CN101372741A - 一种喷油泵柱塞的表面处理方法 - Google Patents

一种喷油泵柱塞的表面处理方法 Download PDF

Info

Publication number
CN101372741A
CN101372741A CNA2008101558908A CN200810155890A CN101372741A CN 101372741 A CN101372741 A CN 101372741A CN A2008101558908 A CNA2008101558908 A CN A2008101558908A CN 200810155890 A CN200810155890 A CN 200810155890A CN 101372741 A CN101372741 A CN 101372741A
Authority
CN
China
Prior art keywords
injection pump
pump plunger
plunger
content
metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008101558908A
Other languages
English (en)
Inventor
潘明飞
谈仕明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIZHENG WEIYE OIL PUMP AND NOZZLE CO Ltd
Original Assignee
YIZHENG WEIYE OIL PUMP AND NOZZLE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIZHENG WEIYE OIL PUMP AND NOZZLE CO Ltd filed Critical YIZHENG WEIYE OIL PUMP AND NOZZLE CO Ltd
Priority to CNA2008101558908A priority Critical patent/CN101372741A/zh
Publication of CN101372741A publication Critical patent/CN101372741A/zh
Pending legal-status Critical Current

Abstract

一种喷油泵柱塞的表面处理方法，涉及油嘴油泵的结构技术领域。本发明采用对喷油泵柱塞前部进行表面磷化处理。通过磷化处理后，由于金属表面形成了一层不溶于水的磷酸盐保护膜，从而提高了金属工件的抗氧化性能和外观质量，并可大大延长偶件使用寿命。磷化后的金属防腐蚀能力比未磷化的防腐蚀能力提高10～12倍。

Description

一种喷油泵柱塞的表面处理方法
技术领域
本发明涉及油嘴油泵的结构技术领域。
背景技术
柴油发动机的供油系统中需要柱塞偶件，以往的柱塞偶件采用GCr15材料，防腐蚀性一般，燃油经柱塞偶件、出油阀偶件、高压油管进入喷油器的喷油头腔，这种结构及工作原理供油路线长，结构松散，故障率偏高，检修复杂。
发明人发明了一种工作稳定性好、使用寿命长的喷油泵柱塞，由圆柱形柱塞和套筒组成，柱塞的中部设置径向凹颈，柱塞的前端为锥形，通过圆柱形柱塞和套筒之间的轴向往复相对滑动完成吸油和压缩过程。吸油时，燃油从进油孔进入，经柱塞中部的凹颈，到达回油孔；当圆柱形柱塞继续向套筒后端移动时，柱塞中部的凹颈不再与进油孔、回油孔连通，自进油孔进入套筒的出油通道，由柱塞前端的锥形外侧向喷油头腔泵入高压油，使油、气混合喷入燃烧室。本发明通过柱塞的上、下往复运动将高压燃油压入喷油头，柱塞往复运动一次，便完成一个循环的进油、计量、升压和喷射的全过程。本发明结构紧凑、可靠性高、检修简单。
但如果采用通用金属件，柱塞前端，即喷油头部不能长期经受高温，易受腐蚀，至使产品寿命缩短。
发明内容
本发明目的在于发明一种可加长使用寿命的一种喷油泵柱塞的表面处理方法。
本发明采用对喷油泵柱塞前部进行表面磷化处理。
通过磷化处理后，由于金属表面形成了一层不溶于水的磷酸盐保护膜，从而提高了金属工件的抗氧化性能和外观质量，并可大大延长偶件使用寿命。磷化后的金属防腐蚀能力比未磷化的防腐蚀能力提高10～12倍。
本发明在磷化前，先以表面调调整液对喷油泵柱塞表面进行喷淋。
另外，磷化液温度为30～50℃，磷化时间10～20min。
本发明每升磷化液中，磷酸二氢锌含量为40～50L，酸式磷酸锰含量为20～30L，复合促进剂含量为1.6～2.1g，络合剂含量为5g，表面活性剂含量为0.06～0.1g。
具体实施方式
一、制备磷化液：
1、将ZnO用水溶解调成糊状，将H3PO4缓慢倒入糊状ZnO中，搅拌反应完全。缓慢加入HNO3，反应完全后得含有Zn(H2PO3)2的水溶液。
2、用水溶解络合剂、酸式磷酸锰、表面活性剂和复合促进剂。
3、将上述两种溶液混合，加水至每升磷化液中磷酸二氢锌含量为40～50L、酸式磷酸锰含量为20～30L、复合促进剂含量为1.6～2.1g、络合剂含量为5g、表面活性剂含量为0.06～0.1g，得含有Zn(H2PO3)2、Zn(NO3)2和Mn(H2PO4)2的浓磷化液。
4、静置熟化24h以上，备用。
若配制工作液需将上述磷化液稀释两倍，加入适量促进剂，用Na2CO3调整酸度至工艺范围，搅拌均匀，备用。
二、加工工艺步骤：
1、除油：采用工业清洗剂去除表面油污。
2、水洗：采用清水将零件清洗干净。
3、除锈：采用稀盐酸溶液对柱塞前部去除锈斑。
4、水洗：采用清水将零件清洗干净。
5、表面调整：
用表面调调整液对工件进行喷淋，时间为15～30s。
6、磷化
将工件浸入温度为30～50℃的磷化工作液中，保持10～20min。
可见膜层随时间延长而增厚，颜色也逐步加深。通过控制温度和时间，可得到由灰至灰黑的颜色。
7、水洗：采用工业清洗剂、清水将零件清洗干净。
8、干燥：通风晾干。

Claims (4)

1.一种喷油泵柱塞的表面处理方法，其特征在于在洁净的表面进行磷化处理。
2.根据权利要求1所述喷油泵柱塞的表面处理方法，其特征在于磷化前先以表面调调整液对喷油泵柱塞表面进行喷淋。
3.根据权利要求1所述喷油泵柱塞的表面处理方法，其特征在于磷化液温度为30～50℃，磷化时间10～20min。
4.根据权利要求1所述喷油泵柱塞的表面处理方法，其特征在于每升磷化液中，磷酸二氢锌含量为40～50L，酸式磷酸锰含量为20～30L，复合促进剂含量为1.6～2.1g，络合剂含量为5g，表面活性剂含量为0.06～0.1g。
CNA2008101558908A 2008-10-17 2008-10-17 一种喷油泵柱塞的表面处理方法 Pending CN101372741A (zh)