CN101333430A - Anti-static coating composition and method for manufacturing antistatic coating using same - Google Patents
Anti-static coating composition and method for manufacturing antistatic coating using same Download PDFInfo
- Publication number
- CN101333430A CN101333430A CNA2008101249904A CN200810124990A CN101333430A CN 101333430 A CN101333430 A CN 101333430A CN A2008101249904 A CNA2008101249904 A CN A2008101249904A CN 200810124990 A CN200810124990 A CN 200810124990A CN 101333430 A CN101333430 A CN 101333430A
- Authority
- CN
- China
- Prior art keywords
- weight
- coating composition
- antistatic
- antistatic coating
- based compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an antistatic coating compound and a method for producing antistatic coating films by using the compound. The antistatic coating compound has the advantages of excellent scratching resistance and solvent resistance, inhibiting generation of static, good antistatic performance and incapability of changing enduring reliability. The invention is characterized in that the antistatic coating compound contains 1-30 wt% of conductive macromolecule dispersion liquid, 5-15 wt% of water-soluble acrylic binder resin represented by the chemical formula 1, 0.5-1.5 wt% of crosslink agent, 10-30 wt% of alcohol solvent, 5-30 wt% of organic solvent, water as the rest. In the chemical formula 1, by the mol ratio, x is 30-60%, y is 30-60%, z is 0.1-10%, R represents alkyl having 1-10 C, A represents independently H or substituted group.
Description
Technical field
The present invention relates to antistatic coating composition, particularly relate to following antistatic coating composition and the manufacture method of utilizing the antistatic films of said composition, described composition has excellent scuff resistance and solvent resistance, can fully suppress simultaneously electrostatic and produce, and have excellent antistatic property and durable reliability is changed.
Background technology
Among information-based industry, for most electronic units, static causes variety of issue.Static adsorbs the pollution substances such as dust of damage product properties when the manufacturing of electronic products.And modern electronics is also very high because of the tendency that static discharge is subjected to temporary transient or permanent damage.Particularly when making liquid crystal indicator, for polaroid attached to after peeling off special-shaped film with binder layer on the liquid crystal cell, produce static, the static of Chan Shenging exerts an influence to the liquid crystal aligning of liquid crystal indicator inside like this, thereby induced defect.
Surface protection film is attached on the surface of base material, protects the surface of base material thus.Representative example as the purposes of such film, dispatch from the factory at polaroid, preserve, when reprocessing, it on purpose is used for the quality inspection of polaroid, at this moment, static resistance when peeling off with light characteristic and film is a fundamental characteristics, requires it that external impact is had scuff resistance (scratch-resistant) and chemical resistant properties (solvent resistance) for the damage that prevents TAC (cellulosetri-acetate) film when the quality of polaroid is checked.
An example as the known technology that obtains antistatic effect, Mitsubishi chemistry polyester film (Polyester Film) society discloses a kind of antistatic polyester film in following patent documentation 1, this film uses diallyl dimethyl ammoniumchloride as static inhibitor, and in this film, use acrylic resin and polyvinyl alcohol as binding agent to improve the cohesive force of itself and base material, use melamine resin as solidifying agent in order to produce solvent resistance.But as the static inhibitor that uses in the above-mentioned patent, the polymer static inhibitor of cationic or anionic property demonstrates enough low resistance characteristic as protective membrane with static inhibitor, but still has problems.
On the other hand, as the static inhibitor that is used for antistatic layer, known have a multiple compound, wherein, discloses the electroconductive polymer body that makes thiophene (thiophene) derivative polymerization reaction take place and obtain in the following patent documentation 2 as static inhibitor.Disclosed electroconductive polymer has following feature: have high conductivity, have the transparency simultaneously, the adjusting of specific conductivity is easy, does not make the change in physical of base material, particularly it has following significant advantage: do not produce impurity, even also never kept through the several years specific conductivity with changing.But such electroconductive polymer has following shortcoming: compare with the low molecule-type or the polymer static inhibitor of general use, its price is higher, and it has the character of the light that absorbs the visible region and transmittance is reduced, and is disadvantageous to being used for blooming therefore.
