CN101125994B - 一种机械装备环保耐酸防腐涂料 - Google Patents

一种机械装备环保耐酸防腐涂料 Download PDF

Info

Publication number
CN101125994B
CN101125994B CN2007101498921A CN200710149892A CN101125994B CN 101125994 B CN101125994 B CN 101125994B CN 2007101498921 A CN2007101498921 A CN 2007101498921A CN 200710149892 A CN200710149892 A CN 200710149892A CN 101125994 B CN101125994 B CN 101125994B
Authority
CN
China
Prior art keywords
shares
parts
mechanical equipment
acid
environmental protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2007101498921A
Other languages
English (en)
Other versions
CN101125994A (zh
Inventor
孙向辉
张安利
金薇
孙继亮
张洪刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daqing Petroleum Administration Bureau
Original Assignee
Daqing Petroleum Administration Bureau
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daqing Petroleum Administration Bureau filed Critical Daqing Petroleum Administration Bureau
Priority to CN2007101498921A priority Critical patent/CN101125994B/zh
Publication of CN101125994A publication Critical patent/CN101125994A/zh
Application granted granted Critical
Publication of CN101125994B publication Critical patent/CN101125994B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种机械装备环保耐酸防腐涂料。该机械装备环保耐酸防腐涂料各组分按重量份配比，腰果酚改性酚醛树脂520份、醇酸树脂230份、金红石钛白粉160份、200#溶剂油73份、润湿剂8份、抗沉分散剂5份、消泡剂PerenolR2份、高效复合催干剂1.5份及防结皮剂0.5份。该防腐涂料具有环保、耐酸及耐磨的特点。

