CN101423949A - 一种不锈钢酸洗生产线用玻璃钢棒及其生产工艺 - Google Patents
一种不锈钢酸洗生产线用玻璃钢棒及其生产工艺 Download PDFInfo
- Publication number
- CN101423949A CN101423949A CN 200810156012 CN200810156012A CN101423949A CN 101423949 A CN101423949 A CN 101423949A CN 200810156012 CN200810156012 CN 200810156012 CN 200810156012 A CN200810156012 A CN 200810156012A CN 101423949 A CN101423949 A CN 101423949A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- layer
- resin
- sulfuric acid
- production line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不锈钢酸洗生产线用玻璃钢棒及其生产工艺，所述玻璃钢棒从内至外分三层，内层为填充层、中间层为强度层、外表层为防腐层，上述三层紧密配合成一个整体；采用拉挤成型工艺，制作中间层的圆管；制作外表层，将碳纤维和树脂以一定的比例浸润后均匀涂抹在中间层上成型；中间层内部即内层使用聚氨酯树脂浇注填充而成。本发明的玻璃钢棒用于不锈钢板酸洗生产线中不锈钢板的侧面导向支撑。
Description
技术领域
本发明涉及一种玻璃钢棒及其生产方法，具体涉及一种不锈钢酸洗生产线用玻璃钢棒及其生产工艺。
背景技术
目前大多酸洗生产线使用聚丙烯或尼龙材料的塑料棒，但在酸洗液腐蚀性环境下塑料棒使用寿命都小于一年，容易造成腐蚀损坏；在生产过程中酸洗大尺寸、大重量的不锈钢板时塑料棒受钢板的侧向力后形成弯曲，不能恢复原状，甚至出现断裂，从而出现钢板卡死，或塑料棒卡死的现象，影响生产线的正产运行。
发明内容
本发明提供了一种不锈钢酸洗生产线用玻璃钢棒及其生产工艺，该工艺生产的玻璃钢棒具有不易变形、抗疲劳性好的特点。
为了解决以上技术问题，本发明的一种不锈钢酸洗生产线用玻璃钢棒，其特征在于：所述玻璃钢棒从内至外分三层，内层为填充层、中间层为强度层、外表层为防腐层，上述三层紧密配合成一个整体。
所述防腐层主要成分为碳纤维和防腐树脂。
所述玻纤层为浸泡有树脂的连续玻璃纤维纱拉挤而成。
所述树脂为普通不饱和聚酯树脂。
所述树脂为聚氨酯树脂。
一种制造不锈钢酸洗生产线用玻璃钢棒的生产工艺步骤如下：
a、先制作中间层的圆管，封闭的模具，使用普通不饱和聚酯树脂和连续玻璃纤维纱，采用拉挤成型工艺，将其在封闭的模具内固化成型后取出；b、中间层完成后，对外表面进行打磨，打磨除去外表面的脱模剂；c、制作外表层，使用碳纤维和树脂，将碳纤维和树脂以一定的比例浸润后均匀涂抹在中间层上成型；d、中间层内部即内层使用聚氨酯树脂浇注填充而成。
步骤a中的固化温度为80℃。
所述步骤c中外表层的玻璃纤维：树脂的含量比为：10％—30％：90％—70％；所述外表层的厚度为2.5mm。
以上结构及工艺的优点在于：本专利所指的玻璃钢棒用于不锈钢板酸洗生产线中，连续生产的不锈钢板在酸洗过程中并连续向前移动，该棒用于不锈钢板的侧面导向支撑。
