CN101397476A - 混凝土中钢筋防腐专用水性漆 - Google Patents

混凝土中钢筋防腐专用水性漆 Download PDF

Info

Publication number
CN101397476A
CN101397476A CNA2007101336240A CN200710133624A CN101397476A CN 101397476 A CN101397476 A CN 101397476A CN A2007101336240 A CNA2007101336240 A CN A2007101336240A CN 200710133624 A CN200710133624 A CN 200710133624A CN 101397476 A CN101397476 A CN 101397476A
Authority
CN
China
Prior art keywords
corrosion
agent
concrete
zinc
rust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007101336240A
Other languages
English (en)
Inventor
孙立为
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2007101336240A priority Critical patent/CN101397476A/zh
Publication of CN101397476A publication Critical patent/CN101397476A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种防腐涂料，特别是一种用于混凝土中钢筋防腐的专用水性漆。它通过活性颜料及防锈颜料在无机酸作用下，进而形成吸收稳定铁锈的氮碱离子基因使活泼的铁锈失去活性达到配位络合作用。使漆浆充分渗透到钢铁表面的微孔中，把铁锈分离并包围在漆浆中，成膜后通过缓慢的水解而相互反应，进一步形成难溶的杂多酸络合物即将铁锈转化成新的稳定保护层，并渗透到金属表面及针孔，将金属表面的锈蚀层转化为有益的保护层，并牢牢的附着在金属表面，阻止混凝土中的钢筋腐蚀，延长钢结构在混凝土中的使用寿命。

Description

混凝土中钢筋防腐专用水性漆
技术领域
本发明涉及一种防腐涂料，特别是一种用于混凝土中钢筋防腐的专用水性漆。
背景技术
目前在建筑领域，钢筋混凝土是建筑构造的最主要材料，然而钢筋腐蚀引起的混凝土结构失效以及如何提高其耐久性等问题一直困扰着材料科学工作者。大量的工程实践表明，混凝土修复和加固费用远比原始建设时要高，尽管很多时候效果还不能让人满意。由于选材、施工、养护等过程的不同，混凝土结构发生破坏的时间也就大不相同，从几年到几十年。在某些条件的共同作用下，钢筋腐蚀造成的损害会在瞬间发生，造成重大安全事故，威胁人民生命财产安全。因此，阻止混凝土中钢筋腐蚀工作迫在眉睫。引起混凝土破坏失效的主要原因有钢筋腐蚀、混凝土碳化、碱基料反应、冻融破坏，其中，以钢筋腐蚀的危害最为严重。
发明内容
本发明的目的是要提供一种混凝土中钢筋防腐专用水性漆，通过活性颜料及防锈颜料在无机酸作用下，进而形成吸收稳定铁锈的氮碱离子基因使活泼的铁锈失去活性达到配位络合作用。使漆浆充分渗透到钢铁表面的微孔中，把铁锈分离并包围在漆浆中，成膜后通过缓慢的水解而相互反应，进一步形成难溶的杂多酸络合物即将铁锈转化成新的稳定保护层，并渗透到金属表面及针孔，将金属表面的锈蚀层转化为有益的保护层，并牢牢的附着在金属表面，阻止混凝土中的钢筋腐蚀，延长钢结构在混凝土中的使用寿命。
本发明的目的是以如下技术方案实现的：一种混凝土中钢筋防腐专用水性漆，(1)本发明的组分是：原料：聚胺酯丙烯酸共聚物乳液，填料：磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉，试剂：分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂、调节剂、去离子水；(2)本发明的主要成分重量比是：聚胺酯丙烯酸共聚物乳液44-46，填料：磷酸锌3-4、氧化锌2、三聚磷酸二氢铝5-6、锌黄2、沉淀硫酸钡8-10、云母粉6-8，试剂：分散剂0.4、润湿剂0.4、流平剂0.4、179缓蚀剂1-1.5、增稠剂0.6-0.8、醇脂12成膜助剂3、调节剂0.45、去离子水13-15；
所述的混凝土中钢筋防腐专用水性漆的制备方法按如下步骤进行；
(1)在去离子水中加入聚胺酯丙烯酸共聚物乳液和磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉后，搅拌混合；
(2)加入色料搅拌；
(3)在上述经搅拌混合的料中再加入分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂后，搅拌；
(4)对上述充分搅拌过的料进行粗砂磨，细砂磨；
(5)加入调节剂后，搅拌，置化；
(6)对上述置化后的料，作黏度调整，包装入库。
本发明的优点是；本产品属于渗透型产品，它可以渗透到钢筋里层，将金属表面的锈蚀层转化为有益的保护层，并牢牢的附着在金属表面，阻止混凝土中的钢筋腐蚀，延长钢结构在混凝土中的使用寿命。
下面结合具体实施方式对本发明做进一步说明；
实施例1.
一种混凝土中钢筋防腐专用水性漆，(1)本发明的组分是：原料：聚胺酯丙烯酸共聚物乳液，填料：磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉，试剂：分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂、调节剂、去离子水；(2)本发明的主要成分重量比是：聚胺酯丙烯酸共聚物乳液44，填料：磷酸锌3、氧化锌2、三聚磷酸二氢铝5、锌黄2、沉淀硫酸钡8、云母粉6，试剂：分散剂0.4、润湿剂0.4、流平剂0.4、179缓蚀剂1、增稠剂0.6、醇脂12成膜助剂3、调节剂0.45、去离子水13；
所述的混凝土中钢筋防腐专用水性漆的制备方法按如下步骤进行；
(1)在去离子水中加入聚胺酯丙烯酸共聚物乳液和磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉后，搅拌混合；
(2)加入色料搅拌；
(3)在上述经搅拌混合的料中再加入分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂后，搅拌；
(4)对上述充分搅拌过的料进行粗砂磨，细砂磨；
(5)加入调节剂后，搅拌，置化；
(6)对上述置化后的料，作黏度调整，包装入库。
实施例2.
一种混凝土中钢筋防腐专用水性漆，(1)本发明的组分是：原料：聚胺酯丙烯酸共聚物乳液，填料：磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉，试剂：分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂、调节剂、去离子水；(2)本发明的主要成分重量比是：聚胺酯丙烯酸共聚物乳液46，填料：磷酸锌4、氧化锌2、三聚磷酸二氢铝6、锌黄2、沉淀硫酸钡10、云母粉8，试剂：分散剂0.4、润湿剂0.4、流平剂0.4、179缓蚀剂1..5、增稠剂0.8、醇脂12成膜助剂3、调节剂0.45、去离子水15；
所述的混凝土中钢筋防腐专用水性漆的制备方法按如下步骤进行；
(1)在去离子水中加入聚胺酯丙烯酸共聚物乳液和磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉后，搅拌混合；
(2)加入色料搅拌；
(3)在上述经搅拌混合的料中再加入分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂后，搅拌；
(4)对上述充分搅拌过的料进行粗砂磨，细砂磨；
(5)加入调节剂后，搅拌，置化；
(6)对上述置化后的料，作黏度调整，包装入库。

