CN101104736B - 一种阻燃增强型pa66组合物 - Google Patents

一种阻燃增强型pa66组合物 Download PDF

Info

Publication number
CN101104736B
CN101104736B CN 200610028821 CN200610028821A CN101104736B CN 101104736 B CN101104736 B CN 101104736B CN 200610028821 CN200610028821 CN 200610028821 CN 200610028821 A CN200610028821 A CN 200610028821A CN 101104736 B CN101104736 B CN 101104736B
Authority
CN
China
Prior art keywords
flame retardant
composition
weight
parts
flame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 200610028821
Other languages
English (en)
Other versions
CN101104736A (zh
Inventor
朱江磊
陈永东
张祥福
周文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Pret Composites Co Ltd
Zhejiang Pret New Materials Co Ltd
Chongqing Pret New Materials Co Ltd
Original Assignee
PULIT COMPOSITE MATERIAL CO Ltd SHANGHAI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PULIT COMPOSITE MATERIAL CO Ltd SHANGHAI filed Critical PULIT COMPOSITE MATERIAL CO Ltd SHANGHAI
Priority to CN 200610028821 priority Critical patent/CN101104736B/zh
Publication of CN101104736A publication Critical patent/CN101104736A/zh
Application granted granted Critical
Publication of CN101104736B publication Critical patent/CN101104736B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及的一种阻燃增强型PA66组合物，由PA66基础树脂、玻纤、主阻燃剂、辅助阻燃剂三氧化二锑、增韧剂马来酸酐接枝POE、稳定剂、润滑剂硬脂酸以及抗氧剂受阻酚类和亚磷酸酯类组成，其特征在于：所用的主阻燃剂为分子量10000以上的溴化环氧树脂，所用的稳定剂是水滑石；各组成物的掺入量分别是：PA66基础树脂430～530重量份、玻纤200～300重量份、主阻燃剂180～200重量份、辅助阻燃剂40～50重量份、增韧剂20～40重量份、稳定剂5～10重量份、润滑剂2～5重量份、抗氧剂4～9重量份。阻燃增强尼龙组合物，由于不仅具有刚性高、耐热性和尺寸稳定性好的特点、并且具备良好的加工性，可作为塑壳断路器等低压电器壳体的适用材料。

Description

一种阻燃增强型PA66组合物
技术领域
本发明涉及一种阻燃增强型PA66组合物，属于高分子合金领域。
背景技术
由于尼龙具有优良的力学强度、耐磨性、自润滑性、耐腐蚀性和较好的成型加工性，但耐热性和低温条件下的耐冲击强度不足，尺寸稳定性和电性能方面的缺陷，使它的推广使用受到一定的局限。近些年以来，随着尼龙改性技术的进展，作为电器元部件专用材料中的新材料，不仅要求其刚性高、耐热性和尺寸稳定性好、并且需要良好的加工性以及阻燃性，所以阻燃增强型PA66有很大的市场前景。
同时，由于增强型PA66的加工温度很高，所以要求用于增强型PA66的阻燃剂要有很好的耐热性，目前常用的阻燃剂主要有溴化聚苯乙烯，十溴二苯醚，十溴二苯乙烷，焦磷酸三聚氰胺，红磷等。但这些阻燃剂要么价格昂贵，要么加工困难，要么颜色不佳，都有自己的缺点。
发明内容
本发明目的：旨在提供一种具有优异机械性能，良好外观的阻燃增强型PA66组合物。
本发明的上述目的可以通过以下技术方案实现：
这种阻燃增强型PA66组合物，由PA66基础树脂、玻纤、主阻燃剂、辅助阻燃剂三氧化二锑、增韧剂马来酸酐接枝POE、稳定剂、润滑剂硬脂酸钙以及抗氧剂受阻酚类和亚磷酸酯类组成，其特征在于：所用的主阻燃剂为分子量10000以上的溴化环氧树脂，所用的稳定剂是水滑石；各组成物的掺入量分别是：PA66基础树脂430～530重量份、玻纤200～300重量份、主阻燃剂180～200重量份、辅助阻燃剂40～50重量份、增韧剂20～40重量份、稳定剂5～10重量份、润滑剂2～5重量份、抗氧剂4～9重量份。
所用的PA66基础树脂的黏度在2.4—3.2。
所用玻纤为经偶联剂处理过的无捻粗纱。
所用的辅助阻燃剂为粒径在0.3—0.5微米的超细三氧化二锑。
所用的增韧剂为马来酸酐接枝EPDM或POE。
所用的稳定剂为日本或大连海晨化工生产的水滑石。
所用的润滑剂为脂肪酸或脂肪肽胺类。
所用的润滑剂为硬脂酸盐类中的锌、钙、铝的二价金属盐或三价金属盐。
所用的受阻酚类抗氧剂是1076、1098或1010。
所用的亚磷酸酯类抗氧剂是168或626。
根据以上技术方案提出的阻燃增强尼龙组合物，由于不仅具有刚性高、耐热性和尺寸稳定性好的特点、并且具备良好的加工性以及阻燃性，所以可作为塑壳断路器等低压电器壳体、接线盒、接插件、开关等电子电气零部件产品的材料，尤其适合作为塑壳断路器等低压电器壳体的材料。
具体实施方式
以下给出本发明的实施例，并进一步阐述本发明。
实施例1～3的配方
 
