CN101402804B - Information coating formula without plate seam - Google Patents
Information coating formula without plate seam Download PDFInfo
- Publication number
- CN101402804B CN101402804B CN 200810198247 CN200810198247A CN101402804B CN 101402804 B CN101402804 B CN 101402804B CN 200810198247 CN200810198247 CN 200810198247 CN 200810198247 A CN200810198247 A CN 200810198247A CN 101402804 B CN101402804 B CN 101402804B
- Authority
- CN
- China
- Prior art keywords
- percent
- butanone
- agent
- methyl methacrylate
- butyl acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the technical field of a laser film material, in particular to a non plate-clearance information coat prescription. According to weight percentage, the non plate-clearance information coat prescription comprises the following components: 15 to 25 percent of methyl methacrylate; 20 to 30 percent of butyl acrylate; 25 to 45 percent of butanone; 5 to 20 percent of methylisobutylketone; 0.15 to 0.3 percent of silicone antifoam agent; and 0.1 to 0.2 percent of flatting agent. When a laser information layer is pressed and printed, the prescription does not generate the plate-clearance without laser effect or over-remarkable laser effect phenomenon, thus greatly improving the qualified rate of products.
Description
Technical field:
The present invention relates to the laser film material technical field, particularly information coating formula without plate seam.
Background technology:
Radium-shine film has laminate structure, comprises glue layer, aluminium lamination, laser information layer and release layer from bottom to top.Present laser information layer formula when impression laser information layer, can produce the version seam of no laser effect, or version is sewed with laser effect, but laser effect is too obvious, makes product defective.
Summary of the invention:
The objective of the invention is to overcome the deficiencies in the prior art, and a kind of information coating formula without plate seam is provided.
For achieving the above object, the technical solution used in the present invention is:
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 15~25%
Butyl acrylate 20~30%
Butanone 25~45%
Mibk 5~20%
Silicone antifoam agent 0.15~0.3%
Flow agent 0.1~0.2%.
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 20~25%
Butyl acrylate 25~30%
Butanone 35~45%
Mibk 10~20%
Silicone antifoam agent 0.2~0.3%
Flow agent 0.15~0.2%.
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 24.75%
Butyl acrylate 30%
Butanone 35%
Mibk 10%
Silicone antifoam agent 0.15%
Flow agent 0.1%.
Described silicone antifoam agent is the polysiloxane silicone antifoam agent.
Described flow agent is a silicon class flow agent.
Described silicon class flow agent is the interpolymer of polyether glycol and siloxanes.
Beneficial effect of the present invention is: the present invention by weight percentage, comprise following composition: methyl methacrylate 15~25%, butyl acrylate 20~30%, butanone 25~45%, mibk 5~20%, silicone antifoam agent 0.15~0.3%, flow agent 0.1~0.2% when impression laser information layer, can not produce the version seam of no laser effect, or the too tangible phenomenon of laser effect, improved product percent of pass greatly.
Embodiment:
The following examples can make those skilled in the art more fully understand the present invention, but do not limit the present invention in any way.
Embodiment 1
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 24.75%
Butyl acrylate 30%
Butanone 35%
Mibk 10%
Polysiloxane silicone antifoam agent 0.15%
The interpolymer flow agent 0.1% of polyether glycol and siloxanes.
Embodiment 2
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 25%
Butyl acrylate 30%
Butanone 36%
Mibk 8.75%
Polysiloxane silicone antifoam agent 0.15%
The interpolymer flow agent 0.1% of polyether glycol and siloxanes.
Embodiment 3
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 25%
Butyl acrylate 30%
Butanone 25%
Mibk 19.5%
Polysiloxane silicone antifoam agent 0.3%
The interpolymer flow agent 0.2% of polyether glycol and siloxanes.
Embodiment 4
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 15%
Butyl acrylate 25%
Butanone 45%
Mibk 14.75%
Polysiloxane silicone antifoam agent 0.15%
The interpolymer flow agent 0.1% of polyether glycol and siloxanes.
Embodiment 5
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 14.6%
Butyl acrylate 20%
Butanone 45%
Mibk 20%
Polysiloxane silicone antifoam agent 0.2%
The interpolymer flow agent 0.2% of polyether glycol and siloxanes.
Embodiment 6
Information coating formula without plate seam by weight percentage, comprises following composition:
Methyl methacrylate 20%
Butyl acrylate 19.5%
Butanone 40%
Mibk 20%
Polysiloxane silicone antifoam agent 0.3%
The interpolymer flow agent 0.2% of polyether glycol and siloxanes.
Claims (4)
1. seamless information coating is characterized in that: by weight percentage, comprise following composition:
Methyl methacrylate 15~25%
Butyl acrylate 20~30%
Butanone 25~45%
Mibk 5~20%
Polysiloxane silicone antifoam agent 0.15~0.3%
Silicon class flow agent 0.1~0.2%.
2. seamless information coating according to claim 1 is characterized in that: by weight percentage, comprise following composition:
Methyl methacrylate 20~25%
Butyl acrylate 25~30%
Butanone 35~45%
Mibk 10~20%
Polysiloxane silicone antifoam agent 0.2~0.3%
Silicon class flow agent 0.15~0.2%
Each component sum equals 100%.
3. seamless information coating according to claim 1 is characterized in that: by weight percentage, comprise following composition:
Methyl methacrylate 24.75%
Butyl acrylate 30%
Butanone 35%
Mibk 10%
Polysiloxane silicone antifoam agent 0.15%
Silicon class flow agent 0.1%.
4. according to any described seamless information coating of claim 1-3, it is characterized in that: described silicon class flow agent is the interpolymer of polyether glycol and siloxanes.