CN101487157A - Lining cloth for cloth and cloth - Google Patents
Lining cloth for cloth and cloth Download PDFInfo
- Publication number
- CN101487157A CN101487157A CNA2009100032124A CN200910003212A CN101487157A CN 101487157 A CN101487157 A CN 101487157A CN A2009100032124 A CNA2009100032124 A CN A2009100032124A CN 200910003212 A CN200910003212 A CN 200910003212A CN 101487157 A CN101487157 A CN 101487157A
- Authority
- CN
- China
- Prior art keywords
- lining cloth
- weft yarn
- dress material
- wiring
- hot melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims to provide an interlining material for cloth with appropriate flexual rigidity, rebound elasticity, and light weight, and the cloth made from the interlining material. The interlining material for cloth includes a weft yarn and a warp yarn, wherein the weft yarn is produced by at least twisting synthetic fiber monofilament and hot-melt wiring. The synthetic fiber monofilament is selected from at least one from the polyester fiber monofilament or the nylon fiber monofilament. The warp yarn is produced by not only twisting synthetic fiber monofilament and hot-melt wiring, but also twisting synthetic fiber treated by false twisting.
Description
Technical field
The present invention relates to dress material with lining cloth material and dress material, wherein, described dress material is mainly used in for example predecessor of heavy dress material clothes such as western-style clothes, jacket with the lining cloth material.
Background technology
All the time, in order to give dress material, use mao lining as its lining cloth at the predecessor place of grade of heavy dress material with formability and shape-retaining ability.Because the warp thread or the weft yarn that require to constitute this mao lining have appropriate rigidity and resilience, therefore to use the raw material of animal hair fibre blended yarn (line slightly is 9～18 public (メ-ト Le kind hand)) as its warp thread or weft yarn, described animal hair fibre blended yarn by to heavy denier, have in the animal hair fibre (goat, camel, karakul sheep, yak etc.) of tension force the blending artificial fibre or mao etc. make.And, when described animal hair fibre blended yarn is carried out the arrangement procedure of processing of cloth, by carrying out the resin finishing step so that feel conditioning agent (polyvinyl alcohol resin or vinyl acetate resinoid etc.) attached on the goods, can further improve its rigidity and resilience, make its formability and shape-retaining ability can give full play to (with reference to patent documentation 1).
, in recent years, along with western-style clothes, jacket are tending towards lighting gradually, not only require lining cloth to have suitable flexual rigidity, resilience, also expectation realizes their lighting.
The 0002nd section of [patent documentation 1] TOHKEMY 2004-218162 communique etc.
Summary of the invention
Problem to be solved by this invention
Yet,, can't make it satisfy above-mentioned lighting requirement because traditional hair lining is heavier.The present invention is in view of above problem, purpose is to provide a kind of dress material with lining cloth material and dress material with lining cloth made from the lining cloth material with this dress material, wherein, described dress material not only has suitable flexual rigidity, resilience with the lining cloth material, still a kind of light dress material lining cloth material.The method of dealing with problems
(1) main points of the 1st aspect of the present invention are a kind of dress materials with warp thread and weft yarn with lining cloth material (dress material with core ground cloth and silk), and wherein, described weft yarn (synthesizes by the synthetic fiber monofilament of twisting thread at least
モ ノ Off イ ラ メ Application ト) and the hot melt wiring (
Connect
) and obtain.
Because dress material of the present invention has the weft yarn that gets by twist thread at least synthetic fiber monofilament and hot melt wiring with the lining cloth material, therefore not only have suitable flexual rigidity, resilience, also have portability.
In addition, dress material of the present invention is to make synthetic fiber monofilament and warp thread etc. that welding take place with the hot melt wiring role in the lining cloth material.Thus, even under the surface smoothing of for example synthetic fiber monofilament, the situation that is easy to slide, the caused synthetic fiber monofilament of external force when also being difficult for producing by dress or washing clothes is outstanding, weft yarn splits line etc.