And, a kind of protective membrane is disclosed in the following patent documentation 3, it is to use quaternary ammonium is that the polymer static inhibitor produces as the static inhibitor that constitutes antistatic layer.The polymer static inhibitor has following advantage: it uprises the weather resistance of antistatic layer, increase less because of static inhibitor moves the mist degree that causes to the top layer, and the less generation of adhesion (blocking), but general polymer static inhibitor has following shortcoming: the stretchiness deficiency, the coating coated film has fine cracking and does not have static resistance when using online coating (inline coating) manufacturing antistatic film.
Patent documentation 1: Republic of Korea's patent application 2002-54251 number
Patent documentation 2: a day disclosure is speciallyyed permit 2000-26817 number
Patent documentation 3: a day disclosure is speciallyyed permit 2000-168015 number
Summary of the invention
Have excellent static resistance and antistatic coating composition transparent and that base material is had sticking power in order to solve above-mentioned prior art problems, to the invention provides.
And, the object of the present invention is to provide the manufacture method of antistatic coating composition and antistatic films, by the acrylic adhesive resin that can improve coating characteristic among the use water system resin glue, thereby make this antistatic coating composition have excellent scuff resistance and solvent resistance.
In order to achieve the above object, the invention provides a kind of antistatic coating composition, it is characterized in that, described composition contains 1 weight %～30 weight % electroconductive polymer aqueous dispersions; The water-soluble acrylic resin glue that 5 weight %～15 weight % represent with following Chemical formula 1; 0.5 weight %～1.5 weight % linking agents; 10 weight %～30 weight % alcoholic solvents; 5 weight %～30 weight % organic solvents; Water with surplus.
[Chemical formula 1]
In above-mentioned Chemical formula 1, be benchmark with mol ratio content, x is 30%～60%, and y is 30%～60%, and z is 0.1%～10%, and R is that carbonatoms is 1～10 alkyl, A is hydrogen or substituting group independently of one another.
And, the invention provides the manufacture method of antistatic films, it comprises: coating contains the step of the coating fluid of above-mentioned antistatic coating composition on base material; With the coating fluid exsiccant step that makes after the described coating.
Antistatic coating composition of the present invention and utilized filming of described coating composition not only to have excellent static resistance and the transparency and to the sticking power of base material, but also owing to use the acrylic adhesive resin that can make the coating strength excellence to have the scuff resistance and the solvent resistance of excellence.And antistatic coating composition of the present invention is a liquid type coating composition, thereby has shortened activity time, and the productivity of operation is improved, and moreover, also forms environmentally friendly because of it for water-soluble solvent.
Embodiment
Below, describe the present invention in detail.
Antistatic coating composition of the present invention is characterised in that, contains 1 weight %～30 weight % electroconductive polymer aqueous dispersions; The water-soluble acrylic resin glue that 5 weight %～15 weight % represent with above-mentioned Chemical formula 1; 0.5 weight %～1.5 weight % linking agents; 10 weight %～30 weight % alcoholic solvents; 5 weight %～30 weight % organic solvents; Water with surplus.
As the employed electroconductive polymer of antistatic coating composition of the present invention, can use the electroconductive polymer aqueous dispersions of selling on the market, perhaps also the electroconductive polymer compound can be dispersed in the water and use.As described electroconductive polymer compound, can use Polythiophene system, polypyrrole system, polyphenylamine series macromolecular compound or their mixture, preferred Polythiophene based compound, more preferably polyethylene dioxythiophene (polyethylene dioxythiophene; PEDOT).Preferably the content of electroconductive polymer is 0.01 weight %～20 weight % in the described electroconductive polymer aqueous dispersions that uses.
As a specific examples, in above-mentioned polyethylene dioxythiophene,, can use Baytron-P, the Baytron-PH (trade(brand)name) etc. of German H.C.Starck society as the goods of commercial distribution.Baytron-P will be for being dispersed in the goods that form in the water with the polyethylene dioxythiophene that doping agent (dopant) processing polystyrolsulfon acid (polystyrene sulfonate) obtains, and the content of polyethylene dioxythiophene is about 1.4 weight %.Described PEDOT can further bigger with water, alcohol or specific inductivity functional solvent thorough mixing, therefore dilutes with such solvent and can easily be coated with.
