CN101293631B - 水葫芦的用途 - Google Patents
水葫芦的用途 Download PDFInfo
- Publication number
- CN101293631B CN101293631B CN2008100390933A CN200810039093A CN101293631B CN 101293631 B CN101293631 B CN 101293631B CN 2008100390933 A CN2008100390933 A CN 2008100390933A CN 200810039093 A CN200810039093 A CN 200810039093A CN 101293631 B CN101293631 B CN 101293631B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- herba eichhorniae
- mixed slurry
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种水葫芦的用途,即水葫芦在制备用于生产合成气或燃料燃烧的混合浆料中的应用。所说的用于生成合成气或燃料燃烧的混合浆料,以重量份数计,包括:100~200重量份数的含碳物质,20~150重量份数的水葫芦,0.001~1重量份数的改性剂和0.001~5重量份数的分散剂。本发明所制备的含水葫芦混合浆料的浆浓度达60wt%以上,其表观黏度小于1000mPa·s(25℃)。此外,在发明所制备的含水葫芦混合浆料过程中无需额外添加稳定剂,且所述的含水葫芦混合浆料久置后不会产生硬沉淀、适合泵送。
Description
技术领域
本发明涉及一种水葫芦的用途。
背景技术
水葫芦,又名凤眼莲、水荷花、假水仙和水生风信子等,属单子叶多年生植物,雨久花科凤眼兰属。
水葫芦一般生长于湖泊、河流和池塘等地,繁殖力、生存力强。它具有较强的净化水体的能力,湖泊中有一定数量的水葫芦对水质的提高、抑制蓝藻等藻类的生长、美化环境是有益的。但是,正因为它繁殖力强,代谢较快,如不及时打捞,根茎叶等又会腐烂于水中,又会给水质造成严重污染。
迄今,水葫芦主要用作饲料、沤肥、普通燃料或制备沼气。由于水葫芦所含热值较高(其干基热值约为13MJ/kg,是煤热值一半以上),因此,就现有水葫芦的应用状况而言,其所含热值尚未得到充分利用。此外,由于打捞的水葫芦含有大量水分(含水量大于90wt%),因此,在使用前(特别是作为普通燃料用)需进行脱水,这不仅需要特殊的脱水设备,而且脱水过程耗能巨大。
鉴于此,提供一种具有“高附加值”的水葫芦的用途,就成为本发明需要解决的技术问题。
发明内容
本发明的发明人经广泛且深入的研究发现:将水葫芦经粉碎后,与含碳物质、分散剂和水等组分混合,可制成一种用于生产合成气的混合浆料或燃料燃烧的混合浆料,且所得的混合浆料具有良好的稳定性(无需额外添加稳定剂)。如此,不仅大规模地、有效快捷地处理了水葫芦,而且使水葫芦中的热值得以从分利用。
所说的用于生产合成气的混合浆料或燃料燃烧的混合浆料,以重量份数计,包括如下组分及含量:
100~200重量份数的含碳物质,20~150重量份数的水葫芦,0.001~1重量份数的改性剂和0.001~5重量份数的分散剂;
其中,所说的含碳物质选自煤、石油焦或生物质中一种、二种或二种以上;
所说的水葫芦取自生长于湖泊、河流或池塘等中的水葫芦,且经粉碎(优选粒径小于5mm的水葫芦)、含水量大于90wt%;
所说的分散剂为分子量大于2,000的萘磺酸盐、分子量大于10,000的聚羧酸盐或分子量大于3,000木质素磺酸盐中的一种、二种或二种以上;
所说的改性剂为碳酸钙、碳酸钠、碳酸氢钠、碳酸钾、氧化钙、氢氧化钙、氢氧化钠、氢氧化钾、水溶性铁盐或水溶性铜盐中的一种、二种或二种以上。
具体实施方式
一种制备本发明所述的用于生产合成气的混合浆料或燃料燃烧的混合浆料的方法,包括如下步骤:
(1)将含水率为90wt%以上的水葫芦粉碎,与改性剂按上述比例混合得浆料;
(2)将由步骤(1)所得浆料,再与含碳物质和分散剂按前述比例混合得混合物,该混合物经研磨后(使其所含固体的粒径小于0.5mm),得目标物。
本发明所制备的含水葫芦混合浆料的浆浓度达60wt%以上,其表观黏度小于1000mPa·s(25℃)。此外,在发明所制备的含水葫芦混合浆料过程中无需额外添加稳定剂,且所述的含水葫芦混合浆料久置后不会产生硬沉淀、适合泵送。
下面通过实施例对本发明作进一步说明,其目的仅在于更好理解本发明的内容。因此所举之例并不限制本发明的保护范围。
实施例1
1、原料:
(1)某湖泊产生的水葫芦(水含量94wt%);
(2)某炼油厂石油焦(硫含量3wt%,灰分含量0.6wt%);
(3)水;
(4)氢氧化钙;
(5)分子量大于3500的甲基萘磺酸钠甲醛缩合物;
2、目标物制备:
将200重量份数的石油焦,110重量份数的水葫芦,10重量份数的水,0.1重量份数的氢氧化钙和0.5重量份数的分子量大于3500的甲基萘磺酸钠甲醛缩合物经混合、粉碎后得灰黑色浆体(目标物)。目标物的固含量为64wt%,表观黏度(25℃)小于1000mPa·s,可泵送。
3、应用:
将由步骤2所制的目标物替代现有的水煤浆,用于如专利98110616.1所述的多喷嘴对置式水煤浆气化炉制备合成气(制备合成气的工艺条件与用水煤浆时的工艺条件相同),所得有效气成分(CO+H2)可达85%,碳转化率在98%以上。
实施例2
1、原料
(1)某湖泊产生的水葫芦(水含量94wt%);
(2)某煤矿块煤(灰分含量10wt%);
(3)水;
(4)碳酸氢钠;
(5)分子量大于5000的木质素磺酸钠;
2、目标物制备:
100重量份数的块煤,40重量份数的水葫芦,30重量份数的水,0.4重量份数的碳酸氢钠和0.6重量份数的分子量大于5000的木质素磺酸钠经混合、粉碎后得灰黑色浆体(目标物)。目标物的固含量为60wt%,表观黏度(25℃)小于1000mPa·s,可泵送。
3、应用:
将由步骤2所制的目标物替代现有的水煤浆,用于如专利98110616.1所述的多喷嘴对置式水煤浆气化炉制备合成气(制备合成气的工艺条件与用水煤浆时的工艺条件相同),所得有效气成分(CO+H2)可达82%,碳转化率在99%以上。
Claims (1)
1.水葫芦在制备用于生产合成气的混合浆料中的应用:
其中,所说的混合浆料,包括如下组分及含量:
100重量份数~200重量份数的含碳物质,
20重量份数~150重量份数的水葫芦,
0.001重量份数~1重量份数的改性剂,
0.001重量份数~5重量份数的分散剂;
所说的含碳物质为煤、石油焦、生物质或/和含碳固体废弃物;
所说的水葫芦取自生长于湖泊、河流或池塘中的水葫芦,含水量为80wt%~98wt%;
所说的分散剂为分子量大于2,000的萘磺酸盐、分子量大于10,000的聚羧酸盐或/和分子量大于3,000木质素磺酸盐;
所说的改性剂为碳酸钙、碳酸钠、碳酸氢钠、碳酸钾、氧化钙、氢氧化钙、氢氧化钠、氢氧化钾、水溶性铁盐或/和水溶性铜盐。