Weft yarn among the present invention can be only twist thread synthetic fiber monofilament and hot melt wiring and weft yarn, also can be not only twist thread synthetic fiber monofilament and hot melt wiring, the resulting weft yarn of other line of further also twisting thread.As described other line, can enumerate and for example pass through the synthetic fiber that false twisting is processed, yarn etc.Add yarn and can give the fine hair of goods staple fibre, its surface touch is dissimilated.
The radical of synthetic fiber monofilament in the above-mentioned weft yarn can be set according to the flexual rigidity of necessity, 1 or many can be set at.As described synthetic fiber monofilament, can enumerate for example polyester fiber, nylon fiber etc.The preferred rugosity of synthetic fiber monofilament be 56 minutes Tekes (following note is made 56dtex) to 220dtex.When 56dtex is above, easily obtain suitable rigidity, resilience.In addition, when 220dtex is following, can avoid operability variation in the processing of twisting thread.
Described hot melt wiring comprises polyesters, nylon-type, polyethylene kind, polyurethanes etc., but is not limited to these.The preferred rugosity of hot melt wiring is 33dtex to 110dtex.When 33dtex is above, the caking property height between weft yarn and the warp thread.In addition, when 110dtex is following, many (many く of the commissure Ga な り of adhesive surface
ぎ), dress material is opened coarse like that with the feel of the lining cloth material sensitive paper that can not become.
(2) main points of the 2nd aspect of the present invention are: according to the dress material lining cloth material described in the 1st aspect, wherein, described synthetic fiber monofilament is to be selected from least a in polyester fiber monofilament or the nylon fiber monofilament.
Dress material of the present invention not only has suitable flexual rigidity, resilience with the lining cloth material, also has portability.The caused synthetic fiber monofilament of external force when in addition, dress material of the present invention is difficult for producing by dress or washing clothes with the lining cloth material is outstanding, weft yarn splits line etc.
(3) main points of the 3rd aspect of the present invention are: according to the dress material lining cloth material described in the 1st aspect or the 2nd aspect, wherein, described hot melt wiring be selected from the wiring of polyesters hot melt, the wiring of nylon-type hot melt, the wiring of polyethylene kind hot melt, and the wiring of polyurethanes hot melt at least a.
Dress material of the present invention not only has suitable flexual rigidity, resilience with the lining cloth material, also has portability.The caused synthetic fiber monofilament of external force when in addition, dress material of the present invention is difficult for producing by dress or washing clothes with the lining cloth material is outstanding, weft yarn splits line etc.
(4) main points of the 4th aspect of the present invention are: according to each described dress material lining cloth material in the 1st aspect～the 3rd aspect, wherein, except twisted thread described synthetic fiber monofilament and described hot melt wiring, also twist thread and passed through the synthetic fiber of false twisting processing in the described weft yarn.
Dress material of the present invention is not only twist thread synthetic fiber monofilament and hot melt wiring with the weft yarn in the lining cloth material, also twists thread through the resulting weft yarn of synthetic fiber of false twisting processing.Since this weft yarn have the height bulkiness (high high property), can give dress material with the lining cloth material with sense of fullness (sense of swollen ら body).
(5) main points of the 5th aspect of the present invention are a kind of dress materials, and this dress material has the lining cloth of being made with the lining cloth material by each described dress material in the 1st～the 4th aspect.
The lining cloth of dress material of the present invention not only has suitable flexual rigidity, resilience, also has portability.The caused synthetic fiber monofilament of external force when in addition, dress material of the present invention is difficult for producing by dress or washing clothes is outstanding, weft yarn splits line etc.
As described dress material, can enumerate for example heavy dress material such as western-style clothes, jacket (heavy dress material).
Description of drawings
The key diagram of the chuck state of test portion when Fig. 1 is expression mensuration flexual rigidity.
Fig. 2 is the key diagram that the method for calculating the flexual rigidity value is asked in expression.
Symbol description
1,2 chucks
3 test portions
The value added of the bending moment between 4 curvature 0.5 and 1.5 (bent げ モ-メ Application ト)
The value added of the bending moment between 5 curvature-0.5 and-1.5
The specific embodiment
Based on embodiment embodiments of the present invention are described.