Preferably the electroconductive polymer aqueous dispersions is 1 weight %～30 weight % in antistatic coating composition of the present invention.If the consumption of described electroconductive polymer is less than 1 weight %, the surface resistivity of then filming increases, thereby has the problem that antistatic property reduces, if described consumption is greater than 30 weight %, then exist antistatic property to improve especially, and the problem that the coating performance of base material is reduced.
Resin glue used in the present invention has been given play to following effect: improved electroconductive polymer dispersiveness, improved the homogeneity of filming, tack and the film toughness (comprising scuff resistance and solvent resistance) that form.The compound of water-soluble binder resin used in the present invention for representing with following Chemical formula 1.
[Chemical formula 1]
In above-mentioned Chemical formula 1, be benchmark with mol ratio content, x is 30%～60%, and y is 30%～60%, and z is 0.10%～10%, and R is that carbonatoms is 1～10 alkyl, A is hydrogen or substituting group independently of one another.Preferably this substituting group is hydrogen, halogens, CH when A is substituting group
3, CH
2CH
3, more preferably described R is that ethyl and A are hydrogen.
The resin glue of representing with above-mentioned Chemical formula 1 can have hydroxyl by making, the monomer copolymerization of amide group, carboxyl is made.Preferred described resin is made as described monomer with hydroxyl, amide group, carboxyl by the following monomer of polymerization: 2-hydroxyethyl methacrylate, Hydroxyethyl acrylate, Propylene glycol monoacrylate, vinylformic acid hydroxy butyl ester etc. contain the monomer of hydroxyl; Acrylamide, N hydroxymethyl acrylamide etc. contain the monomer of amide group; Or vinylformic acid, methacrylic acid, methylene-succinic acid, maleic anhydride etc. contain the monomer of carboxyl.
In addition, can also further add methyl acrylate, ethyl propenoate, n-butyl acrylate, ethyl acrylate, methyl methacrylate, Jia Jibingxisuanyizhi, Propenoic acid, 2-methyl, isobutyl ester, methacrylic acid-hydrophobic monomers such as 2-ethylhexyl and make resin glue.
In antistatic composition of the present invention, the content of preferred above-mentioned water-soluble binder resin is 5 weight %～15 weight %.If the content of described water-soluble binder resin is less than 5 weight %, the problem that then has homogeneity, cohesive force and film toughness (comprising scuff resistance and the solvent resistance) reduction of filming, if the problem that described content greater than 15 weight %, then exists the dispersiveness of electroconductive polymer to reduce.
Antistatic coating composition of the present invention contains linking agent.Described linking agent has mutual solubility to the water-soluble binder resin, antistatic coating composition is improved to the coating strength (hardness/solvent resistance) and the adhesion property of base material, and can use trimeric cyanamide system, urea system, epoxy system, isocyanate-based, carbodiimide, oxazoline system or silane coupling agent based compound as linking agent, preferred trimeric cyanamide based compound.
Preferably the content at linking agent described in the antistatic coating composition of the present invention is 0.5 weight %～1.5 weight %.If described consumption is less than 0.5 weight %, the intensity (hardness) and the adhesion property characteristic of filming are fully improved, if described consumption is greater than 1.5 weight %, then exist the surface resistivity of filming to increase and problem that the frequency that takes place to stain during coating increases, thereby not preferred.
And, in the present invention, owing to making curing speed, improves the curing characteristics of described linking agent, in order to reduce solidification value, can also contain the independent a kind of compound in phosphate ester based compound, tosic acid based compound, Witco 1298 Soft Acid based compound or the trifluoromethanesulfonic acid based compound etc. or the mixture of two or more compounds.Special preferably phosphate ester based compound.100 weight part solids components with linking agent are benchmark, and described catalyzer is preferably 0.5 weight part～3 weight parts, and are if described consumption greater than 3 weight parts, then causes the dispersion stabilization of coating composition to reduce sometimes, therefore not preferred.
