CN101323501A - 用于石英玻璃沉积管的连续焙烧方法 - Google Patents
用于石英玻璃沉积管的连续焙烧方法 Download PDFInfo
- Publication number
- CN101323501A CN101323501A CNA2008100095218A CN200810009521A CN101323501A CN 101323501 A CN101323501 A CN 101323501A CN A2008100095218 A CNA2008100095218 A CN A2008100095218A CN 200810009521 A CN200810009521 A CN 200810009521A CN 101323501 A CN101323501 A CN 101323501A
- Authority
- CN
- China
- Prior art keywords
- optical fiber
- quartzy
- deposited tube
- less
- optical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (23)