[embodiment 1]
With the number of times of twisting thread of 300 times/m twist thread monofilament polyester 160dtex, polyester false twist yarn 165dtex48f, polyesters thermal welding silk (180 ℃ of fusing points) 77dtex24f, make weft yarn.In addition, the warp thread of use is the warp thread of polyester 100%, rugosity 40/1.Then, weaving coarse cloth (Sheng Machine), density is 51/2.5cm of warp thread, 40/2.5cm of weft yarn.Subsequently, put processing in order.This arrangement processing is carried out according to the order of destarch, heat setting.Destarch is the continuous destarch refiner of employing, carries out handling in 30 minutes with the enzyme desizing agent under 60 ℃ of temperature, and the agent of warp thread slurry is decomposed, and by washing it is cleaned again.In the heat setting process, in order to make setting and to be undertaken fully by the welding of polyesters hot melt wiring, under 190 ℃ of temperature, carry out handling in 40 seconds, thereby obtain to be commonly called the dress material lining cloth material of " increasing lining (increasing the core) ", formalizing in above-mentioned is in order to make polyester material have DIMENSIONAL STABILITY.
Use this dress material lining cloth material, utilize known method to make the dress material lining cloth, further, use this dress material to make jacket, western-style clothes with lining cloth.
[embodiment 2]
Except when making weft yarn, having used 2 monofilament polyester 160dtex, carry out the method identical and made the dress material lining cloth material that is commonly called " shoulder increases lining " with the foregoing description 1.And, use this dress material lining cloth material, utilize known method to make the dress material lining cloth, further, use this dress material to make jacket, western-style clothes with lining cloth.
(comparative example 1)
Making warp thread is cotton 100%, rugosity 40/2.In addition, weft yarn is weaved with the ratio of artificial fibre 65%, goats hair 30%, polyester 5%, makes its rugosity 1/11.Then, weaving coarse cloth, density is 38/2.5cm of warp thread, 37/2.5cm of weft yarn.Subsequently, put processing in order.This arrangement processing is carried out according to the order of singing, boiling suede, resin finishing.Singing is to utilize the firepower burning of burner to remove to be exposed to lip-deep common and braid wool, carries out this processing on the two sides of fabric.Boil suede and be in order to make the cloth surface become smooth in 90 ℃ of baths, add and depress 15 minutes of carrying out and handle, wash subsequently.Resin finishing is to be coated with anti-piping compound, feel conditioning agent on liner, and utilizes stenter to make it cure reaction under 160 ℃ temperature.Thus, made the dress material lining cloth material that is commonly called " increasing lining ".
(comparative example 2)
With the number of times of twisting thread of 300 times/m twist thread polyester multifibres 165dtex48f, polyester false twisting processing line 165dtex48f, and polyesters thermal welding silk (180 ℃ of fusing points) 77dtex24f, make weft yarn.All the other adopt the method identical with the foregoing description 1 to make coarse cloth, and put processing in order, thereby obtain the lining cloth material.
(comparative example 3)
With the number of times of twisting thread of 300 times/m twist thread monofilament polyester 160dtex, polyester false twisting processing line 165dtex48f, and polyester multifibres 83dtex36f, make weft yarn.All the other adopt the method identical with the foregoing description 1 to make coarse cloth, and put processing in order, thereby obtain the lining cloth material.
(test)
For determine embodiment 1～2, and comparative example 1～3 in the performance of the lining cloth material that obtains, test.Pilot project is following 5 projects: flexual rigidity, anti-crawl agentdefiection recovery, weight, weft yarn split line, the washing size changing rate.Flexual rigidity, anti-crawl agentdefiection recovery, weft yarn split line, and the washing size changing rate test method as described below.