Claims (2)

1.一种混凝土中钢筋防腐专用水性漆，其特征是：(1)本发明的组分是：原料：聚胺酯丙烯酸共聚物乳液，填料：磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉，试剂：分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂、调节剂、去离子水；(2)本发明的主要成分重量比是：聚胺酯丙烯酸共聚物乳液44-46，填料：磷酸锌3-4、氧化锌2、三聚磷酸二氢铝5-6、锌黄2、沉淀硫酸钡8-10、云母粉6-8，试剂：分散剂0.4、润湿剂0.4、流平剂0.4、179缓蚀剂1-1.5、增稠剂0.6-0.8、醇脂12成膜助剂3、调节剂0.45、去离子水13-15；
2、一种权利要求1所述的混凝土中钢筋防腐专用水性漆的制备方法，其特征是：
(1)在去离子水中加入聚胺酯丙烯酸共聚物乳液和磷酸锌、氧化锌、三聚磷酸二氢铝、锌黄309、沉淀硫酸钡、云母粉后，搅拌混合；
(2)加入色料搅拌；
(3)在上述经搅拌混合的料中再加入分散剂、润湿剂、流平剂、179缓蚀剂、增稠剂、醇脂12成膜助剂后，搅拌；
(4)对上述充分搅拌过的料进行粗砂磨，细砂磨；
(5)加入调节剂后，搅拌，置化；
(6)对上述置化后的料，作黏度调整，包装入库。
CNA2007101336240A 2007-09-26 2007-09-26 混凝土中钢筋防腐专用水性漆 Pending CN101397476A (zh)