CN101225236A - Composition used for polychloroethylene resin plasticizer and method of use thereof - Google Patents
Composition used for polychloroethylene resin plasticizer and method of use thereof Download PDFInfo
- Publication number
- CN101225236A CN101225236A CNA2007101922124A CN200710192212A CN101225236A CN 101225236 A CN101225236 A CN 101225236A CN A2007101922124 A CNA2007101922124 A CN A2007101922124A CN 200710192212 A CN200710192212 A CN 200710192212A CN 101225236 A CN101225236 A CN 101225236A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- chloride resin
- compound
- pvc
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a nontoxic plasticizer compound which can reduce the melt temperature of polyvinyl chloride resin, increase the softness of polyvinyl chloride resin and an application method of the plasticizer compound. The mass percentages of the components of the compound are 10 to 90 percent epoxy soybean oil and 10 to 90 percent alkyl pyrrolidone C12-C18. The content of compound as the plasticizer of the polyvinyl chloride resin in the polyvinyl chloride resin is 10 to 100 phr. The nontoxic plasticizer compound has the advantages that: when the compound is added into the polyvinyl chloride resin, the polyvinyl chloride resin has a performance of less than 100 Shore A hardness, the polyvinyl chloride resin with the compound is suitable for manufacturing calendering plates, plastisol, film, nominal tubes and tube fittings.
Description
Technical field
The present invention relates to a kind of composition as the polyvinyl chloride (PVC) RESINS softening agent, and the concrete using method of said composition during as softening agent.
Background technology
As everyone knows, some thermoplastic polymers commonly used have the second-order transition temperature (Tg) that is higher than room temperature, and below the temperature, polymkeric substance shows as the glazed brittle state of class at this, more than the temperature, then present bigger rebound resilience, snappiness and shock strength at this.Make polymkeric substance have practical value, its second-order transition temperature is dropped to below the use temperature.Softening agent is exactly an analog assistant of introducing in the polymkeric substance for addressing this problem.
Softening agent in the polyvinyl chloride (PVC) RESINS is to play plastification by the polar attraction power that reduces between the halogen atom in polymkeric substance interchain cohesive energy density(CED) and the polyvinyl chloride (PVC) RESINS.
At present, a large amount of organism has been in the news and has can be used as the softening agent of polyvinyl chloride (PVC) RESINS.Comprising Tetra hydro Phthalic anhydride and C
4-C
15Ester class, epoxy soybean oil, trimellitate, benzoate and citrate and halohydrocarbon etc. that Fatty Alcohol(C12-C14 and C12-C18) (straight or branched) reaction obtains.The high-molecular weight polyester that dibasic alcohol and hexanodioic acid or sebacic acid reaction obtain also is used as softening agent.In these softening agent, the most extensive with the use of phthalic ester plasticizer.Also there are some shortcomings in above-mentioned softening agent, if any carinogenicity arranged, cause endocrine regulation easily, bigger etc. to genotoxicity; The low-temperature pliability of resin, ductibility are good etc. after the use that has.
Summary of the invention
A technical problem to be solved by this invention is: will provide a kind of nontoxic, can reduce the polyvinyl chloride (PVC) RESINS melt temperature, improve the composition as the polyvinyl chloride (PVC) RESINS softening agent of polyvinyl chloride (PVC) RESINS flexibility, another problem that the present invention will solve is: the concrete using method that above-mentioned composition will be provided.
For solving above-mentioned first problem, the technical solution used in the present invention is: as containing mass percent in the composition of polyvinyl chloride (PVC) RESINS softening agent is 10~90% epoxy soybean oil, preferred 20~80%, especially preferred 20~60%; Contain 10~90% C in the composition
12-C
18Alkyl pyrrolidone, preferred 20~80%, especially preferred 40~80%.
For solving above-mentioned second problem, the technical solution used in the present invention is: the concrete using method of above-mentioned composition is: as the softening agent of polyvinyl chloride (PVC) RESINS, and the amount of said composition in polyvinyl chloride (PVC) RESINS is 10~100phr (with respect to the add-on of per hundred parts of resins), especially preferred 20~80phr.