The assay method of Flexurally rigid: as shown in Figure 1, with working sample 3 be held on chuck 1 and chuck 2 (the chuck spacing: 1cm), mobile chuck 2, the deflection rate that makes sample 3 is 0～+ 2.5～-2.5～0, and obtains the curve of bending moment～curvature, as shown in Figure 2.With the mean value of following two-value as flexual rigidity: in 0 →+2.5 bending deformation process bending moment～curvature curve the value added (4) of the bending moment between curvature 0.5 and 1.5 and in 0 →-2.5 bending deformation process the absolute value of the value added (5) of the bending moment of bending moment～curvature curve between curvature-0.5 and-1.5.In addition, in the mensuration of flexual rigidity, make working sample carry out bending towards the bending direction of weft yarn.That is, in Fig. 1, weft yarn extends along above-below direction.The anti-crawl agentdefiection recovery also adopts with quadrat method and measures.
The assay method of anti-crawl agentdefiection recovery: the assay method during with the mensuration flexual rigidity is identical, as shown in Figure 1, working sample 3 is held on chuck 1 and chuck 2 (chuck spacing: 1cm), mobile chuck 2, the deflection rate that makes sample 3 is 0～+ 2.5～-2.5～0, and obtain the curve of bending moment～curvature, as shown in Figure 2.Get curvature and be 1.0 o'clock delay amplitude and curvature mean value for-1.0 o'clock delay amplitude, with this mean value as 2HB.In addition, with the value of flexual rigidity as B.Then the anti-crawl agentdefiection recovery can utilize 2HB/B to try to achieve.
The split assay method of line of weft yarn: the square test portion of pair warp and weft 20cm carry out continuously 5 times commercial with dry-cleaning, number goes out the line radical that splits of weft yarn.
The assay method of washing size changing rate: measure by the JIS.L.1096.F-1 method.
Result of the test is as shown in table 1.
[table 1]
| Assessment item | Embodiment 1 | |
Comparative example 1 | Comparative example 2 | Comparative example 3 |
| Flexual rigidity (latitude) | 2.58 | 6.00 | 3.08 | 0.21 | 2.30 |
| Anti-crawl agentdefiection recovery (latitude) | 0.09 | 0.07 | 0.45 | 0.12 | 0.08 |
| Weight (g/m 2) | 110 | 139 | 199 | 110 | 113 |
| The weft yarn line (root) that splits | 5 | 4 | 5 | 4 | 10 |
| Washing size changing rate warp * latitude (%) | -0.5×-0.5 | -0.5×-0.5 | -3.0×-2.5 | -0.5×-0.5 | -0.5×-0.5 |
| Overall merit | ◎ | ◎ | ○ | × | × |
As shown in table 1, the lining cloth material of embodiment 1～2 is excellence aspect flexual rigidity, anti-crawl agentdefiection recovery, washing size changing rate, and weight is also than the more lighting of lining cloth material of comparative example 1, and the weft yarn line that splits is also less, its excellent combination property.
In contrast, weight, the deflection recovery of the lining cloth material of comparative example 1 (traditional increase lining) are relatively poor.In addition, the flexual rigidity of the lining cloth material of comparative example 2 is soft excessively; The weft yarn of the lining cloth material of comparative example 3 line that splits is more, can't use.
In addition, the present invention is not subject to above-mentioned embodiment, clearly, as long as in not exceeding scope of the present invention, can take variety of way to implement the present invention.
Claims (5)
1. dress material lining cloth material, this dress material has warp thread and weft yarn with the lining cloth material, and wherein, described weft yarn obtains by at least synthetic fibre single thread and hot melt wiring being twisted thread.
2. dress material lining cloth material according to claim 1, wherein, described synthetic fiber monofilament is to be selected from least a in polyester fiber monofilament and the nylon fiber monofilament.
3. dress material lining cloth material according to claim 1, wherein, described hot melt wiring be selected from the wiring of polyesters hot melt, the wiring of nylon-type hot melt, the wiring of polyethylene kind hot melt, and the wiring of polyurethanes hot melt at least a.
4. dress material lining cloth material according to claim 1, wherein, not only twisted thread in the described weft yarn described synthetic fiber monofilament and described hot melt wiring are also twisted thread through the synthetic fiber of false twisting processing.
5. dress material, this dress material has the lining cloth of being made with the lining cloth material by the described dress material of claim 1.