Antistatic coating composition of the present invention contains the alcoholic solvent of 10 weight %～30 weight %.The effect that described alcoholic solvent performance improves the coatings such as drying property of coating composition as described alcoholic solvent, can be used the normally used alkylol cpd of antistatic coating composition, a wider range of employed alkylol cpd.Preferred to select to use carbonatoms be 1～5 alcohol, further preferred the use 5 weight parts～20 parts by weight of ethanol and alcohol solvent mixture that 1 weight part～20 weight part Virahols mix etc.
In antistatic coating composition, if the content of described alcoholic solvent less than 10 weight %, then drying property and dispersiveness might reduce, if described content greater than 30 weight %, the favorable dispersity of electroconductive polymer then, but the problem that exists surface resistivity to rise.
When antistatic coating composition of the present invention contains above-mentioned alcoholic solvent, also contain the functional organic solvent of such coating such as the solvability that improves coating composition, dispersiveness, drying property, film uniformity.As described functional organic solvent, can use methyl-sulphoxide (dimethylsulfoxide=DMSO), propylene glycol monomethyl ether (propylene glycol methyl ether=PGME), N-Methyl pyrrolidone (N-methylpyrrolidone=NMP), 3-ethoxyl ethyl propionate (ethyl-3-ethoxy propionate=EEP), propylene glycol methyl ether acetate (propylene glycolmonomethyl ether acetate=PGMEA), diethylene glycol monobutyl ether (butyl carbitol=BC), normal-butyl Trivalin SF acetic ester (n-butyl carbitol acetate=BCA) or their mixture etc., preferred especially methyl-sulphoxide (DMSO).
In whole coating composition, the content of above-mentioned functions organic solvent is 5 weight %～30 weight %, is preferably 10 weight %～30 weight %.If the content of described organic solvent is less than 5 weight %, then exist the dispersiveness and the coating of coating composition to reduce, form the problem of nonuniform film, the problem that drying property reduces if described content greater than 30 weight %, then exists coating performance not improved especially.
The remaining component of electroconductibility coating composition of the present invention is a water (deionized water; D.I.W), in whole coating composition, the consumption of described water is preferably 10 weight %～50 weight %.Described consumption can further make coating improve in above-mentioned scope the time.
And, the invention provides the manufacture method of antistatic films, it is characterized in that coating contains the coating fluid of above-mentioned antistatic coating composition on base material, and makes its drying.As described base material, film that is formed by organic polymers such as polyester, polyimide, polymeric amide, polycarbonate, polyacrylic ester, polyethylene, polypropylene etc. is arranged, utilize rod to be coated with methods such as method, gravure coating method, method of spin coating and on described base material, be coated with.
In the manufacture method of antistatic films of the present invention, can use the coating fluid that forms with water (D.I.W) and the above-mentioned antistatic coating composition of the further dilution of alcoholic acid mixing solutions to be coated with.Can use with water and alcoholic acid blending ratio is that (water: the diluting soln that the dilution of ethanol) part by weight forms, the diluting soln of Zhi Zaoing can be with antistatic coating composition like this: diluting soln was that 1: 1～1: 5 part by weight dilutes antistatic coating composition and uses in 1: 1～1: 10.
As the drying conditions of filming, select to be fit to the condition of each coating method, normally used condition is to implement 5 seconds～120 seconds 60 ℃～120 ℃ temperature, is preferably 80 ℃～120 ℃ temperature to implement 10 seconds～100 seconds further preferred coating back under 80 ℃ temperature condition dry 1 minute.
Below, by embodiment and comparative example, be described more specifically the present invention, but the present invention is not limited by following embodiment.In following embodiment and comparative example, as long as not statement in addition, percentage and ratio of mixture all are benchmark with weight.
