CN101412836A - Covering water transfer printing polyvinyl alcohol blank base film prescription and production technique - Google Patents
Covering water transfer printing polyvinyl alcohol blank base film prescription and production technique Download PDFInfo
- Publication number
- CN101412836A CN101412836A CNA2008102161322A CN200810216132A CN101412836A CN 101412836 A CN101412836 A CN 101412836A CN A2008102161322 A CNA2008102161322 A CN A2008102161322A CN 200810216132 A CN200810216132 A CN 200810216132A CN 101412836 A CN101412836 A CN 101412836A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- transfer printing
- base film
- water transfer
- blank base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of prescription that is used for printing the covering water transfer printing polyvinyl alcohol blank base film of calligraphy and painting pattern at complex-shaped changeable product surface.It is processed by following proportioning raw material: polyvinyl alcohol 75%-85%, water 5%-15%, ethylene glycol 0.1%-1%, W-Gum 1.5%-3.5%, o-phthalic acid dibutyl ester 0.1%-1%, alkyl-sulphate are tensio-active agent 2%-5.5%, glycerol 1%-2%, tbp 0.1%-1.0%.The present invention also provides the production technique of producing covering water transfer printing polyvinyl alcohol blank base film, and it is to adopt the hydrostomia film-forming process, and its processing step is as follows: place reactor to be heated to 50 ℃-70 ℃ polyvinyl alcohol; Adding entry, ethylene glycol, W-Gum, o-phthalic acid dibutyl ester, alkyl-sulphate then successively is tensio-active agent, glycerol, tbp, stirs and makes slurry in 150 minutes-180 minutes; With slurry on coating machine evenly the coating, then by 90 ℃-100 ℃ drying tunnel heat be wound into membranaceous.By printing calligraphy and painting pattern is printed onto in the present invention, transfer printing is transferred to calligraphy and painting pattern on the complex-shaped changeable product surface through water again, make product designer be given full play to imagination ground deisgn product structural shape and style, and then the image appearance and the market sale that can improve product.
Description
Technical field
The present invention relates to a kind of prescription and production technique of organic film, particularly, it relates to a kind of prescription and production technique that is used at the covering water transfer printing polyvinyl alcohol blank base film of complex-shaped changeable product surface printing calligraphy and painting pattern.
Background content
Existing typography can only be printed onto calligraphy and painting pattern shape clocklike on the article usually, as the plane, sphere, cylindrical surface etc., but calligraphy and painting pattern can not be printed onto surface shape on the object comparatively complicated and changeable, because a large amount of Industrial products such as phone housings, antitheft door, various furniture, household electrical appliances etc., because of surface shape is a curved surface comparatively complicated and changeable, can not utilize the printing calligraphy and painting pattern to be decorated, or for can be at calligraphy and painting pattern in the product surface printing, have to product design is become the stiff style of structure, influence the image appearance and the market sale of product, caused its price low.
Summary of the invention
The objective of the invention is to overcome above-mentioned the deficiencies in the prior art, a kind of prescription and production technique of the blank base film that can use on the water transfer printing coating technology of complex-shaped changeable product surface printing calligraphy and painting pattern is provided.
The invention provides a kind of covering water transfer printing polyvinyl alcohol blank base film, it is processed by following proportioning raw material:
Polyvinyl alcohol 75%-85%, water 5%-15%, ethylene glycol 0.1%-1%, W-Gum 1.5%-3.5%, o-phthalic acid dibutyl ester 0.1%-1%, alkyl-sulphate are tensio-active agent 2%-5.5%, glycerol 1%-2%, tbp 0.1%-1.0%.
The invention provides a kind of covering water transfer printing polyvinyl alcohol blank base film, it is especially processed by following proportioning raw material:
Polyvinyl alcohol 80%, water 10%, ethylene glycol 0.5%, W-Gum 2.5%, o-phthalic acid dibutyl ester 0.5%, alkyl-sulphate are tensio-active agent 4.5%, glycerol 1.5%, tbp 0.5%.
The present invention also provides the production technique of producing covering water transfer printing polyvinyl alcohol blank base film, and it is to adopt the hydrostomia film-forming process, and its processing step is as follows:
(1) polyvinyl alcohol is placed reactor be heated to 50 ℃-70 ℃;
(2) adding entry, ethylene glycol, W-Gum, o-phthalic acid dibutyl ester, alkyl-sulphate then successively is tensio-active agent, glycerol, tbp, stirs and makes slurry in 150 minutes-180 minutes;
(3) with slurry on coating machine evenly the coating, then by 90 ℃-100 ℃ drying tunnel heat be wound into membranaceous.