Description

一种机械装备环保耐酸防腐涂料
技术领域：
本发明涉及一种防腐涂料，尤其是一种机械装备环保耐酸防腐涂料。
背景技术：
随着人们对环境、绿色产品的逐步重视，国家在2002年颁布了有害物质限量的强制性技术标准(GB18581-2001)，规定要求挥发性有机化合物VOC(g/L)小于550，苯百分含量小于0.5，甲苯和二甲苯总和的百分含量小于10，传统上防腐涂料在上述指标方面均不能达标。机械装备环保耐酸防腐漆要求符合1994年日本涂料工业协会JIS标准，也符合美国联邦(Code Of Federal Regulation 1302.3)标准要求，重金属铬含量小于0.03％，铅含量小于0.06％，涂刷温度在-10℃以上。
发明内容：
为了克服背景技术中的不足，本发明提供一种机械装备环保耐酸防腐涂料。该防腐涂料具有环保、耐酸及耐磨的特点。
本发明的采用的技术方案是：该机械装备环保耐酸防腐涂料的各组分按重量份配比：腰果酚改性酚醛树脂520份、醇酸树脂230份、金红石钛白粉160份、200#溶剂油73份、润湿剂8份、抗沉分散剂5份、消泡剂PerenolR2份、高效复合催干剂1.5份及防结皮剂0.5份。
本发明具有如下有益效果：该机械装备环保耐酸防腐涂料主要以腰果酚改性酚醛树脂为主要成膜物质，钛白粉、超细硫酸钡、超细重钙等填料，配以一些不含铅、铬、镉、汞等重金属的催干剂、颜料和功能助剂加工而成。腰果酚改性酚醛树脂能够溶于200#石油溶剂、二甲苯、松节油等有机溶剂。由于酚醛树脂漆能耐一定浓度的硫酸、盐酸、醋酸和磷酸，和大多数盐类和有机溶剂等介质腐蚀，在硬度、光泽、快干、耐磨、耐热、耐水、耐弱碱、以及抗老化等方面有较好的性能，所以可广泛应用于石油贮罐、化工设备、桥梁、各种交通车辆底盘、船舶水线以上建筑物、钢结构、高架铁塔、暖气片、机械设备等方面。与其它工业重防腐涂料(环氧、丙烯酸、聚氨酯类)相比较，具有较高的性价比。该防腐涂料使用温度可达180℃，耐磨性大于5000次，醇酸树脂漆使用温度小于90℃，耐磨性小于3500次。在耐盐水、耐无机酸、耐氧化性酸、外用耐久性等方面均优于醇酸树脂漆。酚醛树脂漆施工方便，金属表面无须底漆准备。符合国家在2002年颁布了有害物质限量的强制性技术标准(GB18581-2001)，符合1994年日本涂料工业协会JIS标准，符合美国联邦(Code Of FederalRegulation 1302.3)标准要求，重金属铬含量小于0.03％，铅含量小于0.06％，涂刷温度在-10℃以上。
具体实施方式：
下面结合实施例对本发明作进一步说明：
实施例1、将腰果酚改性酚醛树脂520公斤、醇酸树脂230公斤、金红石钛白粉160公斤、200#溶剂油73公斤、润湿剂8公斤、抗沉分散剂5公斤、消泡剂PerenolR2公斤、高效复合催干剂1.5公斤及防结皮剂0.5公斤混合制得本发明的防腐涂料。
机械装备环保耐酸防腐涂料原料见表1
表1
  序号   原材料名称   规格型号   生产厂家
1   腰果酚改性酚醛树脂 KP-208 上海黄渡助剂厂
  2   醇酸树脂   160公斤/桶   奥维涂料
  3   金红石钛白粉   R-930   美国杜邦
  5   润湿剂   RF-106   三东省安丘市润丰有机化工厂
  6   抗沉分散剂   ZW-2   三东省安丘市润丰有机化工厂
  7   消泡剂Perenol<sup>R</sup>   AMH<sub>2</sub>   海川化工
  8   高效复合催干剂   TG B<sub>2</sub>   沈阳市应用技术实验厂
  9   防结皮剂   甲乙酮肟   沈阳市应用技术实验厂
上述的KP-208漆用酚醛树脂是由工业腰果壳液(简称CNSL，分子式C15H27)作为主要原料，经过处理后，再加入桐油等原料，经醇解、酯化合成得到的腰果酚改性酚醛树脂；高效复合催干剂是氧化聚合型催干剂，取代钴、锰、铅、锌、钙催干剂，简化生产工艺，降低涂料中重金属含量。
对上述防腐涂料进行性能实验：
(1)符合国家在2002年颁布了有害物质限量的强制性技术标准(GB18581-2001)，符合1994年日本涂料工业协会JIS标准，也符合美国联邦(Code Of Federal Regul ation 1302.3)标准要求，重金属铬含量小于0.03％，铅含量小于0.06％，涂刷温度在-10℃以上。
(2)机械装备环保耐酸防腐漆使用温度可达180℃(检测标准GB1735-79)，耐磨性大于5000次(检测标准GB1768-79)；醇酸树脂漆使用温度小于90℃，耐磨性小于3500次。
(3)耐酸实验：实验结果见表2。
表2
  检测项目   检测要求   检测标准
  10％H<sub>2</sub>SO<sub>4</sub>溶液   48h小时无变化   GB1763-79
  检测项目   检测要求   检测标准
  10％HCI溶液   48h小时无变化   GB1763-79
  37％甲醛溶液   48h小时无变化   GB1763-79
  3.5％NaCI溶液   96h小时无变化   GB1763-79
  机油   96h小时无变化   GB1763-79
  热水(≤60℃)   96h小时无变化   GB1763-79
  海水   48h小时无变化   GB1763-79
  90#汽油   96h小时无变化   GB1763-79
  啤酒   96h小时无变化   GB1763-79
由表2可以看出：本发明的防腐涂料耐一定浓度的硫酸、盐酸、醋酸和硝酸，和大多数盐类和有机溶剂等介质的腐蚀。

Claims (1)

1.一种机械装备环保耐酸防腐涂料，其特征在于：下列各组分按重量份配比，腰果酚改性酚醛树脂520份、醇酸树脂230份、金红石钛白粉160份、200#溶剂油73份、润湿剂8份、抗沉分散剂5份、消泡剂PerenolR2份、型号为TG B2的高效复合催干剂1.5份及防结皮剂0.5份。
CN2007101498921A 2007-09-21 2007-09-21 一种机械装备环保耐酸防腐涂料 Expired - Fee Related CN101125994B (zh)