CN101521072B - 功率型电感器铁氧体锰镁锌材料及用途 - Google Patents
功率型电感器铁氧体锰镁锌材料及用途 Download PDFInfo
- Publication number
- CN101521072B CN101521072B CN2008102347980A CN200810234798A CN101521072B CN 101521072 B CN101521072 B CN 101521072B CN 2008102347980 A CN2008102347980 A CN 2008102347980A CN 200810234798 A CN200810234798 A CN 200810234798A CN 101521072 B CN101521072 B CN 101521072B
- Authority
- CN
- China
- Prior art keywords
- oxide
- magnesium
- manganese
- power
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种功率型电感器铁氧体锰镁锌材料及用途，由氧化铁、氧化镁、氧化锌、氧化锰混合煅烧后，再加入辅助材料，并经常规砂磨、烘干、制粒后压制成型得到。本发明生产成本低，具有高磁通密度(Bs达4000G)、高居里温度(Tc达210℃)、高绝缘电阻率(达103MΩ(500V))，可广泛应用于制备功率电感器磁芯元件等材料。
Description
技术领域：
本发明涉及一种新型材料。
背景技术：
电子行业飞速发展，一般用于阴极射线显示器、液晶显示器、等离子显示器、数码相机及其他电子设备和通讯设备的电源部分材料，为镍锌材料，但其存在成本高，磁导性能不理想等缺陷。
发明内容：
本发明的目的在于提供一种具有高磁通密度，生产成本低的功率型电感器铁氧体锰镁锌材料及用途。
本发明的技术解决方案是：
一种功率型电感器铁氧体锰镁锌材料，其特征是：由氧化铁、氧化镁、氧化锌、氧化锰混合煅烧后，再加入辅助材料，并经砂磨、烘干、制粒后压制成型得到。
氧化铁、氧化镁、氧化锌、氧化锰四种材料用量百分比为：
氧化铁 45～50mol％
氧化镁 25～35mol％
氧化锌 15～20mol％
氧化锰 5～10mol％；
四种材料的用量之和为100％；
所述辅助材料和相对于上述四种材料之和的用量为：
CuO 1～2wt％
Bi2O3 1～2wt％。
一种功率型电感器铁氧体锰镁锌材料在制备功率电感器磁芯元件中的应用。
本发明生产成本低，具有高磁通密度(Bs达4000G)、高居里温度(Tc达210℃)、高绝缘电阻率(达103MΩ(500V))，可广泛应用于制备功率电感器磁芯元件等材料。
下面结合实施例对本发明作进一步说明。
具体实施方式：
一种功率型电感器铁氧体锰镁锌材料，由氧化铁、氧化镁、氧化锌、氧化锰混合煅烧后，再加入辅助材料，并经常规砂磨、烘干、制粒后压制成型得到。
氧化铁、氧化镁、氧化锌、氧化锰四种材料用量百分比为：
氧化铁 45～50mol％(例45mol％、48mol％、50mol％)
氧化镁 25～35mol％(例25mol％、30mol％、35mol％)
氧化锌 15～20mol％(例15mol％、17mol％、20mol％)
氧化锰 5～10mol％(例5mol％、8mol％、10mol％)；
四种材料的用量之和为100％；
所述辅助材料和相对于上述四种材料之和的用量为：
CuO 1～2wt％(例1wt％、1.5wt％、2wt％)
Bi2O3 1～2wt％(例1wt％、1.5wt％、2wt％)。
上述功率型电感器铁氧体锰镁锌材料在制备功率电感器磁芯元件中的应用。
Claims (2)
1.一种功率型电感器铁氧体锰镁锌材料，其特征是：由氧化铁、氧化镁、氧化锌、氧化锰混合煅烧后，再加入辅助材料，并经砂磨、烘干、制粒后压制成型得到；氧化铁、氧化镁、氧化锌、氧化锰四种材料用量百分比为：
氧化铁 45～50mol％
氧化镁 25～35mol％
氧化锌 15～20mol％
氧化锰 5～10mol％；
四种材料的用量之和为100％；
所述辅助材料和相对于上述四种材料之和的用量为：
CuO 1～2wt％
Bi2O3 1～2wt％。
2.一种权利要求1所述的功率型电感器铁氧体锰镁锌材料在制备功率电感器磁芯元件中的应用。