CN101508017B - 一种铸渣机脱模剂 - Google Patents
一种铸渣机脱模剂 Download PDFInfo
- Publication number
- CN101508017B CN101508017B CN2009101164455A CN200910116445A CN101508017B CN 101508017 B CN101508017 B CN 101508017B CN 2009101164455 A CN2009101164455 A CN 2009101164455A CN 200910116445 A CN200910116445 A CN 200910116445A CN 101508017 B CN101508017 B CN 101508017B
- Authority
- CN
- China
- Prior art keywords
- slag
- lead
- releasing agent
- lime
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种铸渣机的脱模剂，脱模剂是由炼铅本系统的收尘产物铅烟灰、石灰和水组成，所述的铅烟灰的质量为所述石灰3～5倍，所述水的质量为所述的铅烟灰和石灰总质量的6～10倍；脱模剂各组成成分配合后，通入压缩空气进行搅拌。本发明利用炼铅收尘产物铅烟灰为主要原料，其与熔融状态的高铅渣冷却凝固过程中熔合在一起，使得渣模与渣块之间形成一定的空隙，脱模非常容易，脱模效果显著改善。
Description
技术领域
本发明涉及适用于有色金属炼铅行业的铸渣机脱模剂。
背景技术
目前，各氧气底吹炼铅厂家氧气底吹熔炼炉中产出的熔融高铅渣均直接流入链式铸渣机中，在铸渣机渣模内铸成渣块落下后再加入鼓风炉中进行还原熔炼，产出二次粗铅。高铅渣在铸渣机中铸块后不易脱模，通常各炼铅厂家均采用一定的措施，以帮助脱模，例如：在铸渣机头部设置机械振打装置敲打渣模，使渣块落下，但同时也容易造成渣块的粉碎，严重影响了渣块在鼓风炉内的还原熔炼效果。于是各炼铅厂家纷纷采用脱模剂来改善脱模效果，所采用的脱模剂通常都是由石灰水泥浆搅拌而成，脱模效果仍然较差，且脱模剂极易附着在渣模内，造成渣模内表面粗糙不平，常有难以脱模的现象发生，给生产的连续性带来了一定的影响。
发明内容
本发明的目的是提供一种铸渣机脱模剂，利用炼铅收尘产物铅烟灰为主要原料，其与熔融状态的高铅渣冷却凝固过程中熔合在一起，使得渣模与渣块之间形成一定的空隙，脱模非常容易，脱模效果显著改善。
本发明的技术方案如下：
一种铸渣机脱模剂，所述的脱模剂是由铅烟灰、石灰和水组成，所述的铅烟灰的质量为所述石灰3～5倍，所述水的质量为所述的铅烟灰和石灰总质量的6～10倍。
所述的铅烟灰为炼铅本系统的收尘产物。
所述的脱模剂各组成成分配合后，通入压缩空气进行搅拌。
本发明铸渣机脱模剂采用铅冶炼系统的收尘产物铅烟灰作为主要原料，既改善了脱模效果，又降低了鼓风炉熔炼高铅渣过程中所产出的渣量，提高了铅冶炼的金属回收率，降低了能耗，经济效益明显。
具体实施方式
铸渣机脱模剂是由铅冶炼系统的收尘产物铅烟灰、石灰和水组成，铅烟灰的质量为石灰3～5倍，水的质量为铅烟灰和石灰总质量的6～10倍。脱模剂各组成成分配合后，通入压缩空气进行充分搅拌。
Claims (3)
1.一种铸渣机脱模剂，其特征在于：所述的脱模剂是由铅烟灰、石灰和水组成，所述的铅烟灰的质量为所述石灰3～5倍，所述水的质量为所述的铅烟灰和石灰总质量的6～10倍，所述的铅烟灰为铅冶炼系统的收尘产物。
2.根据权利要求1所述的一种铸渣机脱模剂，其特征在于：所述的铅烟灰为炼铅本系统的收尘产物。
3.根据权利要求1所述的一种铸渣机脱模剂，其特征在于：所述的脱模剂各组成成分配合后，通入压缩空气进行搅拌。