CN101318787A - 一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法 - Google Patents

一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法 Download PDF

Info

Publication number
CN101318787A
CN101318787A CNA2007101059712A CN200710105971A CN101318787A CN 101318787 A CN101318787 A CN 101318787A CN A2007101059712 A CNA2007101059712 A CN A2007101059712A CN 200710105971 A CN200710105971 A CN 200710105971A CN 101318787 A CN101318787 A CN 101318787A
Authority
CN
China
Prior art keywords
slag
technology
described technology
red mud
gas generator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007101059712A
Other languages
English (en)
Other versions
CN101318787B (zh
Inventor
王文举
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2007101059712A priority Critical patent/CN101318787B/zh
Publication of CN101318787A publication Critical patent/CN101318787A/zh
Application granted granted Critical
Publication of CN101318787B publication Critical patent/CN101318787B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于资源化利用的方法。它是利用铝工业在生产过程中所产出的固体废物——赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、化灰渣、煤气发生炉渣、污泥六种废渣自身的物质属性，通过干燥、粉碎、合理配比、加工成型(碾压、挤压)固结或烧结工艺，转化为新型的路用材料和建筑墙体材料。其特征是废渣利用率为100％。①所生产的路用材料--固化剂，用于公路路基补强、路面结构层(基层、底基层)和建筑物的基础补强，可替代全部的水泥、石灰和砂石材料，其性能能满足现行国家(行业)标准和环保标准。②所生产的建筑墙体材料--非承重砖、承重砖、空心砖、空心砌块以及普通瓦、琉璃瓦、彩色瓦，其性能优于国家现行标准。具有节能、保温、高强、抗腐蚀、抗风化、无污染的特点。

