CN101412236B - 一种膨润修复枯萎竹简的方法 - Google Patents
一种膨润修复枯萎竹简的方法 Download PDFInfo
- Publication number
- CN101412236B CN101412236B CN2008101979786A CN200810197978A CN101412236B CN 101412236 B CN101412236 B CN 101412236B CN 2008101979786 A CN2008101979786 A CN 2008101979786A CN 200810197978 A CN200810197978 A CN 200810197978A CN 101412236 B CN101412236 B CN 101412236B
- Authority
- CN
- China
- Prior art keywords
- bamboo
- inscribed
- writing
- ancient times
- shriveled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种膨润修复枯萎竹简的方法,涉及一种竹简文物的修复方法;具体地说,涉及考古发掘获得的低强度竹简及枯萎竹简修复材料的组分、制备和修复方法。本发明包括下列步骤:①用蒸馏水将枯萎竹简清洗干净;②将洗净的枯萎竹简浸泡在竹类膨润材料中3-7天;③再将胀润后的枯萎竹简放到竹类修复材料中浸泡7-10天;④置于阴凉通风处自然干燥。本发明明显提高了竹简强度;增强了竹简的耐折度、撕裂度、耐破度、抗张强度,滤水性提高。本发明适用于枯萎竹简的膨润修复。
Description
技术领域
本发明涉及一种竹简文物的修复方法,尤其涉及一种膨润修复枯萎竹简的方法;具体地说,涉及考古发掘获得的低强度竹简及枯萎竹简修复材料的组分、制备和修复方法。
背景技术
竹简文物是研究我国历史、文化艺术和科学技术发展史的极其重要的珍贵史料,它直接告诉考古工作者和文史工作者真实的历史,同时也给科研工作者真实材料分析先人们当时的生产工艺。许多竹简文物是稀世珍宝,甚至价值连城;保护好竹简文物是我们义不容辞的责任。由于技术上的原因,竹简文物保护问题很多,如不及时解决,势必造成不可挽回的损失。
每年我国考古发掘都会出土大量珍贵的竹简文物;其中有不少竹简文物因地下埋藏环境的交替改变,出土时已经严重枯萎收缩和扭曲变形,称其为枯萎竹简,其极低的机械强度和高度的炭化使考古工作者无法辨认竹简上的文字。
过去对竹简文物的保护技术研究及其应用,基本上限于形态较完整、未发生枯萎扭曲变形的竹简,采用的方法也只是较为传统的物理和化学方法。对枯萎竹简的整形复原研究少有涉及,也未见国内外的相关报导。因此,枯萎竹简的整形复原,已成为国际难题,急需研究攻克。
发明内容
本发明的目的就在于克服现有技术存在的上述缺点和不足,提供一种膨润修复枯萎竹简的方法。
本发明的目的是这样实现的:
1、竹类膨润材料
(1)竹类膨润材料的组分(重量百分比)
竹类膨润材料的组分主要是:
氢氧化钠 9-11%,
木素净 0.3-2.3%,
NNO分散剂 0.1-0.2%,
水 87-89%。
验证:
*所有组分下限之和小于100%,所有组分上限之和大于100%;
*每一组分的下限加其它组分的上限之和大于100%;
*每一组分的上限加其它组分的下限之和小于100%。
(2)竹类膨润材料的制备方法
将上述组分置于气混容器里混搅均匀即可。
2、竹类修复材料
(1)竹类修复材料的组分(重量百分比)
糖 7.6-9.6%,
聚乙二醇(PEG) 30-32%,
水 50-53.4%,
糠醛 7.6-9.6%。
验证:
*所有组分下限之和小于100%,所有组分上限之和大于100%;
*每一组分的下限加其它组分的上限之和大于100%;
*每一组分的上限加其它组分的下限之和小于100%。
(2)竹类修复材料的制备方法
将上述组分置于气混容器里混搅均匀即可。
3、膨润修复枯萎竹简的方法
膨润修复枯萎竹简的方法包括下列步骤:
①用蒸馏水将枯萎竹简清洗干净;
②将洗净的枯萎竹简浸泡在竹类膨润材料中3-7天;
③再将胀润后的枯萎竹简放到竹类修复材料中浸泡7-10天;
④置于阴凉通风处自然干燥。
本发明具有下列优点和积极效果:
①用常规方法(一般用碱14%-16%)对竹简润胀,会使天然纤维受到极大的破坏,降解程度大,导致竹简强度低、黑度高、不易洗涤;
采用本发明,除有氢氧化钠外,还添加了新型助剂木素清、可溶性糖和糠醛,因其具有较强渗透能力和反应活性,在较小碱比(10-12%)和较低温条件下,也能润胀竹简的木质素,因而对纤维破坏性较小,明显提高了竹简强度;较低温度条件下的润胀增强了竹简的耐折度、撕裂度、耐破度、抗张强度,滤水性提高。
②木质素定向降解转化,使纤维素的氢键重排,制成具有新性能的材料,使之便于竹简的润胀。
③本发明适用于枯萎竹简的膨润修复。
具体实施方式
下面结合实施例详细说明
一、最佳值
1、竹类膨润材料的组分(重量百分比)最佳值
氢氧化钠 12%,
木素净 1.5%,
NNO分散剂 0.3%,
水 86.2%。
2、竹类修复材料的组分(重量百分比)最佳值
糖 9.5%,
聚乙二醇(PEG) 33%,
水 52%,
糠醛 5.5%。
二、实验
1、荆州谢家桥一号墓出土的西汉枯萎竹简
枯萎竹简的尺寸是:宽3.2毫米、长30毫米、厚0.2毫米;
放入竹类膨润材料浸泡3天,尺寸是:变为宽6.7毫米、长30毫米、厚0.4
毫米。
浸泡在竹类修复材料中7天,后经自然干燥,尺寸是:宽6.6毫米、长30毫米、厚0.36毫米。
2、江西靖安李洲坳墓竹席残片
竹席残片的尺寸是:宽3.0毫米、长14毫米、厚0.2毫米;
放入竹类膨润材料浸泡3天,尺寸是:宽6.2.毫米、长14毫米、厚0.34毫米。
浸泡在竹类修复材料中7天后经自然干燥,尺寸是:宽6.0.毫米、长14毫米、厚0.32毫米。
由上述试验可知,枯萎竹简的形状基本得到恢复,而且强度较高。
Claims (1)
1.一种膨润修复枯萎竹简的方法,其特征在于包括下列步骤:
①用蒸馏水将枯萎竹简清洗干净;
②将洗净的枯萎竹简浸泡在竹类膨润材料中3-7天;
③再将胀润后的枯萎竹简放到竹类修复材料中浸泡7-10天;
④置于阴凉通风处自然干燥;
所述的竹类膨润材料,其组分的重量百分比是:
氢氧化钠 9-11%,
木素净 0.3-2.3%,
NNO分散剂 0.1-0.2%,
水 87-89%;
所述的竹类修复材料,其组分的重量百分比是:
糖 7.6-9.6%,
聚乙二醇 30-32%,
水 50-53.4%,
糠醛 7.6-9.6%。