CN101503286B - Attapulgite putty powder for exterior wall - Google Patents
Attapulgite putty powder for exterior wall Download PDFInfo
- Publication number
- CN101503286B CN101503286B CN2009100301050A CN200910030105A CN101503286B CN 101503286 B CN101503286 B CN 101503286B CN 2009100301050 A CN2009100301050 A CN 2009100301050A CN 200910030105 A CN200910030105 A CN 200910030105A CN 101503286 B CN101503286 B CN 101503286B
- Authority
- CN
- China
- Prior art keywords
- concavo
- attapulgite
- powder
- putty powder
- convex rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses lacquer putty powder for the external wall of a concavo-convex rod. The technical proposal thereof comprises the key points that: the lacquer putty powder for the external wall of the concavo-convex rod consists of a purified concavo-convex rod, white bentonite, white Portland cement, high strength gypsum powder, hydroxypropyl methylcellulose and rutile type titanium dioxide. The method for producing the lacquer putty powder for the external wall of the concavo-convex rod is to prepare, crush, grind and pack the raw materials to a finished product of the lacquer putty powder for the external wall of the concavo-convex rod, wherein the lacquer putty powder for the external wall of the concavo-convex rod is placed in a vessel to be immersed by water for 5 to 30 minutes, and the proportion of the lacquer putty powder for the external wall of the concavo-convex rod to the water is 1:0.5-1:4; after being sufficiently and evenly stirred, the powder can be applied for scraping and coating. The lacquer putty powder for the external wall of the concavo-convex rod has the characteristics of good cohesive property, strong adhesive attraction, stable filming performance, high strength, long service life, water resistance, crack resistance, powder falling prevention, firm viscosity with coatings and paint conservation, and is applicable to coating project of construction.
Description
Technical field
The present invention relates to coating, be specifically related to a kind of attapulgite putty powder for exterior wall.
Background technology
The quality of putty quality directly influences the ornamental and weather resistance of coating ornamental surface; product that use properties is inferior or inner wall putty external application; often cause finally engineering delivery to be used promptly occurring soon that metope comes off, hollowing, cracking; part or big area coating are lost original decoration and defencive function, have had a strong impact on the normal use of buildings.Construction work is mainly reflected on the indexs such as cohesive strength, initial stage splitting resistance and dynamic splitting resistance the specification of quality of exterior wall putty, and cohesive strength is important technology index wherein.Often relatively poor in the building operation because of the putty quality product, cause the putty can't be normally attached to surface of wall, cause the efflorescence of putty top layer or come off, even peeling, leave the foaming vestige after the drying.
Chinese patent publication number: CN1796467, open day: on July 5th, 2006, name is called " lacquer putty paste, powder capable of for purifying air in use on inner wall and outer wall ", disclose that " a kind of lacquer putty paste, powder capable of for purifying air in use on inner wall and outer wall is characterized in that: following raw materials according is made according to following weight proportion: tourmalinite 10-20 part, talcum powder 800-1000 part, carboxymethyl cellulose 20-40 part, 1.5 parts of water 300-500 of formaldehyde 0.4-0.8 part whitening agent part.Advantage of the present invention is: 1, have antibiotic, bacteriostatic effect, have the function that purifies air, can dispel multiple toxic gases such as indoor formaldehyde, ammonia, radon, benzene.2, because tourmalinite can be launched the efficient far infrared rays of 4-14um, the 0.06M A bioelectric current of generation and human-body biological electric current 0.06M A are complementary.Therefore the present invention can reach and keep HUMAN HEALTH, strengthens the effect of the physique of human body.”
The weak point of above-mentioned patent is that this technology is to be main material production " lacquer putty paste, powder capable of for purifying air in use on inner wall and outer wall " with the talcum powder, and talcum powder is a kind of filler, though in prescription, added carboxymethyl cellulose, therefore but its proportion seldom, is easy to cause putty coating efflorescence, cracking, hollowing and comes off.
Summary of the invention
The objective of the invention is to overcome weak point in the prior art, a kind of attapulgite putty powder for exterior wall is provided.
Attapulgite putty powder for exterior wall is made up of Concavo-convex stick after purifying, white wilkinite, white portland cement, high strength gypsum powder, Vltra tears and Rutile type Titanium Dioxide.
The production method of attapulgite putty powder for exterior wall is: batching, pulverizing, abrasive dust, be packaged as the finished product of attapulgite putty powder for exterior wall.
Attapulgite clay is a kind of nanometer porous fibrous silicate clay mineral of Shuifu County's magnesium that contains, and when Attapulgite content 〉=80% in the attapulgite clay was above, its specific surface area was bigger, can reach 500m
2More than/the g.Use " Attapulgite wet beneficiation craft ", the screening of mineral such as the hydromica in the attapulgite clay, quartz, opal and carbonate is got rid of, obtain a kind of Concavo-convex stick after purifying.
Attapulgite clay soil property exquisiteness, smooth surface, quality is lighter, is viscosity and plasticity-when moist, and its viscosity can reach more than the 3000mPas, helps the bonding between the raw material; The attapulgite clay drying shrinkage is little, and do not produce be full of cracks, can improve the sticking power of putty powder to building wall, attapulgite clay also has viscosity and thixotropy preferably, Concavo-convex stick after purifying adds in the putty, good dispersity under external force stirs forms stable not stratified mineral colloid.
