CN101177785B - 镀锌钝化液及制备方法 - Google Patents

镀锌钝化液及制备方法 Download PDF

Info

Publication number
CN101177785B
CN101177785B CN2007100930725A CN200710093072A CN101177785B CN 101177785 B CN101177785 B CN 101177785B CN 2007100930725 A CN2007100930725 A CN 2007100930725A CN 200710093072 A CN200710093072 A CN 200710093072A CN 101177785 B CN101177785 B CN 101177785B
Authority
CN
China
Prior art keywords
solution
zinc
nitric acid
plated
galvanization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2007100930725A
Other languages
English (en)
Other versions
CN101177785A (zh
Inventor
蒲小琴
李晓懿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING CONSTRUCTION ELECTROMECHANICAL CO., LTD.
Original Assignee
Chongqing Jianshe Motorcycle Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Jianshe Motorcycle Co Ltd filed Critical Chongqing Jianshe Motorcycle Co Ltd
Priority to CN2007100930725A priority Critical patent/CN101177785B/zh
Publication of CN101177785A publication Critical patent/CN101177785A/zh
Application granted granted Critical
Publication of CN101177785B publication Critical patent/CN101177785B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种镀锌钝化液及制备方法，所述镀锌钝化液的组成为(每升水中所含试剂的量)镀锌彩色钝膜粉8～24克；硝酸5～15毫升。取镀锌彩色钝膜粉8～24克，加少量水溶解，再加入硝酸5～15毫升，搅拌后加水至1升，调整溶液的pH值为1.0～3.8即得到镀锌钝化液。本发明所述镀锌钝化液中的六价铬的含量非常低，清洗液可以直接排放，钝化液稳定，对操作人员身体没有危害。使用本钝化液对镀锌后的金属制品进行表面处理，其金属制品耐腐蚀性好，抗变色能力强。

