wire gauze and one naked spandex yarn plating yarn together to obtain a weft-knitted single-face plain knitting platedwork fabric; and (3) heating and pre-shaping the weft-knitted single-face plain knitting platedwork fabric, and then dyeing and shaping the weft-knitted single-face plain knitting platedwork fabric to obtain the fuzz-pilling resistant cellulose fiber weft-knitted fabric. The invention not only solves the problem of fuzz-pilling resistance of a blended fabric taking the cellulose fiber as the main part, but also has large elastic extension and small elastic-restoring force, and also has soft and comfortable hand feeling after being knitted into clothes and trousers.
Description
Technical field
The cellulose fibre that is used for underskirt shirt trousers that the present invention relates in a kind of textile material is main Weft knitted fabric.
Background technology
Traditionally, the knit fabric that is used for underskirt shirt trousers weaves with cotton.In recent years, along with people constantly pursue comfortable and easy to wearization, the more and more cellulose fibres that adopt of the knit fabric of underskirt shirt trousers.Cellulose fibre is more soft than cotton, and hygroscopicity is better.But the greatest weakness of cellulose fiber knitted thing is easy pilling.
In the prior art, in order to overcome the pilling phenomenon of cellulose fiber knitted thing, often improve with cellulose fibre and other fiber blend.But to significantly improve the pilling phenomenon, then will be with the low ratio of cellulose fibre, other fiber comes blending at high proportion.Like this, the comfortableness advantage of cellulose fibre is just not remarkable in the fabric.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of Weft knitted fabric of cellulose fibre of anti-fluffing and anti-pilling, to overcome the above-mentioned defective that prior art exists.
Method of the present invention comprises the steps:
(1) spun yarn processing: add Ministry of worker's section at spun yarn and introduce drawing process, with cellulose fibre bar and cotton two ribbons of forming, one side drafting is spun yarn on one side, obtain the blended yarn of cellulose fiber peacekeeping cotton fiber, the blended yarn that is obtained is not two yarns and similar pair of yarn, strengthened fiber and in yarn, assembled, made yam surface bright and clean, having weaved neutralization and being difficult for fluffing in taking;
Preferably, in the yarn, the weight content of cellulose fibre is 55%～80%, and the weight content of cotton fiber is 20%～45%, is difficult for the fiber of pilling owing to added some, makes fabric be difficult for pilling;
Said cellulose is Modal, bamboo pulp fiber or tencel fiber;
Said " Modal " is a kind of improved cellulose fibre, and English claims Modal, can adopt the product of the blue smart company of Britain;
The fineness of cellulose fibre is 0.66～0.88dtex, and the fineness of cotton fiber is about 1.67dtex, and the fineness of blended yarn is 14.9～28.4dtex;
(2) blended yarn of the cellulose fiber peacekeeping cotton fiber that obtains with step (1) is wire gauze and the knitting braid method of the naked spandex yarn employing flat pin of latitude, weave, each system for weaving inweaves together with a wire gauze and a naked spandex yarn plaiting line, obtain the flat pin plating structure of a kind of weft-knitted single face lining, this lining shrinks closely, is difficult for pilling;
The naked spandex yarn fineness is 22～44dtex;
The knitting braid method of the flat pin of said latitude is in that " detailed description is arranged on the knitting handbook, and the present invention repeats no more.
In step (2), the wire gauze tissue, i.e. the plain stitch of blended yarn is adopted than conventional little underfill coefficient, and preferred underfill coefficient is 17～19, makes fabric knit relatively closely;
The underfill coefficient is defined as follows:
Underfill coefficient=loop length/yarn diameter;
(3) behind the weaving textile, heat pre-setting, the pre-setting temperature is 190～195 ℃, eliminate the fabric fine wrinkle, spandex wherein combines with semi-molten shape and wire gauze, dyes then and finalizes the design, and obtains the Weft knitted fabric of the cellulose fibre of said anti-fluffing and anti-pilling.
The Weft knitted fabric of the cellulose fibre of the anti-fluffing and anti-pilling that the employing said method is made, fabric size is stable, makes knitting underwear, and elastic extension is big, and elastic-restoring force is little, forms comfortable Clothing Pressure.
The present invention has not only solved the anti-fluffing and anti-pilling problem that cellulose fibre is main BLENDED FABRIC, and elastic extension is big, and elastic-restoring force is little, make knit in behind the clothing trousers, soft comfortable.
