CN101329235A - 网箱用菱形网目聚酰胺经编网片强力测试方法 - Google Patents
网箱用菱形网目聚酰胺经编网片强力测试方法 Download PDFInfo
- Publication number
- CN101329235A CN101329235A CNA200710042141XA CN200710042141A CN101329235A CN 101329235 A CN101329235 A CN 101329235A CN A200710042141X A CNA200710042141X A CN A200710042141XA CN 200710042141 A CN200710042141 A CN 200710042141A CN 101329235 A CN101329235 A CN 101329235A
- Authority
- CN
- China
- Prior art keywords
- sample
- strength
- mesh
- testing
- net sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
网箱用菱形网目聚酰胺经编网片强力测试方法,涉及网片强力检测,需提供强力测试方法。本发明包括网片试样和试验方式,其特征是试样在距离网片边缘10目以上部位取得;试样的工作有效尺寸对应用于网目强力测试或网片断裂强力及断裂伸长率测试;试样裁剪边目脚末端熔融处理;干态试样调湿12h、湿态试样浸泡12h;网目强力测定的夹具装不锈钢钩子或线环,试样施预加张力,强力指标从试验机记录装置中记录并计算;网片断裂强力及断裂伸长率测定试验机上装宽度10cm以上平口夹具,试样加预加张力后夹入夹具,试样断裂强力与断裂伸长率指标从试验机记录装置中记录并计算;试验有效测定次数不少于20次。本发明用于经编网片强力性能的检测。
Description
技术领域:
本发明涉及网箱用菱形网目聚酰胺经编网片强力检测方法。
背景技术
网片是渔业生产中的主要材料,它在捕捞和养殖工程中得到广泛使用。网片按织网用纤维材料的种类可分为聚酰胺网片、聚乙烯网片、聚丙烯网片和聚酯网片;按网结的有无,网片可分无结网片和有结网片两大类;无结网片又分为经编网片、插捻网片、平织网片、绞捻网片;有结网片又分为活结网片、死结网片、双死结网片。菱形网目聚酰胺经编网片是一种无结网片,它以良好的抗冲击、抗疲劳以及抗海水腐蚀性能,成为深水抗风浪网箱、港湾养殖网箱和围网网衣中应用较普遍的网衣材料。有结网片由于结节的存在,网具重量偏重、使用不方便、突出的结节易擦伤养殖鱼体并造成鱼体表面感染引起鱼病害。研究成果显示,菱形网目聚酰胺经编网片比较适合制作深水网箱箱体网衣、港湾养殖网箱箱体网衣和远洋围网网衣,菱形网目聚酰胺经编网片日益引起我国捕捞和养殖业的重视。近年来,由于海洋自然渔业资源尤其是近海渔业资源的衰退,调整海洋渔业生产结构,发展离岸深水网箱养殖业,已成为我国海水网箱养殖业健康发展的重要途径和海洋渔业的政策取向;为此,国内已有多家渔网厂在经销聚酰胺经编网片。随着菱形网目聚酰胺经编网片应用领域的不断扩大,人们迫切需要研究其强力指标。对用聚酰胺经编网片制作的网箱而言,网片强力是影响网箱强度、使用期限并导致它们变形的原因之一。为了反应网箱用菱形网目聚酰胺经编网片的强力性能、更好地评价聚酰胺经编网片质量及使用安全性、为网箱设计人员在选配渔用材料时提供依据,需要进行网箱用菱形网目聚酰胺经编网片强力试验,但目前我国网箱用菱形网目聚酰胺经编网片强力性能的指标及试验方法还没有国家或行业标准。这给养殖户的选用网箱网衣材料带来了困难,也曾发生过生产厂与用户因质量指标不一致而产生纠纷。因为一个网箱网衣材料的价值仅几万元,但一网箱鱼的价值在几十万元以上,一旦发生破网,养殖户损失惨重。这既给渔业生产带来了隐患,又制约了捕捞和渔业工程的可持续健康发展。迫切需要一种可供网箱用菱形网目聚酰胺经编网片强力测试的方法。
