CN101525859B - 一种表面施胶淀粉的制备方法 - Google Patents

一种表面施胶淀粉的制备方法 Download PDF

Info

Publication number
CN101525859B
CN101525859B CN2009100381411A CN200910038141A CN101525859B CN 101525859 B CN101525859 B CN 101525859B CN 2009100381411 A CN2009100381411 A CN 2009100381411A CN 200910038141 A CN200910038141 A CN 200910038141A CN 101525859 B CN101525859 B CN 101525859B
Authority
CN
China
Prior art keywords
starch
weight
preparation
surface sizing
value
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100381411A
Other languages
English (en)
Other versions
CN101525859A (zh
Inventor
陈沛华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN DONGMEI FOOD Co Ltd
Original Assignee
DONGGUAN DONGMEI FOOD Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN DONGMEI FOOD Co Ltd filed Critical DONGGUAN DONGMEI FOOD Co Ltd
Priority to CN2009100381411A priority Critical patent/CN101525859B/zh
Publication of CN101525859A publication Critical patent/CN101525859A/zh
Application granted granted Critical
Publication of CN101525859B publication Critical patent/CN101525859B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明一种表面施胶淀粉的制备方法，包括如下所用物质、物质的重量份数和制备步骤：①将200份淀粉与300份蒸馏水搅拌均匀后移入三口烧瓶中，升温至30～32℃；②用浓度为3％的氢氧化钠溶液调节其pH值为9.0～9.2，加入淀粉重量10～15％的次氯酸钠溶液，紧接着加入淀粉重量1～3％的醋酸乙烯酯，同时进行氧化-酯化反应2～4小时，反应过程使用碳酸钠保持pH值不变；③加入淀粉重量3‰的亚硫酸钠进行脱氯；④用稀盐酸溶液调节pH值为6.2～6.3，经脱水、干燥、粉碎得到表面施胶淀粉成品。本发明的优点在于：用本发明方法，与现有技术相比，淀粉成膜性好，用于造纸行业，文化纸不易掉毛、掉粉，提高了纸的质量。