该棒采用手糊、拉挤、浇注等复合工艺制作，由外层、中间层、内层组成。该棒外表面的防腐层，该防腐层防氢氟酸、盐酸混合酸洗液的腐蚀，用碳纤维作为增强材料采用手糊工艺成型；该棒的中间层采用拉挤工艺成型，其轴向具有很好的强度和弹性模量，可以抵抗不锈钢板在运动过程中侧向的力，钢板移出后玻璃钢棒可以恢复原状；玻璃钢棒中心部分使用树脂浇注成型工艺制作，这一部分可以增强玻璃钢棒的整体刚度，因为玻璃钢刚度是PP材料刚度的10倍以上，并且玻璃钢表面被损坏后这一部分也可以保证玻璃钢棒发挥正常功能，不至于导致生产线停止运行。
附图说明
图为本发明的结构示意图。
具体实施方式
如图所示，所述玻璃钢棒从内至外分a、b、c三层，a层为以聚氨酯填充浇注而成的填充层、b层为浸润有普通不饱和聚酯树脂树脂的连续玻璃纤维纱拉挤而成的强度层、c层为以碳纤维和树脂为主要成分均与涂覆在b层上而成的防腐层，上述三层紧密配合成一个整体。适用于不锈钢板酸洗生产线中，连续生产的不锈钢板在酸洗过程中并连续向前移动，该玻璃棒用于不锈钢板的侧面导向支撑。外层防腐，中间层由于轴向具有很好的强度和弹性模量，可以抵抗不锈钢板在运动过程中侧向的力，保证玻璃钢棒及时恢复原状；内层增加整体刚度，且玻璃钢表面被损坏后这一部分也可以保证玻璃钢棒发挥正常功能，不至于导致生产线停止运行。
上述玻璃棒的制作工艺步骤为：先制作中间层即b层的圆管：封闭的模具，使用浸润有普通不饱和聚酯树脂的连续玻璃纤维纱，采用拉挤成型工艺将其在封闭的模具内固化温度为80°固化成型后取出；中间层完成后，对外表面进行打磨，打磨除去外表面的脱模剂，增加中间层与外层的连接强度。
在中间层即b层外侧制作外表层即c层：使用含量比为10％—30％：90％—70％的碳纤维和树脂，在本实施例中将碳纤维和树脂以含量比为25％：75％的比例均匀涂覆在中间层即b层上成型，涂抹厚度为2.5mm，常温成型后固化。
最后制作内层即a层：在中间层即b层的内部使用聚氨酯树脂浇注填充而成。
所述玻璃钢棒采用以上工艺步骤制作，既能使内、中、外三层紧密配合，又起到了很好的防腐作用；增强轴向强度和弹性模量和玻璃钢棒的整体刚度。
Claims (8)
1、一种不锈钢酸洗生产线用玻璃钢棒，其特征在于：所述玻璃钢棒从内至外分三层，内层为填充层、中间层为强度层、外表层为防腐层，上述三层紧密配合成一个整体。
2、根据权利要求1所述的一种不锈钢酸洗生产线用玻璃钢棒，其特征在于：所述防腐层主要成分为碳纤维和一种防腐树脂。
3、根据权利要求1所述的一种不锈钢酸洗生产线用玻璃钢棒，其特征在于：所述强度层为浸润有树脂的连续玻璃纤维纱拉挤而成。
4、根据权利要求3所述的一种不锈钢酸洗生产线用玻璃钢棒，其特征在于：所述强度层树脂为普通不饱和聚酯树脂。
5、根据权利要求1所述的一种不锈钢酸洗生产线用玻璃钢棒，其特征在于：所述内层树脂为聚氨酯树脂。
6、一种制造权利要求1所述的不锈钢酸洗生产线用玻璃钢棒的生产工艺，其特征在于：a、先制作中间层的圆管，封闭的模具，使用普通不饱和聚酯树脂和连续玻璃纤维纱，采用拉挤成型工艺，将其在封闭的模具内固化成型后取出；b、中间层完成后，对外表面进行打磨，打磨除去外表面的脱模剂；c、制作外表层，使用碳纤维和防腐树脂，将碳纤维和树脂以一定的比例浸润后均匀涂抹在中间层上成型；d、中间层内部即内层使用聚氨酯树脂浇注填充而成。
7、根据权利要求6所述的一种制造权利要求1所述的不锈钢酸洗生产线用玻璃钢棒的生产工艺，其特征在于：步骤a中的固化温度为80℃。
8、根据权利要求6所述的一种制造权利要求1所述的不锈钢酸洗生产线用玻璃钢棒的生产工艺，其特征在于：所述步骤c中外表层的玻璃纤维：树脂的含量比为：10％—30％：90％—70％；所述外表层的厚度为2.5mm。