CN101082128B - 多功能环保金属除油除锈防锈液 - Google Patents
多功能环保金属除油除锈防锈液 Download PDFInfo
- Publication number
- CN101082128B CN101082128B CN2007100290199A CN200710029019A CN101082128B CN 101082128 B CN101082128 B CN 101082128B CN 2007100290199 A CN2007100290199 A CN 2007100290199A CN 200710029019 A CN200710029019 A CN 200710029019A CN 101082128 B CN101082128 B CN 101082128B
- Authority
- CN
- China
- Prior art keywords
- sodium
- rust
- water
- environment protection
- protection metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种多功能环保金属除油除锈防锈液,其特殊之处在于:包括下列组分制成:聚氧乙烯烷基醚、十二烷基磺酸钠、1.3—二丁基硫脲、六次甲基四胺、磷酸二氢锌、磷酸、丁基萘磺酸钠、丁二酸酯磺酸钠、三乙醇胺、碳酸氢钠、酒石酸、1.3—二乙基硫脲。按比例称取上原料,固体原料用水溶解成溶液,液体原料用水稀释,然后将原料分别投入到反应釜中,搅拌15~30分钟,经120目纱网过滤,即制成成品。由于各成分的协同作用,它不仅适应流水线作业,对金属表面进行一次性除油、除锈、磷化、钝化和防锈,而且对人体无害,对环境无污染。
Description
技术领域
本发明涉及金属表面处理技术领域,尤其是一种对金属材料及其制品的表面进行表面预处理的除油除锈液。
背景技术
目前现有技术,金属表面的除油除锈基本运用人工、物理和化学三种方法,人工除油除锈劳动强度大,效率低且不能完全彻底除油除锈,余存大量的空白点,影响产品质量,且产生大量的粉尘,污染环境,危害劳动者健康;物理除锈,主要是超声波的除油除锈作用,由于投资大,应用范围不普遍;化学除油除锈是金属表面处理最普通也最经济的方法,传统的除油是用强碱NaOH和四氯乙烯处理,除锈用强酸如HCl和H2SO4进行,这些原料是强腐蚀、强刺激性物质,对人体可造成严重损害,存在安全隐患,必须谨慎小心,且强酸、强碱的废水排放,将会严重污染水源和环境。鉴于强酸、强碱除油除锈的缺陷,国内外纷纷研究生产出金属材料表面处理的化学除油除锈液。如申请号为88100060的除锈钝化剂,其组成为:磷酸、磷酸二氢锌、草酸、硝酸锌、聚乙二醇苯基烷基醚、六次甲基四胺和水组成。这种除锈钝化剂,主要功能是除锈和钝化,除油效果差,且使用时加热温度高(60~80℃)浪费能源,且生产成本高。
申请号为CN86107238A中,公开了一种除油除锈防锈剂,组成为:铝粉、氢氧化钠、六次甲四胺、聚氧乙烯脂肪醇醚、环氧乙烷、磷酸和水。这种防锈剂,简化了金属表面处理的工艺过程,但该配方中环氧乙烷是有毒物质,易燃易爆,对环境造成污染,不利安全生产。
发明内容
本发明的目的是:提供一种多功能环保金属除油除锈防锈液,它不仅适应流水线作业,对金属表面进行一次性除油、除锈、磷化、钝化和防锈,而且对人体无害,对环境无污染。
本发明是这样实现的:一种多功能环保金属除油除锈防锈液其特殊之处在于:包括下列组分制成(用量为重量份)
聚氧乙烯烷基醚 1~6 十二烷基磺酸钠 1~8
1.3-二丁基硫脲 0.5~10 六次甲基四胺 0.5~5
磷酸二氢锌 1~10 磷酸 10~40
丁基萘磺酸钠 0~5 丁二酸酯磺酸钠 0~5
三乙醇胺 0~8 碳酸氢钠 0~5
酒石酸 0~10 1.3-二乙基硫脲 0~10
水 20~75。
原料采用工业一级品。
按比例称取上原料,固体原料用水溶解成溶液,液体原料用水稀释,然后将原料分别投入到反应釜中,搅拌15~30分钟,经120目纱网过滤,即制成成品。水温25~75℃。
本发明一种多功能环保金属除油除锈防锈液,磷酸起除锈和磷化作用;酒石酸起除锈及络合作用;三乙醇胺起除油作用;碳酸氢钠起除油缓蚀作用;磷酸二氢锌起加速除锈过程和钝化作用;六次甲基四胺起增加磷化液渗透性、起缓蚀防锈作用;1.3-二丁基硫脲起除油和缓蚀钝化作用,并避免金属氢脆;1.3-二乙基硫脲,起除油、缓蚀、钝化和防锈作用,并且避免金属氢脆;丁二酸酯磺酸钠、丁基萘磺酸钠起加速渗透作用、催化除油和加速除锈过程;十二烷基苯磺酸钠起除油、除锈促进形成钝化膜起防锈作用;聚氧乙烯烷基醚具有去油污功能。
本发明配方配比制成的多功能环保金属除油除锈防锈液,由于各成分的协同作用,(一)不含强酸、强碱,不会对金属材料造成过度腐蚀及氢脆,原料无毒无害,无易燃、易爆的危险;(二)可循环使用,不污染环境和水源;(三)在常温下,金属表面处理时间5~25分钟即可,如果加温到45~60℃,处理效果更好:(四)在加工过程中可替代车间底漆,经过处理的金属材料,在室内保留三个月以上不生锈;(五)使通常需要多个工序的工作,由一个工序即可完成,降低了劳动强度,提高了工作效率。
具体实施方式
下面对本发明作进一步描述。
实施例1
一种多功能环保金属除油除锈防锈液其特殊之处在于:包括下列组分制成(用量为重量份)。
聚氧乙烯烷基醚 1 十二烷基磺酸钠 1
1.3-二丁基硫脲 0.5 六次甲基四胺 0.5
磷酸二氢锌 1 磷酸 10
水 20
按比例称取上述原料,用水将固体溶解成溶液,对液体进行稀释,然后将各种原料分别投入到反应釜中,搅拌15~30分钟,120目纱网过滤,即制成成品。水温25℃。
实施例2
聚氧乙烯烷基醚 4 十二烷基磺酸钠 5
1.3-二丁基硫脲 6 六次甲基四胺 3
磷酸二氢锌 6 磷酸 25
丁基萘磺酸钠 3 丁二酸酯磺酸钠 3
三乙醇胺 5 碳酸氢钠 3
酒石酸 7 1.3-二乙基硫脲 5
水 50。
按比例称取上述原料,用水将固体溶解成溶液,对液体进行稀释,然后将各种原料分别投入到反应釜中,搅拌15~30分钟,120目纱网过滤,即制成成品。水温50℃。
实施例3
聚氧乙烯烷基醚 6 十二烷基磺酸钠 8
1.3-二丁基硫脲 10 六次甲基四胺 5
磷酸二氢锌 10 磷酸 40
丁基萘磺酸钠 5 丁二酸酯磺酸钠 5
三乙醇胺 8 碳酸氢钠 5
酒石酸 10 1.3-二乙基硫脲 10
水 75。
按比例称取上原料,固体原料用水溶解成溶液,然后将原料分别投入到反应釜中,搅拌15~30分钟,经120目纱网过滤,即制成成品。水温25~75℃。
Claims (2)