CN101428389A - Method of manufacturing thin titanium/steel composite board - Google Patents
Method of manufacturing thin titanium/steel composite board Download PDFInfo
- Publication number
- CN101428389A CN101428389A CNA2008102269553A CN200810226955A CN101428389A CN 101428389 A CN101428389 A CN 101428389A CN A2008102269553 A CNA2008102269553 A CN A2008102269553A CN 200810226955 A CN200810226955 A CN 200810226955A CN 101428389 A CN101428389 A CN 101428389A
- Authority
- CN
- China
- Prior art keywords
- titanium
- steel
- plate
- rolling
- steel composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a thin-type titanium or steel composite plate, and particularly relates to a method for preparing a composite plate manufactured by the titanium steel-based composite plate through explosion and pack rolling. The method is characterized in that in the preparation process of the thin-type titanium or steel composite plate, the titanium or steel composite plate is compounded and formed by the titanium plate and the steel plate through explosion, then two composite plates are folded and welded into a billet body, and then the thin-type titanium or steel composite plate is formed through rolling. The preparation method adopts the explosive composite process, the rolling billet body has high bonding strength after explosive compounding, the titanium or steel composite plate billet is folded and welded for rolling, and the deformation amount is in 4 to 7 times; therefore, the preparation method not only ensures higher bonding strength of the titanium or steel composite plate after rolling, but also ensures the respective thickness requirements, the prepared titanium or steel composite plate has good processing technological property, the explosive composite billets of the titanium plate and the steel plate after pack rolling have good bonding property, the bending test is performed without layering, the titanium plate surface is free from cracks and impurities, and the method has the advantages of higher bonding strength, corrosion resistance and fatigue resistance.
Description
Technical field
A kind of method of manufacturing thin titanium/steel composite board is specifically related to a kind of titanium, base steel compound plate base are made composite plate through blast, ply rolling preparation method.
Background technology
The titanium/steel composite board that main equipments such as chemical industry electrolytic cell, reactor are used, the multiple layer of base is all thinner, and titanium layer is generally about 1mm, and steel plate is generally about 2~5mm.The preparation method of this type of composite plate, commonly used at present has three kinds: the first kind adopts directly blast composite algorithm, the titanium/steel composite board that obtains with this kind method, bond strength is higher, but maximum shortcoming is because the limitation of explosion cladding process, the area of the titanium/steel composite board that obtains is less, and it is bigger to handle difficulty at the leveling of follow-up composite plate, can't satisfy the requirement on the current device; Second class adopts direct roll-bonding method, and with the titanium/steel composite board that this kind method obtains, the plate face is bigger, can satisfy, but that its shortcoming is a bond strength is low than the requirement on the large equipment, and higher to the Capability Requirement of milling train, use few at present in China; The 3rd class adopts blast-roll-bonding method, adopts the titanium/steel composite board of this kind method preparation, and breadth is big, the bond strength height, but owing to be subjected to the rolling equipment capabilities limits, adopt this technology can't directly prepare the titanium/steel composite board of thickness less than 6mm.
Summary of the invention
The object of the invention is exactly the deficiency that exists at above-mentioned prior art, a kind of bond strength is provided, also can accurately controls titanium/steel composite board thickness, effectively guarantee its serviceability, cost is lower, and the high thickness produced of efficient is less than the method for manufacturing thin titanium/steel composite board of 6mm.
The objective of the invention is to be achieved through the following technical solutions.
A kind of method of manufacturing thin titanium/steel composite board, it is characterized in that its thin titanium/steel composite board preparation process be with titanium plate and steel plate after blast is compounded to form titanium/steel composite board, after superimposed and assembly welding becomes rolling blank body with two composite plates again, form through rolling again.
A kind of method of manufacturing thin titanium/steel composite board of the present invention, it is characterized in that the described process that superimposed and assembly welding becomes rolling blank body with two composite plates is after the compound back of blast titanium/steel composite board is carried out carrying out leveling with hydraulic press, the steel face carries out relatively between any two, welds all around to connect and forms rolling blank body.
A kind of method of manufacturing thin titanium/steel composite board of the present invention, it is characterized in that the described operation of rolling is the rolling blank body of titanium/steel composite board that assembly welding is good, being heated to temperature is 700~1000 ℃, behind insulation 1~4h, rolling through 6~10 passages, final composite plate thickness is at 2.5~6mm.
Method of the present invention, adopt explosion cladding process, make the rolling blank in the compound back of blast agree that high bond strength is arranged, to be rolled behind the superimposed assembly welding of titanium/steel composite board blank, its deflection is at 4~7 times, guaranteed the existing higher binding strength of titanium/steel composite board after rolling, can guarantee its thickness requirement separately again, the titanium/steel composite board of preparation has good process industrial art performance, the blast composite blank of titanium plate and steel plate its binding ability after ply rolling is good, bend test does not have layering, titanium plate surface flawless and impurity thing etc., and have higher binding strength, corrosion resistance and fatigue resistance.
