CN101168637A - Water highlight high conglutination-resistance printing gloss oil and its preparation method and application - Google Patents
Water highlight high conglutination-resistance printing gloss oil and its preparation method and application Download PDFInfo
- Publication number
- CN101168637A CN101168637A CNA2006101229117A CN200610122911A CN101168637A CN 101168637 A CN101168637 A CN 101168637A CN A2006101229117 A CNA2006101229117 A CN A2006101229117A CN 200610122911 A CN200610122911 A CN 200610122911A CN 101168637 A CN101168637 A CN 101168637A
- Authority
- CN
- China
- Prior art keywords
- water
- wax
- resin liquid
- acrylate resin
- conglutination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides water-based high gloss and high anti-adhesion printing clean oil, which relates to a printing coating mainly used for the paper printing. The invention chooses styrene-acrylate core/shell latex and soft/hard acrylic resin emulsion to be matched mutually. The core in the styrene-acrylate core/shell latex and the soft acrylic resin emulsion endow with good film forming performance to the water-based clean oil, thereby improving the evenness and the brightness of the print; the shell in the styrene-acrylate core/shell latex and the hard acrylic resin emulsion endow with good high temperature resistant performance and good waterproof performance after the water-based clean oil forms a film, thereby improving the anti-adhesion of the print, thus, under the circumstance of adding a small amount of wax powder wax emulsion and other accessory ingredient, the effects of the brightness and the anti-adhesion of the print printed with the prepared water-based clean oil are both good.
Description
Technical field:
The present invention relates to a kind of water high light, high conglutination-resistance printing gloss oil and preparation method thereof and application.
Background technology:
The luminance brightness of printed matter and resistance to blocking are two important indicators of check brightening water-based oil for printing quality quality.Be that (for example: wax powder, wax emulsion etc.) percentage composition increases the luminance brightness of printing back printed matter by increasing high photopolymer resin or reduction delustring auxiliary agent when preparing brightening water-based oil for printing usually; The raising of printed matter resistance to blocking then is to realize by means of the wax powder of water resistant, high temperature resistant or wax liquid, and the wax powder or the wax liquid that add in the preparation of brightening water-based oil for printing are many more, and the resistance to blocking of printed matter is good more.So printed matter luminance brightness and resistance to blocking are two conflicting indexs, be difficult to allow these two indexs of printed matter reach best simultaneously according to the compound method of the brightening water-based oil for printing of routine.
Summary of the invention:
The objective of the invention is to overcome the defective that prior art exists, a kind of water high light, high conglutination-resistance printing gloss oil are provided.The present invention is by using the benzene emulsion of nucleocapsid structure and the interworking of soft or hard acrylate resin liquid earlier, make that under the situation of adding auxiliary agents such as a spot of wax powder or wax emulsion, the luminance brightness and the resistance to blocking of printed matter reach good effect simultaneously after the brightening water-based oil for printing printing that preparation is come out.
Another object of the present invention is to provide the preparation method of a kind of water high light, high conglutination-resistance printing gloss oil.
A further object of the invention is water high light, high conglutination-resistance printing gloss oil are applied to print field.
For achieving the above object, the present invention is achieved by the following technical solutions:
Water high light of the present invention, high conglutination-resistance printing gloss oil are selected the benzene emulsion of nucleocapsid structure for use, nuclear mainly is made up of Tg lower butyl acrylate and ethyl propenoate, it gives brightening water-based oil for printing good film forming properties, improves the smoothness and the luminance brightness of printed matter; Shell mainly is made up of Tg higher methyl methacrylate and vinylbenzene, and they give good high temperature resistant and water resistance after the brightening water-based oil for printing film forming, promptly improves the resistance to blocking of printed matter.
The interworking of soft or hard acrylate resin liquid is to select the acrylate resin liquid of a kind of high Tg and a kind of low Tg for use, and interworking is used in accordance with the appropriate ratio.High Tg acrylate resin liquid to the contribution of brightening water-based oil for printing with the shell in the nucleocapsid benzene emulsion; Low Tg acrylate resin liquid to the contribution of brightening water-based oil for printing with the nuclear in the nucleocapsid benzene emulsion.
Water high light, its component of high conglutination-resistance printing gloss oil and weight percent are as follows:
Composition quality percentage composition (%)
Nucleocapsid benzene emulsion 20～80
High Tg acrylate resin liquid 10～60
Low Tg acrylate resin liquid 10～60
Poly-tetrafluoro modification polyhexene wax 0.2～2
Moistening temperature agent 0.5～3.5
Flow agent 0.2～1.5
Surface slip agent 0.15～0.5
Defoamer 0.1～2
Wax emulsion 1～10
Water 1～10.
It is to be noted:
High and low Tg acrylate resin liquid all is water soluble resin liquid, and the Tg of high Tg acrylate resin can be 90～110 ℃, and the Tg of low Tg acrylate resin liquid can be 60～80 ℃;
Moistening temperature agent, flow agent and surface slip agent can be polyether-modified polysiloxane compounds;
Defoamer can be mineral oils or silicoorganic compound;
The wax emulsion can be the water dispersion of poly-tetrafluoro modification polyhexene wax or polyethylene wax, and the quality percentage composition of wax can be 20～40%;
Water can be deionized water.
