CN101318435A - Forming method for surface pattern of golf club - Google Patents
Forming method for surface pattern of golf club Download PDFInfo
- Publication number
- CN101318435A CN101318435A CNA2008101090423A CN200810109042A CN101318435A CN 101318435 A CN101318435 A CN 101318435A CN A2008101090423 A CNA2008101090423 A CN A2008101090423A CN 200810109042 A CN200810109042 A CN 200810109042A CN 101318435 A CN101318435 A CN 101318435A
- Authority
- CN
- China
- Prior art keywords
- mentioned
- golf club
- pattern
- macromolecule membrane
- formation method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a forming method of a surface pattern of a golf head which includes the following steps: A, a pattern with a component of ink is formed on a polymeric membrane which comprises a component of activating agent; B, the polymeric membrane is placed into water for moistening for a period of time, then the polymeric membrane is taken out and stuck on the proper position of the outer surface of the golf head; C, the polymeric membrane is roasted to lead the pattern with the component of ink to be separated from the polymeric membrane and lead the pattern to be printed on the golf head; D, the polymeric membrane is taken from the golf head. The pattern printed on the golf head by the forming method of the invention has broad selectivity; when the pattern needs to be replaced or modified, after removing the original ink pattern on the golf head, another ink pattern is only needed to be formed by the forming method, thus leading the updating and modifying of the pattern to be simpler and more convenient.
Description
Technical field
The invention relates to a kind of formation method of surface pattern of golf club.
Background technology
Specific lines or pattern on the golf club, manually to spray paint or other artificial printing waits coating process to finish, it is comparatively numerous and diverse that these traditional methods are not only processed, and because of the operation on the volume production limits, be difficult to make the comparatively layout of complexity traditionally.
For overcoming above problem, TW518281 TaiWan, China patent provides the moulding manufacture method of the walnut wood grain coloured silk on a kind of bulb surface, it is through sandblast with metal golf club, spraying with the priming paint of colour system after the appropriateness baking, so that its prime coat has outer hard interior tough characteristic, then utilize immerse the walnut glued membrane in the water and spray activator and make the printing ink activation after, the pattern transfer printing of being printed on the glued membrane is coated in that this rod head noumenon surface (priming paint) is gone up and after washing (cutting) handles, its rod head noumenon is utilized continuous conveying again, and the roasting mode that promotes temperature gradually removes its remaining moisture content, through being sprayed a transparent colored paint again after the cooling naturally, spray finish paint then, treat finish paint finish after and with its place again baking oven through two the degree bakings, and after the cooling naturally of leaving standstill, bestow surface finish and handle, so that the rod head noumenon after its moulding manufacturing has the outward appearance of walnut wood grain.
The technology contents that case disclosed must be inserted the transcription epithelium in the water before this, whole bulb is inserted in the water after spraying activator, utilizes hydraulic pressure to make pattern transfer on the film to bulb.Not only operation is difficult for, and the required tank of transfer printing also causes the planning problem of volume production moving-wire.Therefore, for adapting to the figure ornament variation of bulb surface with complicated market-oriented, develop a kind of method for coating surface that is more suitable for volume production is the target that the golf club field does one's utmost to pursue always.
Summary of the invention
The objective of the invention is, a kind of formation method of surface pattern of golf club is provided, can make the bulb surface pattern be easy to modifications by this formation method.
Above-mentioned purpose of the present invention can adopt following technical proposal to realize, a kind of formation method of surface pattern of golf club, and described method comprises the following steps:
A, on the macromolecule membrane that includes the activator composition, form pattern with ink ingredient;
B, above-mentioned macromolecule membrane is positioned in the water takes out after wetting a period of time, and be attached at the suitable position of the outer surface of this golf club;
C, toast above-mentioned macromolecule membrane, the pattern of its ink ingredient is separated with macromolecule membrane, and above-mentioned pattern is printed on this golf club;
D, above-mentioned macromolecule membrane is taken off from above-mentioned golf club.
In preferred implementation, also comprise step e after the above-mentioned steps D: protective paint is sprayed at the position with pattern at above-mentioned golf club.
In preferred implementation, also comprise step F behind the above-mentioned steps E: dry above-mentioned protective paint.
In preferred implementation, after also comprising the following steps: A1 among the above-mentioned steps A, being immersed in above-mentioned macromolecule membrane in the activator in advance, take out dry so that this macromolecule membrane has the activator composition; A2, with above-mentioned pattern ink printing or ink-jet on this macromolecule membrane.