Description

镀锌钝化液及制备方法
技术领域
本发明涉及一种金属钝化液，特别涉及一种彩色镀锌钝化液及其制备方法。
背景技术
金属制件的合金层或镀锌层常需要对其表面进行钝化处理，以增加耐腐蚀性和装饰性。目前采用的方法是用铬酐、硫酸和硝酸对合金层或镀锌层的表面进行钝化处理。这种方法所用的铬酐、硫酸和硝酸三酸钝化液，虽然有镀层质感膜层厚实、颜色艳丽的优点，但由于铬酸消耗大，清洗水中的有毒的六价铬含量高，不能直接排放，并且污水处理困难。由于铬酸的挥发性强，挥发气体中六价铬的毒性，对操作人员的身体健康有危害，同时用三酸钝化液在金属表面形成的钝化膜的防腐性能和抗色变能力差。
发明内容
本发明的目的提供一种镀锌钝化液和制备方法。使用本钝化液进行表面处理的金属制品耐腐蚀性好，抗变色能力强，金属表面得到一种蓝白色钝化膜。它可以使钝化液中的六价铬的含量非常低，清洗液可以直接排放，并且钝化液稳定，对操作人员身体没有危害
为达上述目的，本发明镀锌钝化液的组成为(每升水中所含试剂的量)：镀锌彩色钝膜粉8～24克；62％的硝酸5～15毫升。
上述各组分含量较好的为(每升水中所含试剂的量)：镀锌彩色钝膜粉12～20克；62％的硝酸8～10毫升。
制备镀锌钝化液的方法，取镀锌彩色钝膜粉8～24克，加少量水溶解，再加入62％的硝酸5～15毫升，搅拌后加水至1升，调整溶液的PH值为1.0～3.8即得到镀锌钝化液。
上述所用试剂：镀锌彩色钝膜粉采用福州八达表面工程技术研究所生产的型号为FK-400的同名产品，硝酸采用市售的化学纯或工业纯均可。
本发明所述金属制件为用普通钢铁材料制作的金属制件，如套筒扳手、摩托车的随车工具、摩托车指示片、垫圈、双头螺栓、摩托车后轮轴、摩托车前轮轴等。
本发明由于镀锌彩色钝膜粉的主要成分是铬酐和三氯化铬，而其中铬酐含量非常低，为4克/升左右，因此钝化后的清洗液中六价铬的含量低于国家标准0.5mg/l，可以直接排放而不会污染环境。又由于镀锌彩色钝膜粉中挥发性的六价铬含量低，因此对操作人员身体没有危害。另外，钝化后的镀锌制品经封闭后，钝化膜的孔隙率降低，金属制品表面不易产生电化学腐蚀，有耐腐蚀性好，抗变色能力强的特点。
下面通过实施例对本发明做进一步的说明。但本发明不仅限于这些例子。
具体实施方式
实施例1
配置镀锌钝化液：在常温常压下，取FK-400镀锌彩色钝膜粉9克，加少量水溶解，再加入62％的硝酸6毫升，搅拌后加水至1升，调整溶液的PH值为1.0-3.8即得到镀锌钝化液。
将镀锌后的摩托车后臂转轴放入稀HNO3或HNO3-HCl溶液中，待镀锌后的摩托车后臂转轴表面光亮，停留片刻，取出用清水清洗后，浸于上述镀锌钝化液中浸放20～65秒，取出，经水洗、烫干、封闭(用0.5％的铬酐，温度在50-70℃溶液中浸0.5-1分钟封闭)、烘干，即使金属表面得到颜色艳丽如彩虹的七彩钝化膜。
实施例2
配置镀锌钝化液：在常温常压下，取FK-400镀锌彩色钝膜粉11克，加少量水溶解，再加入62％的硝酸8毫升，搅拌后加水至1升，测定溶液的PH值为1.0-3.8即得到镀锌钝化液。
将镀锌后的垫片放入稀HNO3或HNO3-HCl溶液中，待镀锌后的垫片表面光亮，停留片刻，取出用清水清洗后，浸于上述镀锌钝化液中浸放20～65秒，取出，经水洗、烫干、封闭、烘干，即使金属表面得到一种彩色钝化膜。
实施例3
配置镀锌钝化液：在常温常压下，取FK-400镀锌彩色钝膜粉14克，加少量水溶解，再加入62％的硝酸10毫升，搅拌后加水至1升，调整溶液的PH值为1.0-3.8即得到镀锌钝化液。
将镀锌后的双头螺栓放入稀HNO3或HNO3-HCl溶液中，待镀锌后的双头螺栓表面光亮，停留片刻，取出用清水清洗后将出光清洗后，浸于上述镀锌钝化液中浸放20～65秒，取出，经水洗、烫干、封闭(用0.5％的铬酐，温度在50-70℃溶液中浸0.5-1分钟封闭)、烘干，即使金属表面得到一种彩色钝化膜。
实施例4
配置镀锌钝化液：在常温常压下，取FK-400镀锌彩色钝膜粉18克，加少量水溶解，再加入62％的硝酸12毫升，搅拌后加水至1升，调整溶液的PH值为1.0-3.8即得到镀锌钝化液。
将镀锌后的摩托车后轮轴放入稀HNO3或HNO3-HCl溶液中，待镀锌后的摩托车后轮轴表面光亮，停留片刻，取出用清水清洗后将出光清洗后，浸于上述镀锌钝化液中浸放20～65秒，取出，经水洗、烫干、封闭(用0.5％的铬酐，温度在50-70℃溶液中浸0.5-1分钟封闭)、烘干，即使金属表面得到一种彩色钝化膜。
实施例5
配置镀锌钝化液：在常温常压下，取FK-400镀锌彩色钝膜粉24克，加少量水溶解，再加入62％的硝酸15毫升，搅拌后加水至1升，调整溶液的PH值为1.0-3.8即得到镀锌钝化液。
将镀锌后的套筒放入稀HNO3或HNO3-HCl溶液中，待镀锌后的套筒表面光亮，停留片刻，取出用清水清洗后将扳手出光清洗后，浸于上述镀锌钝化液中浸放20～65秒，取出，经水洗、烫干、封闭(用0.5％的铬酐，温度在50～70℃溶液中浸0.5-1分钟封闭)、烘干，即使金属表面得到一种彩色钝化膜。

Claims (2)

1.一种镀锌钝化液，其特征在于：所述镀锌钝化液的组成为镀锌彩色钝膜粉和硝酸，其中每升水中所含试剂的含量为：
镀锌彩色钝膜粉  12～20克；
硝酸            8～10毫升；
所述硝酸的浓度为62％。
2.制备如权利要求1所述镀锌钝化液的方法，其特征在于：取镀锌彩色钝膜粉12～20克，加少量水溶解，再加入浓度为62％硝酸8～10毫升，搅拌后加水至1升，调整溶液的pH值为1.0～3.8即得到镀锌钝化液。
CN2007100930725A 2007-11-29 2007-11-29 镀锌钝化液及制备方法 Expired - Fee Related CN101177785B (zh)