Embodiment 1
In mixing vessel, add 19 weight parts waters, 24.985 weight part methyl-sulphoxides, 10 parts by weight of ethanol, 15 weight part Virahols, stirred 1 hour.To wherein adding 10 weight parts water soluble acrylic resinoids (in above-mentioned Chemical formula 1, with mol ratio content is benchmark, x is 45%, y is 45%, and z is 10%, and R is an ethyl, A is a hydrogen) (huge society, F/K#147-1) and 1 weight part trimeric cyanamide be resin (SciTech society, CYMEL385) after, restir 1 hour.Thereafter, add 20 weight account polyethylene dioxy thiophene (PEDOT) aqueous dispersions (1.4 weight % solids components, H.C.Starck society, Baytron-P) after, restir 1 hour produces coating composition.With pure water (D.I.W) and ethanol mixed solvent (water: alcoholic acid weight ratio=1: 3) further dilute the coating composition of so making, produce final antistatic coating composition (antistatic coating composition: the weight ratio of diluting solvent=1: 3).
Utilize rod to be coated with machine (bar coater) coating composition of above-mentioned manufacturing is applied on the PET film, after on 80 ℃ the hot-plate dry 1 minute, filmed.
Embodiment 2
Appending and using 0.015 weight part phosphate ester is that (SciTech society CYCAT296-9), in addition, utilizes the method identical with the foregoing description 1 to carry out, thereby filmed acid catalyst.
Embodiment 3
Use in 16 weight part the foregoing descriptions 1 the water-soluble acrylic resin that uses in the aqueous dispersions that uses, 14 weight part the foregoing descriptions 1, in addition, utilize the method identical to carry out, thereby filmed with the foregoing description 2.
Comparative example 1
(in above-mentioned Chemical formula 1, be benchmark with mol ratio content, x is 50%, and y is 50% to use 10 weight parts water soluble acrylic resinoids, z is 0, and R is an ethyl, and A is a hydrogen) (huge society, F/K#147-2), in addition, utilize the method identical to carry out, thereby filmed with the foregoing description 2.
Comparative example 2
Use 16 weight account polyethylene dioxy thiophene (PEDOT) aqueous dispersions (H.C.Starck societies, Baytron-P), (huge society of the water-soluble acrylic resin in the above-mentioned comparative example 1 of 14 weight parts, F/K#147-2), in addition, utilize the method identical to carry out, thereby filmed with the foregoing description 2.
Comparative example 3
Use 10 weight part water soluble polyurethane resins (Noveon society, Sancure-777) and 1 weight part trimeric cyanamide be that (BASF society Luwipal073), in addition, utilizes the method identical with the foregoing description 1 to carry out, thereby filmed resin.
Comparative example 4
Use 16 weight account polyethylene dioxy thiophene (PEDOT) aqueous dispersions (H.C.Starck societies, Baytron-P), 14 weight part water soluble polyurethane resin (Noveon societies, Sancure-777) and 1 weight part trimeric cyanamide be resin (BASF society, Luwipal073), in addition, utilize the method identical to carry out, thereby filmed with the foregoing description 1.
According to following benchmark, the antistatic films of making in the foregoing description 1～3 and the comparative example 1～4 is carried out evaluating characteristics.
(1) surface resistivity (Ω/sq)
Use the surface resistivity tester ST-3 of SIMCO society, sample is arranged under the environment of 23 ℃ of temperature, relative humidity 50%RH, measure its surface resistivity.
(2) scuff resistance
When the angle of cotton rod is maintained 45 degree, make its with the speed of 5cm/sec at the 25cm that handles through above-mentioned coating
2Face (5cm * 5cm) goes up back and forth each 10 times, and each length is 5cm.State according to following benchmark evaluation coated face.
Zero: static resistance does not almost change and does not have the situation of cut
△: static resistance slightly reduces and has the situation of some cuts
*: the situation that situation that static resistance disappears or coated face are peeled off
(3) solvent resistance
After cotton rod is gone up adhesional wetting ethanol, when the angle of cotton rod is maintained 45 degree, make its with the speed of 5cm/sec at the 25cm that handles through above-mentioned coating
2Face (5cm * 5cm) goes up back and forth each 10 times, and each length is 5cm.State according to following benchmark evaluation coated face.