In preferred implementation, also comprise the following steps: A1 among the above-mentioned steps A, activator is coated on this macromolecule membrane in advance with coating method; A2, with above-mentioned pattern ink printing or ink-jet on this macromolecule membrane.
In preferred implementation, above-mentioned steps B comprises the following steps: B1, at the suitable position coating adhesion layer of the outer surface of above-mentioned golf club; B2, above-mentioned macromolecule membrane is positioned in the water takes out after wetting a period of time, and be attached at above-mentioned adhesion layer.
In preferred implementation, above-mentioned adhesion layer is a priming paint, and this priming paint is sprayed at the outer surface of this golf club.
In preferred implementation, also comprise step B12 between above-mentioned steps B1 and the B2: toasted above-mentioned priming paint 10 minutes with 90 ℃ temperature.
In preferred implementation, among the above-mentioned steps B, above-mentioned macromolecule membrane is attached at the outer surface of above-mentioned golf club after, impose scraper this macromolecule membrane be processed into formation state.
In preferred implementation, the suitable position among the above-mentioned steps B is meant the position beyond the hitting panel of this golf club or the beater plate, above-mentioned pattern account for this suitable position area ratio more than 5%.
In preferred implementation, among the above-mentioned steps B, above-mentioned macromolecule membrane wetting time in water is 4-20 second.
In preferred implementation, among the above-mentioned steps C, with 5 fens clock times of 80 ℃ of temperature baking macromolecule membranes.
In preferred implementation, also comprise step between above-mentioned steps D and the E: clean with solvent wiping.
Characteristics of the present invention and advantage are:
The present invention contains the transfer film of activator composition and the printing ink pattern is transferred on the golf club from film by use.This kind transfer film itself has the activator composition, immerse it in water after, just can be wetting simultaneously and the ink ingredient of activation printed patterns.The benefit of making bulb surface figure ornament with this kind film is wettingly can carry out simultaneously with activation, does not follow-uply also need to prepare facility such as tank, relies on the pressure of hydraulic pressure to make pattern transfer on bulb.
Make the pattern of printing on the golf club by formation method of the present invention, has selectivity widely, when needs are changed or are revised pattern, only need after the original printing ink pattern removal on the golf club, again form another printing ink pattern by this formation method and get final product, make pattern renewal, revise comparatively easy.
Description of drawings
The following drawings only is intended to the present invention done and schematically illustrates and explain, not delimit the scope of the invention.Wherein,
Fig. 1 is the schematic diagram of the golf club of first preferred embodiment of the present invention.
Fig. 2 A is the front view of the golf push rod bulb of second preferred embodiment of the present invention.
Fig. 2 B is the rearview of the golf push rod bulb of second preferred embodiment of the present invention.
Fig. 3 is the schematic diagram of the golf clubs of the 3rd preferred embodiment of the present invention.
Fig. 4 is the schematic diagram of the golf push rod of the 4th preferred embodiment of the present invention.
The specific embodiment
Understand for technical characterictic of the present invention, purpose and effect being had more clearly, now contrast description of drawings the specific embodiment of the present invention.Wherein, identical parts adopt identical label.
The general manufacturing principle of golf club has been that those skilled in the art can understand, therefore explanation hereinafter only is elaborated at the external coating manufacturing process, just no longer does complete description in this as for other general manufacturing process such as encapsulate, polishing, sandblasts.
The formation method of the surface pattern of the golf club that the present invention proposes, wherein, this golf club is preferably rod head or push rod cup, and wherein the rod head for example can be the rod of kicking off, Fairway Woods or hophornbeam bar etc.This formation method may further comprise the steps:
A, on the macromolecule membrane that includes the activator composition, form pattern with ink ingredient; Wherein this pattern can be pattern, drawing, symbol, literal or other lines of photo, computer design, has increased the selection of pattern on the one hand, has reduced on the other hand and has manually sprayed paint or the artificial manufacturing time of method such as printing, increases work efficiency.
B, above-mentioned macromolecule membrane is positioned in the water takes out after wetting a period of time, and be attached at the suitable position of the outer surface of this golf club.
C, toast above-mentioned macromolecule membrane, the pattern of its ink ingredient is separated with macromolecule membrane, and above-mentioned pattern is printed on this golf club.
D, above-mentioned macromolecule membrane is taken off from above-mentioned golf club.
In preferred implementation; also comprise E after above-mentioned steps D: protective paint is sprayed at the position with pattern at above-mentioned golf club; this protective paint is good with transparent polish lacquer; so that pattern has excellent wear resistance, not loss of gloss and resistance to water; and the pattern difficult drop-off can keep its unique sense of worth.Preferably, after above-mentioned steps E, also comprise step F again: dry above-mentioned protective paint, with the drying of acceleration protection lacquer.
