CN101117490A - 以有机和无机成膜物与水泥配制成的防水涂料制作工艺 - Google Patents
以有机和无机成膜物与水泥配制成的防水涂料制作工艺 Download PDFInfo
- Publication number
- CN101117490A CN101117490A CNA2006100151863A CN200610015186A CN101117490A CN 101117490 A CN101117490 A CN 101117490A CN A2006100151863 A CNA2006100151863 A CN A2006100151863A CN 200610015186 A CN200610015186 A CN 200610015186A CN 101117490 A CN101117490 A CN 101117490A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- cement
- organic
- cooled
- natural temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种以有机和无机两种成膜物与水泥及添加剂配制成的防水涂料制作工艺,首先将50公斤水放入反应釜中,加热后放入3公斤聚乙烯醇边加热边搅拌,在60℃溶解1小时,待其完全溶解后,冷却至自然温度,加入0.5公斤乙二醛,继续搅拌20分钟,再缓慢升温至80℃,再冷却至自然温度,依次加入5公斤六偏磷酸钠、4公斤硅溶胶、0.5公斤三氯化铁,搅拌至充分溶解装入容器中密封即可;将50公斤水泥、20公斤滑石粉、5公斤膨胀粉充分混合均匀装袋即可。本发明具有以下优点:无三废污染,防水性能可靠,成本低。
Description
技术领域
本发明涉及一种以有机和无机成膜物与水泥配制成的防水涂料制作工艺。
背景技术
现有的建筑防水材料,有机抗老化差,使用年限短,价格高,污染环境;无机韧性差,没有抗裂变能力,自重过大,防水效果不理想。均因功能单一,使用范围受到限制。
发明内容
本发明的目的在于克服上述的缺陷,提供一种以有机和无机成膜物与水泥配制成的防水涂料制作工艺。
本发明的技术方案是:一种以有机和无机两种成膜物与水泥及添加剂配制成的防水涂料制作工艺,其特征在于:聚乙烯醇2%、乙二醛1%、六偏磷酸钠0.5%、三氯化铁0.5%、硅溶胶4%、水92%;普通硅酸盐水泥60%、滑石粉30%、膨胀粉10%,将水放入反应釜中,加热后放入聚乙烯醇边加热边搅拌,在70-90℃下溶解1小时,待其完全溶解后,冷却至自然环境温度,加入乙二醛,继续搅拌20分钟,再缓慢升温至50℃,然后再冷却至自然温度,依次加入六偏磷酸钠、硅溶胶、三氯化铁,搅拌至充分溶解即可;将水泥、滑石粉、膨胀粉充分混合均匀即可。
本发明具有以下优点:无三废污染,防水性能可靠,成本低。
具体实施方式
实施例:一种以有机和无机两种成膜物与水泥及添加剂配制成的防水涂料制作工艺,首先将50公斤水放入反应釜中,加热后放入3公斤聚乙烯醇边加热边搅拌,在60℃溶解1小时,待其完全溶解后,冷却至自然温度,加入0.5公斤乙二醛,继续搅拌20分钟,再缓慢升温至80℃,再冷却至自然温度,依次加入5公斤六偏磷酸钠、4公斤硅溶胶、0.5公斤三氯化铁,搅拌至充分溶解装入容器中密封即可;将50公斤水泥、20公斤滑石粉、5公斤膨胀粉充分混合均匀装袋即可。
Claims (1)
1.一种以有机和无机两种成膜物与水泥及添加剂配制成的防水涂料制作工艺,其特征在于:首先将50公斤水放入反应釜中,加热后放入3公斤聚乙烯醇边加热边搅拌,在60℃溶解1小时,待其完全溶解后,冷却至自然温度,加入0.5公斤乙二醛,继续搅拌20分钟,再缓慢升温至80℃,再冷却至自然温度,依次加入5公斤六偏磷酸钠、4公斤硅溶胶、0.5公斤三氯化铁,搅拌至充分溶解装入容器中密封即可;将50公斤水泥、20公斤滑石粉、5公斤膨胀粉充分混合均匀装袋即可。