Attapulgite clay has the selection adsorptive power, as polar molecule water, ammonia, methyl alcohol, ethanol, aldehyde, ketone, alkene, hydrocarbon etc. can be absorbed by access opening, then can not enter the duct to non-polar molecule such as oxygen etc., utilize this characterization of adsorption, formaldehyde and volatile organic matter in the energy absorbed air purify air.
The white wilkinite has the flight of colors of going out and absorption property, also has good plasticity, cohesiveness and perviousness, helps increasing the sticking power of attapulgite putty powder for exterior wall to building wall.
White portland cement has the pure white exquisiteness of color and luster, intensity height, sticking power is good, cohesive force is big and anti-rimose characteristics, can strengthen the later strength of attapulgite putty powder for exterior wall, can avoid exterior wall to produce and return white phenomenon.
Good fluidity before the sclerosis of high strength gypsum powder has the little characteristics of higher degree of compactness, intensity and shrinking percentage after the sclerosis.
Vltra tears cohesive strength height, the water-holding agent performance is good, after Vltra tears adds attapulgite paste exterior wall putty, can make the putty coating light fine and smooth, not shedding improves flow leveling, improves putty-painting and prolongs operable time, putty can be because of not doing to such an extent that chap too soon after smearing, and can strengthen the intensity after putty hardens.
Rutile type Titanium Dioxide has the strong characteristics of opacifying power, reducing power and flowing property, and aspects such as ornamental, the weathering resistance of putty, chemical-resistant stability are played keying action.
The present invention is achieved by following technical proposals:
1, the batching of attapulgite putty powder for exterior wall is made up of following component by weight percentage: Concavo-convex stick after purifying 25～45%, white wilkinite 10～40%, white portland cement 10～35%, high strength gypsum powder 5～25%, Vltra tears 0.5～5% and Rutile type Titanium Dioxide 0.1～5%.
Described Concavo-convex stick after purifying is: the wet beneficiation craft that uses Attapulgite, the Attapulgite ore deposit mixture that will contain earth impurity, import in the hydrolytic tank after crushed, soak after 24 hours, dash with high-pressure pump and to turn over, and the sieve of the drum by making with stainless steel steel wire sieve removes the impurity more than 1 millimeter, send in the acclive settling tank, continuation is dashed with high-pressure pump and is turned over, after 12 hours, because the proportion in Attapulgite ore deposit is lighter, its the superiors in whole throw out draws this part Attapulgite ore deposit with slush pump and sends in the flat settling tank, emits unnecessary water after 15 hours, through 2-3 days seasoning, take out this part Attapulgite and be Concavo-convex stick after purifying;
Above-mentioned technology is to adopt " the Attapulgite wet beneficiation craft " in application on September 18th, 2003 by the inventor, and the Chinese patent Granted publication number is: CN1224463, Granted publication day: on October 26th, 2005.
2, the production method of attapulgite putty powder for exterior wall is: after the batch mixes with attapulgite putty powder for exterior wall, pulverize in the input pulverizer, particle fineness after the pulverizing is less than 0.250 millimeter, carry out abrasive dust in the mixture input superfine mill after will pulverizing again, particle fineness behind the abrasive dust is packaged as the finished product of attapulgite putty powder for exterior wall less than 0.025 millimeter.
Using method: attapulgite putty powder for exterior wall is put into container, added water infiltration 5～30 minutes, the ratio of attapulgite putty powder for exterior wall and water is 1: 0.5～1: 4, through after stirring, just can carry out knife-coat application.
Attapulgite putty powder for exterior wall has that cohesiveness is good, strong adhesion, film forming properties are stable, intensity high life length, water-fast freedom from cracking, not shedding, with dope viscosity firmly and the characteristics of saving coating.
Attapulgite putty powder for exterior wall is applicable to the architectural finish engineering.
Embodiment
The invention will be further described below in conjunction with embodiment:
1, the batching of attapulgite putty powder for exterior wall is made up of following component by weight percentage: Concavo-convex stick after purifying 38%, white wilkinite 26%, white portland cement 20%, high strength gypsum powder 12%, Vltra tears 3% and Rutile type Titanium Dioxide 1%.
2, the production method of attapulgite putty powder for exterior wall is: after the batch mixes with attapulgite putty powder for exterior wall, pulverize in the input pulverizer, particle fineness after the pulverizing is less than 0.250 millimeter, carry out abrasive dust in the mixture input superfine mill after will pulverizing again, particle fineness behind the abrasive dust is packaged as the finished product of attapulgite putty powder for exterior wall less than 0.025 millimeter.
Claims (1)
1. attapulgite putty powder for exterior wall, it is characterized in that the batching of attapulgite putty powder for exterior wall is made up of following component by weight percentage: Concavo-convex stick after purifying 25～45%, white wilkinite 10～40%, white portland cement 10～35%, high strength gypsum powder 5～25%, Vltra tears 0.5～5% and Rutile type Titanium Dioxide 0.1～5%;
Described Concavo-convex stick after purifying is: the wet beneficiation craft that uses Attapulgite, the Attapulgite ore deposit mixture that will contain earth impurity, import in the hydrolytic tank after crushed, soak after 24 hours, dash with high-pressure pump and to turn over, and the sieve of the drum by making with stainless steel steel wire sieve removes the impurity more than 1 millimeter, send in the acclive settling tank, continuation is dashed with high-pressure pump and is turned over, after 12 hours, because the proportion in Attapulgite ore deposit is lighter, its the superiors in whole throw out draws this part Attapulgite ore deposit with slush pump and sends in the flat settling tank, emits unnecessary water after 15 hours, through 2-3 days seasoning, take out this part Attapulgite and be Concavo-convex stick after purifying.