Covering water transfer printing polyvinyl alcohol blank base film provided by the invention can be printed onto calligraphy and painting pattern on the covering water transfer printing polyvinyl alcohol blank base film by printing, transfer printing is transferred to calligraphy and painting pattern on the complex-shaped changeable product surface through water, make product designer be given full play to imagination ground deisgn product structural shape and style, also can avoid simultaneously void seal normal existing in the general plate face stamp, and in printing-flow, because product surface does not need to contact with print film, can avoid damaging product surface and integrity thereof.And be applicable to unlike material, more owing to pattern, color and luster vividly and significantly improve added value of product.And then the image appearance and the market sale that can improve product.
Embodiment
The embodiment of form is described in further detail foregoing of the present invention again by the following examples.But this should be interpreted as that the scope of the above-mentioned theme of the present invention only limits to following example.All technology that realizes based on foregoing of the present invention all belong to scope of the present invention.
Embodiment
Embodiment 1
Take by weighing each proportion raw material: polyvinyl alcohol 75%-85%, water 5%-15%, ethylene glycol 0.1%-1%, W-Gum 1.5%-3.5%, o-phthalic acid dibutyl ester 0.1%-1%, alkyl-sulphate are tensio-active agent 2%-5.5%, glycerol 1%-2%, tbp 0.1%-1.0%.
(1) polyvinyl alcohol is placed reactor be heated to 50 ℃-70 ℃;
(2) adding entry, ethylene glycol, W-Gum, o-phthalic acid dibutyl ester, alkyl-sulphate then successively is tensio-active agent, glycerol, tbp, stirs and makes slurry in 150 minutes-180 minutes;
(3) with slurry evenly coating on coating machine, then heating by 90 ℃-100 ℃ drying tunnel, to be wound into thickness be 30 microns covering water transfer printing polyvinyl alcohol blank base film.
Embodiment 2
Take by weighing each proportion raw material: polyvinyl alcohol 80%, water 10%, ethylene glycol 0.5%, W-Gum 2.5%, o-phthalic acid dibutyl ester 0.5%, alkyl-sulphate are tensio-active agent 4.5%, glycerol 1.5%, tbp 0.5%.
(1) polyvinyl alcohol is placed reactor be heated to 50 ℃-70 ℃;
(2) adding entry, ethylene glycol, W-Gum, o-phthalic acid dibutyl ester, alkyl-sulphate then successively is tensio-active agent, glycerol, tbp, stirs and makes slurry in 150 minutes-180 minutes;
(3) with slurry evenly coating on coating machine, then heating by 90 ℃-100 ℃ drying tunnel, to be wound into thickness be 35 microns covering water transfer printing polyvinyl alcohol blank base film.
Embodiment 3
Take by weighing each proportion raw material: polyvinyl alcohol 80%, water 10%, ethylene glycol 0.5%, W-Gum 2.5%, o-phthalic acid dibutyl ester 0.5%, alkyl-sulphate are tensio-active agent 4.5%, glycerol 1.5%, tbp 0.5%.
(1) polyvinyl alcohol places reactor to be heated to 50 ℃-70 ℃;
(2) adding entry, ethylene glycol, W-Gum, o-phthalic acid dibutyl ester, alkyl-sulphate then successively is tensio-active agent, glycerol, tbp, stirs and makes slurry in 150 minutes-180 minutes;
(3) with slurry evenly coating on coating machine, then heating by 90 ℃-100 ℃ drying tunnel, to be wound into thickness be 40 microns covering water transfer printing polyvinyl alcohol blank base film.
Claims (3)
1, covering water transfer printing polyvinyl alcohol blank base film is characterized in that its prescription consists of: polyvinyl alcohol 75%-85%, water 5%-15%, ethylene glycol 0.1%-1%, W-Gum 1.5%-3.5%, o-phthalic acid dibutyl ester 0.1%-1%, alkyl-sulphate are tensio-active agent 2%-5.5%, glycerol 1%-2%, tbp 0.1%-1.0%.
2, covering water transfer printing polyvinyl alcohol blank base film according to claim 1 is characterized in that its prescription consists of: polyvinyl alcohol 80%, water 10%, ethylene glycol 0.5%, W-Gum 2.5%, o-phthalic acid dibutyl ester 0.5%, alkyl-sulphate are tensio-active agent 4.5%, glycerol 1.5%, tbp 0.5%.
3, the production technique of covering water transfer printing polyvinyl alcohol blank base film adopts the hydrostomia film-forming process, and its processing step is as follows:
(1) polyvinyl alcohol is placed reactor be heated to 50 ℃-70 ℃;
(2) adding entry, ethylene glycol, W-Gum, o-phthalic acid dibutyl ester, alkyl-sulphate then successively is tensio-active agent, glycerol, tbp, stirs and makes slurry in 150 minutes-180 minutes;
(3) with slurry on coating machine evenly the coating, then by 90 ℃-100 ℃ drying tunnel heat be wound into membranaceous.