Can learn that from the above description the present invention contains the transfer film of activator composition and the printing ink pattern is transferred on the golf club from film by use.This kind transfer film itself has the activator composition, immerse it in water after, just can be wetting simultaneously and the ink ingredient of activation printed patterns.The benefit of making bulb surface figure ornament with this kind film is wettingly can carry out simultaneously with activation, does not follow-uply also need to prepare facility such as tank, relies on the pressure of hydraulic pressure to make pattern transfer on bulb.
Below more above-mentioned steps are illustrated in greater detail:
In above-mentioned steps A, the method that comprises the composition of activator on the macromolecule membrane (for example plastic sheeting) is had: after being immersed in above-mentioned macromolecule membrane in the activator in advance, to take out drying, so that this macromolecule membrane has the activator composition; Or activator is coated on (steps A 1) on this macromolecule membrane in advance with coating method.Then, with above-mentioned pattern ink printing or ink-jet on above-mentioned macromolecule membrane with activator composition (steps A 2).
Generally speaking, as shown in Figure 1, golf club 1 (is example with the rod head) comprises hollow body 10 with opening and the hitting panel 11 that is sealedly attached to this opening, and hollow body 10 comprises bottom 101, top 102 and the lateral margin 103 that is connected in this bottom 101 and top 102.In above-mentioned steps B, " suitable position " preferable to be meant the position except that hitting panel 11 on the golf club, promptly on the outer surface of hollow body 10, and better be on the top 102 or lateral margin 103 of hollow body 10; It is preferable more than 5% that above-mentioned pattern 13 accounts for the area ratio of outer surface suitable position of hollow body 10.Macromolecule membrane wetting time in water can be 4-20 second, and the preferable time is 7-13 second, and after wetting a period of time in the water during macromolecule membrane is positioned over, activator can be with the printing ink activation of pattern.
In the better embodiment of above-mentioned steps B, at the outer surface coating adhesion layer (step B1) of above-mentioned hollow body, adhere on it in advance so that the printing ink of pattern is easier; Then the macromolecule membrane after wetting is attached to (step B2) on this adhesion layer.Wherein the most easy generation type of this adhesion layer is a spraying priming paint, also can spray the macromolecular material that other has more tack certainly.The color of priming paint is good with most of color of the pattern that is different from macromolecule membrane; Certainly, the color of priming paint also can be same as most of color of the pattern of macromolecule membrane, but need have different chromas or lightness, to show contrast effect.
In preferred implementation, further can impose the baking program with cured primer behind the spraying priming paint, it is 90 degrees centigrade that baking condition is roughly temperature, the 10 minutes time (step B12).
In preferred implementation, above-mentioned macromolecule membrane is attached to the outer surface of this hollow body after, impose scraper macromolecule membrane be processed into formation state, to reach effect more attractive in appearance.
In above-mentioned steps C, toast above-mentioned macromolecule membrane after step B handles, and be preferably with 80 ℃ of temperature and toast about 5 minutes clock times, because macromolecule membrane is after water-wet among the above-mentioned steps B, printing ink on it is activated, leave standstill a period of time (for example about 10 seconds) after, again through overbaking, printing ink can separate with macromolecule membrane, thereby printing ink is transferred on the golf club from macromolecule membrane.
Between above-mentioned steps D and E, also comprise step: clean with solvent wiping.
Above-mentioned steps E and step F can be substituted by the following step:
G, color spray lacquer, this colored paint is made up of host, curing agent and diluent, and toasts 10 minutes with 100 ℃ of temperature behind the above-mentioned colored paint of spraying;
H, spray polish lacquer, this polish lacquer is made up of host, curing agent and diluent equally, and toasts 30 minutes with 120 ℃ of temperature behind the above-mentioned polish lacquer of spraying.
Other structures, operation principle and the beneficial effect of present embodiment is identical with embodiment 1, does not repeat them here.
Golf club in the present embodiment is a push rod bulb 2, shown in Fig. 2 A, 2B, it mainly comprises body 20, this body 20 has bottom 201, from the bottom the upwardly extending strike of 201 leading edges portion 202, the top 203 that extends back of strike portion 202 upper limbs, toe 204 and heel 205 etc. certainly, " suitable position " in the present embodiment specifically is meant the position except that strike portion 202 on the body 20 of golf push rod bulb.
Other structures, operation principle and the beneficial effect of present embodiment is identical with embodiment 1, does not repeat them here.