The specific embodiment
Embodiment 1
(1) spun yarn processing: with cellulose fibre bar and cotton fiber bar, on one side drafting one side spun yarn, the blended yarn of acquisition cellulose fiber peacekeeping cotton fiber;
The weight content of cellulose fibre is 55%, and the weight content of cotton fiber is 45%;
Said cellulose is a bamboo pulp fiber;
The fineness of cellulose fibre is 0.88dtex, and the fineness of cotton fiber is 1.67dtex, and the fineness of blended yarn is 18.6dtex;
(2) blended yarn of the cellulose fiber peacekeeping cotton fiber that obtains with step (1) is wire gauze and naked spandex yarn employing latitude plain stitch braid method, weave, each system for weaving inweaves together with a wire gauze and a naked spandex yarn plaiting line, obtains the flat pin plating structure of weft-knitted single face lining;
The naked spandex yarn fineness is 22dtex;
The underfill coefficient that the plain stitch of blended yarn is adopted is 17;
(3) behind the weaving textile, heat pre-setting, the pre-setting temperature is 190 ℃, dyes then and finalizes the design, and obtains the Weft knitted fabric of the cellulose fibre of said anti-fluffing and anti-pilling.
Adopt national standard to detect:
Pilling resistance: 4～5 grades
The washing size changing rate: directly to: 2.3%, horizontal 2.9%
Pellet shot from a slingshot bursting strength: 293N.
Embodiment 2
(1) spun yarn processing: with the ribbon of cellulose fiber peacekeeping cotton, on one side drafting one side spun yarn, the blended yarn of acquisition cellulose fiber peacekeeping cotton fiber;
The weight content of cellulose fibre is 80%, and the weight content of cotton fiber is 20%;
Said cellulose is a day silk;
The fineness of cellulose fibre is 0.77dtex, and the fineness of cotton fiber is 1.67dtex, and the fineness of blended yarn is 15.6tex;
(2) blended yarn of the cellulose fiber peacekeeping cotton fiber that obtains with step (1) is wire gauze and the knitting braid method of the naked spandex yarn employing flat pin of latitude, weave, each system for weaving inweaves together with a wire gauze and a naked spandex yarn plaiting line, obtains the flat pin plating structure of weft-knitted single face lining;
The naked spandex yarn fineness is 33dtex;
The underfill coefficient that the plain stitch of blended yarn is adopted is 19;
(3) behind the weaving textile, heat pre-setting, the pre-setting temperature is 195 ℃, dyes then and finalizes the design, and obtains the Weft knitted fabric of the cellulose fibre of said anti-fluffing and anti-pilling.
Adopt national standard to detect,
The anti-fluffing and anti-pilling performance is as follows: 4 grades
The washing size changing rate: directly to: 3.1%, horizontal 4.6%
Pellet shot from a slingshot bursting strength: 246N.
Embodiment 3
Adopt the method identical with embodiment 1, cellulose is a Modal.
Adopt the national standard standard to detect,
Pilling resistance: 4～5 grades
The washing size changing rate: directly to: 2.0%, horizontal 2.6%
Pellet shot from a slingshot bursting strength: 322N.
Claims (5)
1. the preparation method of the Weft knitted fabric of the cellulose fibre of an anti-fluffing and anti-pilling is characterized in that, comprises the steps:
(1) spun yarn is processed: with cellulose fibre bar and cotton two ribbons of forming, on one side drafting one side spun yarn, the blended yarn of acquisition cellulose fiber peacekeeping cotton fiber;
(2) blended yarn of the cellulose fiber peacekeeping cotton fiber that obtains with step (1) is that wire gauze weaves with naked spandex yarn employing latitude plain stitch braid method, each system for weaving inweaves together with a wire gauze and a naked spandex yarn plaiting line, obtains the flat pin plating structure of weft-knitted single face lining;
The underfill coefficient of the plain stitch of blended yarn is 17～19;
(3) heat pre-setting then, make that said naked spandex yarn is in the semi-molten state in the fabric, dye again and finalize the design, obtain the Weft knitted fabric of the cellulose fibre of said anti-fluffing and anti-pilling.
2. method according to claim 1 is characterized in that, the weight content of cellulose fibre is 55%～80%, and the weight content of cotton fiber is 20%～45%.
3. method according to claim 2 is characterized in that, said cellulose fibre is Modal, bamboo pulp fiber or tencel fiber.
4. method according to claim 1 is characterized in that, the fineness of cellulose fibre is 0.66～0.88dtex, and the fineness of cotton fiber is 1.67dtex, and the fineness of blended yarn is 14.9～28.4dtex.
5. method according to claim 1 is characterized in that, the naked spandex yarn fineness is 22～44dtex.