CN101428951B - 污水厂污泥固化/稳定化循环处理方法 - Google Patents
污水厂污泥固化/稳定化循环处理方法 Download PDFInfo
- Publication number
- CN101428951B CN101428951B CN2008102354221A CN200810235422A CN101428951B CN 101428951 B CN101428951 B CN 101428951B CN 2008102354221 A CN2008102354221 A CN 2008102354221A CN 200810235422 A CN200810235422 A CN 200810235422A CN 101428951 B CN101428951 B CN 101428951B
- Authority
- CN
- China
- Prior art keywords
- solidification
- sludge
- mud
- solidify material
- stabilization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是一种污水厂污泥固化/稳定化循环处理方法，一、将污泥和固化材料按照一定的比例混合、搅拌均匀，进行固化/稳定化处理；二、将固化/稳定化处理后的污泥粉碎后按照一定的比例添加进污泥中，并根据要求再添加固化材料，或将粉碎后的固化/稳定化污泥与固化材料混合均匀后添加进污泥中；三、将混合后的污泥、固化材料以及固化/稳定化污泥搅拌均匀，完成污泥的固化/稳定化过程。优点：将固化/稳定化污泥进行重复利用，能够增加污泥中无机矿物的成分，降低固化材料的用量，并降低处理成本。而且本发明所涉及的工艺流程简单易行，所增加的设备也极为有限，简单易行、有效的污泥固化/稳定化处理新方法。
Description
技术领域
本发明涉及一种将固化/稳定化污泥作为辅助材料进行再利用对污水厂脱水污泥进行固化/稳定化循环处理的方法，属于资源环境保护技术领域。
背景技术
污泥经过固化/稳定化处理能够提高强度、降低含水率并稳定污染物，处理后的污泥能够安全进行填埋或进行再生资源利用。由于污泥含水率高、有机质含量高，因此在处理过程中需要消耗大量的固化材料，处理成本也随之增加。
发明内容
本发明提出一种可以将固化/稳定化污泥作为辅助材料处理污泥的方法，旨在减少固化/稳定化材料用量，降低成本。污泥经过固化/稳定化处理后的主要成分为硅酸盐、粘土矿物等无机物，作为一种辅助材料，增加污泥中的无机矿物成分，极大的减少污泥处理过程中的固化材料用量，降低固化/稳定化处理的成本。在填埋场也能够减少填埋体的体积，延长填埋场的使用年限。
本发明的技术解决方案：其特征是该方法包括如下工艺步骤：
一、为了保证污泥经过固化/稳定化处理后能够满足填埋处置或资源化利用的要求，污泥固化/稳定化处理所要求的质量百分比为：
污泥 60-85％，
固化材料 15-40％；
二、将按照上述质量百分比的污泥和固化材料混合均匀，完成污泥固化/稳定化的处理过程，将固化/稳定化污泥粉碎，粉碎后的固化/稳定化污泥加入待处理的污泥中或加入固化材料中，并添加固化材料，污泥、固化材料、粉碎后的固化/稳定化污泥是按照如下的质量百分比：
污泥 58-83％；
固化材料 10-30％；
粉碎后的固化/稳定化污泥 5-20％；
三、将上述比例的污泥、固化材料以及粉碎后的固化/稳定化污泥重新混合搅拌。
本发明的优点：将固化/稳定化污泥进行重复利用，能够增加污泥中无机矿物的成分，降低固化材料的用量，并降低处理成本。而且本发明所涉及的工艺流程简单易行，所增加的设备也极为有限，是一种简单易行、有效的污泥固化/稳定化处理新方法。
具体实施方式
实施例1
工程要求固化/稳定化污泥7天后的强度达到50kPa，污泥固化/稳定化处理所要求的质量百分比为：
污泥 80％
固化材料 20％
将按照上述质量百分比的污泥和固化材料混合均匀，完成污泥固化/稳定化的处理过程。固化材料主要由水泥、石灰、粉煤灰、粘土矿物按照一定比例混合而成，按照质量百分比，其中水泥60％，石灰10％，粉煤灰5％，粘土矿物25％。将固化/稳定化污泥粉碎，按照一定比例加入待处理的污泥中，并添加一定比例的固化材料。按照质量百分比：
污泥 77％
固化材料 17％
粉碎后的固化/稳定化污泥 6％
将上述比例的污泥、固化材料以及粉碎后的固化/稳定化污泥重新混合搅拌，所得到的固化/稳定化污泥7天后的强度达到50kPa，达到同样的强度条件下固化材料用量节约了3％。
实施例2
工程要求固化/稳定化污泥3天后的强度达到100kPa，污泥固化/稳定化处理所要求的质量百分比为：
污泥 70％
固化材料 30％
将按照上述质量百分比的污泥和固化材料混合均匀，完成污泥固化/稳定化的处理过程。固化材料主要由水泥、石灰、粉煤灰、粘土矿物按照一定比例混合而成，按照质量百分比，其中水泥65％，石灰8％，粉煤灰6％，粘土矿物21％。将固化/稳定化污泥粉碎，按照一定比例加入待处理的污泥中，并添加一定比例的固化材料。按照质量百分比：
污泥 58％
固化材料 22％
粉碎后的固化/稳定化污泥 20％
将上述比例的污泥、固化材料以及粉碎后的固化/稳定化污泥重新混合搅拌，所得到的固化/稳定化污泥3天后的强度达到100kPa，达到同样的强度条件下固化材料用量节约了8％。
实施例3
工程要求固化/稳定化污泥1天的强度达到30kPa，污泥固化/稳定化处理所要求的质量百分比为：
污泥 75％
固化材料 25％
将按照上述质量百分比的污泥和固化材料混合均匀，完成污泥固化/稳定化的处理过程。固化材料主要由水泥、石灰、粉煤灰、粘土矿物按照一定比例混合而成，按照质量百分比，其中水泥70％，石灰4％，粉煤灰3％，
粘土矿物23％。将固化/稳定化污泥粉碎，按照一定比例加入固化材料中。按照质量百分比：
污泥 65％，
固化材料 20％，
粉碎后的固化/稳定化污泥 15％，
1天后的强度达到30kPa，达到同样的强度条件下固化材料用量节约了5％。
Claims (1)
1.一种污水厂污泥固化/稳定化循环处理方法，其特征是该方法包括如下工艺步骤：
一、工程要求固化/稳定化污泥达到填埋处置的目标，污泥固化/稳定化处理所要求的质量百分比为：
污泥 60-85％，
固化材料 15-40％；
二、将按照上述质量百分比的污泥和固化材料混合均匀，完成污泥固化/稳定化的处理过程，将固化/稳定化污泥粉碎，粉碎后的固化/稳定化污泥加入待处理的污泥或固化材料中，污泥、固化材料、粉碎后的固化/稳定化污泥是按照如下的质量百分比：
污泥 58-83％；
固化材料 10-30％；
粉碎后的固化/稳定化污泥 5-20％；
三、将上述比例的污泥、固化材料以及粉碎后的固化/稳定化污泥重新混合搅拌，所述的固化材料包括水泥、石灰、粉煤灰、粘土矿物，它们间的质量百分比，水泥60-70％，石灰6-10％，粉煤灰3-6％，粘土矿物21-25％。