As shown in Figure 3, in the present embodiment a kind of golf clubs, it comprises in above-mentioned embodiment 1 or 2 golf club 1 that forms surface pattern, shaft 31, is sleeved on the handle 32 of shaft 31 1 ends, this golf club 1 is connected in the other end of this shaft 31.
Other structures, operation principle and the beneficial effect of present embodiment is identical with embodiment 1, does not repeat them here.
Embodiment 5
As shown in Figure 4, in the present embodiment a kind of golf clubs, it comprises in the above-mentioned embodiment 3 golf club 2 that forms surface pattern, shaft 41, is sleeved on the handle 42 of shaft 41 1 ends, this golf club 2 is connected in the other end of this shaft 41.
Other structures, operation principle and the beneficial effect of present embodiment is identical with embodiment 1, does not repeat them here.
The above is only for the schematic specific embodiment of the present invention, is not in order to limiting scope of the present invention, and for example above-mentioned embodiment also can be applicable to iron club.Any those skilled in the art, equivalent variations and the modification done under the prerequisite that does not break away from design of the present invention and principle all should belong to the scope of protection of the invention.
Claims (13)
1, a kind of formation method of surface pattern of golf club is characterized in that, described method comprises the following steps:
A, on the macromolecule membrane that includes the activator composition, form pattern with ink ingredient;
B, above-mentioned macromolecule membrane is positioned in the water takes out after wetting a period of time, and be attached at the suitable position of the outer surface of this golf club;
C, toast above-mentioned macromolecule membrane, the pattern of its ink ingredient is separated with macromolecule membrane, and above-mentioned pattern is printed on this golf club;
D, above-mentioned macromolecule membrane is taken off from above-mentioned golf club.
2, the formation method of the surface pattern of golf club as claimed in claim 1 is characterized in that, also comprise step e after the above-mentioned steps D: protective paint is sprayed at the position with pattern at above-mentioned golf club.
3, the formation method of the surface pattern of golf club as claimed in claim 2 is characterized in that, also comprises step F behind the above-mentioned steps E: dry above-mentioned protective paint.
4, the formation method of the surface pattern of golf club as claimed in claim 2 is characterized in that, also comprises the following steps: among the above-mentioned steps A
A1, be immersed in above-mentioned macromolecule membrane in the activator in advance after, take out dry so that this macromolecule membrane has the activator composition;
A2, with above-mentioned pattern ink printing or ink-jet on this macromolecule membrane.
5, the formation method of the surface pattern of golf club as claimed in claim 2 is characterized in that, also comprises the following steps: among the above-mentioned steps A
A1, activator is coated on this macromolecule membrane in advance with coating method;
A2, with above-mentioned pattern ink printing or ink-jet on this macromolecule membrane.
6, as the formation method of the surface pattern of each described golf club of claim 1-5, it is characterized in that above-mentioned steps B comprises the following steps:
B1, at the suitable position coating adhesion layer of the outer surface of above-mentioned golf club;
B2, above-mentioned macromolecule membrane is positioned in the water takes out after wetting a period of time, and be attached at above-mentioned adhesion layer.
7, the formation method of the surface pattern of golf club as claimed in claim 6 is characterized in that, above-mentioned adhesion layer is a priming paint, and this priming paint is sprayed at the outer surface of this golf club.
8, the formation method of the surface pattern of golf club as claimed in claim 7 is characterized in that, also comprises step B12 between above-mentioned steps B1 and the B2: toasted above-mentioned priming paint 10 minutes with 90 ℃ temperature.
9, as the formation method of the surface pattern of each described golf club of claim 1-5, it is characterized in that, among the above-mentioned steps B, above-mentioned macromolecule membrane is attached at the outer surface of above-mentioned golf club after, impose scraper this macromolecule membrane be processed into formation state.
10, as the formation method of the surface pattern of each described golf club of claim 1-5, it is characterized in that, suitable position among the above-mentioned steps B is meant the position beyond the hitting panel of this golf club or the beater plate, above-mentioned pattern account for this suitable position area ratio more than 5%.
11, as the formation method of the surface pattern of each described golf club of claim 1-5, it is characterized in that among the above-mentioned steps B, above-mentioned macromolecule membrane wetting time in water is 4-20 second.
12, as the formation method of the surface pattern of each described golf club of claim 1-5, it is characterized in that, among the above-mentioned steps C, with 5 fens clock times of 80 ℃ of temperature baking macromolecule membranes.
13, as the formation method of the surface pattern of each described golf club of claim 2-5, it is characterized in that, also comprise step between above-mentioned steps D and the E: clean with solvent wiping.