Description

一种表面施胶淀粉的制备方法
技术领域
本发明一种表面施胶淀粉的制备方法，涉及淀粉的制备方法。
背景技术
现有技术表面施胶淀粉的制备方法，制备步骤中，只有氧化反应，没有酯化反应，其不足之处在于：这种淀粉用于造纸行业，文化纸易掉毛，掉粉。
发明内容
本发明所要解决的技术问题就是为了上述不足之处而提供一种表面施胶淀粉的制备方法，在制备过程中，加入次氯酸钠溶液后，紧接着加入醋酸乙烯酯，同时进行氧化-酯化反应，双重变性，改善了淀粉浆的成膜性，用于造纸行业，文化纸不易掉毛、掉粉。
本发明采用如下技术方案。
一种表面施胶淀粉的制备方法，包括如下所述的所用物质、物质的重量份数和制备步骤：
①.将200份淀粉分散于300份蒸馏水中，搅拌均匀后移入三口烧瓶中，升温至30～32℃，得到淀粉浆A；
②.用浓度为3％的氢氧化钠溶液调节淀粉浆A的pH值为9.0～9.2，加入次氯酸钠溶液，加入量为淀粉重量的10～15％，紧接着加入醋酸乙烯酯，加入量为淀粉重量的1～3％，同时进行氧化-酯化反应，反应时间为2～4小时，反应过程使用碳酸钠保持pH值不变，得到淀粉浆B；
③.加入亚硫酸钠到淀粉浆B中进行脱氯，加入量为淀粉重量的3‰，得到淀粉浆C；
④.用稀盐酸溶液调节淀粉浆C的pH值为6.2～6.3，经脱水、干燥、粉碎得到表面施胶淀粉成品。
步骤②所述的所加入的次氯酸钠溶液的加入量为淀粉重量的12％或15％，紧接着加入醋酸乙烯酯的加入量为淀粉重量的1.5％或2％，反应时间为2.5小时或3小时。
本发明的优点在于：现有技术表面施胶淀粉在制备过程中只有氧化反应，没有酯化反应，淀粉浆的成膜性较差，用于造纸行业导致文化纸易掉毛、掉粉。使用本发明的方法，制备表面施胶淀粉，在加入次氯酸钠溶液后，紧接着加入醋酸乙烯酯，同时进行氧化-酯化反应，一步法制备，双重变性，节约时间，提高了生产效率，成膜性好，用于造纸行业，文化纸不易掉毛、掉粉，提高了纸的质量，这种纸用于印刷，不易掉毛、掉粉到印刷板上，每印9000张才需清洗一次印版，而现有技术造纸每印4000张就需清洗一次印版，本发明可提高印刷质量和效率，深受造纸行业厂商欢迎。
具体实施方式
实施例一：
一种表面施胶淀粉的制备方法，包括如下所述的所用物质、物质的重量份数和制备步骤：
①.将200份淀粉分散于300份蒸馏水中，搅拌均匀后移入三口烧瓶中，升温至30～32℃，得到淀粉浆A；
②.用浓度为3％的氢氧化钠溶液调节淀粉浆A的pH值为9.0～9.2，加入次氯酸钠溶液，加入量为淀粉重量的15％，紧接着加入醋酸乙烯酯，加入量为淀粉重量的2％，同时进行氧化-酯化反应，反应时间为3小时，反应过程使用碳酸钠保持pH值不变，得到淀粉浆B；
③.加入亚硫酸钠到淀粉浆B中进行脱氯，加入量为淀粉重量的3‰，得到淀粉浆C；
④.用稀盐酸溶液调节淀粉浆C的pH值为6.2～6.3，经脱水、干燥、粉碎得到表面施胶淀粉成品。
实施例二：
一种表面施胶淀粉的制备方法，包括如下所述的所用物质、物质的重量份数和制备步骤：
①.将200份淀粉分散于300份蒸馏水中，搅拌均匀后移入三口烧瓶中，升温至30～32℃，得到淀粉浆A；
②.用浓度为3％的氢氧化钠溶液调节淀粉浆A的pH值为9.0～9.2，加入次氯酸钠溶液，加入量为淀粉重量的12％，紧接着加入醋酸乙烯酯，加入量为淀粉重量的1.5％，同时进行氧化-酯化反应，反应时间为2.5小时，反应过程使用碳酸钠保持pH值不变，得到淀粉浆B；
③.加入亚硫酸钠到淀粉浆B中进行脱氯，加入量为淀粉重量的3‰，得到淀粉浆C；
④.用稀盐酸溶液调节淀粉浆C的pH值为6.2～6.3，经脱水、干燥、粉碎得到表面施胶淀粉成品。

Claims (2)

1.一种表面施胶淀粉的制备方法，其特征在于：包括如下所述的所用物质、物质的重量份数和制备步骤：
①.将200份淀粉分散于300份蒸馏水中，搅拌均匀后移入三口烧瓶中，升温至30～32C，得到淀粉浆A；
②.用浓度为3％的氢氧化钠溶液调节淀粉浆A的pH值为9.0～9.2，加入次氯酸钠溶液，加入量为淀粉重量的10～15％，紧接着加入醋酸乙烯酯，加入量为淀粉重量的1～3％，同时进行氧化-酯化反应，反应时间为2～4小时，反应过程使用碳酸钠保持pH值不变，得到淀粉浆B；
③.加入亚硫酸钠到淀粉浆B中进行脱氯，加入量为淀粉重量的3‰，得到淀粉浆C；
④.用稀盐酸溶液调节淀粉浆C的pH值为6.2～6.3，经脱水、干燥、粉碎得到表面施胶淀粉成品。
2.根据权利要求1所述的一种表面施胶淀粉的制备方法，其特征在于：步骤②所述的所加入的次氯酸钠溶液的加入量为淀粉重量的12％或15％，紧接着加入醋酸乙烯酯的加入量为淀粉重量的1.5％或2％，反应时间为2.5小时或3小时。
CN2009100381411A 2009-03-24 2009-03-24 一种表面施胶淀粉的制备方法 Expired - Fee Related CN101525859B (zh)