CN101169384A - 化学纤维长丝热收缩率试验方法标准 - Google Patents

化学纤维长丝热收缩率试验方法标准 Download PDF

Info

Publication number
CN101169384A
CN101169384A CNA2007101340706A CN200710134070A CN101169384A CN 101169384 A CN101169384 A CN 101169384A CN A2007101340706 A CNA2007101340706 A CN A2007101340706A CN 200710134070 A CN200710134070 A CN 200710134070A CN 101169384 A CN101169384 A CN 101169384A
Authority
CN
China
Prior art keywords
thermal treatment
standard
long filament
testing
chemical fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007101340706A
Other languages
English (en)
Inventor
程前
辛婷芬
师百同
吴爱民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Shenghong Chemical Fiber Co Ltd
Original Assignee
Jiangsu Shenghong Chemical Fiber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Shenghong Chemical Fiber Co Ltd filed Critical Jiangsu Shenghong Chemical Fiber Co Ltd
Priority to CNA2007101340706A priority Critical patent/CN101169384A/zh
Publication of CN101169384A publication Critical patent/CN101169384A/zh
Pending legal-status Critical Current

Abstract

本发明方案提供一种化学纤维长丝热收缩率试验方法标准，适用范围扩大到粘胶纤维(纤维素纤维类)长丝，已经超出了合成纤维的范畴，所以名称改为“化学纤维长丝热收缩率试验方法”；增加了煮沸时试样包布方法：纱布法；增加沸水收缩率实验方法：仪器法，仪器法测热收缩率，由计算机控制，可以自动连续测试多个试样，可自动调节标准张力，并能自动计算结果；试样平衡时间改为涤纶热处理前平衡4h以上，热处理后平衡12h以上，锦纶热处理前平衡12h以上，热处理后平衡12h以上。仪器法测热收缩率，其测试精度高，误差较小，操作方便，快速高效。