The specific embodiment
A kind of method of manufacturing thin titanium/steel composite board after blast is compounded to form titanium/steel composite board, after superimposed and assembly welding becomes rolling blank body with two composite plates again, forms titanium plate and steel plate again through rolling; The process that assembly welding becomes rolling blank body is that the steel face carried out relatively between any two, welds connection all around after the compound back of blast titanium/steel composite board was carried out carrying out leveling with hydraulic press; The rolling blank body of titanium/steel composite board that assembly welding is good when rolling, being heated to temperature is 700~1,000 ℃, behind insulation 1~4h, rolling through 6~10 passages, final composite plate thickness is at 2.5~6mm.
The concrete operations step comprises:
Getting composition is GB/T 3620 TA1, TA2, ASTM B265Gr.1﹠amp; Gr.2, thickness are the titanium plate of 3~8mm;
Composition is Q235B, 16MnR, SS400, ASTM A516 Gr.70 plate, and thickness is the steel substrate of 15~30mm;
With titanium plate and steel substrate carry out that conventional surface treatment, blast are compound, composite plate assembly welding and step such as rolling, detailed process is as follows:
1. multiple layer titanium plate is pressed school shape annealing;
2. multiple layer titanium plate and basic unit's steel plate carry out cleaning surfaces, polishing;
3. assembly is installed:
4. ignite electric cap, moment is realized multiple layer titanium plate and basic unit's two kinds of compound connections of Metal Explosion of steel plate;
5. the compound titanium/steel composite board that explodes is carried out carrying out leveling with hydraulic press, the steel face carries out relatively between any two, welds all around, and leaves steam vent;
6. the good titanium/steel composite board of assembly welding is heated in resistance furnace, temperature is 700~1000 ℃, insulation 1~4h;
7. be rolled after blank is come out of the stove, rolling through 6~10 passages, final composite plate thickness is at 2.5~6mm.
Embodiment 1
With TA1 is plied timber; thickness 6mm; Q235B is a base material; thickness 30mm carries out sanding and polishing to its surface and handles, and carries out assembly then according to a conventional method: coat protective layer above the TA1; on protective layer, be distributed into ammonium nitrate class composite explosives equably; and the insertion electric cap, behind the ignition charge, moment realizes that the blast of TA1 and Q235B is compound.Then titanium/steel composite board is carried out assembly welding, the steel face is relative during assembly welding, and leave steam vent, blank behind the assembly welding is put into heat-treatment furnace and is heat-treated, Technology for Heating Processing is 700 ℃/4h, hangs on milling train after coming out of the stove and is rolled, and the titanium layer thickness of the titanium steel composite board after rolling is 1mm, steel plate thickness is 5mm, and its bond strength is higher.
Embodiment 2
With TA2 is plied timber; thickness 6mm; 16MnR is a base material; thickness 24mm carries out sanding and polishing to its surface and handles, and carries out assembly then according to a conventional method: coat protective layer above the TA1; on protective layer, be distributed into ammonium nitrate class composite explosives equably; and the insertion electric cap, behind the ignition charge, moment realizes that the blast of TA2 and 16MnR is compound.Then titanium steel composite board is carried out assembly welding, the steel face is relative during assembly welding, and leave steam vent, putting into heat-treatment furnace behind the assembly welding heat-treats, Technology for Heating Processing is 1000 ℃/1, hangs on milling train after coming out of the stove and is rolled, and the titanium layer thickness of the titanium steel composite board after rolling is 1mm, steel plate thickness is 4mm, and its bond strength is higher.
Claims (3)
1. method of manufacturing thin titanium/steel composite board, it is characterized in that its thin titanium/steel composite board preparation process be with titanium plate and steel plate after blast is compounded to form titanium/steel composite board, after superimposed and assembly welding becomes rolling blank body with two composite plates again, form through rolling again.
2. a kind of method of manufacturing thin titanium/steel composite board according to claim 1, it is characterized in that the described process that superimposed and assembly welding becomes rolling blank body with two composite plates is after the compound back of blast titanium/steel composite board is carried out carrying out leveling with hydraulic press, the steel face carries out relatively between any two, welds all around to connect and forms rolling blank body.
3. a kind of method of manufacturing thin titanium/steel composite board according to claim 1, it is characterized in that the described operation of rolling is the rolling blank body of titanium/steel composite board that assembly welding is good, being heated to temperature is 700~1,000 ℃, behind insulation 1~4h, rolling through 6~10 passages, its deflection is at 4~7 times.