Zero: static resistance does not almost change and does not have the situation of cut
△: static resistance slightly reduces and has the situation of some cuts
*: the situation that situation that static resistance disappears or coated face are peeled off
(4) transmittance
Use MCPD-3000 (spectrum analyser of Otsuka society), get the polyester film of 10cm * 10cm size, with this polyester film is reference (reference), with filming of making in the foregoing description and the comparative example is test piece, making wavelength is the light transmission of 400nm～700nm, measures the value of shown transmittance.
(5) cohesive force
Measure cohesive force according to ASTMD 3359 methods.
Evaluation result to each assessment item of the antistatic films of manufacturing in the foregoing description 1～3 and comparative example 1～4 is listed in the table below 1.
Table 1
By above-mentioned table 1 as can be known, compare with filming of comparative example 1～4, the static resistance of filming, transparency, solvent resistance and the adhesion property of embodiments of the invention 1～embodiment 3 are excellence simultaneously, particularly can confirm, the transmittance of filming, scuff resistance and the solvent resistance of embodiments of the invention 1～embodiment 3 is significantly excellent.
Claims (9)
1. an antistatic coating composition is characterized in that, described composition contains 1 weight %～30 weight % electroconductive polymer aqueous dispersions; The water-soluble acrylic resin glue that 5 weight %～15 weight % represent with following Chemical formula 1; 0.5 weight %～1.5 weight % linking agents; 10 weight %～30 weight % alcoholic solvents; 5 weight %～30 weight % organic solvents; With the water of surplus,
[Chemical formula 1]
In above-mentioned Chemical formula 1, be benchmark with mol ratio content, x is 30%～60%, and y is 30%～60%, and z is 0.1%～10%, and R is that carbonatoms is 1～10 alkyl, A is hydrogen or substituting group independently of one another.
2. antistatic coating composition as claimed in claim 1, it is characterized in that described electroconductive polymer aqueous dispersions is that to be selected from by Polythiophene be that macromolecular compound, polypyrrole are the aqueous dispersions of the material in the group formed of macromolecular compound, polyphenylamine series macromolecular compound and their mixture.
3. antistatic coating composition as claimed in claim 1, it is characterized in that described linking agent is more than one the compound that is selected from the group of being made up of trimeric cyanamide based compound, urea based compound, epoxy based compound, isocyanic ester based compound, carbodiimide compound, oxazoline based compound, silane coupling agent based compound.
4. antistatic coating composition as claimed in claim 1, it is characterized in that, with respect to the described linking agent of 100 weight parts, described composition also contains the following compound of 0.5 weight part～3 weight parts: phosphate ester based compound, tosic acid based compound, Witco 1298 Soft Acid based compound or trifluoromethanesulfonic acid based compound.
5. antistatic coating composition as claimed in claim 1 is characterized in that, described alcoholic solvent is the mixture of ethanol and Virahol.
6. antistatic coating composition as claimed in claim 1, it is characterized in that described organic solvent is more than one the solvent that is selected from the group of being made up of methyl-sulphoxide, propylene glycol monomethyl ether, N-Methyl pyrrolidone, 3-ethoxyl ethyl propionate, propylene glycol methyl ether acetate, diethylene glycol monobutyl ether and normal-butyl Trivalin SF acetic ester.
7. the manufacture method of an antistatic films, it comprises: coating contains the step of the coating fluid of the described antistatic coating composition of claim 1 on base material; With the coating fluid exsiccant step that makes after the described coating.
8. the manufacture method of antistatic films as claimed in claim 7, it is characterized in that, described coating fluid is with described antistatic coating composition: diluting soln was that 1: 1～1: 5 part by weight utilizes diluting soln to dilute described antistatic coating composition to obtain, and described diluting soln mixes water and ethanol and obtains with 1: 1～1: 10 part by weight.
9. the manufacture method of antistatic films as claimed in claim 7 is characterized in that, described drying was implemented 5 seconds～120 seconds 60 ℃～120 ℃ temperature.