CN101234868A - 沥青基渗透结晶型水泥混凝土防水防腐剂 - Google Patents
沥青基渗透结晶型水泥混凝土防水防腐剂 Download PDFInfo
- Publication number
- CN101234868A CN101234868A CNA2007101159388A CN200710115938A CN101234868A CN 101234868 A CN101234868 A CN 101234868A CN A2007101159388 A CNA2007101159388 A CN A2007101159388A CN 200710115938 A CN200710115938 A CN 200710115938A CN 101234868 A CN101234868 A CN 101234868A
- Authority
- CN
- China
- Prior art keywords
- cement concrete
- crystallization type
- asphalt
- type cement
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种沥青基渗透结晶型水泥混凝土防水防腐剂及其制备方法,包括氢氧化钠、膨润土、云母、水、十二烷基三甲基氯化铵、10#建筑沥青、60#道路沥青、硅酸钠、乙醇;本发明防水、防潮、防漏、防腐、有韧性、耐磨、使用寿命长。可广泛应用于水泥混凝土表面层的防水、防腐中。
Description
所属技术领域 本发明涉及一种沥青基渗透结晶型水泥混凝土防水防腐剂,可广泛应用于水泥混凝土表面层的防水、防腐,尤其应用于水利、水工、水电、地下、桥梁、隧道、水泥路面、停车场、防水坝、污水处理池、化工地面、卫生间、内外墙水泥混凝土建筑工程中的防水、防腐过程中。
背景技术 混凝土结构由于其脆性大,在工程应用中,往往不可避免产生开裂,这种开裂导致混凝土结构渗漏、腐蚀,影响工程的使用寿命,甚至无法正常使用,这是建筑界普遍存在的问题。混凝土结构中裂缝的产生主要有两大类原因:一类有变形引起,包括因温度、湿度变化产生收缩、膨胀,导致不均匀沉陷;另一类是外动、静载荷直接应力引起。
目前,防水材料众多,可分为柔性防水与刚性防水两大类。从国内外多年的实践证明,传统的涂料柔性防水材料,虽然具有柔性特点,耐久性也较好,但与基面混凝土粘结力弱,尤其在表面潮湿或有渗水的情况下无法使用,不宜作潮湿基面的防水。刚性水泥基防水材料具有柔性材料无法比拟的性能而广泛应用,但目前普遍使用的水泥基防水材料,有易吸水、无韧性、不耐磨三大缺点,水泥混凝土的老化现象非常严重,影响了各类建筑物的使用寿命,给社会经济造成了很大的损失。
发明内容 为了克服上述缺点,本发明的目的在于提供一种防水、防潮、防漏、防腐、有韧性、耐磨、使用寿命长的沥青基渗透结晶型水泥混凝土防水防腐剂及其制备方法。
为了达到上述目的,本发明沥青基渗透结晶型水泥混凝土防水防腐剂,包括氢氧化钠、膨润土、云母、水、十二烷基三甲基氯化铵、10#建筑沥青、60#道路沥青、硅酸纳、乙醇;各组分重量比为:
氢氧化钠 2~4; 膨润土 15~25;
云母 6~12; 水 55~65;
十二烷基三甲基氯化铵 8~12; 10#建筑沥青 25~35;
60#道路沥青 65~75; 硅酸纳 8~12;
乙醇 6~10。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,各组分重量比为:
氢氧化钠 2~4; 膨润土 18~22;
云母 8~10; 水 60~62;
十二烷基三甲基氯化铵 9~11; 10#建筑沥青 30~32;
60#道路沥青 70~72; 硅酸纳 9~11;
乙醇 7~9。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,可添加适量的渗透促进剂C2H5OH和催化剂NaHCO3。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,通过渗透结晶过程,进行有效防水。当本发明沥青基渗透结晶型水泥混凝土防水防腐剂涂覆在水饱和的的混凝土基面上时,由于混凝土表面能够形成高的离子浓度,形成的浓度梯度为渗透创造了条件,其离子从高浓度处向低浓度处迁移。随着离子的迁移,本发明中的化学物质及胶凝成分也迁移到水泥表面的孔隙中,便开始进行水化反应,形成水化晶体,生成的大量晶体填充、封堵混凝土的孔隙,使水无法进入混凝土,从而达到防水的目的。由于本发明的渗透作用,本发明晶体能够很好地渗入到混凝土结构中,填充孔隙,渗透能力强。即使本发明涂层磨损掉,混凝土结构仍不透水。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,石油沥青主要化学成分以C、H为主体,由于沥青是原油中最重部分,相对分子量最大,绝大多数重金属元素都集中在沥青质和胶质中,这些沥青胶质是一种憎水性有机胶凝材料,构造致密,有良好的隔潮、防水、耐磨、耐腐蚀性能。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,所说的十二烷基三甲基氯化铵,可溶于水和乙醇。它的化学稳定性良好,耐热、耐光、耐压、耐强酸强碱,它还具有优良的渗透性、乳化性、柔软性。