发明内容
本发明需要解决的技术问题是提供一种网箱用菱形网目聚酰胺经编网片强力测试方法。
本发明的技术方案包括网片试样的取样及试样裁剪边末端的处理、试样调湿平衡和强力试验方式,其特征是试样在距离网片边缘10目以上的部位取得,同时裁取干态和湿态试样时,在试样被拉伸的方向每次连续裁取二个试样;试样的工作有效尺寸对应用于网目强力测试或网片纵(横)向断裂强力及断裂伸长率测试,分别为3目×3目及30cm长、4.5目宽;试样裁剪边断裂目脚的末端用融化法熔融处理;干态试样在温度17℃~23℃、湿度62%~68%的大气条件下至少调湿平衡12h、湿态试样在水温17℃~23℃的容器内至少浸泡12h;网目强力测定前在强力试验机的平口夹具中安装不锈钢钩子,在强力试验机上进行试样操作时,应将3目×3目网片试样中心处的单个网目钩挂在不锈钢钩子上,施加合适的预加张力,网目强力测试时干态试样的预加张力值等于相同粗度聚酰胺网线500m长度的自重,湿态试样的预加张力等于相同粗度250m聚酰胺网线长度的自重,以保证满足规定的平均断裂时间17s~23s,然后对试样进行拉伸直至网目目脚断裂,试样的网目强力指标从试验机的记录装置中记录并计算;在网片断裂强力及断裂伸长率测定前在强力试验机上安装宽度为10cm以上平口夹具,将矩形试样宽度方向的一端全部平整地夹入上夹具,并使目脚互相靠紧,在矩形试样宽度方向的另一端按干态试样或湿态试样分别加以特定预加张力后夹入下平口夹具,网片断裂强力测定时干态试样的预加张力值等于相同粗度聚酰胺网线2250m长度的自重,湿态试样的预加张力等于相同粗度1125m聚酰胺网线长度的自重,在规定的平均断裂时间17s~23s下对试样进行拉伸直至断裂,试样的断裂强力与断裂伸长率指标从试验机的记录装置中记录并计算;试验有效测定次数均不少于20次。
本发明为解决网箱用菱形网目聚酰胺经编网片的网片强力的检测和质量评价提供了一种简明有效的方法,为工程技术人员在养殖网箱设计及渔用材料选用上提供了可靠依据。本方法也适用于围网用菱形网目聚酰胺经编网片、民用菱形网目聚酯经编网片等菱形网目经编网片强力性能的检测和质量评价。
附图说明
图1是工作有效尺寸为3目×3目的网目强力测试用试样示意图。
图2是工作有效尺寸为30cm长、4.5目宽的网片纵(横)向断裂强力及断裂伸长率测试用矩形试样示意图。
图3表示使用不锈钢钩子测定网目强力示意图。
图4表示使用线环测定网目强力示意图。
图5表示网片纵(横)向断裂强力及断裂伸长率测试示意图。
具体实施方式
以下按影响网箱用菱形网目聚酰胺经编网片强力测试结果的大气条件、取样和试样处理、测试条件、测试方式、数据处理和结果表示,详述实施本发明的最好方式:
网箱用菱形网目聚酰胺经编网片的网片强力试验过程中实验室的大气条件控制在温度(20±3)℃,湿度(65±3)%。