对照例 实施例1 实施例2 实施例3
基础树脂 PA66 480 530 440 430
玻纤 GF 300 200 300 300
阻燃剂 十溴二苯乙烷 120
主阻燃剂 溴化环氧树脂 200 180 180
辅助阻燃剂 三氧化二锑 40 50 40 40
增韧剂 MAH—POE 30 20 30 40
稳定剂 水滑石 10 5 7 10
润滑剂 硬脂酸钙 5 2 4 5
抗氧剂 1098 2 2 3 4
抗氧剂 168 3 5 3 2
在实际生产中，这种阻燃增强型PA66组合物，所用PA66基础树脂黏度为2.4—3.2，优选为2.8-3.2。如Dupont，优选为2.8-3.2。如Dupont，Basf，平顶山神马生产的产品。
所用主阻燃剂为以色列死海溴公司生产的分子量10000以上的溴化环氧树脂，如3100，2100H，2400等。
所用辅助阻燃剂为粒径0.3—0.5微米的超细三氧化二锑。
所用增韧剂为马来酸酐接枝POE，EPDM，PP中的一种。
所用稳定剂为日本协和及大连海晨化工生产的水滑石中的一种。
所用的润滑剂为脂肪酸、硬脂酸盐类或脂肪酸胺类，所述的硬脂酸盐类为锌、钙、铝各类二价金属盐或三价金属盐。
所用的抗氧剂可选择有机受阻酚类、胺类、亚磷酸酯类等抗氧剂，可为一种或两种，受阻酚类为1076，1098，1010等，亚磷酸酯类为168，626等。
本发明所述的阻燃增强尼龙组合物可选择双螺杆挤出机，一般加工温度范围可控制在240—250℃之间。
本发明所述的阻燃增强尼龙组合物可作为塑壳断路器等低压电器壳体、接线盒、接插件、开关等电子电气零部件产品的材料，尤其适合作为塑壳断路器等低压电器壳体的材料。
下面实施例进一步描述本发明，但所述实施例仅用于说明本发明而不是限制本发明。
PA66树脂和各种添加剂经高混机高速混匀后，经双螺杆挤出机进行熔融挤出，玻纤由侧向玻纤加料口加入，再经过冷却造粒就可得该组合物，工艺温度为240—250℃。对照例加工温度250—260度。采用下列物料：
PA66 平顶山神马生产，牌号EPR27
玻纤 巨石集团生产，牌号ER—13
溴化环氧树脂 死海溴 牌号3100
十溴二苯乙烷 美国雅宝 牌号8010
三氧化二锑 上海涵丰化工
MAH—POE 自制
水滑石 大连海晨化工 DHT-4A型
硬脂酸钙 上海嘉卓化工
抗氧剂1098 瑞士Ciba生产的Irganox1098
抗氧剂168 瑞士Ciba生产的Irganox168
拉伸强度根据ASTMD638测试。
弯曲强度和模量按ASTMD790测试。
冲击强度和缺口冲击强度按ASTMD256测试。
热变形温度按ASTMD1525测试
根据美国UL94标准测试垂直燃烧性能。
所得材料的测试结果如下：
 
对照例 实施例1 实施例2 实施例3
拉伸强度(MPa) 150 125 144 145
弯曲强度(MPa) 220 180 208 210
弯曲模量(MPa) 8700 7000 8100 8200
冲击强度(KJ/m2) 50 50 65 55
缺口冲击强度(KJ/m2) 10 9.5 11 10.5
热变形温度1.82MPa 242 210 238 238
阻燃性UL94，1.6mm V0 V0 V0 V0
颜色 很黄 白 稍黄 白
由上表知实施例与对照例相比机械性能稍有下降，但实施例有好的外观，证明溴化环氧树脂和水滑石确实对阻燃增强PA66有效，而且溴化环氧树脂的加入提高了流动性，使加工温度下降了10—20度，降低了生产成本，提高了生产率。

Claims (7)

1.一种阻燃增强型PA66组合物，由PA66基础树脂、玻纤、主阻燃剂、辅助阻燃剂三氧化二锑、增韧剂马来酸酐接枝POE、稳定剂、润滑剂硬脂酸钙以及抗氧剂受阻酚类和亚磷酸酯类组成，其特征在于：所用的主阻燃剂为分子量10000以上的溴化环氧树脂，所用的稳定剂是水滑石；各组成物的掺入量分别是：PA66基础树脂430～530重量份、玻纤200～300重量份、主阻燃剂180～200重量份、辅助阻燃剂40～50重量份、增韧剂20～40重量份、稳定剂5～10重量份、润滑剂2～5重量份、抗氧剂4～9重量份。
2.如权利要求1所述的一种阻燃增强型PA66组合物，其特征在于：所用的PA66基础树脂的黏度在2.4-3.2。
3.如权利要求1所述的一种阻燃增强型PA66组合物，其特征在于：所用玻纤为经偶联剂处理过的无捻粗纱。
4.如权利要求1所述的一种阻燃增强型PA66组合物，其特征在于：所用的辅助阻燃剂为粒径在0.3-0.5微米的超细三氧化二锑。
5.如权利要求1所述的一种阻燃增强型PA66组合物，其特征在于：所用的稳定剂为日本或大连海晨化工生产的水滑石。
6.如权利要求1所述的一种阻燃增强型PA66组合物，其特征在于：所用的受阻酚类抗氧剂是1076、1098或1010。
7.如权利要求1所述的一种阻燃增强型PA66组合物，其特征在于：所用的亚磷酸酯类抗氧剂是168或626。
CN 200610028821 2006-07-11 2006-07-11 一种阻燃增强型pa66组合物 Active CN101104736B (zh)