Description

化学纤维长丝热收缩率试验方法标准
技术领域
本发明涉及一种化学纤维试验方法标准，尤其是一种化学纤维长丝热收缩率试验方法标准。
背景技术
热收缩率是化学纤维长丝的品质之一，是反映长丝热定型程度和尺寸稳定性的一项指标，且与染色性能有一定的关系，而染色均匀性是涤纶长丝必须具备的性能，我们要求每个筒子的染色性能一样，否则织成织物后会有色差。基于这些原因，如何准确获得热收缩率，试验方法尤为重要。由于近几年来纺织行业发展的较快，一些好的、先进的试验方法不断涌现。为了保持标准的先进性和适用性，进一步提高标准技术水平，确定了以2001标准为基础，采用国际化学标准化局(简称BISFA)制订的《涤纶长丝国际商定试验方法》(1995年版)和《锦纶长丝试验方法》(1995年版)等标准中的热收缩率试验方法对适用范围和试验方法部分进行修订。
发明内容
本发明的任务是：提供一种化学纤维长丝热收缩率试验方法标准，来适应纺织行业较快的发展。
本发明技术构成如下：
一种化学纤维长丝热收缩率试验方法标准，是反映长丝热定型程度和尺寸稳定性的一项指标，为了使标准的通用性更强，适用范围扩大到粘胶纤维(纤维素纤维类)长丝，已经超出了合成纤维的范畴，所以将《合成纤维长丝热收缩率试验方法》改为《化学纤维长丝热收缩率试验方法》；增加了煮沸时试样包布方法：纱布法；增加沸水收缩率实验方法：仪器法，仪器法测热收缩率，由计算机控制，可以自动连续测试多个试样，可自动调节标准张力，并能自动计算结果；预张力的说明，仪器法测热收缩率是固定预张力改变绞丝圈数，绞丝
Figure S2007101340706D00021
(注：根据2001标准中绞丝圈数的确定)仪器的预张力重锤＝绞丝总线密度×标准预张力，绞丝总线密度按GB/T6506-2001规定执行，一般为2500dtex，因为本标准仅适用于牵伸丝，标准预张力为(0.05±0.005)cN/dtex，所以仪器的预张力重锤是固定值125cN；试样平衡时间由原来涤纶热处理前平衡2h以上，热处理后平衡2h以上，锦纶热处理前平衡3h以上，热处理后平衡4h以上改为涤纶热处理前平衡4h以上，热处理后平衡12h以上，锦纶热处理前平衡12h以上，热处理后平衡12h以上。
这样相对于原来的进步效果是：通用性更强，适用范围扩大到粘胶纤维(纤维素纤维类)长丝，仪器法测热收缩率，其测试精度高，误差较小，操作方便，快速高效。
具体实施方式
在具体实施过程中，四个规格牵伸丝在热处理时加2.5cN砝码和不加张力的对比试验数据(注：Lo-热处理前长度；Ls-热处理后长度；S-热收缩率；)
加2.5cN砝码的情况下
Figure S2007101340706D00022
不加张力的情况下
通过以上的试验结果可以看出，加不加2.5cN砝码对测试结果没有影响。
本次重复性试验是由同一个操作者、用同一台仪器对规格为55dtex/24f、45dtex/24f的进行试验的结果。
规格     次数   Lo(mm)   Lo(mm)   S(％)  规格     次数   Lo(mm)   Lo(mm)   S(％)
55dtex/24f     1   990.3   917.2   7.38  45dtex/24f     1   991.8   926.0   6.63
    2   992.8   919.4   7.40     2   990.5   924.5   6.66
    3   993.9   920.8   7.36     3   990.3   924.4   6.66
    4   994.2   920.9   7.38     4   990.4   924.3   6.68
    5   994.9   922.1   7.32     5   989.0   922.7   6.70
    6   995.0   922.1   7.32     6   988.7   922.4   6.71
    7   993.3   921.0   7.28     7   986.7   921.0   6.66
    8   996.6   923.9   7.29     8   985.3   919.4   6.70
9   995.1   922.6   7.28 9 985.9  920.3  6.66
10   996.7   924.1   7.29 10 986.9  921.0  6.68
最大值   996.7   924.1   7.40 最大值 991.8  926.0  6.71
最小值   990.3   917.2   7.28 最小值 985.3  919.4  6.63
平均值   994.3   922.4   7.33 平均值 988.6  922.6  6.67
标准差   1.88   2.06   0.05 标准差 2.23  2.16  0.02
从以上数据可以看出，该试验方法的重复性非常好。
甲、乙、丙三名操作者，同一台仪器对三种规格的同一批样品的测试结果。
规格 样品编号     甲     乙     丙 相对误差％
    S(％)     S(％)     S(％)
    167dtex/98f     1     7.53     7.64     7.60     0.7
83dtex/36f     2     7.14     7.24     7.11     0.9
    3     7.43     7.60     7.99     3.7
55dtex/72f     4     6.97     7.31     7.38     2.8
    5     7.26     6.82     6.98     3.2
从试验结果可以看出，仪器测试热收缩率的误差较小。

Claims (4)

1.一种化学纤维长丝热收缩率试验方法标准，其特征是一种反映长丝热定型程度和尺寸稳定性的指标，为了使标准的通用性更强，适用范围扩大到粘胶纤维(纤维素纤维类)长丝，已经超出了合成纤维，将《合成纤维长丝热收缩率试验方法》改为《化学纤维长丝热收缩率试验方法》。
2.如权利要求1所述的方法标准，其特征在于增加了煮沸时试样包布方法纱布法。
3.如权利要求1所述的方法标准，其特征在于增加沸水收缩率实验方法仪器法，仪器法测热收缩率，由计算机控制，可以自动连续测试多个试样，可自动调节标准张力，并能自动计算结果。
4.如权利要求1所述的方法标准，其特征在于试样平衡时间由原来涤纶热处理前平衡2h以上，热处理后平衡2h以上，锦纶热处理前平衡3h以上，热处理后平衡4h以上改为涤纶热处理前平衡4h以上，热处理后平衡12h以上，锦纶热处理前平衡12h以上，热处理后平衡12h以上。
CNA2007101340706A 2007-10-18 2007-10-18 化学纤维长丝热收缩率试验方法标准 Pending CN101169384A (zh)