CN101125435A - Technology for producing parquet wood composite floor and its product - Google Patents
Technology for producing parquet wood composite floor and its product Download PDFInfo
- Publication number
- CN101125435A CN101125435A CNA2007102016610A CN200710201661A CN101125435A CN 101125435 A CN101125435 A CN 101125435A CN A2007102016610 A CNA2007102016610 A CN A2007102016610A CN 200710201661 A CN200710201661 A CN 200710201661A CN 101125435 A CN101125435 A CN 101125435A
- Authority
- CN
- China
- Prior art keywords
- product
- wood composite
- composite floor
- production technology
- parquet wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a manufacturing technique of matched wood composite floor. The method comprises grooving a substrate (1) with common technique, which comprises the following steps: a. the substrate (1), a dash board (2) and a base board (3) are coated for assembly so as to obtain A product; b. combined design and shape are done to A product by a hot-press so as to obtain B product; c. hot pressing to B product is done for molding so as to obtain C product; d. the health of C product is preserved so as to obtain D product; e. D product is trimmed for precisely sanding so as to obtain E product; f. E product is led into a paint line for painting so as to obtain the finished product. The matching structure of the present invention is rich, with low requirement of material choice, high utilization rate of material, steady state of product use, non-easy deformation, good stability between units, and good durability and aesthetic effect. The product has easy manufacturing and operation, low manufacturing cost, high production efficiency and steady quality of product; moreover, the floor has clear wood grain and ideal paint film, and is bright and smooth, clean and aesthetic.
Description
Technical field
The present invention relates to a kind of timber floor production technology and products thereof, belong to the woodwork technical field of producing.
Background technology
Parquet floor can embody comparatively complicated graceful pattern and be subjected to liking of people, but the fiber of parquets unit is long in the conventional parquet floor, stressed back easy deformation, and selection requires complicated, the parquets structure is comparatively dull, and the leftover pieces of unit timber can't re-use, and the parquets unit is subjected to weather and temperature effect to occur the crack easily simultaneously, between the unit with the passing of service time will come out rough situation, durability and the considerable restraint that all has been subjected to attractive in appearance.
Summary of the invention
The objective of the invention is to: production technology of a kind of parquet wood composite floor and products thereof is provided, and its parquets structure is abundant, and selection requires low, the stock utilization height, the behaviour in service of product is stable, and is not yielding, good stability between the unit, durability and aesthetic are good.
The present invention is achieved in that the production technology of parquet wood composite floor, and it comprises slots base material 1 usefulness common process, may further comprise the steps;
A, will base material 1, carry out assembly behind dash board 2 and base plate 3 gluings, the A product;
B, adopt hot press to carry out parquets, typing the A product, the B product;
C, the B product are carried out hot-forming, the C product;
D, the C product are carried out health, the D product;
E, will the D product carry out washed ore light behind the saw limit, the E product;
F, the E product imported painted line carry out japanning processing, finished product.
The production technology of above-mentioned parquet wood composite floor, the material of base material 1 are that eucalyptus is assorted, and the material of dash board 2 be that science and technology is wooden, and the material of base plate 3 is a weedtree.
The production technology of aforesaid parquet wood composite floor, among the step c, hot-forming pressure is 550～650 tons, and hot pressing time is 6～10 minutes, and hot pressing temperature is 110～130 ℃.
The production technology of aforesaid parquet wood composite floor, in the steps d, the conditioned time of C product is 5～9 days.
The production technology of aforesaid parquet wood composite floor, among the step f, japanning is processed as the processing of UV leaching paint.
Parquet wood composite floor, its formation comprises base material 1, and base material 1 top is dash board 2, and its bottom is a base plate 3; Dash board 2 rearranges for some parquets pieces 4.
Compared with prior art, parquets structure of the present invention is abundant, and selection requires low, the stock utilization height, the behaviour in service of product is stable, and is not yielding, good stability between the unit, durability and aesthetic are good, and this production is easy, easy to implement, production cost is low, production efficiency height, constant product quality, the wood grain on floor is clear, paint film is plentiful, and is bright smooth, clean attractive in appearance.
Description of drawings
Fig. 1 is the parquet wood composite floor structural representation.
The specific embodiment
Embodiments of the invention 1: the production technology of parquet wood composite floor, it comprises slots base material 1 usefulness common process, may further comprise the steps: with material is the assorted base material 1 of eucalyptus, material for the dash board 2 of science and technology wood and material are to carry out assembly behind base plate 3 gluings of weedtree, the A product; Adopt hot press to carry out parquets, typing the A product, get the B product; It is 600 tons that the B product are carried out hot-forming, hot-forming pressure, and hot pressing time is 8 minutes, and hot pressing temperature is 120 ℃, gets the C product; The C product are carried out health, and conditioned time is 7 days, gets the D product; To carry out washed ore light behind the D product saw limit, get the E product; The E product are imported painted line carry out the processing of UV leaching paint, get finished product.
In this example the structure of parquet wood composite floor as shown in Figure 1, its constitutes and to comprise base material 1, base material 1 top is dash board 2, its bottom is a base plate 3; Dash board 2 rearranges for some parquets pieces 4.
It is that material is made timber floor that the present invention adopts assorted, the scientific and technological wood of eucalyptus, weedtree, they are obtained easily and obtain, the wide material sources of material, production cost is low, helps environmental protection, product adopts hot press to carry out parquets, typing, the mode of parquets is similar to the printing technique of ceramic tile, such production efficiency height, and the parquets kind is abundant, make the parquets sound construction, not yielding; Hot-forming pressure is 600 tons, and hot pressing time is 8 minutes, and hot pressing temperature is 120 ℃, and the hot-forming floor pressurized that makes that carries out under such technology is abundant, and don't can influence the surface quality on floor; Conditioned time is 7 days, can fully eliminate the stress after the hot pressing, and glue is fully solidified; The processing of UV leaching paint can make the floor surface clean mark, and paint film is plentiful, and is bright smooth.
Claims (6)
1. the production technology of parquet wood composite floor, it comprises slots base material (1) with common process, it is characterized in that: may further comprise the steps;
A, will base material (1), carry out assembly behind dash board (2) and base plate (3) gluing, the A product;
B, adopt hot press to carry out parquets, typing the A product, the B product;
C, the B product are carried out hot-forming, the C product;
D, the C product are carried out health, the D product;
E, will the D product carry out washed ore light behind the saw limit, the E product;
F, the E product imported painted line carry out japanning processing, finished product.
2. the production technology of parquet wood composite floor according to claim 1 is characterized in that: the material of base material (1) is that eucalyptus is assorted, and the material of dash board (2) be that science and technology is wooden, and the material of base plate (3) is a weedtree.
3. the production technology of parquet wood composite floor according to claim 1, it is characterized in that: among the step c, hot-forming pressure is 550～650 tons, and hot pressing time is 6～10 minutes, and hot pressing temperature is 110～130 ℃.
4. the production technology of parquet wood composite floor according to claim 1, it is characterized in that: in the steps d, the conditioned time of C product is 5～9 days.
5. the production technology of parquet wood composite floor according to claim 1 is characterized in that: among the step f, japanning is processed as the processing of UV leaching paint.
As the production technology of any described parquet wood composite floor of claim of claim 1 to 5 made parquet wood composite floor, it is characterized in that: its formation comprises base material (1), base material (1) top is dash board (2), and its bottom is base plate (3); Dash board (2) rearranges for some parquets pieces (4).