CN101393789A - 交联聚乙烯绝缘电力电缆内气体的排除方法 - Google Patents
交联聚乙烯绝缘电力电缆内气体的排除方法 Download PDFInfo
- Publication number
- CN101393789A CN101393789A CNA200810195028XA CN200810195028A CN101393789A CN 101393789 A CN101393789 A CN 101393789A CN A200810195028X A CNA200810195028X A CN A200810195028XA CN 200810195028 A CN200810195028 A CN 200810195028A CN 101393789 A CN101393789 A CN 101393789A
- Authority
- CN
- China
- Prior art keywords
- cable
- gas
- bulge
- nitrogen cylinder
- power cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种交联聚乙烯绝缘电力电缆内气体的排除方法，包括如下步骤：将经过挤出机后有鼓包的半成品电缆，电缆一端与1～2.5MPa压力的氮气瓶气管出口连通，电缆另一端保持开口；打开氮气瓶的阀门，开口端电缆不断有气体逸出，鼓包慢慢消失，一直到鼓包消失，关闭阀门即可。采用本发明的工艺排除交联聚乙烯绝缘电力电缆内的气体，时间短，排气效果好，可以将电缆护套与绝缘屏蔽之间的气体全部排除，避免电缆出现质量隐患；本发明的工艺采用高压氮气排除气体，大大降低了烘房烘干的费用，节约了成本；本发明工艺简单，操作方便。
Description
技术领域
本发明涉及电缆内气体的排除方法，尤其是一种交联聚乙烯绝缘电力电缆内气体的排除方法。
背景技术
目前的交联聚乙烯绝缘电力电缆在电力传输线路上得到极其广泛的应用。中压、高压和超高压交联聚乙烯绝缘电力电缆均采用化学方法进行交联，在交联过程中会产生出一种叫苯乙酮的气体，如果在苯乙酮气体没有排净的状态下就流入了下道工序并加工成成品，这样就会在电缆护套与绝缘屏蔽之间充满大量气体，电缆外径大大增加，出现鼓包，俗称“发胖”，用手触摸有柔软感，对于这种内部充满气体的交联电缆必须加以处置，因此在生产中应该有脱气工艺，如采用抽真空的方法排气，这种方法容易因负压而降低电缆的绝缘性能，会造成电缆在耐压试验中或使用中击穿，俗称“放炮”，损失巨大。还有一种方法是将交联线芯置于烘房中或在常温下放置一定时间后再流入下工序，目前国内外电缆厂采用的脱气方法一般是：110KV以上的电缆在烘房内烘干，通常时间长达一周以上；小于35KV的电缆于常温下放置48小时以上。这种排气方法通常花费的时间比较长，而采用在烘房烘干又增加了烘干费用，造成成本上升。
发明内容
发明目的：本发明的目的在于克服现有技术的不足，提供一种能成本低廉、能将电缆内气体全部排出的交联聚乙烯绝缘电力电缆内气体的排除方法。
技术方案：将经过挤出机后有鼓包的半成品电缆，电缆一端与1～2.5MPa压力的氮气瓶气管出口连通，电缆另一端保持开口；打开氮气瓶的阀门，开口端电缆不断有气体逸出，鼓包慢慢消失，一直到鼓包消失，关闭阀门即可。
其中，所述的氮气纯度大于等于99.5％。
其中氮气瓶也可以是其他能够产生氮气的装置，如氮气发生器。
有益效果：(1)采用本发明的工艺排除交联聚乙烯绝缘电力电缆内的气体，时间短，排气效果好，可以将电缆护套与绝缘屏蔽之间的气体全部排除，避免电缆出现质量隐患。(2)本发明的工艺采用高压氮气排除气体，大大降低了烘房烘干的费用，节约了成本。(3)本发明工艺简单，操作方便。(4)使用氮气排除电缆内的气体不会产生负压，因而对电缆的绝缘性能不会产生影响。
具体实施方式
根据下述实施例，可以更好的理解本发明。
实施例1：
取发生鼓包现象，内部有气体，即俗称发胖的半成品220KV的交联聚乙烯绝缘电缆100m，将氮气瓶气管出口的密封帽套在电缆一头，电缆另一头开口，保持氮气瓶内的压力在2.5MPa，氮气纯度99.5％；打开氮气瓶的阀门，半成品电缆内的气体慢慢被高压氮气挤出，鼓包慢慢消失，直至鼓包完全消失时，关闭阀门即可，整个过程持续5小时。
实施例2：
取发生鼓包现象，内部有气体，即俗称发胖的半成品110KV的交联聚乙烯绝缘电缆150m，将氮气瓶气管出口的密封帽套在电缆一头，电缆另一头开口，保持氮气瓶内的压力在2MPa，氮气纯度99.8％；打开氮气瓶的阀门，半成品电缆内的气体慢慢被高压氮气挤出，鼓包慢慢消失，直至鼓包完全消失时，关闭阀门即可，整个过程持续5小时。
实施例3：
取发生鼓包现象，内部有气体，即俗称发胖的半成品35KV的交联聚乙烯绝缘电缆200m，将氮气瓶气管出口的密封帽套在电缆一头，电缆另一头开口，保持氮气瓶内的压力在1.5MPa，氮气纯度99.9％；打开氮气瓶的阀门，半成品电缆内的气体慢慢被高压氮气挤出，鼓包慢慢消失，直至鼓包完全消失时，关闭阀门即可，整个过程持续5小时。
本发明提供了一种交联聚乙烯绝缘电力电缆内气体的排除方法的思路及方法，具体实现该技术方案的方法和途径很多，以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。本实施例中未明确的各组成部份均可用现有技术加以实现。
Claims (2)
1、一种交联聚乙烯绝缘电力电缆内气体的排除方法，其特征在于包括如下步骤：将经过挤出机后有鼓包的半成品电缆，电缆一端与1～2.5MPa压力的氮气瓶气管出口连通，电缆另一端保持开口；打开氮气瓶的阀门，开口端电缆不断有气体逸出，鼓包慢慢消失，一直到鼓包消失，关闭阀门即可。
2、根据权利要求1所述的交联聚乙烯绝缘电力电缆内气体的排除方法，其特征在于：所述的氮气纯度大于等于99.5％。