CN101531834A - Chlorite pearlescent pigment - Google Patents
Chlorite pearlescent pigment Download PDFInfo
- Publication number
- CN101531834A CN101531834A CN200910011228A CN200910011228A CN101531834A CN 101531834 A CN101531834 A CN 101531834A CN 200910011228 A CN200910011228 A CN 200910011228A CN 200910011228 A CN200910011228 A CN 200910011228A CN 101531834 A CN101531834 A CN 101531834A
- Authority
- CN
- China
- Prior art keywords
- chlorite
- pigment
- portions
- pearlescent pigment
- mica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of pigment, and in particular relates to a chlorite pearlescent pigment. The chlorite pearlescent pigment consists of the following raw materials in portion by weight: 10 to 20 portions of mica powder, 5 to 10 portions of phosphoric acid, 50 to 80 portions of chlorite powder, 1 to 10 portions of titanium salt solution, 1 to 10 portions of aqueous alkali, and 0.1 to 0.5 portion of natural perfume. The titanium salt solution is titanyl sulfate. Compared with the pigment produced by mica in the prior art, the chlorite pearlescent pigment has the remarkable characteristics of low cost, simple manufacturing process and rich color. The heat resistance, light resistance, sulfidation resistance and chemical resistance of the product are quite good; and the chlorite pearlescent pigment can be widely applied in the industries such as coating, paint, plastics, packing, papermaking, cosmetics, ornaments and the like, and has good market application prospect.
Description
Technical field
The invention belongs to the technical field of pigment, relate in particular to a kind of chlorite pearlescent pigment.
Background technology
Pigment all be unable to do without in daily life and work, and the kind of pigment is varied, and it is very popular especially to have a pearly pigment of pearliness or metalluster.The source of these pearly pigments has following several: wherein the natural peral powder extracts from fish scale, and the primary pearly pigment is the main synthetic that carries out with lead.Though these pearly pigment aboundresources, its form and aspect are limited, and fast light weathering resistance is relatively poor; Particularly because of it contains heavy metal, thereby make its use range be subjected to very big restriction.Though and traditional metalluster pigment aluminium silver powder and copper bronze metalluster are strong, weathering resistance and chemical-resistant stability are very poor, and need to consume a large amount of nonferrous metal resources.
Just begin constantly to report and paper publishing from the end of the nineties in China relevant for the each side of nacreous mica pigment.Mica is the general name of laminate structure aluminosilicates such as potassium, aluminium, magnesium, iron, lithium.The ubiquity polytypism, the person is common wherein to belong to the oblique system, is trigonal system secondly, and all the other are rare.Mica is six sides usually or rhombohedral is tabular, sheet, column crystalline form.Color is different with the variation of chemical ingredients, mainly increasing and deepen with Fe content.The white mica water white transparency or be light color; Biotite is black extremely brown deeply, dark green isochrome; It is yellow, brown, green or colourless that phlogopite is; Lithionite is lavender, rose to grey.Vitreous luster is pearliness on the cleavage surface.Utilizing mica at present is that weathering resistance and chemical stability are all fine for the pearly pigment of raw material production, and nontoxicity, also have abundant colors, therefore also be subjected to liking very much of people, and also all on industries such as high-grade automobile, coating, printing ink, makeup, enamel, use to some extent.In recent years, China's production technology in this respect also has constantly rapidly raising, but because of the micaceous price very expensive, and its production technique is more complicated also, therefore make the related products that utilizes mica to produce, especially the price of pigment is high always, also therefore makes its related products have certain degree of difficulty and ubiquity on promoting.
Summary of the invention
The present invention be directed to the problem that prior art exists, a kind of chlorite pearlescent pigment is provided, it has distinguishing feature cheap, that technology is simple, rich color is colorful.
The present invention realizes by the following technical solutions:
A kind of nacreous mica pigment, it by following raw materials by weight portion than forming:
Mica powder: phosphoric acid: green mud stone flour: titanium salt solution: alkaline solution: natural perfume=10～20:5～10:50～80:1～10:1～10:0.1～0.5.
Described titanium salt solution is a titanyl sulfate.
Chlorite, crystal belong to monocline, three oblique or quadrature rhombic systems, are the general names of the silicate minerals of gang's laminate structure.Usually said chlorite is to be rich in mafic chlorite.Crystal is false hexagonal flake or tabular, and the thin slice tool is flexible, and aggregate is flakey, earthy, and is light green to deep green; Vitreous luster or pearliness are clear to opaque.Chlorite is extremely similar to mica, but chlorite has the green of feature, has flexible and nonelastic.
The pigment that utilizes mica to produce in the present invention and the prior art is compared, and has distinguishing feature cheap, that manufacture craft is simple, rich color is colorful.The thermotolerance of product of the present invention, photostabilization, sulfidation-resistance and chemical resistant properties are all very good, can be widely used in industries such as coating, paint, plastics, packing, papermaking, makeup, ornament, have better market application.
Embodiment
Embodiment 1:
A kind of nacreous mica pigment by following raw materials by weight portion than forming:
Mica powder: phosphoric acid: green mud stone flour: titanium salt solution: alkaline solution: natural perfume=10:5:80:1:3.5:0.5.
Described titanium salt solution is selected titanyl sulfate for use.
The producing and manufacturing technique of nacreous mica pigment of the present invention is conventional process for producing.
Embodiment 2:
A kind of nacreous mica pigment by following raw materials by weight portion than forming:
Mica powder: phosphoric acid: green mud stone flour: titanyl sulfate: alkaline solution: natural perfume=15:8:70:5.5:1:0.1.
Other is with embodiment 1.
Embodiment 3:
A kind of nacreous mica pigment by following raw materials by weight portion than forming:
Mica powder: phosphoric acid: green mud stone flour: titanyl sulfate: alkaline solution: natural perfume=20:10:49.7:10:10:0.3.
Other is with embodiment 1.
Claims (2)
1, a kind of nacreous mica pigment, it is characterized in that it by following raw materials by weight portion than forming:
Mica powder: phosphoric acid: green mud stone flour: titanium salt solution: alkaline solution: natural perfume=10～20:5～10:50～80:1～10:1～10:0.1～0.5.
2, a kind of nacreous mica pigment according to claim 1 is characterized in that described titanium salt solution is a titanyl sulfate.