试样在距离网片边缘10目以上的各个部位取得,在进行同一项目试验时不允许在试样被拉伸的方向连续取样,但同时裁取干态和湿态试样时,须在试样被拉伸的方向每次连续裁取二个试样,这样使得每一对拉伸断裂强力试验是在含有同样纱线的试样上进行的,在试样上可以标注字母D、W来区别干态试样和湿态试样,在试样上标注字母M、N、T来区别网目强力测试用试样、网片纵向断裂强力及断裂伸长率测试用矩形试样和横向断裂强力及断裂伸长率测试用矩形试样;试样在裁剪时应远离聚酰胺经编网片的网目连接点,并用融化法熔融处理试样裁剪边断裂目脚的末端(图1、图2、图5中的7),以防试样裁剪边断裂目脚的末端松散影响测试效果;网目强力测试用试样的工作有效尺寸为3目×3目(图1),网片纵向断裂强力及断裂伸长率测试用试样的工作有效尺寸为30cm长、4.5目宽(图2);试样必须达到干态和湿态的要求,试样在实验室内的大气条件[温度(20±3)℃;相对湿度(65±3)%]平衡12h以上,为试样的干态;将试样在水温(17~23)℃的容器内至少浸泡12h,使其在继续浸泡更长时间后网片拉伸断裂强力和断裂伸长率无显著差异,为使试样完全浸润,也可以在水中加入不超过0.05%的非离子中性润湿剂,试样取出后在试验室内悬挂试样至不滴水为止,即为试样的湿态。
机械式强力试验机应在公称量程的(25~75)%的范围内使用,而电子式强力试验机可在允许量程范围内使用;网片强力测试根据网箱用菱形网目聚酰胺经编网片的规格选择适当量程的传感器,在强力试验机上安装测试用平口夹具(图3、图4、图5中的1、6),平口夹具的宽度为10cm以上。
网箱用菱形网目聚酰胺经编网片试样的平均断裂时间为(20±3)s,即对一组试样的平均断裂时间,应在规定的限度以内。
网目强力测定前在强力试验机的平口夹具(图3中的1、6)中安装不锈钢钩子(图3中的2),如果网目很小,不能使用不锈钢钩子时,作为一个代替的办法,可以使用比网目目脚(图3、图4、图5中的4)粗的网线穿入网目作线环(图4中的2′),在强力试验机上进行样品操作时,应将3目×3目网片试样中心处的单个网目(图3、图4、图5中的5)小心地钩挂在不锈钢钩子(图3中的2)上或穿进线环(图4中的2′)中,以确保网目连接点(图3、图4、图5中的3)不接触不锈钢钩子或线环;干态试样施加的预加张力值等于相同粗度聚酰胺网线500m长度的自重,湿态试样施加的预加张力等于相同粗度250m聚酰胺网线长度的自重,以保证满足规定的平均断裂时间(17s~23s),然后对试样进行拉伸直至网目目脚断裂,试样的网目强力指标从试验机的记录装置中记录并计算。有效测定不低于20次。
在网片断裂强力及断裂伸长率测定前在强力试验机上安装宽度为10cm以上平口夹具(图5中的1、6),上下夹具间的距离(图5中的L)调整为30cm,将矩形试样宽度方向的一端全部平整地夹入上夹具(图5中的1),并使目脚(图5中的4)互相靠紧,在矩形试样宽度方向的另一端加以特定预加张力后夹入下平口夹具(图5中的6),干态试样的预加张力值等于相同粗度聚酰胺网线2250m长度的自重,湿态试样的预加张力等于相同粗度1125m聚酰胺网线长度的自重,在规定的平均断裂时间达17s~23s对试样进行拉伸直至断裂,试样的断裂强力与断裂伸长率指标从试验机的记录装置中记录并计算;去除夹具处打滑的样品数据,另取试样进行试验,有效测定不低于20次。
计算网目强力、网片纵向干态断裂强力与断裂伸长率、网片纵向湿态断裂强力与断裂伸长率、网片横向干态断裂强力与断裂伸长率和网片横向湿态断裂强力与断裂伸长率对应的算术平均值。
标准偏差按以下公式计算:
式中:S-标准偏差(取三位小数);xi-第i个试样的测试值;
x-被测值的平均值(取三位小数);n-试样数。
变异系数按以下公式计算:
式中:CV-异系数;S-标准偏差(取三位小数);
x-被测值的平均值(取三位小数)。
本发明利用INSTRON 4466型电子式强力试验机进行了网箱用菱形网目聚酰胺经编网片干态试样、湿态试样网片强力的测定,结果表明:网箱用菱形网目聚酰胺经编网片的干态纵向断裂强力大于干态横向断裂强力、干态纵向断裂强力大于湿态纵向断裂强力,符合相关文献理论。测试方法简明有效,测试技术指标是切实可行,合理可靠。实测结果见表1、表2。
表1干态试样纵横向拉伸力学性能测试结果
网片规格 | 网目强力/N | 干态纵向断裂强力/N | 干态纵向断裂伸长率/% | 干态横向断裂强力/N | 干态横向断裂伸长率/% |
PA-23tex×42-30(原色) | 426 | 1690 | 75.0 | 1680 | 74.9 |
PA-23tex×48-35(染色上树脂) | 559 | 1990 | 97.8 | 1800 | 99.0 |
表2干湿态试样纵向拉伸力学性能测试结果
规格 | 网目强力/N | 干态纵向断裂强力/N | 干态纵向断裂伸长率/% | 湿态纵向断裂强力/N | 湿态纵向断裂伸长率/% |
PA-23tex×30-30(染色上树脂) | 418 | 2210 | 77.7 | 1960 | 77.3 |
PA-23tex×60-50(染色上树脂) | 714 | 2820 | 78.6 | 2760 | 78.8 |
Claims (3)
1.网箱用菱形网目聚酰胺经编网片强力测试方法,包括网片试样的取样及试样裁剪边末端的处理、试样调湿平衡和强力试验方式,其特征是试样在距离网片边缘10目以上的部位取得,同时裁取干态和湿态试样时,在试样被拉伸的方向每次连续裁取二个试样;试样的工作有效尺寸用于网目强力测试为3目×3目或用于网片纵(横)向断裂强力及断裂伸长率测试为30cm长、4.5目宽;试样裁剪边断裂目脚的末端用融化法熔融处理;干态试样在温度17℃~23℃、湿度62%~68%的大气条件下至少调湿平衡12h、湿态试样在水温17℃~23℃的容器内至少浸泡12h;网目强力测定前在强力试验机的平口夹具中安装不锈钢钩子,在强力试验机上进行样品操作时,应将3目×3目网片试样中心处的单个网目钩挂在不锈钢钩子上或穿进线环中,网目强力测试时干态试样施加的预加张力值等于相同粗度聚酰胺网线500m长度的自重,湿态试样施加的预加张力等于相同粗度250m聚酰胺网线长度的自重,以保证满足规定的平均断裂时间17s~23s后对试样进行拉伸直至网目目脚断裂,试样的网目强力指标从试验机的记录装置中记录并计算;在网片断裂强力及断裂伸长率测定前在强力试验机上安装宽度为10cm以上平口夹具,将矩形试样宽度方向的一端全部平整地夹入上夹具,并使目脚互相靠紧,在矩形试样宽度方向的另一端按干态试样或湿态试样分别加以特定预加张力后夹入下平口夹具,网片断裂强力测定时干态试样的预加张力值等于相同粗度聚酰胺网线2250m长度的自重,湿态试样的预加张力等于相同粗度1125m聚酰胺网线长度的自重,在规定的平均断裂时间17s~23s下对试样进行拉伸直至断裂,试样的断裂强力与断裂伸长率指标从试验机的记录装置中记录并计算;试验有效测定次数不少于20次。
2.根据权利要求1所述的网箱用菱形网目聚酰胺经编网片强力测试方法,其特征是在浸泡湿态试样的水中加入不超过0.05%的非离子中性润湿剂。
3.根据权利要求1或2所述的网箱用菱形网目聚酰胺经编网片强力测试方法,其特征是采用网线穿入网目作线环代替平口夹具中安装的不锈钢钩子。