CN101337163A - 海水淡化用滤膜的制备方法 - Google Patents

海水淡化用滤膜的制备方法 Download PDF

Info

Publication number
CN101337163A
CN101337163A CNA2007100579866A CN200710057986A CN101337163A CN 101337163 A CN101337163 A CN 101337163A CN A2007100579866 A CNA2007100579866 A CN A2007100579866A CN 200710057986 A CN200710057986 A CN 200710057986A CN 101337163 A CN101337163 A CN 101337163A
Authority
CN
China
Prior art keywords
solution
room temperature
membrane
sol
obtains
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CNA2007100579866A
Other languages
English (en)
Inventor
柴宝成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BAOCHENG MACHINERY GROUP Co Ltd TIANJIN
Original Assignee
BAOCHENG MACHINERY GROUP Co Ltd TIANJIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAOCHENG MACHINERY GROUP Co Ltd TIANJIN filed Critical BAOCHENG MACHINERY GROUP Co Ltd TIANJIN
Priority to CNA2007100579866A priority Critical patent/CN101337163A/zh
Publication of CN101337163A publication Critical patent/CN101337163A/zh
Withdrawn legal-status Critical Current

Abstract

一种海水淡化用滤膜的制备方法，1.将水和无水乙醇混合，加入盐酸，pH值为6，得到溶液1；2.将硅酸乙酯滴加到溶液1中搅拌，得到溶液2；3.加入DCCA；4.密封，剧烈搅拌，得到澄清溶液，保存在密封容器中，在室温下老化得到二氧化硅溶胶；5.将三氧化二铝多孔陶瓷圆片置于溶胶中浸涂，提起后再旋转得溶胶均匀铺开，形成溶胶膜；6.将溶胶膜在室温下自然干燥，得凝胶薄膜；7.将凝胶薄膜热处理保温，随炉冷却到室温，即制薄膜。本发明的有益效果：薄膜无开裂，孔径均匀。

Description

海水淡化用滤膜的制备方法
背景技术
反渗透海水淡化方法，能耗低，但膜的成本高，将低成本、多功能、性能稳定的陶瓷膜应用于海水淡化，克服有机膜的缺陷，降低成本和大规模工业应用是目前尚未解决的难题。
发明内容
本发明的目的在于克服上述的不足，提供一种海水淡化用滤膜的制备方法。
本发明的技术方案是：一种海水淡化用滤膜的制备方法，其特征在于：1、将水和无水乙醇混合，加入盐酸，PH值为6，得到溶液1；2、将硅酸乙酯滴加到溶液1中搅拌，得到溶液2；3、加入DCCA；4、密封，剧烈搅拌，得到澄清溶液，保存在密封容器中，在室温下老化得到二氧化硅溶胶；5、将三氧化二铝多孔陶瓷园片置于溶胶中浸涂，提起后再旋转得溶胶均匀铺开，形成溶胶膜；6、将溶胶膜在室温下自然干燥，得凝胶薄膜；7、将凝胶薄膜热处理保温，随炉冷却到室温，即制薄膜。
本发明的有益效果：薄膜无开裂，孔径均匀。
具体实施方式
实施例：一种海水淡化用滤膜的制备方法，1、将水和无水乙醇混合，加入盐酸，PH值为6，得到溶液1；2、将硅酸乙酯滴加到溶液1中搅拌，得到溶液2；3、加入DCCA；4、密封，剧烈搅拌，得到澄清溶液，保存在密封容器中，在室温下老化得到二氧化硅溶胶；5、将三氧化二铝多孔陶瓷园片置于溶胶中浸涂，提起后再旋转得溶胶均匀铺开，形成溶胶膜；6、将溶胶膜在室温下自然干燥，得凝胶薄膜；7、将凝胶薄膜热处理保温，随炉冷却到室温，即制薄膜。

Claims (1)

1、一种海水淡化用滤膜的制备方法，其特征在于：1、将水和无水乙醇混合，加入盐酸，PH值为6，得到溶液1；2、将硅酸乙酯滴加到溶液1中搅拌，得到溶液2；3、加入DCCA；4、密封，剧烈搅拌，得到澄清溶液，保存在密封容器中，在室温下老化得到二氧化硅溶胶；5、将三氧化二铝多孔陶瓷园片置于溶胶中浸涂，提起后再旋转得溶胶均匀铺开，形成溶胶膜；6、将溶胶膜在室温下自然干燥，得凝胶薄膜；7、将凝胶薄膜热处理保温，随炉冷却到室温，即制薄膜。
CNA2007100579866A 2007-07-03 2007-07-03 海水淡化用滤膜的制备方法 Withdrawn CN101337163A (zh)