CN101357838A - Artificial compound board prepared by granite stone powder waste material - Google Patents
Artificial compound board prepared by granite stone powder waste material Download PDFInfo
- Publication number
- CN101357838A CN101357838A CNA2007101428933A CN200710142893A CN101357838A CN 101357838 A CN101357838 A CN 101357838A CN A2007101428933 A CNA2007101428933 A CN A2007101428933A CN 200710142893 A CN200710142893 A CN 200710142893A CN 101357838 A CN101357838 A CN 101357838A
- Authority
- CN
- China
- Prior art keywords
- weight
- resin
- artificial composite
- composite plank
- promotor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a novel artificial composite board which is prepared by granite waste materials. The formula comprises a resin, a curing agent, a promoter, granite stone powder and broken stone particles, etc. The artificial composite board has more styles, and the length can be made to be large enough, thereby being applied on various possible occasions. At the same time, the technology utilizes the broken stone waste materials and stone powder as raw materials, thereby benefiting for the protection and the conservation of natural resources.
Description
[technical field]
The present invention relates to a kind of manufactured construction materials.More precisely, the present invention relates to the granite waste material and make artificial composite plank.
[background technology]
Along with prosperity of economy development, standard of living increase day by day, Architectural Equipment is more and more.Corresponding is that people are also increasing to the demand of material of construction, for example artificial composite plank or the like.At present, because the restriction of technology, the length of artificial composite plank for building, style are all very limited, have therefore limited the occasion of its application.In view of the above-mentioned defective of prior art, await developing a kind of novel artificial composite plank, can be applied to various possibilities place; Simultaneously can protect and save natural resource as much as possible again.
[summary of the invention]
The purpose of this invention is to provide a kind of novel artificial composite plank, make by the grouan waste material; Simultaneously, the present invention also provides a kind of method for preparing described artificial composite plank.
The present invention realizes above-mentioned purpose by following technical scheme.The prescription for preparing described artificial composite plank is as follows: resin 9～11% weight, solidifying agent 0.135～0.165% weight, promotor 0.09～0.11% weight, granite stone powder 18-20% weight, surplus gravel particle.
Wherein, described resin can be used 191#, 196# unsaturated polyester resin; Solidifying agent can be used methylethylketone; Promotor can be used cobalt iso-octoate; Gravel particle is grouan or marble, preferable particle size 5.0mm 25% weight, 2.0mm 25% weight, following 50% weight of 1.0mm.Granite stone powder can be with the stone flour mud waste material that is produced in the granite building material course of processing, drying, fragmentation, caking, granularity 80～150 orders.If necessary, can in advance granite stone powder be crushed to above-mentioned surmising.
The preparation method of the artificial composition board of the present invention is as follows: resin adds mill base, and (ratio of mill base is 0.35～0.5% of a weight resin, the versicolor look paste of general purchase), after stone flour adopts electric mixer to stir, pour gravel particle into, add promotor, solidifying agent again, be cast on the Cement Concrete body, vacuum vibration then, behind the cure and demold, table stone is handled through fixed thick, polishing.The artificial composition board of the present invention is that panel, Cement Concrete body are bottom plate combined forming by resin composite plates.
The artificial composition board pattern of the present invention is many, and length can accomplish enough big, thereby can be applied to various may places.This technology utilizes rubble waste material and stone flour to be raw material simultaneously, and protection and saving natural resource are benefited.
Below by specific embodiment the present invention is further detailed.These embodiment are just in order to illustrate in greater detail the present invention, and can not be interpreted as it is any limitation of the invention.
[embodiment]
Embodiment 1
The artificial compounded plate prescription is as follows:
Composition weight %
191# unsaturated polyester resin 10%
Curing agent ethyl methyl ketone 0.15%
Promotor cobalt iso-octoate 0.1%
Granite stone powder 20%
Mill base (is benchmark with the weight resin) 0.35～0.5%
The rubble surplus
Resin adds mill base, stone flour adopt electric mixer to stir after, pour gravel particle into, restir adds promotor, solidifying agent after evenly, the vacuum vibration adds one deck Cement Concrete body in the bottom surface behind the cure and demold.By resin composite plates is panel, and the Cement Concrete body is bottom plate combined forming.
Processing parameter: churning time: it is 1～3 hour etc. that temperature condition is looked in 20～30 minutes, vacuum time of vibration 3～5 minutes, set time.
Embodiment 2
The artificial compounded plate prescription is as follows:
Composition weight %
196# unsaturated polyester resin 11%
Curing agent ethyl methyl ketone 0.135%
Promotor cobalt iso-octoate 0.09%
Granite stone powder 18%
Mill base (is benchmark with the weight resin) 0.35～0.5%
The rubble surplus
Make artificial composite plank according to embodiment 1 method.
Embodiment 3
The artificial compounded plate prescription is as follows:
Composition weight %
191# unsaturated polyester resin 9%
Curing agent ethyl methyl ketone 0.165%
Promotor cobalt iso-octoate 0.11%
Granite stone powder 19%
Mill base (is benchmark with the weight resin) 0.35～0.5%
The rubble surplus
Make artificial composite plank according to embodiment 1 method.
It is as follows that the artificial composite plank of making detects data:
1. the Cement Concrete body thickness of ultra-thin composition board: 12-15mm;
2. the shrinkage strain rate of decorative sheet:＜2mm/m;
3. the bending strength of decorative sheet: it is indeformable that 75 kilograms of weights act on mid point.
Claims (9)
1. an artificial composite plank is made by following prescription: resin 9～11% weight, solidifying agent 0.135～0.165% weight, promotor 0.09～0.11% weight, granite stone powder 18-20% weight, surplus gravel particle.
2. artificial composite plank according to claim 1, resin wherein are meant 191# or 196# unsaturated polyester resin.
3. artificial composite plank according to claim 1, wherein solidifying agent is meant methylethylketone.
4. artificial composite plank according to claim 1, wherein promotor is meant cobalt iso-octoate.
5. artificial composite plank according to claim 1, wherein gravel particle is meant grouan or marble, particle diameter 5.0mm 25% weight, 2.0mm 25% weight, following 50% weight of 1.0mm.
6. artificial composite plank according to claim 1 also comprises mill base in the wherein said prescription, its ratio is 0.35～0.5% of a weight resin.
7. the preparation method of an artificial composite plank is made by following prescription: resin 9～11% weight, solidifying agent 0.135～0.165% weight, promotor 0.09～0.11% weight, granite stone powder 18-20% weight, surplus gravel particle; The preparation method comprises the steps: that resin adds mill base, pours gravel particle into after stirring stone flour, adds promotor, solidifying agent again, be cast on the Cement Concrete body, and vacuum vibration then, behind the cure and demold, table stone is handled and is got final product through fixed thick, polishing.
8. according to the preparation method of the described artificial composite plank of claim 7, wherein the ratio of mill base is 0.35～0.5% of a weight resin.
9. according to the preparation method of the described artificial composite plank of claim 7, wherein said resin is 191# or 196# unsaturated polyester resin; Solidifying agent is a methylethylketone; Promotor is cobalt iso-octoate; Gravel particle is grouan or marble, preferable particle size 5.0mm 25% weight, 2.0mm 25% weight, following 50% weight of 1.0mm.