CN101412164A - 发尘量低的钛型药芯焊丝及其制备方法 - Google Patents

发尘量低的钛型药芯焊丝及其制备方法 Download PDF

Info

Publication number
CN101412164A
CN101412164A CNA2008101592909A CN200810159290A CN101412164A CN 101412164 A CN101412164 A CN 101412164A CN A2008101592909 A CNA2008101592909 A CN A2008101592909A CN 200810159290 A CN200810159290 A CN 200810159290A CN 101412164 A CN101412164 A CN 101412164A
Authority
CN
China
Prior art keywords
powder
type flux
percent
preparation
titania
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008101592909A
Other languages
English (en)
Inventor
冯纪东
孙仲宝
张键
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG FEIYUE WELDING INDUSTRY Co Ltd
Original Assignee
SHANDONG FEIYUE WELDING INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG FEIYUE WELDING INDUSTRY Co Ltd filed Critical SHANDONG FEIYUE WELDING INDUSTRY Co Ltd
Priority to CNA2008101592909A priority Critical patent/CN101412164A/zh
Publication of CN101412164A publication Critical patent/CN101412164A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种发尘量低的钛型药芯焊丝及其制备方法，属于焊接技术领域，由钢带包覆药粉，经轧制、拔制而成，其特征在于药粉的配料质量百分组成为：金红石1.38～46％、氧化铝6～10％、石英砂4～8％、锆英砂5～12％、氟化钠0.5～1.5％、硅锰合金10～21％、铝镁合金3～6％、氧化镁3～8％和余量的还原铁粉；配料用水玻璃混合后，经过850～900℃的高温烧结，再造粒制成药粉。药芯焊丝的发尘量少，安全可靠；制备方法科学合理、简单易行。

Description

发尘量低的钛型药芯焊丝及其制备方法
技术领域
本发明涉及一种发尘量低的钛型药芯焊丝及其制备方法，属于焊接技术领域。
背景技术
药芯焊丝发尘量比实芯焊丝高30-40％，尤其是在通风条件不好的仓体内施焊，对焊工的伤害很大。
发明内容
本发明的目的在于提供一种发尘量低的钛型药芯焊丝，药芯焊丝的发尘量少，安全可靠；本发明同时提供了科学合理、简单易行的制备方法。
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石1.38～46％、氧化铝6～10％、石英砂4～8％、锆英砂5～12％、氟化钠0.5～1.5％、硅锰合金10～21％、铝镁合金3～6％、氧化镁3～8％和余量的还原铁粉。
科学合理、简单易行的制备方法如下：
由钢带包覆药粉，经轧制、拔制而成，其中，配料用水玻璃混合后，经过850～900℃的高温烧结，再造粒制成药粉。
水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的0.5～1.5％。
造粒粒径在80～180目筛，即80～180目筛之间的颗粒料。
可直接购买市售的工业纯原料即可。
本发明通过调整药粉组成，解决了发尘量高的问题，脱渣容易、电弧稳定、焊缝成型美观，经应用试验证明，发尘量由原来的8mg/g降至3mg/g，处于国际领先水平，可广泛应用于船舶、石油化工等机械领域的焊接。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石20％、氧化铝8％、石英砂5％、锆英砂10％、氟化钠1％、硅锰合金15％、铝镁合金5％、氧化镁6％和余量的还原铁粉。
制备时，配料用水玻璃混合后，经过850～860℃的高温烧结，再造粒制成药粉，造粒粒径控制在100～120目筛，其它按照常规工艺操作。
其中，水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的1％。
实施例2
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石30％、氧化铝10％、石英砂4％、锆英砂8％、氟化钠0.5％、硅锰合金12.5％、铝镁合金6％、氧化镁7％和余量的还原铁粉。
制备时，配料用水玻璃混合后，经过870～880℃的高温烧结，再造粒制成药粉，造粒粒径控制在90～120目筛，其它按照常规工艺操作。
其中，水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的0.8％。
实施例3
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石15％、氧化铝9％、石英砂7％、锆英砂9％、氟化钠1.5％、硅锰合金18％、铝镁合金4.5％、氧化镁4.5％和余量的还原铁粉。
制备时，配料用水玻璃混合后，经过890～900℃的高温烧结，再造粒制成药粉，造粒粒径控制在80～170目筛，其它按照常规工艺操作。
其中，水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的1.2％。
实施例4
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石40％、氧化铝8％、石英砂6.5％、锆英砂8.5％、氟化钠1％、硅锰合金14％、铝镁合金6％、氧化镁6％和余量的还原铁粉。
制备时，配料用水玻璃混合后，经过855～865℃的高温烧结，再造粒制成药粉，造粒粒径控制在110～150目筛，其它按照常规工艺操作。
其中，水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的0.9％。
实施例5
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石25％、氧化铝10％、石英砂6％、锆英砂7％、氟化钠0.7％、硅锰合金17％、铝镁合金4％、氧化镁6％和余量的还原铁粉。
制备时，配料用水玻璃混合后，经过880～890℃的高温烧结，再造粒制成药粉，造粒粒径控制在100～160目筛，其它按照常规工艺操作。
其中，水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的1.3％。
实施例6
本发明所述的发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其中药粉的配料质量百分组成为：
金红石10.5％、氧化铝10％、石英砂6.5％、锆英砂11％、氟化钠1.1％、硅锰合金20％、铝镁合金6％、氧化镁5％和余量的还原铁粉。
制备时，配料用水玻璃混合后，经过890～900℃的高温烧结，再造粒制成药粉，造粒粒径控制在80～150目筛，其它按照常规工艺操作。
其中，水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1，钾钠水玻璃的配用量占配料总质量的1％。

Claims (5)

1、一种发尘量低的钛型药芯焊丝，由钢带包覆药粉，经轧制、拔制而成，其特征在于药粉的配料质量百分组成为：
金红石1.38～46％、氧化铝6～10％、石英砂4～8％、锆英砂5～12％、氟化钠0.5～1.5％、硅锰合金10～21％、铝镁合金3～6％、氧化镁3～8％和余量的还原铁粉。
2、一种权利要求1所述的发尘量低的钛型药芯焊丝的制备方法，由钢带包覆药粉，经轧制、拔制而成，其特征在于配料用水玻璃混合后，经过850～900℃的高温烧结，再造粒制成药粉。
3、根据权利要求2所述的发尘量低的钛型药芯焊丝的制备方法，其特征在于水玻璃为钾钠水玻璃，其中氧化钾和氧化钠的质量比为2∶1。
4、根据权利要求3所述的发尘量低的钛型药芯焊丝的制备方法，其特征在于钾钠水玻璃占配料总质量的0.5～1.5％。
5、根据权利要求2、3或4所述的发尘量低的钛型药芯焊丝的制备方法，其特征在于造粒粒径在80～180目筛。
CNA2008101592909A 2008-11-28 2008-11-28 发尘量低的钛型药芯焊丝及其制备方法 Pending CN101412164A (zh)