Description

一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法
技术领域
一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法。属于铝工业烧结法、拜耳法工艺生产氧化铝所产出的工业固体废渣资源化利用的方法。
背景技术
具资料显示，我国铝工业利用烧结法、拜耳法工艺生产氧化铝产出大量的工业固体废渣——赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、化灰渣、煤气发生炉渣、污泥六种废渣堆存量约上亿吨。上述废渣中除化灰渣、煤气发生炉渣、锅炉炉渣已开始综合利用外，其余大部分仍处于堆放状态，不仅占用了大量土地和农田，而且也污染着周边的土壤、水体、大气和环境卫生，给人们造成潜在的、长期的危害。我国政府为了扭转这种状况，早在1985年就提出了综合利用“三废”资源，积极发展新型建筑材料。随后，又发布《关于严格限制毁田烧砖，鼓励节约能源、利废、加速发展新型建筑材料的通知》，一方面通过立法等各种手段增强公众的环保意识，控制污染物排放，加大治理力度；另一方面大力倡导废物利用、开源节流、低耗高能、实现循环经济，以期达到我国经济建设可持续和谐发展的目的。国内外许多学者对铝工业工艺废渣的研究，已取得了可喜的成果。如：专利号为92104133.0《赤泥复合砖及制备方法》、专利号为91107435.x《灰渣复合彩色瓦及其制作方法、专利号为89105093.3《粉煤灰复合材料的制造方法》、专利号为00110047.5《高掺量粉煤灰烧结砖的生产工艺》、专利号为00120579.x《粉煤灰页岩铝矾土综合利用的方法》等专利技术，披露了利用赤泥、粉煤灰、锅渣、页岩、铝矾土等工业废物生产墙体材料的工艺和方法。然而，由于铝工业工艺废渣排量大、含水量高，赤泥中含碱、钠量高并且含有放射性元素，使得上述技术在推广过程中有一定的局限性，至使铝工业工艺废渣在全球的积存量仍是有增无减。由此带来了占用农田、污染环境等一系列连锁反应。
本发明的特征是提供一种铝工业工艺废渣资源化利用的有效方法。它是将全部的铝工业工艺废渣-赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、化灰渣、煤气发生炉渣、污泥作为有用资源，利用其有效成份相互搭配，优势互补，通过合理的工艺、优化的配方，制成固化剂和烧结砖。固化剂可用于公路、铁路、水利及大型基础设施的地基改性土补强、公路路面结构层底基层、基层、低标号碾压混凝土；烧结砖可直接用于各种城市和民用建筑。真正起到变废为宝、节约能源、保护环境的作用。为铝工业的可持续发展解除了后顾之忧。
发明内容
本发明的主要内容是将所有的铝工业工艺废渣都能作为筑路材料和新型生态墙体材料。其特点是：1.通过控制赤泥的最大掺量(25％以下)，来解决混合料中Na、CaO的含量以及放射性元素。实现制备出的固化剂或烧制砖，既能满足力学指标，又能满足环保指标；2.用铝选矿矿尾代替粘土、页岩作为塑性材料，具有自身发热量高的特点。其发热量大于700大卡，有利于烧结砖、瓦的自燃与增温，可达到节约能源的目的；3.由于赤泥(发热量≥800大卡)、煤气发生炉渣(发热量≥800大卡)与铝选矿矿尾、锅炉炉渣、污泥五种物质混合后其发热量均＞700大卡，作为自燃烧结砖的主要原料，可以使其内外均匀加热，改善了制品的性能且具有固硫作用，减少向大气中排放二氧化硫量以减少污染。
本发明的主要工艺和方法是：首先将湿排的赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、化灰渣、煤气发生炉渣、污泥烘干(利用隧道窑余热)和粉碎，控制含水量为5％～10％之间，粒径在1.0mm以下；选赤泥(烧结法、拜耳法)、煤气发生炉渣、化灰渣并加入微量外掺剂进行充分搅拌，控制其配比为赤泥∶煤气发生炉渣∶化灰渣＝15～28∶30～60∶10～35(质量比)，利用球磨机磨制后，通过1mm的方筛，密封装袋即为成品固化剂。选赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、煤气发生炉渣、污泥进行对辊拌合，控制其配比为赤泥∶煤气发生炉渣∶选矿尾矿∶污泥∶锅炉炉渣＝5～30∶0～30∶20～60∶15～50∶0～15(质量比)，含水量小于16％，充分搅拌后沉化24小时，经混练后送入制砖机切成砖坯，用码坯机自动码坯装车。通过绞车、拖车、顶车机将坯车顶入隧道窑内，通过排潮、顶热、烧结、冷却等阶段制成砖成品。控制其排潮、烘干温度为80℃~520℃，时间为12小时；烧结温度800℃~1100℃，时间为6~12小时，然后降温，其降温速率为60℃/h。制品出窑时的温度应低于60℃即为成品砖，检验后各项指标均优于现行国家砖、瓦标准。
具体实施方式
本发明的实施方法可按照附图中的工艺进行：首先将赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、化灰渣、煤气发生炉渣、污泥进行预处理——烘干(晾晒)和粉碎，将其含水量控制在10％～20％之间，其粒径应通过1.0mm方筛，按上述的比例输入搅拌机，通过搅拌后，成为配比均匀的混合原料，进入制砖系统。经过挤压成泥条，泥条经过切坏机切成砖坯，用自动码坯机码坯装车。通过绞车、拖车、顶车机将坯车顶入隧道窑内，通过排潮、顶热、烧结、冷却等阶段制成砖成品。
本发明将铝工业工艺废渣全部转型为生态建筑材料，解决了铝工业企业的后顾之忧。所有的铝工业工艺废渣全部成为一种新的资源用于现代化建设，不仅节约了大量的土地、山体资源(如现在使用的页岩)，而且又可消除其对环境的污染，可达到既发展经济又保护环境的双赢目的。
本发明包括不限于下列具体的实例。
实例1
配合比：赤泥+煤气发生炉渣+化灰渣+微量添加剂＝25+52+23(微量添加剂为)
(一)原料烘干：按上述配合比将原料送入隧道窑烘干室烘干至4％含水量。
(二)原料粉碎：用球磨机进行研磨成粉状，粒径通过80目筛。
(三)混料搅拌：将上述原料用双辊搅拌机进行双级双层搅拌均匀。
(四)成品与包装：将搅拌均匀的混合料密封包装，即为固化剂成品。
该固化剂用于焦作市中铝至云台山二级路底基层和基层替代全部的石灰、水泥和砂石，经检测满足《公路工程质量检验评定标准》的要求。
实例2
配合比：赤泥+煤气发生炉渣+选矿尾矿+污泥＝20+25+50+5(质量比)
(一)原料烘干：按上述配合比将原料送入隧道窑烘干室烘干至4％含水量。
(二)原料粉碎：锤式破碎机进行粉碎，粒径≤1.0mm。
(三)混料搅拌：将上述原料充分混合，混合后加水用双辊搅拌机进行双级双层搅拌，混料搅拌时的加水量为混合料重量的12～16％；
(四)沉化：将混合好的材料静至24小时。
(五)挤压成型：将上述混合料用双级真空挤砖机进行挤压成条状。
(六)切制砖坯：将上述挤压成条的坯料用自动垂直切条机、切坯机进行切制成砖坯；
(七)砖坯干燥：将上述制成的砖坯通过绞车、拖用自动码坯机码坯装车。车、顶车机将坯车顶入隧道窑内，经过隧道窑烘干室，其烘干温度为75～95℃。
(八)烧制与冷却：燃烧时烧结温度为900～1100℃，时间为8h，冷却速度为60℃/h，出窑即为成品。
经检测：
强度等级    平均值19.9MPa          标准值16.4Mpa
吸水率      平均值17％             单块最大值17％
饱和系数    平均值0.75             单块最大值0.77
放射性      内照射指数IRa    0.11  外照射指数Iγ  0.52
其它各项尺寸、外观质量均满足国家标准。

