CN101134326A - Fireproof and waterproof composite board - Google Patents
Fireproof and waterproof composite board Download PDFInfo
- Publication number
- CN101134326A CN101134326A CNA200710131851XA CN200710131851A CN101134326A CN 101134326 A CN101134326 A CN 101134326A CN A200710131851X A CNA200710131851X A CN A200710131851XA CN 200710131851 A CN200710131851 A CN 200710131851A CN 101134326 A CN101134326 A CN 101134326A
- Authority
- CN
- China
- Prior art keywords
- board
- plate
- fireproof
- minutes
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fireproof and waterproof composite board with a magnesium oxide board layer. The composite board is formed by compounding a composite layer board with good fireproof and waterproof performance on a wooden base material board; the fireproof waterproof composite board is a magnesium oxide glass fiber board produced by taking magnesium oxide and glass fiber as main raw materials, and the substrate board of the board is as follows: plywood, multiply wood, shaving board and wood-based plate, the adhesive that this board chooseed for use is: resin glue, foaming glue, all-purpose glue and super glue; the process comprises the following steps: coating an adhesive between the magnesium oxide glass fiber board and the substrate board thereof, and then pressing to obtain the magnesium oxide glass fiber board; the fireproof and waterproof composite board has simpler structure and process; the composite board has the advantages of good fireproof and waterproof performance, high strength, impact resistance, environmental protection and no pollution.
Description
Technical field
The present invention relates to have a kind of fireproof and waterproof composite board of magnesia flaggy.
Background technology
At present, wood-based plate, glued board performance of a great variety are different, but because this kind sheet material constitutes by wood materials, tend to occur the drawback of fire-proof and water-proof poor-performing, in order to improve the performance of its fire-proof and water-proof, though each producer also progressively released the composite plate that some have the fire-proof and water-proof performance, its performance is all not ideal enough, at present, also there is not very good solution.
Summary of the invention
In order to solve present composite wood board fire prevention, the relatively poor problem of water resistance, the invention provides a kind of fireproof and waterproof composite board, though this composite plate structure and technology are all fairly simple, but its fire prevention, water resistance are fairly good, can adapt to the place that fire prevention, water resistance have relatively high expectations and use.
The present invention solves the concrete scheme that its technical problem adopts: this composite plate is having fire prevention, composite layered plate that water resistance is good, being compounded on the wooden base material flaggy formation fireproof and waterproof composite board; It is characterized in that: this fire-proof and water-proof composite layered plate 1 is the magnesia glass fiberboard that primary raw material is produced for magnesia and glass fibre, and its thickness is selected 1mm～40mm as requested for use; The backing material plate 3 of this plate is glued board, multi-layer sheet, particieboard and wood-based plate, and its thickness is selected 1mm～40mm for use; The adhesive 2 that this plate is selected for use is resin glue, foamed glue, all-purpose adhesive and seccotine; Its technology is: between magnesia glass fiberboard and its backing material plate, adhesive 2 on the coated, and pressing forms then; Its press pressure is: 1 kilograms per centimeter, 2～10 kilograms per centimeter 2, its hot pressing temperature is: 20 ℃～200 ℃, its hot pressing time is: 3 minutes～360 minutes, pressing under normal temperature condition: pressure was: 1 kilograms per centimeter, 2～10 kilograms per centimeter 2, and hot pressing time is: finished in 3 minutes～360 minutes; 5 finish taking-up after, dispatch from the factory through sanding, shaping, check, packing.
Its beneficial effect is: this fire prevention, waterproof composite board plate, and its structure and technology are all fairly simple; Its fire-proof and water-proof performance is fairly good, and this composite plate intensity is higher, impact resistance, and also very environmental protection is without any pollution.
Description of drawings
The invention will be further described below in conjunction with drawings and the embodiments;
Accompanying drawing is a structural principle schematic diagram of the present invention;
Among the figure, 1 composite layered plate, 2 adhesives, 3 backing material plates.
Specific embodiment
Embodiment 1
Claims (3)
1. fireproof and waterproof composite board, this composite plate are the composite layered plate (1) with fire prevention, water resistance, are compounded on the backing material plate (3) of wood materials; It is characterized in that: the composite layered plate of this plate (1) is the magnesia glass fiberboard, and its thickness is selected 1mm～40mm for use; The backing material plate of this plate (3) is glued board, multi-layer sheet, particieboard and wood-based plate, and its thickness is selected 1mm～40mm for use; The adhesive that this plate is selected for use (2) is: resin glue, foamed glue, all-purpose adhesive and seccotine; Its technology is: between magnesia glass fiberboard and its backing material plate (3), and adhesive on the coated (2), pressing forms then; Its press pressure is: 1 kilograms per centimeter
2～10 kilograms per centimeter
2, its hot pressing temperature is: 20 ℃～200 ℃, its hot pressing time is: 3 minutes～360 minutes; Pressing under normal temperature condition: pressure is: 1 kilograms per centimeter
2～10 kilograms per centimeter
2, hot pressing time is: 3 minutes～360 minutes; Moulding is dispatched from the factory through sanding, shaping, check, packing after taking out.
2. a kind of fireproof and waterproof composite board according to claim 1, it is characterized in that: backing material plate (3) is selected one of the multi-layer sheet of 1220mm * 2440mm * 18mm for use, composite layered plate (1) is selected the thick magnesia glass fiberboard of 3.5mm for use, and adhesive (2) is selected phenolic resin glue for use: 0.5 kilogram, and flour: 015 kilogram, mutually after the blending, be evenly coated on the backing material plate (3) with glue spreader, spread magnesia glass fiberboard plate, precompressed 18 minutes, put into hot press hot pressing then, pressure is: 8 kilograms per centimeter
2, hot pressing temperature is 140 ℃, and the time is 30 minutes, and take out the back, through sanding, shaping, packing, promptly finishes one of the fireproof and waterproof composite board of 1220mm * 2440mm * 20mm.
3. a kind of fireproof and waterproof composite board according to claim 1, it is characterized in that: backing material plate (3) is selected one of the multi-plywood of 1220mm * 2440mm * 15mm for use, the magnesia glass fiberboard of the thick 3mm of composite layered plate (1) adapted, temperature is a normal temperature, adhesive (2) is selected foamed glue for use: 1 kilogram/open pressing pressure: 3 kilograms per centimeter
2, the press time: 40 minutes, after the taking-up, sanding, shaping, packing, one of the fireproof and waterproof composite board of formation 1220mm * 2440mm * 18mm.