CN101457356B - 一种钢铁防腐脂膏 - Google Patents

一种钢铁防腐脂膏 Download PDF

Info

Publication number
CN101457356B
CN101457356B CN2009100005733A CN200910000573A CN101457356B CN 101457356 B CN101457356 B CN 101457356B CN 2009100005733 A CN2009100005733 A CN 2009100005733A CN 200910000573 A CN200910000573 A CN 200910000573A CN 101457356 B CN101457356 B CN 101457356B
Authority
CN
China
Prior art keywords
steel
steel anti
corrosive grease
corrosion grease
polysiloxane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100005733A
Other languages
English (en)
Other versions
CN101457356A (zh
Inventor
候世益
梁智勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100005733A priority Critical patent/CN101457356B/zh
Publication of CN101457356A publication Critical patent/CN101457356A/zh
Application granted granted Critical
Publication of CN101457356B publication Critical patent/CN101457356B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种钢铁防腐脂膏，由以下重量分数的原料制成：聚硅氧烷35-40％、硅烷30-31％、硅树脂15-20％、熔融石英砂10-15％、无机添加剂1.5-3％。本发明有益效果：本发明所述的钢铁防腐脂膏一经浸涂到基材后，在钢铁表面上不会留下任何痕迹，本发明所述的钢铁防腐脂膏能够更深入地渗透到钢铁材料的内部形成一个立体式的保护膜，该产品具有防水性，很强的抗酸性和抗碱性，且具有更强的透气性。