The preparation technology of water high light, high conglutination-resistance printing gloss oil is as follows:
(1), high Tg acrylate resin liquid and low Tg acrylate resin liquid are added in the agitator by a certain percentage, mix, add poly-tetrafluoro modification polyhexene wax and moistening temperature agent, stirring velocity is transferred to 700 rev/mins, stirred two hours.
(2), then add flow agent, surface slip agent and wax emulsion successively, this moment, stirring velocity transferred to 300 rev/mins, stirred half hour.
(3), nucleocapsid benzene emulsion and defoamer are successively added in the above-mentioned resin liquid, stirred one hour.
(4), last water is regulated viscosity to 25～60 second (Cha Shi 4# cup, 25 ℃).
(5), filter packing with 200 order nylon net bags.
Compared with prior art, the present invention has following beneficial effect:
Water high light of the present invention, high conglutination-resistance printing gloss oil are selected the benzene emulsion of nucleocapsid structure for use, nuclear mainly is made up of Tg lower butyl acrylate and ethyl propenoate, it gives brightening water-based oil for printing good film forming properties, improves the smoothness and the luminance brightness of printed matter; Shell mainly is made up of Tg higher methyl methacrylate and vinylbenzene, and they give good high temperature resistant and water resistance after the brightening water-based oil for printing film forming, promptly improves the resistance to blocking of printed matter.
Embodiment:
Below come by specific embodiment that the invention will be further described.
Embodiment 1:
Composition weight percent content (%)
Nucleocapsid benzene emulsion (solid content 50%) 50
High Tg acrylate resin liquid (solid content 35%) 25
Low Tg acrylate resin liquid (solid content 45%) 15
Poly-tetrafluoro modification polyhexene wax 0.5
Moistening temperature agent 2.5
Flow agent 0.3
Surface slip agent 0.2
Defoamer 1.5
Wax emulsion 2
Water 3.
Embodiment 2:
Composition weight percent content (%)
Nucleocapsid benzene emulsion (solid content 50%) 30
High Tg acrylate resin liquid (solid content 35%) 38
Low Tg acrylate resin liquid (solid content 45%) 20
Poly-tetrafluoro modification polyhexene wax 0.2
Moistening temperature agent 1
Flow agent 0.2
Surface slip agent 0.4
Defoamer 1
Wax emulsion 5
Water 4.2.
Wherein, the various additives that used among the embodiment 1 and 2 are all those skilled in the art to be familiar with, and can choose according to concrete needs.
Claims (9)
1. a water high light, high conglutination-resistance printing gloss oil, it is characterized in that: by weight percentage, it comprises the material of following component:
Nucleocapsid benzene emulsion 20～80%
High Tg acrylate resin liquid 10～60%
Low Tg acrylate resin liquid 10～60%
Poly-tetrafluoro modification polyhexene wax 0.2～2%
Wetting agent 0.5～3.5%
Flow agent 0.2～1.5%
Surface slip agent 0.15～0.5%
Defoamer 0.1～2%
Wax emulsion 1～10%
Water 1～10%.
2. a kind of water high light as claimed in claim 1, high conglutination-resistance printing gloss oil, it is characterized in that described benzene emulsion has nucleocapsid structure, wherein, the main component of nuclear is butyl acrylate or ethyl propenoate, and the major ingredient of shell is methyl methacrylate or vinylbenzene.
3. a kind of water high light as claimed in claim 1, high conglutination-resistance oil polish is characterized in that described high Tg acrylate resin liquid and low Tg acrylate resin liquid are water soluble acrylate resin's liquid; The Tg of wherein high Tg acrylate resin liquid is 90～110 ℃, and the Tg of low Tg acrylate resin liquid is 60～80 ℃.
4. a kind of water high light as claimed in claim 1, high conglutination-resistance printing gloss oil is characterized in that described wetting agent, flow agent, surface slip agent are all polyether-modified polysiloxane compounds.
5. a kind of water high light as claimed in claim 1, high conglutination-resistance printing gloss oil is characterized in that defoamer is mineral oils or silicoorganic compound.
6. a kind of water high light as claimed in claim 1, high conglutination-resistance printing gloss oil is characterized in that the water dispersion of wax emulsion for poly-tetrafluoro modification polyhexene wax or polyethylene wax, and the quality percentage composition of wax is 20～40%.
7. a kind of water high light as claimed in claim 1, high conglutination-resistance printing gloss oil is characterized in that described water is deionized water.
8. the preparation method of the described water high light of claim 1, high conglutination-resistance printing gloss oil is characterized in that comprising successively following operation:
(1) high Tg acrylate resin liquid and low Tg acrylate resin liquid are pressed in the formula rate adding agitator, mixed; Add poly-tetrafluoro modification polyhexene wax and wetting agent, stirring velocity is transferred to 700 rev/mins, stirred two hours;
(2) add the flow agent of formula ratio then successively, surface slip agent and wax emulsion; Stirring velocity transfers to 300 rev/mins, stirs half hour;
(3) nucleocapsid benzene emulsion and the defoamer with formula ratio successively adds in the above-mentioned resin liquid, stirs one hour;
(4) last water is regulated viscosity to 25～60 second;
(5) filter packing with 200 order nylon net bags.
9. the described water high light of claim 1, the application of high conglutination-resistance printing gloss oil on print field.