Claims (10)

1一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法，其特征是利用铝工业工艺废渣中的赤泥(烧结法、拜耳法)、煤气发生炉渣、化灰渣并加入微量外掺剂进行烘干、粉碎、搅拌和防潮包装生产固化剂的方法。
2按权利要求1所述的工艺，其特征在于控制其配比(质量比)为：
赤泥∶煤气发生炉渣∶化灰渣＝15～28∶30～60∶10～35，(微量外掺剂为0.01～0.1％)
3按权利要求1所述的工艺，其特征在于混合料的含水量小于10％以下。
4按权利要求1所述的工艺，其特征在于利用粉碎机(球磨机)粉碎后，粒径小于1mm。
5按权利要求1所述的工艺，其特征在于制成的成品固化剂使用于公路、铁路、水利及大型基础设施的地基改性土补强、公路路面结构层底基层、基层、低标号碾压混凝土。
6一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法，其特征是利用赤泥(烧结法、拜耳法)、锅炉炉渣、选矿尾矿、化灰渣、煤气发生炉渣、污泥进行烘干、粉碎、搅拌、沉化、混练、制坯、干燥、焙烧和冷却生产烧结砖制品。
7按权利要求6所述的工艺，其特征在于控制其配比为：
赤泥∶煤气发生炉渣∶选矿尾矿∶污泥∶锅炉炉渣＝5～30∶0～30∶20～60∶15～50∶0～15(质量比)。
8按权利要求6所述的工艺，其特征在于成坯后的含水量低于20％。
9按权利要求6所述的工艺，其特征在于上述废渣混合后的发热量大于600大卡。
10按权利要求6所述的工艺，其特征在于焙烧温度850℃~1100℃。
CN2007101059712A 2007-06-04 2007-06-04 一种铝工业工艺废渣全部转型为生态建筑材料的工艺与方法 Expired - Fee Related CN101318787B (zh)