Advantage of the present invention is: composition of the present invention has nontoxic, as to reduce polyvinyl chloride (PVC) RESINS melt temperature, raising polyvinyl chloride (PVC) RESINS flexibility advantage.After composition of the present invention added polyvinyl chloride (PVC) RESINS, can make polyvinyl chloride (PVC) RESINS have Shore A hardness less than 100 performance.Composition of the present invention can be used in polyvinyl chloride (PVC) RESINS separately or with one or more primary plasticizers or extender plasticizer, and these polyvinyl chloride (PVC) RESINS are fit to make calendering sheet material, plastisol, film, nominal pipe or tube members etc.
Embodiment
Below by specific embodiment the present invention is done to describe further, do not only limit to these embodiment but should not understand the present invention.
Embodiment 1
The prescription of the typical polyvinyl chloride (PVC) RESINS that provides according to the present invention such as following table 1,
Table 1
Proportioning (phr) | |||
Additive | 1 | 2 | 3 |
A | 100 | 100 | 100 |
Dioctyl phthalate (DOP) | 50 | ||
Epoxy soybean oil | 25 | 25 | |
The tetradecyl pyrrolidone | 25 | ||
The octadecyl pyrrolidone | 25 |
Annotate: A is that a kind of K value is 70 suspension PVC.
When adopting the mixture production calendering sheet material of various proportionings in the table 1, the calendering sheet material that has added epoxy soybean oil and alkyl pyrrolidone is more soft and transparent more than the calendering sheet material that has added dioctyl phthalate (DOP).The sheet material that has added the tetradecyl pyrrolidone is that plasticity-is best.
Embodiment 2
Provide the prescription of following table 2 according to the present invention,
Table 2
Proportioning (phr) | |||
Additive | 1 | 2 | 3 |
A | 100 | 100 | 100 |
Dioctyl phthalate (DOP) | 50 | ||
Epoxy soybean oil | 5 | 45 | |
Dodecyl pyrrolidone | 45 | 5 |
Annotate: A is that a kind of K value is 70 suspension PVC.
When adopting the mixture production calendering sheet material of various proportionings in the table 2, the calendering sheet material that has added epoxy soybean oil and alkyl pyrrolidone is more soft and transparent more than the calendering sheet material that has added dioctyl phthalate (DOP).The plasticity-that contains the composition of 10% epoxy soybean oil is best.
Embodiment 3
Provide the prescription of following table 3 according to the present invention,
Table 3
Proportioning (phr) | ||||
Additive | 1 | 2 | 3 | 4 |
B | 100 | 100 | 100 | 100 |
Dioctyl phthalate (DOP) | 80 | |||
Epoxy soybean oil | 5 | 20 | 45 | |
The tetradecyl pyrrolidone | 5 | 20 | 45 | |
The Ca/Zn stablizer | 2.5 | 2.5 | 2.5 | 2.5 |
Annotate: B is that a kind of K value is 71 suspension PVC.
All adopted 200 ℃ temperature when sheet material is rolled in the mixture production of various proportionings in the employing table 3, the former capital has added the Ca/Zn stablizer.
The calendering sheet material that the mixture production of various proportionings obtains in the employing table 3 is determined Shore A hardness, as shown in table 4 below, by table 4 as can be seen, add the 40phr composition and can obtain identical Shore A hardness with interpolation 80phr dioctyl phthalate (DOP), just the neighbour easier polyvinyl chloride (PVC) RESINS that makes of dioctyl phthalate of composition reaches required plasticized condition.
Table 4
The experiment batch | Shore A hardness * |
1 | 75 |
2 | 97 |
3 | 75 |
4 | 42 |
Annotate: testing method is GB2411-1980
Claims (5)
1. as the composition of polyvinyl chloride (PVC) RESINS softening agent, it is characterized in that: contain mass percent in the described composition and be 10~90% epoxy soybean oil, mass percent is 10~90% C
12-C
18Alkyl pyrrolidone.
2. composition according to claim 1 is characterized in that: contain mass percent in the described composition and be 20~80% epoxy soybean oil, 20~80% C
12-C
18Alkyl pyrrolidone.
3. composition according to claim 1 is characterized in that: contain mass percent in the described composition and be 20~60% epoxy soybean oil, 40~80% C
12-C
18Alkyl pyrrolidone.
4. according to the using method of claim 1,2 or 3 described compositions, it is characterized in that: described composition is as the softening agent of polyvinyl chloride (PVC) RESINS, and the amount of said composition in polyvinyl chloride (PVC) RESINS is 10~100phr.
5. the using method of composition according to claim 4, it is characterized in that: the amount of described composition in polyvinyl chloride (PVC) RESINS is 20~80phr.