Description

一种钢铁防腐脂膏
技术领域
本发明涉及防腐材料领域，尤其涉及一种钢铁防腐脂膏。
背景技术
钢铁制品在日常生活中的应用已相当普遍，然而它的腐蚀却一直是一个令人头疼的问题。全世界每年因金属腐蚀造成的直接经济损失约达7000亿美元，是地震、水灾和台风等自然灾害造成损失的总和的六倍，这还不包括由于腐蚀导致的停工，减产和爆炸等造成的间接损失，金属腐蚀的要害处不仅在于金属本身的损失，更严重的是金属制品结构损坏所造成的损失比金属本身要大到无法估量。我们国家是一个钢铁生产大国，每年的钢铁产量已突破2亿吨，位居世界第一。然而每年因氧化、腐锈、损耗的钢铁量竟高达800万吨，占全国钢铁生产年总量的4％，从这个数字中我们可以看出，每年因腐蚀损耗钢铁的数量是相当惊人的。还有一些珍贵铁制文物的腐蚀，其损失价值更是无法估计。钢铁的生锈主要是由于铁原子与外界其它物质，如水份、氧气等或钢铁制品中所含的碳等物质发生化学或电化学反应形成铁锈。一般的金属防腐材料都只是涂刷或附着在金属表面，起到隔离作用，经不起成年累月的自然破坏，保护时间很短。
发明内容
本发明提供一种钢铁防腐脂膏，以克服现有防腐技术的缺陷，有效解决钢铁腐蚀。
本发明解决其技术问题所采用的技术方案是：
一种钢铁防腐脂膏，由以下重量分数的原料制成：聚硅氧烷35-40％、硅烷30-31％、硅树脂15-20％、熔融石英砂10-15％、无机添加剂1.5-3％。
所述的聚硅氧烷通式为：[RnSiO4-n/2]m
其中，R代表有机基团，如甲基、苯基等；n为硅原子上连接的有机基团数目，n在1-3之间，m为聚合度，m不小于2；
所述的硅烷，又称硅氢化合物，通式是SinH2n+2；
所述的硅树脂是具有高度交联网状结构的聚有机硅氧烷，兼具有机树脂及无机材料的双重特性，具有独特的物理化学性能；
所述的熔融石英砂的化学成份：SiO2 99.9-99.99％、Fe2O3 10-25PPM、maxLi2O 1-2PPM、maxAl2O3 20-30PPM、maxK2O 20-25PPM、maxNa2O 10-20PPM；物理性能：外观为无色透明块状、颗粒或白色粉末，真比重2.21，莫氏硬度7.0，PH值6.0；
所述的无机添加剂为Al2O3、SiO2、钙盐等。
将上述原料按照比例混合后在反应釜中进行纳米化处理，直到粒子大小为0.1-100纳米范围，根据进入产品粒子大小的不同，设定不同的工作频率、速度逐步将要处理的粒子变小。
本发明有益效果：本发明所述的钢铁防腐脂膏主要是从以下两方面产生保护作用：①使用以后可以迅速渗透到铁制品内部，与铁原子发生作用，使铁原子不再发生任何运动，并迅速稳定下来，从而使铁原子不再与其它物质发生化学反应；②渗入铁制品表面以后，与铁原子发生作用，在铁制品表层形成一层致密的保护膜，有效的阻止了外界物质(水、氧气等)进入，避免它们与铁原子发生接触，同时也能阻止穿透能力很强的氯离子等的进入，从而阻止了腐蚀原电池的形成，达到保护的目的。本发明所述的钢铁防腐脂膏渗入到金属面层，并在面层行成了一个立体式的防护层，所以说可以从根本上解决金属防腐问题，并且还能保持金属原有的色泽、强度、硬度、密度等理化性质。
具体实施方式
下面结合具体实施例对本发明进一步描述。
实施例1
本实施例所述的一种钢铁防腐脂膏，由以下重量分数的原料制成：聚硅氧烷40％、硅烷31％、硅树脂15％、熔融石英砂10％、无机添加剂1.5％；无机添加剂为Al2O3、SiO2或钙盐；将上述原料按照比例混合后在反应釜中进行纳米化处理，直到粒子大小为0.1-100纳米范围。
实施例2
本实施例所述的一种钢铁防腐脂膏，由以下重量分数的原料制成：聚硅氧烷35％、硅烷30％、硅树脂20％、熔融石英砂15％、无机添加剂3％；将上述原料按照比例混合后在反应釜中进行纳米化处理，直到粒子大小为0.1-100纳米范围。
实施例3
本实施例所述的一种钢铁防腐脂膏，由以下重量分数的原料制成：聚硅氧烷38％、硅烷30％、硅树脂18％、熔融石英砂12％、无机添加剂2％；将上述原料按照比例混合后在反应釜中进行纳米化处理，直到粒子大小为0.1-100纳米范围。
实施例1所述的钢铁防腐脂膏主要用于铸铁的防腐，实施例2与实施例3所述的钢铁防腐剂主要用于钢材的防腐，本发明所述的钢铁防腐脂膏一经浸涂到基材后，在钢铁表面上不会留下任何痕迹，本发明所述的钢铁防腐脂膏能够更深入地渗透到钢铁材料的内部形成一个立体式的保护膜，该产品具有防水性，很强的抗酸性和抗碱性，且具有更强的透气性。

Claims (3)

1.一种钢铁防腐脂膏，其特征在于，由以下重量分数的原料制成：聚硅氧烷35-40％、硅烷30-31％、硅树脂15-20％、熔融石英砂10-15％、无机添加剂1.5-3％；将上述原料按照比例混合后在反应釜中进行纳米化处理，直到粒子大小为0.1-100纳米范围；所述的硅树脂是具有高度交联网状结构的聚有机硅氧烷；所述的无机添加剂为Al2O3、SiO2或钙盐。
2.根据权利要求1所述的钢铁防腐脂膏，其特征在于：所述的聚硅氧烷通式为：[RnSiO4-n/2]m，其中：R代表有机基团；n为硅原子上连接的有机基团数目，n在1-3之间；m为聚合度，m不小于2。
3.根据权利要求1所述的钢铁防腐脂膏，其特征在于：所述的硅烷通式是SinH2n+2。
CN2009100005733A 2009-01-16 2009-01-16 一种钢铁防腐脂膏 Expired - Fee Related CN101457356B (zh)