可利用它的乳化性生产建筑防水涂料乳化剂,广泛应用于沥青乳化及防水涂料乳化,泥浆乳化中。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,天然矿物膨润土、云母加有机活性剂三位一体,在有机活性剂的活动下,形成复合型的沥青溶胀剂,对石油沥青进行乳化,能将沥青质、胶质的紧密结构分子链打开,形成水包柔性的凝胶材料,并且,天然矿物质中的Si、Al分子覆盖了沥青质、胶质的分子,增加了沥青分子的活性,由憎水性物质转变成了亲水性的物质。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,所说的硅酸纳,在建筑行业中,广泛用于制造快干水泥、耐酸水泥防水剂、土壤固化剂、耐火材料等,因此,具有快干、防水、固化、耐火的作用。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,沥青中的沥青质、胶质及微量重金属是极佳的防水物质,天然矿物中的钾硅铝酸盐是天然的防水防腐材料,硅酸纳和矿物质的铝硅酸盐在沥青质的作用下形成了韧性、耐磨物质,醇类物质分子与水分子起到各类物质的分散作用,通过渗透结晶过程,能将这些物质顺利地渗透到水泥混凝土中,有效防水、耐磨,并且有韧性。
本发明前述的沥青基渗透结晶型水泥混凝土防水防腐剂,其制备方法是:
按前述各组分重量比例称量各组分,首先加氢氧化钠、膨润土、云母、常温水,浸泡2小时以上,再加十二烷基三甲基氯化铵,搅拌60分钟,再加温到100℃制成乳液待用;然后,将10#建筑沥青、60#道路石油沥青加温到200℃,进行脱水,再加入硅酸纳,搅拌30分钟,混合均匀制成沥青液待用;最后,将前述制成的待用乳液和沥青液用输送泵同时输入胶体磨中进行乳化,将乳化好的沥青输入储存罐中降温到25℃~5℃,加入乙醇搅拌1小时至均匀,形成本发明沥青基渗透结晶型水泥混凝土防水防腐剂产品。
本发明中,膨润土、云母的细度为200~300目。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,其优点在于:
(1)沥青胶质是一种憎水性有机胶凝材料,构造致密,有良好的隔潮、防水、耐磨、耐腐蚀性能;
(2)防水作用持久性,涂层即使遭受磨损或刮掉,也不影响其防水效果;
(3)沥青胶质是一种憎水性有机胶凝材料,构造致密,有良好的隔潮、防水、耐磨、耐腐蚀性能;
(4)通过渗透结晶过程,能将这些物质顺利地渗透到水泥混凝土中,渗透能力强,有效防水、耐磨,并且有韧性;
(5)由于防水、防潮,因此,不易腐蚀,使用寿命长。
本发明沥青基渗透结晶型水泥混凝土防水防腐剂,反复涂刷30#水泥混凝土板的面层上,在25℃的常温露天环境下干燥1小时后进行试验,结果表明:
(1)柔韧性:10℃,无裂纹、断裂;
(2)耐热度;80℃ 5h,无流淌、起泡和滑动;
(3)抗冻性:-20℃,无起泡、开裂、剥离;
(4)洒水进行检测,水滴呈现荷叶水珠状态;
(5)耐摩擦:200N压力下摩擦20000次无变化;
(6)抗渗性:钻孔5mm深,滴水6小时无渗透现象;
(7)耐酸:25℃,5%的H2SO4溶液侵泡15天无变化;
(8)耐碱:25℃,3%的NaOH溶液侵泡15天无变化;
(9)耐盐:25℃,3%的NaCl溶液侵泡15天无变化。
综上所述,本发明沥青基渗透结晶型水泥混凝土防水防腐剂,具有防水、防潮、防漏、防腐、有韧性、耐磨、使用寿命长的优点。
具体实施方式 本发明沥青基渗透结晶型水泥混凝土防水防腐剂,包括氢氧化钠、膨润土、云母、水、十二烷基三甲基氯化铵、10#建筑沥青、60#道路沥青、硅酸纳、乙醇;在具体实施过程中,各组分重量比为:
按照上述的比例与前述的制备方法,可以制备出性能要求略有差异且适合不同场合的沥青基渗透结晶型水泥混凝土防水防腐剂。
Claims (3)
1、一种沥青基渗透结晶型水泥混凝土防水防腐剂,其特征在于,包括氢氧化钠、膨润土、云母、水、十二烷基三甲基氯化铵、10#建筑沥青、60#道路沥青、硅酸纳、乙醇;各组分重量比为:
氢氧化钠 2~4; 膨润土 15~25;
云母 6~12; 水 55~65;
十二烷基三甲基氯化铵 8~12; 10#建筑沥青 25~35;
60#道路沥青 65~75; 硅酸纳 8~12;
乙醇 6~10。
2、根据权利要求1所述的沥青基渗透结晶型水泥混凝土防水防腐剂,其特征在于,各组分重量比为:
氢氧化钠 2~4; 膨润土 18~22;
云母 8~10; 水 60~62;
十二烷基三甲基氯化铵 9~11; 10#建筑沥青 30~32;
60#道路沥青 70~72; 硅酸纳 9~11;
乙醇 7~9。
3、一种权利要求1所述的沥青基渗透结晶型水泥混凝土防水防腐剂的制备方法,其特征在于,按各组分重量比例称量各组分,首先加氢氧化钠、膨润土、云母、常温水,浸泡2小时以上,再加十二烷基三甲基氯化铵,搅拌60分钟,再加温到100℃制成乳液待用;然后,将10#建筑沥青、60#道路石油沥青加温到200℃,进行脱水,再加入硅酸纳,搅拌30分钟,混合均匀制成沥青液待用;最后,将前述制成的待用乳液和沥青液用输送泵同时输入胶体磨中进行乳化,将乳化好的沥青输入储存罐中降温到25℃~5℃,加入乙醇搅拌1小时至均匀,形成本发明沥青基渗透结晶型水泥混凝土防水防腐剂产品。